CN1060752C - Production method of refractory material for immersed sprue - Google Patents
Production method of refractory material for immersed sprue Download PDFInfo
- Publication number
- CN1060752C CN1060752C CN97100785A CN97100785A CN1060752C CN 1060752 C CN1060752 C CN 1060752C CN 97100785 A CN97100785 A CN 97100785A CN 97100785 A CN97100785 A CN 97100785A CN 1060752 C CN1060752 C CN 1060752C
- Authority
- CN
- China
- Prior art keywords
- river
- mouth
- oxide
- sintering
- magnesium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
Description
Raw material | N | Si | Free Si | ZrO 2 | Al 2O 3 | SiO 2 | Fe 2O 3 | TiO 2 | R 2O | CaO | MgO |
Si 3N 4 | 38.07 | 57.11 | 1.7 | ||||||||
ZrSiO 4 | 64.68 | <0.10 | 33.60 | 0.12 | 0.06 | 0.072 | 0.012 | ||||
Al 2O 3 | 98.78 | 0.08 | Trace | 0.04 | / | / | |||||
SiO 2 | 0.40 | 98.19 | 0.04 | 0.06 | 0.23 | 0.18 | 0.09 |
Material of the present invention | CaO-ZrO 2-C material | O′-ZrO 2-C material | |
Anti-Al 2O 3Deposition index | 1.8 | 2.0 | 1.8 |
The anti-slagging of retractory (mm) | 0.020 | 0.020 | 0.048 |
Anti-molten steel erosion (mm/min) | 0.015 | 0.015 | 0.021 |
Claims (1)