CN106046427A - Polypeptide blend modified pullulan-grafted pineapple fiber packaging film and preparation method thereof - Google Patents
Polypeptide blend modified pullulan-grafted pineapple fiber packaging film and preparation method thereof Download PDFInfo
- Publication number
- CN106046427A CN106046427A CN201610518832.1A CN201610518832A CN106046427A CN 106046427 A CN106046427 A CN 106046427A CN 201610518832 A CN201610518832 A CN 201610518832A CN 106046427 A CN106046427 A CN 106046427A
- Authority
- CN
- China
- Prior art keywords
- parts
- poly
- peptide
- arghan
- pulullan polysaccharide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a polypeptide blend modified pullulan-grafted pineapple fiber packaging film, comprising the following components according to parts by weight: 120-125 parts of pineapple leaf fiber, 6-6.5 parts of composite cellulase, 2.3-2.4 parts of nano magnesia particles, 4.3-4.4 parts of citric acid, 27-28 parts of polypeptide, 37-38 parts of pullulan, 9-10 parts of organic hectorite, 8-9 parts of polyvinylpyrrolidone, 11-12 parts of sodium caseinate, 3-4 parts of cove essential oil, 5-6 parts of soy isoflavones, 16-17 parts of polyvinyl glycol, 3-4 parts of sodium ethoxide, suitable water and suitable deionized water. The polypeptide blend modified pullulan is combined with nano pineapple leaf cellulose solution and other components and subjected to ultrasonic assisted emulsification and shearing to prepare a homogeneous film solution, thus preparing pineapple cellulose film; the application of pineapple cellulose in the field of film materials is achieved, good breathability and spatial structural property are provided, and the addition of clove essential oil promotes the formation of the film.
Description
Technical field
The present invention relates to arghan packaging film technical field, particularly relate to a kind of poly-peptide blending and modifying pulullan polysaccharide
Grafting pina fibre packaging film and preparation method thereof.
Background technology
With cellulose as raw material, the different macromolecule member material of processability is at necks such as medical science, biology and food medicine
Territory plays an important role, and has become as the focus of current research.China often produces substantial amounts of Fructus Ananadis comosi per year, and arghan has
The health-care effecies such as antibacterial, smelly eliminating, utilize arghan to prepare macromolecule member material and have huge development prospect.Pineapple leaves is fine
The fiber macromolecular alignment of dimension crystallization song is neat, regular, and the polyhydroxy structure of fiber molecule and strong hydrogen bonding effect make it clean
Cleanliness and the degree of orientation are higher, and chemical reactivity is low, thus cause its application to be restricted." the agriculture in south such as Wei Xiaoyi, Yang Qin
Journal ", 2016,47(1): 101-106 " arghan element film preparation process optimization " utilizes emulsifying cut mode to make pineapple leaves
Cellulose dissolution improves the chemical reactivity of arghan in ionic liquid, it is achieved the preparation of cellulose membrane, specifically does
Method is: be ground into cotton shape with Universalpulverizer after first being dried by arghan element, and alkali processes and acid treatment realizes it respectively
Purification process, is then being placed in together with ionic liquid in mulser, is carrying out shear treatment, acquisition prepare the cellulose of film from
Sub-liquid homogeneous phase solution, is layered on homogeneous phase solution on the carrier scribbling politef afterwards, through casting solution (glycerol, second
Alcohol) etc. soak drying and forming-film;This process technique improves the chemical reaction activity of arghan element, improves the equal of coating solution
Phase, but operate and employ substantial amounts of acidizer and alkali inorganic agent, adds somewhat to pollute, add Fructus Ananadis comosi
Leaf fibre element film preparation cost, the cellulose membrane function singleness simultaneously prepared.Nano-cellulose have high-crystallinity, high intensity,
The excellent properties such as high-specific surface area, environmental friendliness and low cost, also exist substantial amounts of-OH in its molecular structure, with other skies
So macromole is easily formed intermolecular and intramolecular hydrogen bond when being blended, and when being used for making membrane material, can make the formation of intermingling material
