CN106048444A - Steel low in price - Google Patents
Steel low in price Download PDFInfo
- Publication number
- CN106048444A CN106048444A CN201610417545.1A CN201610417545A CN106048444A CN 106048444 A CN106048444 A CN 106048444A CN 201610417545 A CN201610417545 A CN 201610417545A CN 106048444 A CN106048444 A CN 106048444A
- Authority
- CN
- China
- Prior art keywords
- steel
- carbon
- ferrum
- price
- oxygen
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses steel low in price. The raw materials of the steel include carbon, silicon, manganese, cerium, phosphorus, titanium, molybdenum, iron and impurities. The steel comprises, by weight percentage, 0-0.22% of carbon, 0-0.35% of silicon, 0-0.03% of manganese, 0.32-0.45% of cerium, 1-1.45% of phosphorus, 0-0.055% of titanium, 0-0.045% of molybdenum, and the balance iron and impurities. According to a smelting process of the steel, iron is smelted into the steel in a top-blown converter. Specifically, the iron and waste steel are mixed and poured into the converter, and by introducing oxygen, the oxygen is combined with the carbon in the iron to form carbon monoxide, so that the carbon is taken away. In this way, the use performance of the steel low in price is not affected, and the steel has quite good machining performance and good material strength, is wide in application, can effectively lower the production cost for enterprises and factories, and is favored by customers.
Description
Technical field
The present invention relates to Steel material field, particularly relate to the steel that a kind of price is cheap.
Background technology
Steel are that steel ingot, steel billet or steel make required variously-shaped, size and the material of performance by pressure processing
Material.Structural steel is a class of steel.Steel for building require have higher intensity, preferable plasticity at aspect of performance
With toughness and good processing characteristics.Require there is good solderability, for work at low temperatures simultaneously for Welding Structure
The steel construction made, it is desirable to steel can keep good toughness at low temperatures.For the structure worked under environment in the open, or have
The structural requirement steel worked in the environment of evil erosion medium resistance have preferable rust-proofing ability.Present steel cost is high, can increase
The production cost of enterprise, it is not easy to application.
Summary of the invention
The technical problem that present invention mainly solves is to provide the steel that a kind of price is cheap, can meet modern's need to steel
Ask.
For solving above-mentioned technical problem, the technical scheme that the present invention uses is: provide the steel that a kind of price is cheap, institute
The material composition stating steel includes carbon, silicon, manganese, cerium, phosphorus, titanium, molybdenum, ferrum and impurity, described steel by weight percentage, including former
Material composition has: carbon≤0.22%, silicon≤0.35%, manganese≤0.03%, cerium 0.32-0.45%, phosphorus 1-1.45%, titanium≤0.055%, molybdenum≤
0.045%, ferrum and impurity: surplus, ferrum is smelt steel in top-blown converter by the process for making of described steel, be specially by ferrum with
Steel scrap mixes to be poured in stove, is passed through oxygen and makes oxygen be combined into carbon monoxide with the carbon in ferrum carbon ribbon is walked.
In a preferred embodiment of the present invention, described steel by weight percentage, including material composition have: carbon
0.11%, silicon 0.18%, 0.015%, cerium 0.41%, phosphorus 1.23%, titanium 0.035%, molybdenum 0.022%, ferrum and impurity: surplus.
In a preferred embodiment of the present invention, described in be passed through the technique of oxygen for being blown into oxygen stream.
In a preferred embodiment of the present invention, the described time made steel in top-blown converter is 45-60 minute.
The invention has the beneficial effects as follows: the steel that the price of the present invention is cheap, do not affect the serviceability that steel itself has, tool
There are extraordinary processing characteristics and the preferable strength of materials, are widely used, it is possible to effectively reduce enterprise and the production cost of factory,
Welcome by consumer.
Detailed description of the invention
Technical scheme in the embodiment of the present invention will be clearly and completely described below, it is clear that described enforcement
Example is only a part of embodiment of the present invention rather than whole embodiments.Based on the embodiment in the present invention, this area is common
All other embodiments that technical staff is obtained under not making creative work premise, broadly fall into the model of present invention protection
Enclose.
