CN106007460B - 一种用于瓷砖粘结剂的抗流挂剂 - Google Patents
一种用于瓷砖粘结剂的抗流挂剂 Download PDFInfo
- Publication number
- CN106007460B CN106007460B CN201610365560.6A CN201610365560A CN106007460B CN 106007460 B CN106007460 B CN 106007460B CN 201610365560 A CN201610365560 A CN 201610365560A CN 106007460 B CN106007460 B CN 106007460B
- Authority
- CN
- China
- Prior art keywords
- ceramic tile
- sag
- tile bond
- agent
- sag agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明提供了一种用于瓷砖粘结剂的抗流挂剂,该抗流挂剂是由重量组分为60‑80%的羟丙基甲基纤维素醚、10‑20%分子量为700‑1200万的非离子型聚丙烯酰胺、5‑10%的气相二氧化硅和5‑10%的甲酸钙混合而成。本发明的抗流挂剂配方简单、制备容易,不仅能很好解决现有瓷砖粘结剂施工中易流挂且抗流挂性能随加水量影响很大、开放时间不够等问题,而且还能提高粘结剂的最终粘结强度和浸水强度,利用该抗流挂剂来取代现有瓷砖粘结剂配方中的纤维素醚和淀粉醚,在不明显改变粘结强度的条件下,一定范围内的加水量波动,采用该抗流挂剂的瓷砖粘结剂也具有很好的抗流挂效果,特别适合于水泥基粘结剂的使用。
Description
技术领域
本发明涉及一种助剂,尤其涉及一种有助于改善瓷砖粘结剂施工性能的助剂,更具体是涉及一种有助于解决现有瓷砖粘结剂施工中易流挂、抗流挂性能随加水量影响很大和开放时间不够等问题的抗流挂剂。
背景技术
现代家居装修中,瓷砖由于其美观且易于清洁等性能,已成为使用最为广泛的装修材料之一,随着瓷砖工艺的提升,大面积和低吸水量的瓷砖越来越普及,采用传统的水泥和砂的施工工艺已经无法达到很好的粘贴,粘贴过程中瓷砖易滑移、粘贴后易出现空鼓的现象经常出现,并且这种工艺的施工效率也很低,大大影响施工的进度。在这种情况下,抗流挂型瓷砖粘结剂的出现已成为必然,目前市面上粘结强度较好、具有一定抗流挂性能的瓷砖粘结剂的生产配方为:30-50%水泥、 40-60%细砂、0%-10%重钙、0.5-5%胶粉、0.1-0.6%纤维素醚和0.02-0.1%淀粉醚。
由上述配方可以看出,该配方是通过胶粉来提高粘结力,通过纤维素醚来改善开放时间,通过淀粉醚来改善改流挂效果,因此,纤维素醚和淀粉醚是抗流挂型瓷砖粘结剂必不可少的材料。但在实际的施工过程中,申请人发现,在某一特定的加水量下(一般在24%),上述配方的粘结剂具有很好的抗流挂效果,但只要加水量有轻微的偏离,如偏离了1%,那么抗流挂效果就明显下降或者完全消失,由于工人在施工过程中,无法完全按某一准确的加水量进行,所以抗流挂问题一直无法解决。因此,如何更好解决现场施工中瓷砖粘结剂的抗流挂性,从而解决瓷砖滑移的问题,是本领域技术人员迫切需要解决的技术问题。
发明内容
为解决以上存在的问题,本发明的目的是提供一种用于瓷砖粘结剂中的抗流挂剂,该抗流挂剂的加入,不仅可以解决现有瓷砖粘结剂施工中易流挂且抗流挂性能随加水量影响很大、开放时间不够等问题,而且还能提高粘结剂的最终粘结强度和浸水强度。