Membrane structure more stable.Micro-nano bubble refers to that diameter is between micron bubble (bubble of a diameter of 10-50um in water body)
And the bubble between nano bubble (a diameter of bubble less than 200nm in water body), have big specific surface area, can be at water
In body, the time of staying is long, and micro-nano bubble is when shrinking, it is possible to produce substantial amounts of hydroxyl radical free radical, these substantial amounts of hydroxyls
Free radical can attract the hydrogen bond in arghan element to a certain extent, plays equivalent acidifying alkalization and destroys the effect that hydrogen bond is identical
Really, the nanorize promoting arghan is improved its chemical reaction activity and there is certain facilitation.Pulullan polysaccharide is
The polymer substance of colorless and odorless odorless, has edibility and biodegradability, has good film property, the thin film tool made
There are good gas barrier property and water preventing ability, but containing substantial amounts of hydrophilic radical on pulullan polysaccharide strand, can be with other
Fibrous material combines the fibrous membrane prepared, but these fibrous membranes chance water is instant, limits its application on some packaging films;
The fibrous membrane that arghan based on modified pulullan polysaccharide and high chemical reactivity combines is to improving pineapple leaves
Comprehensive utilization and abundant packaging film kind are significant.
Summary of the invention
The object of the invention is contemplated to make up the defect of prior art, it is provided that a kind of poly-peptide blending and modifying pulullan polysaccharide connects
Branch pina fibre packaging film and preparation method thereof.
The present invention is achieved by the following technical solutions:
A kind of poly-peptide blending and modifying pulullan polysaccharide grafting pina fibre packaging film, including following parts by weight of component: pineapple leaves is fine
Dimension 120-125, compound cellulase 6-6.5, nano oxidized magnesium particle 2.3-2.4, citric acid 4.3-4.4, poly-peptide 27-28, general
Shandong orchid polysaccharide 37-38, organic lithium soapstone 9-10, polyvinylpyrrolidone 8-9, sodium caseinate 11-12, clove oil 3-4, big
Bean isoflavone 5-6, Polyethylene Glycol 16-17, Sodium ethylate 3-4, appropriate water, appropriate deionized water.
A kind of poly-peptide blending and modifying pulullan polysaccharide grafting pina fibre packaging film preparation method, comprises the following steps:
(1), will arghan dry after become cotton shape by pulverization process 30min in Universalpulverizer, afterwards with citric acid with
And the water mixing and stirring of gross weight 4 times to obtain slurry standby, slurry is heated to 60 DEG C, and is continuously added into compound cellulase
Mix and blend enzymolysis 40min, after 100 DEG C of enzyme denaturing, vacuum filtration is also washed, and obtains purification arghan, and purification pineapple leaves is fine
Dimension adds nano oxidized magnesium particle and the deionized water of gross weight 10 times, then the high pressure homogenize machinery process through 700bar
Under 30min, 1400W power, strength supersound process 50min, obtains uniform mixed liquor, is using at intermittent steam blasting procedure explosion
Manage this uniform mixed liquor 5 times, each 10min, obtain nanorize arghan cellulose solution standby;
(2), the deionized water of poly-peptide, Polyethylene Glycol, organic lithium soapstone and gross weight 2 times is mixed, 50 DEG C of heated and stirred
40min, obtains the modified poly-peptide of organic lithium soapstone, adds pulullan polysaccharide afterwards, 80 DEG C of heated and stirred 20min, afterwards spray dried
It is dry that to obtain poly-peptide blending and modifying pulullan polysaccharide standby;
(3), by nanorize arghan cellulose solution, poly-peptide blending and modifying pulullan polysaccharide, polyvinylpyrrolidone, casein
Stir after the deionized water mixing of acid sodium, clove oil, soybean isoflavone, Sodium ethylate and gross weight 3-4 times, then put
Enter the mulser with intense ultrasonic wave is carried out ultrasonic assistant emulsifying shear treatment 40min, then carry out at the microwave of 350W
Reason 2min, obtains homogeneous membrane solution for standby, wherein ultrasonic power 1000W, emulsifying shear rate 15000r/min;
(4), by homogeneous membrane solution with pouring in mould, then deaeration process is carried out through supersound process 15-18min, then at 50-
At 55 DEG C, humidity be 55-60% calorstat in be dried 3-4h, to obtain final product.
