CN106009586A - 一种高强度改性pc/abs合金 - Google Patents
一种高强度改性pc/abs合金 Download PDFInfo
- Publication number
- CN106009586A CN106009586A CN201610372276.1A CN201610372276A CN106009586A CN 106009586 A CN106009586 A CN 106009586A CN 201610372276 A CN201610372276 A CN 201610372276A CN 106009586 A CN106009586 A CN 106009586A
- Authority
- CN
- China
- Prior art keywords
- parts
- abs
- abs alloy
- high intensity
- compatilizer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种高强度改性PC/ABS合金,它由以下重量份的原料组成:PC 35‑68份,ABS 20‑35份,PP 5‑15份,玄武岩纤维 3‑6份,纳米SiO2 1.5‑3份,偶联剂 0.8‑1.5份,阻燃剂 1‑3份,抗氧剂 1‑2份,相容剂 1‑3份。本发明中,通过加入PP,可以提高材料耐低温性能,在低温条件下,材料的也具备优良的抗冲击性能。本发明中,通过加入玄武岩纤维,可以显著提高材料的抗冲击性能、拉伸强度及弯曲强度。本发明中,通过加入纳米SiO2,提高材料抗紫外线性能及抗老化、耐化学性能。
Description
技术领域
本发明属于高分子材料领域,具体涉及一种高强度改性PC/ABS合金。
背景技术
PC/ABS,聚碳酸酯和丙烯腈-丁二烯-苯乙烯共聚物和混合物,是由聚碳酸酯(Polycarbonate)和聚丙烯腈(ABS)合金而成的热可塑性塑胶,结合了两种材料的优异特性,ABS材料的成型性和PC的机械性、冲击强度和耐温、抗紫外线(UV)等性质,颜色是无透明颗粒,可广泛使用在汽车内部零件、商务机器、通信器材、家电用品及照明设备上。
PC/ABS作为世界上销售量最大的商业化聚合物合金,近几年都以10%左右的需求速度增长。PC/ABS较之PC提高了流动性,改善了加工性能,减少了制品对应力的敏感性,因而广泛应用于汽车内饰,外饰,车灯等高强度,高耐热零件。随着人们环保意识的提高,汽车行业ELV等环保可回收法规的相继出台,原材料厂商也不断提供新的解决方案。作为工程塑料行业的领先者适时的推出了新一代PC/ABS合金系列材料,它主要包括了耐水解稳定性的PC/ABS,用于免喷涂内饰的超低光泽PC/ABS,耐化学品优异不易被油漆等侵蚀的耐化学溶剂PC/ABS等系列产品。
随着PC/ABS合金的应用越来越广泛,如何进一步提高PC/ABS合金的综合性能就成为亟待解决的问题。
发明内容
本发明目的是提供一种综合性能更加优良的高强度改性PC/ABS合金。
本发明的技术方案为:一种高强度改性PC/ABS合金,它由以下重量份的原料组成:
PC 35-68份,
ABS 20-35份,
PP 5-15份,
玄武岩纤维 3-6份,
纳米SiO2 1.5-3份,
偶联剂 0.8-1.5份,
阻燃剂 1-3份,
抗氧剂 1-2份,
相容剂 1-3份。
优选地,它由以下重量份的原料组成:
PC 55份,
ABS 30份,
PP 10份,
玄武岩纤维 5份,
纳米SiO2 2份,
偶联剂 1份,
阻燃剂 2份,
抗氧剂 1.5份,
相容剂 2份。
进一步地,玄武岩纤维的直径为4-8μm,长度8-12mm。
进一步地,偶联剂为硅烷偶联剂。
进一步地,阻燃剂为聚硼硅氧烷。
