CN106011438A - Heat treatment induction hardening technique for sprocket wheel - Google Patents
Heat treatment induction hardening technique for sprocket wheel Download PDFInfo
- Publication number
- CN106011438A CN106011438A CN201610503368.9A CN201610503368A CN106011438A CN 106011438 A CN106011438 A CN 106011438A CN 201610503368 A CN201610503368 A CN 201610503368A CN 106011438 A CN106011438 A CN 106011438A
- Authority
- CN
- China
- Prior art keywords
- workpiece
- heat treatment
- sprocket wheel
- quenching
- induction hardening
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a heat treatment induction hardening technique for a sprocket wheel. The heat treatment induction hardening technique adopts the following technical steps of inspecting; cleaning and drying; hardening; cleaning and drying; tempering; detecting and performing rust-resisting treatment. According to the heat treatment induction hardening technique, the technique is simple, environmental protection without pollution in the whole process is realized, the hardness, the strength and wear resistance of the sprocket wheel can be effectively improved, and the service life of the sprocket wheel is prolonged; in the hardening step, an HX-200 medium is adopted to cool, and a workpiece is enabled to be uniformly hardened; a uniform diaphragm is formed on the surface of metal, so that the workpiece is effectively protected from being cracked; and the carried quantity is little, the hardened workpiece does not need to be cleaned, and the medium does not need to be discharged. The heat treatment induction hardening technique is suitable for various materials; the adjustment for the concentration is avoided, so that the production cost is reduced; and energy is saved, so that environmental pollution is reduced, and economic benefits are increased.
Description
Technical field
The present invention relates to a kind of sprocket wheel heat treatment induction hardening process.
Background technology
Alloy steel casting is because having the advantage such as high intensity, high-wearing feature, progressively substitute ordinary carbon steel part, it is widely used in casting field, in actual applications, need rationally to select the intensity of low-alloy steel, hardness and toughness, existing alloy steel casting Technology for Heating Processing is complicated, energy-saving effect is inconspicuous, although in its intensity of the highest raising and hardness, but can could be improved technique for certain high request, high-level workpiece.And in quenching process, go out innage, increase cost, case hardness occurs not because of the phenomenon easily split from one.Current technique, pollutes environment mostly, and the production time is long, and product is short for service life.
Summary of the invention
It is an object of the invention to provide a kind of sprocket wheel heat treatment induction hardening process, with the problem solving to propose in above-mentioned background technology.
The present invention use HX-200 as hardening media, HX-200 is that a kind of concentration contains various material, safety, colorless and odorless, without precipitation, nodeless mesh, environmental protection, the most aging, non-combustible, the high-performance hardening media of non-environmental-pollution, can be fully molten with aqueous phase, it it is moisture evaporation during quenching, concentration of medium improves relatively, after keeping the skin wet, medium composition is constant, cooling performance is constant, its metal surface is made to form uniform epithelium after quenching, stability is high, quenching hardness is high, uniformly it is unlikely to deform, point point is faster than water for high-temperature region cooling, low-temperature space cooling is less than water, workpiece can be effectively protected to prevent cracking, thus it is the hardest thoroughly to solve oil quenching, the problem that shrend is easily split.And HX-200 durability against pollution is strong, corrosion-free to workpiece and equipment, after quenching, workpiece is without cleaning, and viscosity is less than oil, and drag-out is few, low cost;Pyroconductivity is big, and quenching temperature rise is little, and production efficiency is high, is substantially reduced the cool time, saves time and expense, improves production efficiency 20%-30%, and energy-conservation about 10%, save into product integrated cost more than 20% for factory;May act as metal working lubricant, release is good.
For achieving the above object, the present invention provides following technical scheme: a kind of sprocket wheel heat treatment induction hardening process, and processing step is as follows:
A, check that workpiece has flawless, the defect such as damage, shove charge;
B, workpiece is sent into cleaning machine being dried, the time is 1-2min;
C, carry out sensing heating, heat time heating time is 6-10s, and quenching machine power setting is 60%, electric current 500A, quench stop position 1.00mm, cool down position 200mm, speed is 600mm/min, with HX-200 medium quenching cool down, use spray mode cooling down;
D, sent into cleaning-drying 1-2min in cleaning machine by by the workpiece after quenching;
Dried workpiece is tempered by E immediately, and temperature is set as 200-240 DEG C, and temperature retention time is 2-3h;
After F, use cooling medium cooling, check metallographic structure by standard, test product hardness;
G, by after workpiece immersion in liquid preventives water 3-5min take out, complete Technology for Heating Processing.
Compared with prior art, the invention has the beneficial effects as follows:
Present invention process is simple, omnidistance environment friendly and pollution-free, it is possible to the effective raising hardness of sprocket wheel, intensity and wearability, extends the service life of sprocket wheel;Quenching Step use HX-200 medium cool down; making its uniform quenching, metal surface forms uniform epithelium, and effectively protection workpiece prevents cracking; drag-out is few; workpiece No clean after quenching, medium exempts from discharge, it is adaptable to various materials; without adjusting concentration; reduce production cost, save the energy, decrease environmental pollution, increase economic efficiency.
Detailed description of the invention
Below the technical scheme in the embodiment of the present invention is clearly and completely described, it is clear that described embodiment is only a part of embodiment of the present invention rather than whole embodiments.Based on the embodiment in the present invention, the every other embodiment that those of ordinary skill in the art are obtained under not making creative work premise, broadly fall into the scope of protection of the invention.
