CN106077391A - A kind of process of steel alloy forging - Google Patents
A kind of process of steel alloy forging Download PDFInfo
- Publication number
- CN106077391A CN106077391A CN201610603721.0A CN201610603721A CN106077391A CN 106077391 A CN106077391 A CN 106077391A CN 201610603721 A CN201610603721 A CN 201610603721A CN 106077391 A CN106077391 A CN 106077391A
- Authority
- CN
- China
- Prior art keywords
- steel alloy
- forging
- heated
- incubated
- mould
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides the process of a kind of steel alloy forging, comprise the steps: 1) steel alloy is warming up in box type heater 180 DEG C, carry out being incubated 20 min, spray lubricant, the blank after spraying is dried 15min in 100 DEG C of environment；2) steel alloy and mould are heated separately to 1200 and 1500 DEG C, heat 20 min, soaking 10 min；3) again mould being heated to 950 DEG C, mold cavity location put into by the steel alloy that would be heated to 950 DEG C, is incubated 10 min；4) the forging post processing of air cooling is used.The process of a kind of steel alloy forging that the present invention provides, by experimental results demonstrate, using the method stock utilization is 60%, visible, the improvement of technique can be significantly increased stock utilization, reduce and machine man-hour, for meeting the high-tech areas such as Aero-Space, the demand of titanium alloy fine forging is laid a good foundation.
Description
Technical field
The present invention relates to steel technical field, particularly relate to the process of a kind of steel alloy forging.
Background technology
Steel and iron industry is from forming the development having obtained till now advancing by leaps and bounds, and in these steel, considerable quantity is through machine
Field and the occasion of all trades and professions is served in tool processing with the form of part.Along with the cutting speed of machining is increasingly faster,
The technique of steel be it is also proposed higher requirement.
Summary of the invention
For solving the problems referred to above present in prior art and practical situation, the invention provides the forging of a kind of steel alloy
Process, it is characterised in that comprise the steps:
1) steel alloy is warming up in box type heater 180 DEG C, carries out being incubated 20 min, spray lubricant,
Blank after spraying is dried 15min in 100 DEG C of environment；
2) steel alloy and mould are heated separately to 1200 and 1500 DEG C, heat 20 min, soaking 10 min；
3) again mould being heated to 950 DEG C, mold cavity location put into by the steel alloy that would be heated to 950 DEG C, is incubated 10 min；
4) the forging post processing of air cooling is used.
Beneficial effect:
The process of a kind of steel alloy forging that the present invention provides, by experimental results demonstrate, uses the method material use
Rate is 60%, it is seen then that the improvement of technique can be significantly increased stock utilization, reduces and machines man-hour, for meeting Aero-Space
Etc. high-tech area, the demand of titanium alloy fine forging is laid a good foundation.
Detailed description of the invention
Technical solution of the present invention is described in detail below.
The process of a kind of steel alloy forging, it is characterised in that comprise the steps:
1) steel alloy is warming up in box type heater 180 DEG C, carries out being incubated 20 min, spray lubricant,
Blank after spraying is dried 15min in 100 DEG C of environment；
2) steel alloy and mould are heated separately to 1200 and 1500 DEG C, heat 20 min, soaking 10 min；
3) again mould being heated to 950 DEG C, mold cavity location put into by the steel alloy that would be heated to 950 DEG C, is incubated 10 min；
4) the forging post processing of air cooling is used.
Beneficial effect:
The process of a kind of steel alloy forging that the present invention provides, by experimental results demonstrate, uses the method material use
Rate is 60%, it is seen then that the improvement of technique can be significantly increased stock utilization, reduces and machines man-hour, for meeting Aero-Space
Etc. high-tech area, the demand of titanium alloy fine forging is laid a good foundation.
Finally it is noted that the foregoing is only the preferred embodiments of the present invention, it is not limited to the present invention,
Although being described in detail the present invention with reference to previous embodiment, for a person skilled in the art, it still may be used
So that the technical scheme described in foregoing embodiments to be modified, or wherein portion of techniques feature is carried out equivalent.
All within the spirit and principles in the present invention, any modification, equivalent substitution and improvement etc. made, should be included in the present invention's
Within protection domain.
Claims (1)
1. the process of a steel alloy forging, it is characterised in that comprise the steps:
1) steel alloy is warming up in box type heater 180 DEG C, carries out being incubated 20 min, spray lubricant,
Blank after spraying is dried 15min in 100 DEG C of environment；
2) steel alloy and mould are heated separately to 1200 and 1500 DEG C, heat 20 min, soaking 10 min；
3) again mould being heated to 950 DEG C, mold cavity location put into by the steel alloy that would be heated to 950 DEG C, is incubated 10 min；
4) the forging post processing of air cooling is used.