CN106009842A - Waterproof heat-insulating coating and preparation method thereof - Google Patents
Waterproof heat-insulating coating and preparation method thereof Download PDFInfo
- Publication number
- CN106009842A CN106009842A CN201610571116.XA CN201610571116A CN106009842A CN 106009842 A CN106009842 A CN 106009842A CN 201610571116 A CN201610571116 A CN 201610571116A CN 106009842 A CN106009842 A CN 106009842A
- Authority
- CN
- China
- Prior art keywords
- water
- proof heat
- insulating paint
- parts
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses waterproof heat-insulating coating and a preparation method thereof. The waterproof heat-insulating coating is composed of the following materials according to parts by weight: with respect to 20 parts of organic silicon, 200-600 parts of water, 20-50 parts of a drying agent, 25-60 parts of a filling agent, 15-35 parts of acrylic acid, 250-400 parts of resin, and 6-20 parts of a dispersant. The waterproof heat-insulating coating disclosed herein is waterproof and heat-insulating.
Description
Technical field
The present invention relates to coating, be specifically related to water-proof heat-insulating paint and preparation method thereof.
Background technology
Coating can be coated in by different construction technologies to be protected or decorated body surface, and can be with
The formation of coated article body adheres to firmly, has some strength, continuous print solid film.Function based on coating
Dividing, coating can be divided into the most different types, and modal have insulating moulding coating and water-repellent paint etc..
Wavelength can be carried out instead by insulating moulding coating at solar infrared and the ultraviolet of 400nm-2500nm scope
Penetrate, it is to avoid the heat of the sun carries out accumulation at body surface and heats up, and plays heat insulation effect, meanwhile, again
Can automatically carry out heat radiation and reach the purpose of heat radiation, reduce the temperature of object, even if at cloudy day and night
Coating the most still possesses above-mentioned functions, also can radiations heat energy, thus reduce the temperature of object.Water-repellent paint
It is that a class is coated on the protective coating protected or form fine and close film after decorated body surface, in work
Journey building field has increasing application.
In use, the coating only with single performance tends not to enough meet use demand.When being used for being coated with
When being brushed with crackle and need heat insulation object, it is necessary to coating have concurrently waterproof with every thermal property, the most general
Lead to single insulating moulding coating or water-repellent paint cannot meet above-mentioned requirements.
Summary of the invention
An object of the present invention is to provide and has waterproof and insulative properties concurrently, and waterproof and heat-insulating with low cost
Coating.
It is a further object of the present invention to provide mild condition, environmental protection and waterproof and heat-insulating simple to operate to be coated with
The preparation method of material.
The water-proof heat-insulating paint that the present invention provides, is made up of the raw material of following mass parts, relative to 20 parts
Organosilicon, the content of water is 200-260 part, and the content of desiccant is 20-50 part, containing of filler
Amount is 25-60 part, and acrylic acid content is 15-35 part, and the content of resin is 250-400 part, dispersion
The content of agent is 6-20 part.
In above-mentioned water-proof heat-insulating paint, the concrete kind of desiccant used can be selected in wide scope
Select, but in order to improve the waterproof effect of this water-proof heat-insulating paint further, it is preferable that desiccant is selected from
One or more in calcium sulfate, calcium chloride and aluminium oxide.
In above-mentioned water-proof heat-insulating paint, the concrete kind of filler used can be selected in wide scope
Select, taking cost into account, it is preferable that filler one in Pulvis Talci, potter's clay and silicon dioxide
Or it is multiple.
In above-mentioned water-proof heat-insulating paint, the concrete kind of resin used can select in wide scope,
The most taking cost into account, it is preferable that resin is selected from organic siliconresin, fluorocarbon resin and polyvinyl acetate
One or more in resin.
In above-mentioned water-proof heat-insulating paint, the concrete kind of dispersant used can be selected in wide scope
Select, but in order to be further ensured that effective dispersion of this water-proof heat-insulating paint, it is preferable that dispersant is selected from
One or more in paraffin oil, Tissuemat E and OPE.
