CN106047110A - Electric cooker antistatic coating and preparation method thereof - Google Patents
Electric cooker antistatic coating and preparation method thereof Download PDFInfo
- Publication number
- CN106047110A CN106047110A CN201610668025.8A CN201610668025A CN106047110A CN 106047110 A CN106047110 A CN 106047110A CN 201610668025 A CN201610668025 A CN 201610668025A CN 106047110 A CN106047110 A CN 106047110A
- Authority
- CN
- China
- Prior art keywords
- parts
- coating
- antistatic
- electric cooker
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an electric cooker antistatic coating prepared from the following raw materials: alkyd resin, a vinyl acetate-acrylic emulsion, polyamide resin, sodium sulfide, a ferrophosphorus powder, butanediol, aluminum hydroxide, propylene glycol monoethyl ether, a proper amount of deionized water, a catalyst, an antistatic auxiliary agent, and an epoxy adhesive. A preparation method comprises the following steps: (1) preparing a primary mixture; (2) preparing an intermediate liquid; (3) preparing a mixed liquid; and (4) carrying out grinding treatment of the mixed liquid, and sieving to obtain the finished product. With adopting of the scientific preparation method, the organic polymer materials are subjected to optimal combination, the antistatic property of the composition is improved, an obtained coating layer has the advantages of good gloss retention and smooth and fine surface, tensile strength and other indexes are all better than those of an ordinary coating, and use requirements of a coating body can be met; and the coating has the advantages of energy saving, environmental protection, relatively low cost, and short production cycle, and is suitable for industrialized mass production.
Description
Technical field
The invention belongs to coating industry technical field, particularly relate to a kind of electric cooker antistatic coating and preparation method thereof.
Background technology
Coating refers to that coating body surface can form thin film under certain conditions and play protection, decoration or other special merits
Can the class I liquid I of (insulation, antirust, mildew-resistant, heat-resisting etc.) or solid material.Coating belongs to organic chemical industry's macromolecular material, institute's shape
The film become belongs to macromolecular compound type.According to the classification of the chemical products that the modern times pass through, coating belongs to fine chemistry industry and produces
Product.Modern coating the most progressively becomes a polyfunctional engineering material of class, is an important industry in chemical industry.Mesh
Before, the coating industry of China is the most ripe, in addition under the overall situation of green economy globalization, needs to implement promotion green science and technology
The development of industry.
Along with the development of society, the covering with paint of traditional household electrical appliance has had bigger change, the water paint of environmental protection
Gradually substitute thermohardening lacquer, but different electrical equipment has different requirements due to the difference of the aspects such as function to coating, need
Use environmental protection and more personalized coating.The market demand huge in the face of household electrical appliances coating and ever-increasing application prospect, have
Necessity is strengthened research and development capabilities, and updates and improving product performance, accelerates product quality upgrading, develops technically, cost
Above, there is in performance the household electrical appliances coating of powerful competitive advantage.
Summary of the invention
The invention aims to overcome the deficiencies in the prior art, it is provided that a kind of electric cooker antistatic coating and
Its preparation method, the coating products excellent combination property obtained, also there is good antistatic property, be suitable to popularization and application.
For solve above-mentioned technical problem, the present invention by the following technical solutions:
A kind of electric cooker antistatic coating, it is characterised in that be prepared by the raw materials in: alkyd resin 30～45
Part, acrylate and vinyl acetate emulsion 20～35 parts, polyamide 15～25 parts, sodium sulfide 8～15 parts, ferrophosphorus powder 3～6 parts, butanediol 1～3
Part, aluminium hydroxide 2～5 parts, propylene-glycol ethyl ether 5～12 parts, deionized water be appropriate, catalyst 1～3 parts, antistatic auxiliary 1～
2.5 parts, epoxy glue 4～10 parts；
Its preparation method in turn includes the following steps:
(1) alkyd resin, acrylate and vinyl acetate emulsion, polyamide and sodium sulfide are mixed to join batch mixer, stir, add
Heat, to 60～75 DEG C, continues stirring 30～50 minutes, obtains just batch mixing；
(2) ferrophosphorus powder, butanediol, aluminium hydroxide, propylene-glycol ethyl ether and appropriate amount of deionized water are added sequentially to step (1)
In the first batch mixing obtained, being stirred continuously and be warming up to 150～165 DEG C, under 900～1100 revs/min, stirring reaction 1.5～3 is little
Time, obtain intermediate liquid；
(3) intermediate liquid that step (2) obtains is cooled to 60～70 DEG C, adds catalyst and antistatic auxiliary is the most continuous
Stirring, is eventually adding epoxy glue, mix and blend 50～90 minutes, obtains mixed liquor；
(4) it is ground the mixed liquor that step (3) obtains processing, sieves and get product.
Preferably, described catalyst is dibutyl tin laurate.
Preferably, described antistatic auxiliary is alkyl quaternary ammonium salts.
The beneficial effects of the present invention is:
The present invention, by using the preparation method of science, is optimized combination to high-molecular organic material, improves combination
The antistatic property of thing, the indexs such as the coating gloss retention obtained is good, and smooth surface is fine and smooth, hot strength are superior to common coating,
The use requirement of coated-body can be met；Present invention achieves making full use of of resource and the energy, energy-conserving and environment-protective, cost is relatively low, raw
The product cycle is short, is suitable to industrialized mass production.
Detailed description of the invention
Below in conjunction with embodiment, the invention will be further described.
