CN106045312A - High-fineness colored glaze - Google Patents
High-fineness colored glaze Download PDFInfo
- Publication number
- CN106045312A CN106045312A CN201610640870.4A CN201610640870A CN106045312A CN 106045312 A CN106045312 A CN 106045312A CN 201610640870 A CN201610640870 A CN 201610640870A CN 106045312 A CN106045312 A CN 106045312A
- Authority
- CN
- China
- Prior art keywords
- parts
- fineness
- colored glaze
- coloring agent
- clarifier
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses high-fineness colored glaze. The high-fineness colored glaze comprises, by mass, 90-110 parts of quartz sand, 20-30 parts of a clarificant, 10-20 parts of powdered steatile, 5-10 parts of glass fibers, 3-7 parts of a curing agent, 10-15 parts of an oxidizing agent and 10-12 parts of a coloring agent. The clarificant is prepared from cerium dioxide and antimony oxide according to a ratio of 2: 1. The coloring agent is a mixture of cobalt oxide and iron oxide. The high-fineness colored glaze improves colored glaze fineness, guarantees colored glaze transparency and is beautiful.
Description
Technical field
The present invention relates to colored glaze product field, particularly relate to a kind of highly polished coloured glaze.
Background technology
Coloured glaze is a kind of silicate product, has a long history, and its quality is glittering and translucent, bright and glittering, changes irregularly magnificent,
Fully demonstrate the exquisiteness of Asians, fine and smooth and implicit, be a kind of important decoration element, coloured glaze be mainly composed of SiO2.
How (i.e. silicon dioxide), aluminium oxide, flux lead oxide and pigment etc., improve the bright and clean degree of coloured glaze product, it is ensured that coloured glaze
Texture is penetrating, is a problem needing research.
Summary of the invention
The technical problem that present invention mainly solves is to provide a kind of highly polished coloured glaze, it is possible to promote the bright and clean journey of coloured glaze
Degree, it is ensured that coloured glaze texture is penetrating, air attractive in appearance.
For solving above-mentioned technical problem, the technical scheme that the present invention uses is: provide a kind of highly polished coloured glaze,
It is characterized in that, be to be grouped into by the one-tenth of following masses number: quartz sand 90-110 part, clarifier 20-30 part, Pulvis Talci 10-
20 parts, glass fibre 5-10 part, firming agent 3-7 part, oxidant 10-15 part, coloring agent 10-12 part；Described clarifier is dioxy
Changing cerium and antimony oxide is pressed 2:1 proportions and obtained, described coloring agent is the compound of cobalt oxide and ferrum oxide.
In a preferred embodiment of the present invention, described highly polished coloured glaze, is to be grouped by the one-tenth of following masses number
Become: quartz sand 98 parts, clarifier 27 parts, Pulvis Talci 15 parts, glass fibre 7 parts, 5 parts of firming agent, oxidant 10 parts, coloring agent 11
Part.
In a preferred embodiment of the present invention, described highly polished coloured glaze, is to be grouped by the one-tenth of following masses number
Become: quartz sand 105 parts, clarifier 23 parts, Pulvis Talci 14 parts, glass fibre 5 parts, 6 parts of firming agent, oxidant 13 parts, coloring agent
10 parts.
The invention has the beneficial effects as follows: the present invention can promote the bright and clean degree of coloured glaze, it is ensured that coloured glaze texture is penetrating, attractive in appearance
Air.
Detailed description of the invention
Below presently preferred embodiments of the present invention is described in detail so that advantages and features of the invention can be easier to by
It will be appreciated by those skilled in the art that thus protection scope of the present invention is made apparent clear and definite defining.
The embodiment of the present invention includes:
Embodiment 1:
Highly polished coloured glaze, is to be grouped into by the one-tenth of following masses number: quartz sand 98 parts, clarifier 27 parts, Pulvis Talci 15
Part, glass fibre 7 parts, 5 parts of firming agent, oxidant 10 parts, coloring agent 11 parts；Clarifier be ceria and antimony oxide by
2:1 proportions and obtain, described coloring agent is the compound of cobalt oxide and ferrum oxide.Quartz sand and clarifier are mixed and pours into instead
Answer stove, be heated to 800 DEG C, pour Pulvis Talci, glass fibre, firming agent and oxidant into, be heated to 1200 DEG C, keep 16 hours,
Pouring coloring agent into, be heated to 1550 DEG C, keep 16 hours after annealings, temperature is down to 600 DEG C, is often slowly dropped to after keeping 7 hours
Temperature, obtains finished product after refine.
Embodiment 2:
Highly polished coloured glaze, is to be grouped into by the one-tenth of following masses number: quartz sand 105 parts, clarifier 23 parts, Pulvis Talci 14
Part, glass fibre 5 parts, 6 parts of firming agent, oxidant 13 parts, coloring agent 10 parts；Clarifier be ceria and antimony oxide by
2:1 proportions and obtain, described coloring agent is the compound of cobalt oxide and ferrum oxide.Quartz sand and clarifier are mixed and pours into instead
Answer stove, be heated to 800 DEG C, pour Pulvis Talci, glass fibre, firming agent and oxidant into, be heated to 1200 DEG C, keep 16 hours,
Pouring coloring agent into, be heated to 1550 DEG C, keep 16 hours after annealings, temperature is down to 600 DEG C, is often slowly dropped to after keeping 7 hours
Temperature, obtains finished product after refine.
Use ceria and antimony oxide compound are as clarifier, by rational proportion, than using independent two
Cerium oxide or antimony oxide are as clarifier, and its clarity is higher；Add Pulvis Talci and can improve the bright and clean degree of coloured glaze；Add
Adding glass fibre and can improve the light transmission of coloured glaze, by adding mentioned component, the present invention can promote the bright and clean degree of coloured glaze,
Ensure that coloured glaze texture is penetrating, air attractive in appearance.
The foregoing is only embodiments of the invention, not thereby limit the scope of the claims of the present invention, every utilize this
Equivalent structure or equivalence flow process that bright description is made convert, or are directly or indirectly used in other relevant technology necks
Territory, is the most in like manner included in the scope of patent protection of the present invention.
Claims (3)
1. a highly polished coloured glaze, it is characterised in that be to be grouped into by the one-tenth of following masses number: quartz sand 90-110
Part, clarifier 20-30 part, Pulvis Talci 10-20 part, glass fibre 5-10 part, firming agent 3-7 part, oxidant 10-15 part, coloring
Agent 10-12 part；Described clarifier is ceria and antimony oxide is obtained by 2:1 proportions, and described coloring agent is oxidation
Cobalt and the compound of ferrum oxide.
Highly polished coloured glaze the most according to claim 1, it is characterised in that be to be grouped by the one-tenth of following masses number
Become: quartz sand 98 parts, clarifier 27 parts, Pulvis Talci 15 parts, glass fibre 7 parts, 5 parts of firming agent, oxidant 10 parts, coloring agent 11
Part.
Highly polished coloured glaze the most according to claim 1, it is characterised in that be to be grouped by the one-tenth of following masses number
Become: quartz sand 105 parts, clarifier 23 parts, Pulvis Talci 14 parts, glass fibre 5 parts, 6 parts of firming agent, oxidant 13 parts, coloring agent
10 parts.