CN105985086A - Cement imitation wood component and preparation method thereof - Google Patents
Cement imitation wood component and preparation method thereof Download PDFInfo
- Publication number
- CN105985086A CN105985086A CN201510087509.9A CN201510087509A CN105985086A CN 105985086 A CN105985086 A CN 105985086A CN 201510087509 A CN201510087509 A CN 201510087509A CN 105985086 A CN105985086 A CN 105985086A
- Authority
- CN
- China
- Prior art keywords
- component
- cement
- imitation wood
- wood component
- corrosion inhibitor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a cement imitation wood component. The cement imitation wood component is prepared from, by weight, cement, lime, sand, broken stone, fly ash, blast furnace slag, iron tailings and gypsum. According to the cement imitation wood component, all the materials are added into a stirrer in a certain order and fully mixed with water to be uniform, a water reducing agent, a corrosion inhibitor and an expanding agent are finally added, and after pouring is conducted, natural curing molding is conducted. Three-dimensional wooden grain on the surface of the inner side of a silica gel membrane is transferred to the surface of the component, and after a wooden coating is applied, the overall component is just the same as wood, and the imitation effect is good; in addition, through testing, the pressure strength can reach 90 MPa, the component is not corroded after being soaked in saline water for 6 months, and the service life of the component is longer than that of a component prepared through a traditional formula.
Description
Technical field
The invention belongs to cement imitation wood component technology field, especially a kind of cement imitation wood component preparation method.
Background technology
Often building the amusement and leisure such as park, recreation ground place in people's daily life, these places can arrange wayside pavilion, protect
Hurdle, enclosure wall etc., some place, in order to highlight natural main body, often uses timber to build wayside pavilion, guardrail or enclosure wall etc., but
When time is longer or environment is more severe, timber there will be the problems such as burn into breakage.People, in order to solve this problem, develop
Go out cement imitation wood to manufacture said structure, first manufacture component, then multiple components are built into entirety, the raw material bag of component
Include cement, sand etc., it is also possible to adding rubble or reinforcing bar etc., then the Surface Machining at component goes out wood grain, has two here
The method of kind completes wood grain, specifically: 1. manual drawing: directly straight on the cement-imitated timber structure made with finer wire
Connect description, in the case of natural texture, can rely on workmen's to draw out various texture in opposite directions；2.
Fleece is set in cement imitation wood component surface, then utilizes cement and sand coating top layer, then use circular Wood-grain mould pressure
Roller.These two kinds of methods there is problems in that 1. manual modes are very time-consuming, adds at typical products in mass production and has a strong impact on production effect man-hour
Rate；2. manual mode compares the individual skill depending on workmen, a lot of texture deviation naturalness drawn, and very assists
Adjust；3., during the operation of Wood-grain mould pressure roller, add an operation, also reduce the production efficiency of typical products in mass production；4. defect rate
Higher.
Summary of the invention
It is an object of the invention to overcome the deficiencies in the prior art, it is provided that lightweight, intensity is high, long-lived a kind of cement-imitated
Wood component.
The present invention adopts the technical scheme that:
A kind of cement imitation wood component, it is characterised in that: include the following components mixed by weight:
And, the following components including mixing by weight:
And, described water reducer is melamine based water reducer.
And, described corrosion inhibitor is compounded amino alcohol corrosion inhibitor.
It is a further object to provide the preparation method of a kind of cement imitation wood component, it is characterised in that: comprise the following steps:
(1) prepare cement, Calx, sand, rubble, flyash, blast-furnace cinder, iron tailings and Gypsum Fibrosum by metering；
(2) cement, sand and rubble being added in blender, add water stirring 20 minutes；
(3) continuously add flyash, blast-furnace cinder, iron tailings and Gypsum Fibrosum, stir 20 minutes；
(4) add Gypsum Fibrosum and Calx, stir 20 minutes；
(5) it is eventually adding water reducer, corrosion inhibitor and extender and prepares concrete；
(6) the surrounding side at mould is coated with Silicone oil, this Silicone oil inner surface make the projection identical with wood grain and
Groove；
(7) by concreting to mould, natural curing molding；
(8), at the wooden coating of component surface brushing, complete component processing after drying.