The invention have the advantage that
The present invention uses the pulullan polysaccharide of poly-peptide blending and modifying to combine nanorize arghan cellulose solution and other compositions
Shear preparation homogeneous membrane solution through ultrasonic assistant emulsifying and prepare pina fibre element film, it is achieved that pina fibre element is led at membrane material
The application in territory, the cellulose membrane of preparation, because using nanorize pina fibre cellulose solution, has good breathability and space knot
Structure;The clove oil added promotes the formation of film;In preparing membrane process, the poly-peptide of employing has good bio-compatible
Property and biodegradability but itself lack preferable hydrophilic, pulullan polysaccharide is the polymer substance of colorless and odorless odorless,
There is edibility and biodegradability, have good film property, there is good water solublity, first by this tool of organic lithium soapstone
The material having certain three dimensional structure inserts in poly-peptide, changes its space structure, changes adding pulullan polysaccharide to carry out being blended
Property, obtain space structure and hydrophilicity and the most improved modified pulullan polysaccharide of filming performance;Fine for pineapple leaves
The dimension low problem of chemical reaction activity, have employed enzyme purification, highly active nano oxidized magnesium particle additional high pressure homogenizing, strong successively
Supersound process and intermittent steam blasting procedure explosion treatment, it is achieved that the purification of arghan and nanorize, for preparation
High performance arghan film is laid a good foundation;For the homogeneous problem of coating solution, strong supersound process is used to coordinate emulsifying to cut
The mode cut, strong supersound process improves the content of micro-nano bubble in coating solution, helps lend some impetus to the dissolving of each material, improves
Membrane material solution homogeneous.
Detailed description of the invention
A kind of poly-peptide blending and modifying pulullan polysaccharide grafting pina fibre packaging film, including following parts by weight of component: Fructus Ananadis comosi
Leaf fibre 120, compound cellulase 6, nano oxidized magnesium particle 2.3, citric acid 4.3, poly-peptide 27, pulullan polysaccharide 37, organic
Hectorite 9, polyvinylpyrrolidone 8, sodium caseinate 11, clove oil 3, soybean isoflavone 5, Polyethylene Glycol 16, Sodium ethylate
3, appropriate water, appropriate deionized water.
A kind of poly-peptide blending and modifying pulullan polysaccharide grafting pina fibre packaging film preparation method, comprises the following steps:
(1), will arghan dry after become cotton shape by pulverization process 30min in Universalpulverizer, afterwards with citric acid with
And the water mixing and stirring of gross weight 4 times to obtain slurry standby, slurry is heated to 60 DEG C, and is continuously added into compound cellulase
Mix and blend enzymolysis 40min, after 100 DEG C of enzyme denaturing, vacuum filtration is also washed, and obtains purification arghan, and purification pineapple leaves is fine
Dimension adds nano oxidized magnesium particle and the deionized water of gross weight 10 times, then the high pressure homogenize machinery process through 700bar
Under 30min, 1400W power, strength supersound process 50min, obtains uniform mixed liquor, is using at intermittent steam blasting procedure explosion
Manage this uniform mixed liquor 5 times, each 10min, obtain nanorize arghan cellulose solution standby;
(2), the deionized water of poly-peptide, Polyethylene Glycol, organic lithium soapstone and gross weight 2 times is mixed, 50 DEG C of heated and stirred
40min, obtains the modified poly-peptide of organic lithium soapstone, adds pulullan polysaccharide afterwards, 80 DEG C of heated and stirred 20min, afterwards spray dried
It is dry that to obtain poly-peptide blending and modifying pulullan polysaccharide standby;
(3), by nanorize arghan cellulose solution, poly-peptide blending and modifying pulullan polysaccharide, polyvinylpyrrolidone, casein
Stir after the deionized water mixing of acid sodium, clove oil, soybean isoflavone, Sodium ethylate and gross weight 3 times, be then placed in
Mulser with intense ultrasonic wave carries out ultrasonic assistant emulsifying shear treatment 40min, then carries out the microwave treatment of 350W
2min, obtains homogeneous membrane solution for standby, wherein ultrasonic power 1000W, emulsifying shear rate 15000r/min;
(4), by homogeneous membrane solution with pouring in mould, then deaeration process is carried out through supersound process 15min, then at 50 DEG C
Under, humidity be 55% calorstat in be dried 3h, to obtain final product.