进一步地,抗氧剂为2,6-三级丁基-4-甲基苯酚。
进一步地,相容剂为EMH。
本发明与现有技术相比具有如下优点:
1、本发明中,通过加入PP,可以提高材料耐低温性能,在低温条件下,材料的也具备优良的抗冲击性能。
2、本发明中,通过加入玄武岩纤维,可以显著提高材料的抗冲击性能、拉伸强度及弯曲强度。
3、本发明中,通过加入纳米SiO2,提高材料抗紫外线性能及抗老化、耐化学性能。
具体实施方式
实施例1
一种高强度改性PC/ABS合金,它由以下重量份的原料组成:
PC 35份,
ABS 35份,
PP 15份,
玄武岩纤维 3份,
纳米SiO2 3份,
偶联剂 0.8份,
阻燃剂 3份,
抗氧剂 1份,
相容剂 1份。
其中,玄武岩纤维的直径为4-8μm,长度8-12mm;偶联剂为硅烷偶联剂;阻燃剂为聚硼硅氧烷;抗氧剂为2,6-三级丁基-4-甲基苯酚;相容剂为EMH。
实施例2
一种高强度改性PC/ABS合金,它由以下重量份的原料组成:
PC 68份,
ABS 20份,
PP 5份,
玄武岩纤维 6份,
纳米SiO2 1.5份,
偶联剂 1.5份,
阻燃剂 1份,
抗氧剂 2份,
相容剂 3份。
其中,玄武岩纤维的直径为4-8μm,长度8-12mm;偶联剂为硅烷偶联剂;阻燃剂为聚硼硅氧烷;抗氧剂为2,6-三级丁基-4-甲基苯酚;相容剂为EMH。
实施例3
一种高强度改性PC/ABS合金,它由以下重量份的原料组成:
PC 55份,
ABS 30份,
PP 10份,
玄武岩纤维 5份,
纳米SiO2 2份,
偶联剂 1份,
阻燃剂 2份,
抗氧剂 1.5份,
相容剂 2份。
其中,玄武岩纤维的直径为4-8μm,长度8-12mm;偶联剂为硅烷偶联剂;阻燃剂为聚硼硅氧烷;抗氧剂为2,6-三级丁基-4-甲基苯酚;相容剂为EMH。
制备方法为:按重量配比将干燥的ABS和PP在加入高速混合机中,然后加入纳米SiO2,偶联剂,阻燃剂和抗氧剂,搅拌均匀后加入双螺杆挤出机中进行熔融共混后挤出,冷却造粒,然后将PC与造粒物加入高速混合机中,加入相容剂,搅拌混匀后加入双螺杆挤出机的主喂料口,同时从侧喂料口加入玄武岩纤维,控制加工温度240-260℃,螺杆转速200-400r/min,熔融共混后挤出、造粒即得成品。
以上所述实施例仅表达了本申请的具体实施方式,其描述较为具体和详细,但并不能因此而理解为对本申请保护范围的限制。应当指出的是,对于本领域的普通技术人员来说,在不脱离本申请技术方案构思的前提下,还可以做出若干变形和改进,这些都属于本申请的保护范围。
Claims (7)
1.一种高强度改性PC/ABS合金,其特征在于,它由以下重量份的原料组成:
PC 35-68份,
ABS 20-35份,
PP 5-15份,
玄武岩纤维 3-6份,
纳米SiO2 1.5-3份,
偶联剂 0.8-1.5份,
阻燃剂 1-3份,
抗氧剂 1-2份,
相容剂 1-3份。
2. 根据权利要求1所述的一种高强度改性PC/ABS合金,其特征在于,它由以下重量份的原料组成:
PC 55份,
ABS 30份,
PP 10份,
玄武岩纤维 5份,
纳米SiO2 2份,
偶联剂 1份,
阻燃剂 2份,
抗氧剂 1.5份,
相容剂 2份。
3. 根据权利要求1所述的一种高强度改性PC/ABS合金,其特征在于,玄武岩纤维的直径为4-8μm,长度8-12mm。
4. 根据权利要求1所述的一种高强度改性PC/ABS合金,其特征在于,偶联剂为硅烷偶联剂。
5. 根据权利要求1所述的一种高强度改性PC/ABS合金,其特征在于,阻燃剂为聚硼硅氧烷。
6. 根据权利要求1所述的一种高强度改性PC/ABS合金,其特征在于,抗氧剂为2,6-三级丁基-4-甲基苯酚。
7. 根据权利要求1所述的一种高强度改性PC/ABS合金,其特征在于,相容剂为EMH。