Embodiment 1:
A kind of electric cooker antistatic coating, it is characterised in that be prepared by the raw materials in: alkyd resin 30 parts,
Acrylate and vinyl acetate emulsion 20 parts, polyamide 15 parts, 8 parts of sodium sulfide, 3 parts of ferrophosphorus powder, butanediol 1 part, aluminium hydroxide 2 parts, propylene glycol
Ether 5 parts, deionized water are appropriate, catalyst 1 part, antistatic auxiliary 1 part, epoxy glue 4 parts；
Its preparation method in turn includes the following steps:
(1) alkyd resin, acrylate and vinyl acetate emulsion, polyamide and sodium sulfide are mixed to join batch mixer, stir, add
Heat, to 60～75 DEG C, continues stirring 30 minutes, obtains just batch mixing；
(2) ferrophosphorus powder, butanediol, aluminium hydroxide, propylene-glycol ethyl ether and appropriate amount of deionized water are added sequentially to step (1)
In the first batch mixing obtained, it is stirred continuously and is warming up to 150～165 DEG C, stirring reaction 3 hours under 900～1100 revs/min,
To intermediate liquid；
(3) intermediate liquid that step (2) obtains is cooled to 60～70 DEG C, adds catalyst and antistatic auxiliary is the most continuous
Stirring, is eventually adding epoxy glue, mix and blend 50 minutes, obtains mixed liquor；
(4) it is ground the mixed liquor that step (3) obtains processing, sieves and get product.
Embodiment 2:
A kind of electric cooker antistatic coating, it is characterised in that be prepared by the raw materials in: alkyd resin 45 parts,
Acrylate and vinyl acetate emulsion 35 parts, polyamide 25 parts, 15 parts of sodium sulfide, 6 parts of ferrophosphorus powder, butanediol 3 parts, aluminium hydroxide 5 parts, propylene glycol
Ether 12 parts, deionized water are appropriate, catalyst 3 parts, antistatic auxiliary 2.5 parts, epoxy glue 10 parts；
Its preparation method in turn includes the following steps:
(1) alkyd resin, acrylate and vinyl acetate emulsion, polyamide and sodium sulfide are mixed to join batch mixer, stir, add
Heat, to 60～75 DEG C, continues stirring 50 minutes, obtains just batch mixing；
(2) ferrophosphorus powder, butanediol, aluminium hydroxide, propylene-glycol ethyl ether and appropriate amount of deionized water are added sequentially to step (1)
In the first batch mixing obtained, it is stirred continuously and is warming up to 150～165 DEG C, stirring reaction 1.5 hours under 900～1100 revs/min,
Obtain intermediate liquid；
(3) intermediate liquid that step (2) obtains is cooled to 60～70 DEG C, adds catalyst and antistatic auxiliary is the most continuous
Stirring, is eventually adding epoxy glue, mix and blend 90 minutes, obtains mixed liquor；
(4) it is ground the mixed liquor that step (3) obtains processing, sieves and get product.
In the above embodiment of the present invention: described catalyst is dibutyl tin laurate, described antistatic auxiliary is alkyl
Quaternary ammonium salt.
In the embodiment of the present invention, by high-molecular organic material is optimized combination, improve the antistatic of compositions
Performance, the indexs such as the coating gloss retention obtained is good, and smooth surface is fine and smooth, hot strength are superior to common coating, can meet application
The use requirement of body, and energy-conserving and environment-protective, cost is relatively low, with short production cycle.
Finally it should be noted that above example only in order to illustrative not limiting technical scheme, although reference
The present invention has been described in detail by above-described embodiment, it will be appreciated by those skilled in the art that and still can carry out the present invention
Amendment or equivalent, any modification or partial replacement without departing from the spirit and scope of the present invention, it all should be contained
In scope of the presently claimed invention.
Claims (3)
1. an electric cooker antistatic coating, it is characterised in that be prepared by the raw materials in: alkyd resin 30～45
Part, acrylate and vinyl acetate emulsion 20～35 parts, polyamide 15～25 parts, sodium sulfide 8～15 parts, ferrophosphorus powder 3～6 parts, butanediol 1～3
Part, aluminium hydroxide 2～5 parts, propylene-glycol ethyl ether 5～12 parts, deionized water be appropriate, catalyst 1～3 parts, antistatic auxiliary 1～
2.5 parts, epoxy glue 4～10 parts；
Its preparation method in turn includes the following steps:
(1) alkyd resin, acrylate and vinyl acetate emulsion, polyamide and sodium sulfide are mixed to join batch mixer, stir, be heated to
60～75 DEG C, continue stirring 30～50 minutes, obtain just batch mixing；
(2) ferrophosphorus powder, butanediol, aluminium hydroxide, propylene-glycol ethyl ether and appropriate amount of deionized water are added sequentially to step (1) obtain
First batch mixing in, be stirred continuously and be warming up to 150～165 DEG C, under 900～1100 revs/min stirring reaction 1.5～3 hours,
To intermediate liquid；
(3) intermediate liquid that step (2) obtains is cooled to 60～70 DEG C, adds catalyst and antistatic auxiliary and constantly stir
Mix, be eventually adding epoxy glue, mix and blend 50～90 minutes, obtain mixed liquor；
(4) it is ground the mixed liquor that step (3) obtains processing, sieves and get product.
A kind of electric cooker antistatic coating the most according to claim 1, it is characterised in that described catalyst is tin dilaurate
Dibutyl tin.
A kind of electric cooker antistatic coating the most according to claim 1, it is characterised in that described antistatic auxiliary is alkyl
Quaternary ammonium salt.