为实现以上目的,本发明的用于瓷砖粘结剂中的抗流挂剂,是由重量组分为60-80%的羟丙基甲基纤维素醚、10-20%分子量为700-1200万的非离子型聚丙烯酰胺、5-10%的气相二氧化硅和5-10%的甲酸钙混合而成。
上述抗流挂剂在水泥基瓷砖粘结剂中推荐添加量为瓷砖粘结剂总重量的0.3-0.6%。
为了更好改善施工性和开放时间,上述羟丙基甲基纤维素醚优选粘度在75000-100000mPa.s的速溶型羟丙基甲基纤维素醚。
为了更好提高抗流挂效果,上述非离子型聚丙烯酰胺的粒径优选80-100目。
为了更好改善粘结剂的施工性,上述气相二氧化硅为比表面积在200m2/g的亲水型气相二氧化硅。
为了更好提高粘结剂的早期强度和浸水强度,上述甲酸钙为净含量在98%以上、粒径在60-100目的甲酸钙。
本发明的用于瓷砖粘结剂中的抗流挂剂,采用具有较好保水性能、且对瓷砖粘结剂的开放时间有明显帮助的羟丙基甲基纤维素醚作为基础物质,配合在一定分子量范围内的非离子型聚丙烯酰胺,利用这种聚丙烯酰胺在碱性条件下具有很好增稠性和稳定性、且在砂浆中具有较好吸水率及在施工过程中不粘刀的特性,很好解决现有瓷砖粘结剂施工中易流挂且抗流挂性能随加水量影响很大、开放时间不够等问题,而添加一定量的二氧化硅和甲酸钙,可以很好提高施工速度以及粘结剂的早期粘结强度和浸水后的粘结强度。本发明的抗流挂剂,利用上述四种材料各自的性能特点和相互间的配合,并针对水泥基粘结剂对这种材料的性能要求,通过合理的选配,得到一种性能优越的抗流挂剂,利用该抗流挂剂来取代现有瓷砖粘结剂配方中的纤维素醚和淀粉醚,在不明显改变粘结强度的条件下,一定范围内的加水量波动,采用该抗流挂剂的瓷砖粘结剂也具有很好的抗流挂效果。
具体实施方式
下面通过具体的实施例对本发明的技术方案做进一步说明,但这些实施例并非用于限制本发明的保护范围,在不脱离本发明理念的前提下,对各组分的等同代换或各组分配比的调整,均应属于本发明的保护范围。
实施例1
1、配方(按重量百分比计)
2、制备
按上述配方将各组分搅拌均匀后,得到本发明的抗流挂剂1和抗流挂剂2。
3、应用
将上述抗流挂剂应用于水泥基瓷砖粘结剂中,下面是现有水泥基粘结剂的配方(按重量计)和添加本发明抗流挂剂的粘结剂的配方:
4、性能测试
按不同的加水量,根据JC/T547-2005《陶瓷墙地砖胶粘剂》对上述粘结剂进行性能测试,结果如下:
由以上结果可以看出,添加有本发明抗流挂剂的水泥基瓷砖粘结剂,在不同的加水量下,其抗滑移性能明显好于现有配方的瓷砖粘结剂,并且浸水后的拉伸胶粘强度和冻融循环后拉伸胶粘强度明显也好于现有配方的瓷砖粘结剂。
Claims (5)
1.一种用于瓷砖粘结剂中的抗流挂剂,其特征在于:所述抗流挂剂是由重量组分为60-80%的羟丙基甲基纤维素醚、10-20%分子量为700-1200万的非离子型聚丙烯酰胺、5-10%的气相二氧化硅和5-10%的甲酸钙混合而成;羟丙基甲基纤维素醚为粘度在75000-100000mPa· s的速溶型羟丙基甲基纤维素醚。
2.根据权利要求1所述的用于瓷砖粘结剂中的抗流挂剂,其特征在于:所述抗流挂剂在水泥基瓷砖粘结剂中推荐添加量为瓷砖粘结剂总重量的0.3-0.6%。
3.根据权利要求1或2所述的用于瓷砖粘结剂中的抗流挂剂,其特征在于:所述非离子型聚丙烯酰胺的粒径为80-100目。
4.根据权利要求3所述的用于瓷砖粘结剂中的抗流挂剂,其特征在于:所述气相二氧化硅为比表面积在200m2/g的亲水型气相二氧化硅。
5.根据权利要求4所述的用于瓷砖粘结剂中的抗流挂剂,其特征在于:所述甲酸钙为净含量在98%以上、粒径在60-100目的甲酸钙。