Advantages of the present invention and good effect be:
In the present invention, prepare cement, Calx, sand, rubble, flyash, blast-furnace cinder, iron tailings and stone including by metering
Cream, fully mixes with water in sequence each material being added blender, is eventually adding water reducer, corrosion inhibitor and extender
Prepare, after pouring, natural curing molding.The stereo wooden texture surveying surface in Silicone oil is transferred to component surface, is coated with
After one layer of wooden coating, overall just the same with timber, simulated effect is good, and through test, comprcssive strength can reach 90,000,000
Handkerchief, saline soak does not the most corrode for 6 months, and service life is longer compared with conventional formulation.
Detailed description of the invention
Below in conjunction with embodiment, the present invention is further described, and following embodiment is illustrative, is not determinate, it is impossible to
Protection scope of the present invention is limited with following embodiment.
A kind of cement imitation wood component, the innovation of the present invention is: include the following components mixed by weight:
Preferred scheme is: include the following components mixed by weight:
Wherein, described water reducer is melamine based water reducer.Described corrosion inhibitor is compounded amino alcohol corrosion inhibitor.
The preparation method of above-mentioned cement imitation wood component comprises the following steps:
(1) prepare cement, Calx, sand, rubble, flyash, blast-furnace cinder, iron tailings and Gypsum Fibrosum by metering；
(2) cement, sand and rubble being added in blender, add water stirring 20 minutes；
(3) continuously add flyash, blast-furnace cinder, iron tailings and Gypsum Fibrosum, stir 20 minutes；
(4) add Gypsum Fibrosum and Calx, stir 20 minutes；
(5) it is eventually adding water reducer, corrosion inhibitor and extender and prepares concrete；
(6) the surrounding side at mould is coated with Silicone oil, this Silicone oil inner surface make the projection identical with wood grain and
Groove；
(7) by concreting to mould, natural curing molding；
(8), at the wooden coating of component surface brushing, complete component processing after drying.
In the present invention, prepare cement, Calx, sand, rubble, flyash, blast-furnace cinder, iron tailings and stone including by metering
Cream, fully mixes with water in sequence each material being added blender, is eventually adding water reducer, corrosion inhibitor and extender
Prepare, after pouring, natural curing molding.The stereo wooden texture surveying surface in Silicone oil is transferred to component surface, is coated with
After one layer of wooden coating, overall just the same with timber, simulated effect is good, and through test, comprcssive strength can reach 90,000,000
Handkerchief, saline soak does not the most corrode for 6 months, and service life is longer compared with conventional formulation.
Claims (5)
1. a cement imitation wood component, it is characterised in that: include the following components mixed by weight:
A kind of cement imitation wood component the most according to claim 1, it is characterised in that: include mixing by weight with
Lower component:
A kind of cement imitation wood component the most according to claim 1 and 2, it is characterised in that: described water reducer is melamine system
Water reducer.
A kind of cement imitation wood component the most according to claim 3, it is characterised in that: described corrosion inhibitor is compounded amino alcohol
Corrosion inhibitor.
5. the preparation method of a kind of cement imitation wood component described in a claim 4, it is characterised in that: comprise the following steps:
(1) prepare cement, Calx, sand, rubble, flyash, blast-furnace cinder, iron tailings and Gypsum Fibrosum by metering；
(2) cement, sand and rubble being added in blender, add water stirring 20 minutes；
(3) continuously add flyash, blast-furnace cinder, iron tailings and Gypsum Fibrosum, stir 20 minutes；
(4) add Gypsum Fibrosum and Calx, stir 20 minutes；
(5) it is eventually adding water reducer, corrosion inhibitor and extender and prepares concrete；
(6) the surrounding side at mould is coated with Silicone oil, this Silicone oil inner surface make the projection identical with wood grain and
Groove；
(7) by concreting to mould, natural curing molding；
(8), at the wooden coating of component surface brushing, complete component processing after drying.