The preparation method of the above-mentioned water-proof heat-insulating paint that the present invention provides, the method includes: by water and resin
Mixing, prepares liquid material；Again desiccant, filler, acrylic acid, dispersant and organosilicon are added liquid material,
Stirring mixing, prepares water-proof heat-insulating paint；Calculate with mass parts, wherein, relative to 20 mass parts
Organosilicon, the content of described water is 200-260 part, and the content of described desiccant is 20-50 part, described
The content of filler is 25-60 part, and described acrylic acid content is 15-35 part, the content of described resin
For 250-400 part, the content of described dispersant is 6-20 part.
In above-mentioned preparation method, water and the mode of mixed with resin and time can be selected in wide scope
Select, consider from the preparation efficiency and energy-conserving and environment-protective angle of this water-proof heat-insulating paint, it is preferable that mixing
Mode is to be 10-20min ultrasonic, the ultrasonic time.
In above-mentioned preparation method, speed and the time of stirring mixing can select in wide scope, but
It is the preparation efficiency in order to improve this water-proof heat-insulating paint further, it is preferable that the speed of stirring mixing
500-800rpm, the time is 30-45min.
By technique scheme, the present invention by first preparing liquid material by water and crylic acid ester mixture, then incites somebody to action
Other each material is added thereto stirring mixing, is in close contact, produces synergism each other between material,
Thus prepare water-proof heat-insulating paint.The method is a kind of with low cost, mild condition, environmental protection and behaviour
Making simple method, prepared water-proof heat-insulating paint has concurrently waterproof and every thermal property.
Other features and advantages of the present invention will be described in detail in detailed description of the invention part subsequently.
Detailed description of the invention
Hereinafter the detailed description of the invention of the present invention is described in detail.It should be appreciated that this place is retouched
The detailed description of the invention stated is merely to illustrate and explains the present invention, is not limited to the present invention.
Embodiment 1
According to mass parts meter: 205 parts of water and 255 parts of organic siliconresins are carried out ultrasonic mixing 12min system
Obtain liquid material, then by 22 parts of calcium sulfate, 28 parts of Pulvis Talci, 17 parts of acrylic acid, 9 parts of paraffin oil and 20
Part organosilicon joins in liquid material, is stirred mixing 34min under the rotating speed of 550rpm, prepares anti-
Water insulating moulding coating A1.
Embodiment 2
According to mass parts meter: 255 parts of water and 380 parts of fluorocarbon resins are carried out ultrasonic mixing 18min and prepare
Liquid material, then by 47 parts of calcium chloride, 53 parts of potter's clay, 32 parts of acrylic acid, 17 parts of Tissuemat Es and 20 parts
Organosilicon joins in liquid material, is stirred mixing 41min, prepares waterproof under the rotating speed of 780rpm
Insulating moulding coating A2.
Embodiment 3
According to mass parts meter: 235 parts of water and 320 parts of polyvinyl acetate resins are carried out ultrasonic mixing 15min
Prepare liquid material, then by 32 parts of aluminium oxidies, 40 parts of silicon dioxide, 23 parts of acrylic acid, 12 parts of poly-second of oxidation
Alkene wax and 20 parts of organosilicons join in liquid material, are stirred mixing 38min under the rotating speed of 650rpm,
Prepare water-proof heat-insulating paint A3.
Comparative example 1
Coating B1 is prepared relative to embodiment 1, except that, the consumption adding calcium sulfate is 10 matter
Amount part.
Comparative example 2
Coating B2 is prepared relative to embodiment 2, except that, the consumption adding potter's clay is 5 mass
Part, the consumption of Tissuemat E is 0.5 mass parts.
Detection example 1
The coating preparing above-described embodiment and comparative example carries out waterproof experiment test, method particularly includes: will
The coating that above-described embodiment and comparative example prepare is brushed several times on the glass plate playing wax, coating total thickness
Degree is 1.5 millimeters, quiet for glass plate putting 7 days is placed in baking oven 50 DEG C ± 2 DEG C and is dried 24 hours, takes out
Place within 3 hours, be placed on pressure be 0.3MPa under water, keep 30 minutes, observe with or without Seepage,
Concrete outcome is shown in Table 1.