After tested, this packaging film impingement rate is 16.01kJ/m2, and anti-to stretch intensity be 23.5MPa, elongation at break 42.1%,
The OTR oxygen transmission rate of film is reached for 3.5 × 10-5cm3/ (m2 d Pa), and after soil buries 150d, its biological degradation rate reaches 99%, display
Go out excellent biological degradability.
Claims (2)
1. a poly-peptide blending and modifying pulullan polysaccharide grafting pina fibre packaging film, it is characterised in that include following weight portion
Component: arghan 120-125, compound cellulase 6-6.5, nano oxidized magnesium particle 2.3-2.4, citric acid 4.3-4.4,
Poly-peptide 27-28, pulullan polysaccharide 37-38, organic lithium soapstone 9-10, polyvinylpyrrolidone 8-9, sodium caseinate 11-12, fourth
Essential oil 3-4, soybean isoflavone 5-6, Polyethylene Glycol 16-17, Sodium ethylate 3-4, appropriate water, appropriate deionized water.
2. poly-peptide blending and modifying pulullan polysaccharide grafting pina fibre packaging film preparation method, it is characterised in that include with
Lower step:
(1), will arghan dry after become cotton shape by pulverization process 30min in Universalpulverizer, afterwards with citric acid with
And the water mixing and stirring of gross weight 4 times to obtain slurry standby, slurry is heated to 60 DEG C, and is continuously added into compound cellulase
Mix and blend enzymolysis 40min, after 100 DEG C of enzyme denaturing, vacuum filtration is also washed, and obtains purification arghan, and purification pineapple leaves is fine
Dimension adds nano oxidized magnesium particle and the deionized water of gross weight 10 times, then the high pressure homogenize machinery process through 700bar
Under 30min, 1400W power, strength supersound process 50min, obtains uniform mixed liquor, is using at intermittent steam blasting procedure explosion
Manage this uniform mixed liquor 5 times, each 10min, obtain nanorize arghan cellulose solution standby;
(2), the deionized water of poly-peptide, Polyethylene Glycol, organic lithium soapstone and gross weight 2 times is mixed, 50 DEG C of heated and stirred
40min, obtains the modified poly-peptide of organic lithium soapstone, adds pulullan polysaccharide afterwards, 80 DEG C of heated and stirred 20min, afterwards spray dried
It is dry that to obtain poly-peptide blending and modifying pulullan polysaccharide standby;
(3), by nanorize arghan cellulose solution, poly-peptide blending and modifying pulullan polysaccharide, polyvinylpyrrolidone, casein
Stir after the deionized water mixing of acid sodium, clove oil, soybean isoflavone, Sodium ethylate and gross weight 3-4 times, then put
Enter the mulser with intense ultrasonic wave is carried out ultrasonic assistant emulsifying shear treatment 40min, then carry out at the microwave of 350W
Reason 2min, obtains homogeneous membrane solution for standby, wherein ultrasonic power 1000W, emulsifying shear rate 15000r/min;
(4), by homogeneous membrane solution with pouring in mould, then deaeration process is carried out through supersound process 15-18min, then at 50-
At 55 DEG C, humidity be 55-60% calorstat in be dried 3-4h, to obtain final product.