CN105985558A - Composition of antistatic plastic product and production method thereof - Google Patents
Composition of antistatic plastic product and production method thereof Download PDFInfo
- Publication number
- CN105985558A CN105985558A CN201510063311.7A CN201510063311A CN105985558A CN 105985558 A CN105985558 A CN 105985558A CN 201510063311 A CN201510063311 A CN 201510063311A CN 105985558 A CN105985558 A CN 105985558A
- Authority
- CN
- China
- Prior art keywords
- vistanex
- antistatic
- plastic goods
- static plastic
- antistatic master
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a composition of an antistatic plastic product and a production method thereof. The method comprises the following steps: mixing polyolefin resin, a polymer permanent antistatic agent, polyethylene wax, and zinc stearate, performing extrusion cutting on a mixture to obtain an antistatic master batch, mixing the antistatic master batch and polyene resin, performing film blowing and extruding or injection molding on the mixture to obtain various antistatic plastic products. Compared with the prior art, the composition has obvious and persistent antistatic performance, can increase the processing speed of the plastic product, saves the production cost, reduces waste, and increases the qualified product ratio.
Description
Technical field
The present invention relates to field of plastic products, particularly relate to constituent and the manufacture method of a kind of anti-static plastic goods.
Background technology
Owing to plastic is fabricated by through copolymerization mixing in process of manufacture under the high temperature conditions, therefore the dust that the product surface produced can produce electrostatic and adsorb in air, cause the dust of plastic to pollute.
Plastics Industry widely used antistatic mode is to directly utilize antistatic additive to mix according to a certain percentage with vistanex at present, is processed into plastic product.Although the product that this method prepares can play anlistatig effect, but the waste of raw material when the mixing time being the increase in production and equipment cleaning time and cleaning equipment, and goods in production can be produced disperse uneven or bubble owing to existing and cause waste.And manually production cost is high, efficiency is low.
Summary of the invention
The purpose of the present invention, is to provide constituent and the manufacture method of a kind of anti-static plastic goods, so that the technology of the present invention has following effect and promotes: antistatic effect is more notable, persistently；Not exclusively rely on water absorbent surface, so being affected smaller by the humidity of environment；Reduce the wastage of material caused due to cleaning equipment during use, reduce the disqualification rate of product.
For achieving the above object, the present invention provides the constituent of a kind of anti-static plastic goods, including antistatic master granule and vistanex；This antistatic master granule composition mainly by: vistanex, macromolecule permanent antistatic agent, Tissuemat E, zinc stearate etc. are according to suitably very than mixing granule.
Further, the present invention provides the manufacture method of a kind of anti-static plastic goods, including:
Step one: vistanex, macromolecule permanent antistatic agent, Tissuemat E, zinc stearate are respectively respectively put into high-speed mixer mixture according to appropriate percentage ratio, function mixing material good for mixture is put into equidirectional parallel double-screw extruder extrusion pelletizing, in this, as antistatic master granule；Wherein, antistatic master batch size specification is set in every particle diameter 1 ~ 3 millimeter of scope is optimal；This vistanex is polyisobutylene.
Step 2: uniformly mixed according to the requirements set proper proportion of shaped article with vistanex by antistatic master granule, uses the formulation of extrusion molding or injection forming method to make a reservation for all kinds of anti-static plastic goods；Wherein, vistanex is polypropylene.
Use above technical scheme, useful the having the technical effect that of the present invention
1, use antistatic master granule and vistanex to make plastic, due to wherein antistatic master granule main component by vistanex, macromolecule permanent antistatic agent, Tissuemat E, zinc stearate is mixing forms.By the effect of the vistanex in antistatic master granule, at plastics processing temperature (120-200 degree Celsius), antistatic master batch stability is strong, adds the plastic stability to light and heat.
2, in the antistatic master granule composition of the present invention, by using macromolecule permanent antistatic agent, the antistatic effect of products in kind can be effectively increased, and because it reaches antistatic effect to reduce material volume resistivity, not exclusively rely on water absorbent surface, so being affected smaller by the humidity of environment.
3, in the antistatic master granule composition of the present invention, by using zinc stearate, add the lubricity of antistatic master granule, reduce the pollution to equipment time mixing of antistatic master granule and vistanex, and then reduce the raw material and waste of time caused due to cleaning equipment, and improve the qualification rate of product.
In sum, use the present invention, there is antistatic effect more notable persistently, it is also possible to improve plastic process velocity, save production cost, reduce waste, improve conforming product rate.
Accompanying drawing explanation
Fig. 1 show the constituent manufacturing process block chart of anti-static plastic goods of the present invention.
Label declaration:
1, vistanex；2, macromolecule permanent antistatic agent；3, zinc stearate；4, Tissuemat E；5, antistatic master granule；6, extrusion molding or ejection formation produce all types of plastic goods.
Detailed description of the invention
Below in conjunction with embodiment, the invention will be further described, but is not intended as the foundation limiting the present invention.