Embodiment one
A kind of sprocket wheel heat treatment induction hardening process, processing step is as follows:
A, check that workpiece has flawless, the defect such as damage, shove charge;
B, workpiece is sent into cleaning machine being dried, the time is 1min;
C, carry out sensing heating, heat time heating time is 6s, and quenching machine power setting is 60%, electric current 500A, quench stop position 1.00mm, cool down position 200mm, speed is 600mm/min, with HX-200 medium quenching cool down, use spray mode cooling down;
D, sent into cleaning-drying 1min in cleaning machine by by the workpiece after quenching;
Dried workpiece is tempered by E immediately, and temperature is set as 200 DEG C, and temperature retention time is 2h;
After F, use cooling medium cooling, check metallographic structure by standard, test product hardness;
G, by after workpiece immersion in liquid preventives water 3min take out, complete Technology for Heating Processing.
Embodiment two
A kind of sprocket wheel heat treatment induction hardening process, processing step is as follows:
A, check that workpiece has flawless, the defect such as damage, shove charge;
B, workpiece is sent into cleaning machine being dried, the time is 2min;
C, carry out sensing heating, heat time heating time is 8s, and quenching machine power setting is 60%, electric current 500A, quench stop position 1.00mm, cool down position 200mm, speed is 600mm/min, with HX-200 medium quenching cool down, use spray mode cooling down;
D, sent into cleaning-drying 2min in cleaning machine by by the workpiece after quenching;
Dried workpiece is tempered by E immediately, and temperature is set as 190 DEG C, and temperature retention time is 3h;
After F, use cooling medium cooling, check metallographic structure by standard, test product hardness;
G, by after workpiece immersion in liquid preventives water 4min take out, complete Technology for Heating Processing.
Embodiment three
A kind of sprocket wheel heat treatment induction hardening process, processing step is as follows:
A, check that workpiece has flawless, the defect such as damage, shove charge;
B, workpiece is sent into cleaning machine being dried, the time is 2min;
C, carry out sensing heating, heat time heating time is 7s, and quenching machine power setting is 60%, electric current 500A, quench stop position 1.00mm, cool down position 200mm, speed is 600mm/min, with HX-200 medium quenching cool down, use spray mode cooling down;
D, sent into cleaning-drying 1min in cleaning machine by by the workpiece after quenching;
Dried workpiece is tempered by E immediately, and temperature is set as 200 DEG C, and temperature retention time is 2.5h;
After F, use cooling medium cooling, check metallographic structure by standard, test product hardness;
G, by after workpiece immersion in liquid preventives water 5min take out, complete Technology for Heating Processing.
Embodiment four
A kind of sprocket wheel heat treatment induction hardening process, processing step is as follows:
A, check that workpiece has flawless, the defect such as damage, shove charge;
B, workpiece is sent into cleaning machine being dried, the time is 1min;
C, carry out sensing heating, heat time heating time is 9s, and quenching machine power setting is 60%, electric current 500A, quench stop position 1.00mm, cool down position 200mm, speed is 600mm/min, with HX-200 medium quenching cool down, use spray mode cooling down;
D, sent into cleaning-drying 1min in cleaning machine by by the workpiece after quenching;
Dried workpiece is tempered by E immediately, and temperature is set as 1950 DEG C, and temperature retention time is 3h;
After F, use cooling medium cooling, check metallographic structure by standard, test product hardness;
G, by after workpiece immersion in liquid preventives water 5min take out, complete Technology for Heating Processing.
Embodiment five
A kind of sprocket wheel heat treatment induction hardening process, processing step is as follows:
A, check that workpiece has flawless, the defect such as damage, shove charge;
B, workpiece is sent into cleaning machine being dried, the time is 2min;
C, carry out sensing heating, heat time heating time is 10s, and quenching machine power setting is 60%, electric current 500A, quench stop position 1.00mm, cool down position 200mm, speed is 600mm/min, with HX-200 medium quenching cool down, use spray mode cooling down;
D, sent into cleaning-drying 2min in cleaning machine by by the workpiece after quenching;
Dried workpiece is tempered by E immediately, and temperature is set as 180 DEG C, and temperature retention time is 2h;
After F, use cooling medium cooling, check metallographic structure by standard, test product hardness;
G, by after workpiece immersion in liquid preventives water 3min take out, complete Technology for Heating Processing.
Experimental example:
The heat treatment induction hardening process that sprocket wheel uses ordinary heat treatment and various embodiments of the present invention processes, the experimental data obtained such as following table:
From above table data, the sprocket wheel quenching using the technique of embodiment five to obtain has optimum efficiency.
Although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, being appreciated that and these embodiments can carry out multiple change without departing from the principles and spirit of the present invention, revise, replace and modification, the scope of the present invention be defined by the appended.
Claims (1)
1. a sprocket wheel heat treatment induction hardening process, it is characterised in that: processing step is as follows:
A, check that workpiece has flawless, the defect such as damage, shove charge;
B, workpiece is sent into cleaning machine being dried, the time is 1-2min;
C, carry out sensing heating, heat time heating time is 6-10s, and quenching machine power setting is 60%, electric current 500A, quench stop position 1.00mm, cool down position 200mm, speed is 600mm/min, with HX-200 medium quenching cool down, use spray mode cooling down;
D, sent into cleaning-drying 1-2min in cleaning machine by by the workpiece after quenching;
Dried workpiece is tempered by E immediately, and temperature is set as 180-200 DEG C, and temperature retention time is 2-3h;
After F, use cooling medium cooling, check metallographic structure by standard, test product hardness;
G, by after workpiece immersion in liquid preventives water 3-5min take out, complete Technology for Heating Processing.