Embodiment one:
Thering is provided the steel that a kind of price is cheap, the material composition of described steel includes carbon, silicon, manganese, cerium, phosphorus, titanium, molybdenum, ferrum and impurity, institute
State steel by weight percentage, including material composition have: carbon 0.11%, silicon 0.18%, 0.015%, cerium 0.41%, phosphorus
1.23%, titanium 0.035%, molybdenum 0.022%, ferrum and impurity: surplus, the process for making of described steel is to be refined in top-blown converter by ferrum
Cheng Gang's, it is specially to mix ferrum and steel scrap and pours in stove, be passed through oxygen and make oxygen be combined into an oxidation with the carbon in ferrum
Carbon walks carbon ribbon.The described technique of oxygen that is passed through is for being blown into oxygen stream.The described time made steel in top-blown converter is 55 minutes.
Embodiment two:
Thering is provided the steel that a kind of price is cheap, the material composition of described steel includes carbon, silicon, manganese, cerium, phosphorus, titanium, molybdenum, ferrum and impurity, institute
State steel by weight percentage, including material composition have: carbon 0.19%, silicon 0.15%, manganese 0.01%, cerium 0.45%, phosphorus 1%,
Titanium 0.043%, molybdenum 0.035%, ferrum and impurity: surplus, ferrum is smelt steel in top-blown converter by the process for making of described steel,
Being specially to mix ferrum and steel scrap pours in stove, is passed through oxygen and makes oxygen be combined into carbon monoxide carbon ribbon with the carbon in ferrum
Walk.The described technique of oxygen that is passed through is for being blown into oxygen stream.The described time made steel in top-blown converter is 60 minutes.
Embodiment three:
Thering is provided the steel that a kind of price is cheap, the material composition of described steel includes carbon, silicon, manganese, cerium, phosphorus, titanium, molybdenum, ferrum and impurity, institute
State steel by weight percentage, including material composition have: carbon 0.06%, silicon 0.27%, manganese 0.025%, cerium 0.32%, phosphorus
1.45%, titanium 0.024%, molybdenum 0.012%, ferrum and impurity: surplus, the process for making of described steel is to be refined in top-blown converter by ferrum
Cheng Gang's, it is specially to mix ferrum and steel scrap and pours in stove, be passed through oxygen and make oxygen be combined into an oxidation with the carbon in ferrum
Carbon walks carbon ribbon.The described technique of oxygen that is passed through is for being blown into oxygen stream.The described time made steel in top-blown converter is 45 minutes.
The invention has the beneficial effects as follows:
One, the steel that described price is cheap does not affect the serviceability that steel itself has, and has extraordinary processing characteristics with preferable
The strength of materials;
Two, the steel that described price is cheap is widely used, it is possible to effectively reduce enterprise and the production cost of factory, by consumer
Welcome.
The foregoing is only embodiments of the invention, not thereby limit the scope of the claims of the present invention, every utilize this
Equivalent structure or equivalence flow process that bright description is made convert, or are directly or indirectly used in other relevant technology neck
Territory, is the most in like manner included in the scope of patent protection of the present invention.
Claims (4)
1. the steel that a price is cheap, it is characterised in that the material composition of described steel includes carbon, silicon, manganese, cerium, phosphorus, titanium, molybdenum, ferrum
And impurity, described steel by weight percentage, including material composition have: carbon≤0.22%, silicon≤0.35%, manganese≤0.03%, cerium
0.32-0.45%, phosphorus 1-1.45%, titanium≤0.055%, molybdenum≤0.045%, ferrum and impurity: surplus, the process for making of described steel be by
Ferrum is smelt steel in top-blown converter, is specially to mix ferrum and steel scrap and pours in stove, is passed through oxygen and makes in oxygen and ferrum
Carbon be combined into carbon monoxide carbon ribbon walked.
The steel that price the most according to claim 1 is cheap, it is characterised in that described steel by weight percentage, including
Material composition has: carbon 0.11%, silicon 0.18%, 0.015%, cerium 0.41%, phosphorus 1.23%, titanium 0.035%, molybdenum 0.022%, ferrum and
Impurity: surplus.
The steel that price the most according to claim 1 is cheap, it is characterised in that described in be passed through the technique of oxygen for being blown into oxygen
Stream.
The steel that price the most according to claim 1 is cheap, it is characterised in that described in top-blown converter steel-making time be
45-60 minute.