Detection example 2
The coating preparing above-described embodiment and comparative example is thermally shielded experiment test, method particularly includes: will
The coating that above-described embodiment and comparative example prepare is coated on cavate vessel surface, is placed under the sun by container sudden and violent
Test container internal temperature after shining 10 hours, concrete outcome is shown in Table 1.
Table 1
| A1 | A2 | A3 | B1 | B2 | |
| Waterproof experiment | Ne-leakage | Ne-leakage | Ne-leakage | Seepage | Seepage |
| Temperature/DEG C | 27 | 26 | 30 | 46 | 47 |
By above-mentioned detection example, the water-proof heat-insulating paint prepared by above-described embodiment can be waterproof, every
Heat.Being learnt by the testing result of above-described embodiment, the water-proof heat-insulating paint that the present invention provides has concurrently waterproof
With every thermal property, with low cost.Additionally, from the preparation process of the present invention it can be seen that the present invention carries
The preparation method mild condition of the water-proof heat-insulating paint of confession, environmental protection, preparation is simple.
The preferred embodiment of the present invention described in detail above, but, the present invention is not limited to above-mentioned reality
Execute the detail in mode, in the technology concept of the present invention, can be to the technical side of the present invention
Case carries out multiple simple variant, and these simple variant belong to protection scope of the present invention.
It is further to note that each the concrete technology described in above-mentioned detailed description of the invention is special
Levy, in the case of reconcilable, can be combined by any suitable means, in order to avoid need not
The repetition wanted, various possible compound modes are illustrated by the present invention the most separately.
Additionally, combination in any can also be carried out between the various different embodiment of the present invention, as long as its
Without prejudice to the thought of the present invention, by the raw material of each mass parts is mixed in a reservoir, contact, phase
Producing synergism between Hu, thus obtain water-proof heat-insulating paint, it should be considered as presently disclosed equally
Content.
Claims (9)
1. a water-proof heat-insulating paint, it is characterised in that described water-proof heat-insulating paint is by following mass parts
Raw material composition, the organosilicon relative to 20 parts, the content of water is 200-260 part, containing of desiccant
Amount is 20-50 part, and the content of filler is 25-60 part, and acrylic acid content is 15-35 part, resin
Content be 250-400 part, the content of dispersant is 6-20 part.
Water-proof heat-insulating paint the most according to claim 1, wherein, described desiccant is selected from sulphuric acid
One or more in calcium, calcium chloride and aluminium oxide.
Water-proof heat-insulating paint the most according to claim 1, wherein, described filler is selected from Talcum
One or more in powder, potter's clay and silicon dioxide.
Water-proof heat-insulating paint the most according to claim 1, wherein, described resin is selected from organosilicon
One or more in resin, fluorocarbon resin and polyvinyl acetate resin.
Water-proof heat-insulating paint the most according to claim 1, wherein, described dispersant is selected from paraffin
One or more in oil, Tissuemat E and OPE.
6. a preparation method for the water-proof heat-insulating paint as described in any one in claim 1-5,
It is characterized in that: by described water and mixed with resin, prepare liquid material；Again by described desiccant, filler,
Acrylic acid, dispersant and organosilicon add described liquid material, stirring mixing, prepare described water-proof heat-insulating paint.
The preparation method of water-proof heat-insulating paint the most according to claim 6, wherein, described mixing
Mode be ultrasonic, the described ultrasonic time is 10-20min.
The preparation method of water-proof heat-insulating paint the most according to claim 6, wherein, described stirring
The speed of mixing is 500-800rpm, and the time of described stirring mixing is 30-45min.
The preparation method of polyacrylate water-repellent paint the most according to claim 7, wherein, institute
The speed stating stirring mixing is 600-1000rpm, and the time is 1-3h.