Fig. 1 is constituent and the manufacturing process block chart of a kind of anti-static plastic goods.The constituent of anti-static plastic goods of the present invention, mainly comprises: 4% ~ 10% antistatic master granule 5,90% ~ 96% vistanex 1,5% ~ 10% Tissuemat E 4, heated mixing forms.Depending on the anti-static plastic article characteristic of the percentage by weight Main Basis molding to be manufactured of aforementioned each component.
Concrete, described antistatic master granule 4 composition includes: the granule that vistanex 1, macromolecule permanent antistatic agent 2, zinc stearate 3, Tissuemat E 4 are made according to percentage by weight.
Further, the constituent vistanex 1 of described antistatic master granule 5 is polyisobutylene.
Further, in the manufacture method of a kind of anti-static plastic goods of the explanation present invention, its work flow is as described below:
Step one: first the Tissuemat E 4 of the zinc stearate 3,5% ~ 10% of vistanex 1,15% ~ 30% macromolecule permanent antistatic agent 2,1% ~ 3% that percentage by weight is 65% ~ 80% is respectively put into high-speed mixer mixture, setting high-speed mixer rotating speed is between 845 ~ 1100 circle/point (r/min), function mixing material good for mixture is put into equidirectional parallel double-screw extruder extrusion pelletizing, this particle diameter is set in 1 ~ 3 millimeter (mm), length 2 ~ 4 millimeters (mm), in this, as antistatic master granule 5；Wherein, ten temperature controlled region design temperatures of parallel double-screw extruder group are heated to be optimal between 150 ~ 165 degrees Celsius.
Step 2: be manufactured into antistatic product plastic 6 with extrusion molding or injection molding method, its percentage composition includes: after 4% ~ 10% antistatic master granule 5,90% ~ 96% vistanex 1 uniformly mixes, and extrusion or ejection formation manufacture all kinds of antistatic, the plastic 6 of environmental protection；Wherein vistanex 1 is polypropylene.This plastic antistatic effect is more notable persistently, it is also possible to improves plastic process velocity, saves production cost, reduce waste, improves conforming product rate.
Being described in detail embodiment provided by the present invention above, principle and the embodiment of the present invention are set forth by specific case used herein, and the explanation of above example is only intended to help to understand method and the core concept thereof of the present invention.It should be pointed out that, for those skilled in the art, under the premise without departing from the principles of the invention, it is also possible to the present invention is carried out some improvement and modification, these improve and modify in the protection domain also falling into the claims in the present invention.
Claims (10)
1. the constituent of anti-static plastic goods, it is characterised in that including: antistatic master batch is heated with vistanex mixing to be formed.
The constituent of a kind of anti-static plastic goods the most according to claim 1, it is characterised in that wherein this antistatic master batch includes: the granule that vistanex, macromolecule permanent antistatic agent, Tissuemat E, zinc stearate cut into through mixing, extruding.
The constituent of a kind of anti-static plastic goods the most according to claim 2, it is characterized in that, wherein, described vistanex percentage by weight is 65% ~ 80%, zinc stearate percentage by weight is 1% ~ 3%, macromolecule permanent antistatic agent percentage by weight is 15% ~ 30%, and Tissuemat E percentage by weight is 5% ~ 10%.
The constituent of a kind of anti-static plastic goods the most according to claim 2, it is characterised in that the constituent vistanex of described antistatic master batch is polyisobutylene.
5. a manufacture method for anti-static plastic goods, its processing procedure includes:
Step one: vistanex, macromolecule permanent antistatic agent, Tissuemat E, zinc stearate are respectively put into high-speed mixer mixture, puts into equidirectional parallel double-screw extruder extrusion pelletizing, in this, as antistatic master granule by function mixing material good for mixture；
Step 2: uniformly mixed with vistanex by antistatic master granule, directly makes all kinds of moulded products by forming machine.
The manufacture method of a kind of anti-static plastic goods, it is characterised in that wherein the speed setting of the high-speed mixer of this fabrication steps one is between 845 ~ 1100 circle/point (r/min).
The manufacture method of a kind of anti-static plastic goods, it is characterised in that ten temperature controlled region design temperatures of the parallel double-screw extruder group of this fabrication steps one are heated between 150 ~ 165 degrees Celsius.
The manufacture method of a kind of anti-static plastic goods, it is characterised in that the antistatic master granule diameter of this fabrication steps one is at 1 ~ 3(mm) between, length is between 2 ~ 4 millimeters (mm).
The manufacture method of a kind of anti-static plastic goods, it is characterised in that the vistanex of this fabrication steps two is polypropylene.
The manufacture method of a kind of anti-static plastic goods, it is characterised in that the percentage composition of this fabrication steps two is: antistatic master granule 4% ~ 10%, vistanex is 90% ~ 96%, respectively adjusts according to shaped article purposes is different.