CN105950264A - Lubricant for enameled wires resistant to oil immersion - Google Patents
Lubricant for enameled wires resistant to oil immersion Download PDFInfo
- Publication number
- CN105950264A CN105950264A CN201610309442.3A CN201610309442A CN105950264A CN 105950264 A CN105950264 A CN 105950264A CN 201610309442 A CN201610309442 A CN 201610309442A CN 105950264 A CN105950264 A CN 105950264A
- Authority
- CN
- China
- Prior art keywords
- parts
- lubricant
- paraffin
- acid
- enameled wires
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A lubricant for enameled wires resistant to oil immersion is prepared from raw materials in parts by weight as follows: 48-60 parts of paraffin, 32-39 parts of docosahexaenoic acid, 15-25 parts of sodium stearate, 15-25 parts of evening primrose seed oil, 11-17 parts of ethylene oxide, 8-10 parts of peanut oil, 8-10 parts of succinic acid diene propyl ester, 50-60 parts of absolute ethyl alcohol and 10-18 parts of a lubrication aid. Breakage of the enameled wires cannot be caused by use of the lubricant, wire winding and unwinding speeds are increased, the lubricant is particularly applicable to lubrication of the enameled wires resistant to oil immersion, properties of the enameled wires can be stabilized, the service life of the enameled wires can be prolonged, and meanwhile, the lubricant is very good in high-temperature resistance and low-temperature resistance.
Description
Technical field
The present invention relates to technical field of lubricant, be specifically related to a kind of oil resistant dipping lacquer envelope curve with lubricator.
Background technology
Enamel-covered wire is the main raw material(s) of the products such as motor, electrical equipment and household electrical appliance, electric power the most in recent years
Industrial realization maintains sustained and rapid growth, and developing rapidly of household electrical appliance is brought broader to the application of enamel-covered wire
Field, the thing followed is to have higher requirement enamel-covered wire.Product structure for this enamel-covered wire is adjusted
Just inevitable, matched raw material (copper, paint), enamelling technique, technological equipment and detection means etc. are also
Anxious research to be developed.
Enamel-covered wire includes heart yearn and is coated in the enamelled coating outside heart yearn, after the annealed softening of bare wire, then passes through
Repeatedly painting, baking forms, and possesses mechanical performance, chemical property, electrical property, the big performance of hot property four.
Enamel-covered wire makes with lubricator when producing, and winding displacement can be made neat, and take-up is tight.At present, China's paint
Envelope curve is to use kerosene, countless transformer oil as the lubricant of surface of insulating layer mostly in producing.Also have
It is dissolved in gasoline as enameled wire surface lubricating oil with paraffin.But, current lubricant is easy when using
Cause enamel-covered wire coiling, unwrapping wire fracture, and paraffin wax lubricants easily has Precipitation.
Summary of the invention
The technical problem to be solved is to provide a kind of oil resistant dipping lacquer envelope curve with lubricator.
The technical problem to be solved realizes by the following technical solutions:
A kind of oil resistant dipping lacquer envelope curve with lubricator, is made up of the raw material of following weight portion: paraffin 48-60 part,
Docosahexenoic acid 32-39 part, sodium stearate 15-25 part, Radix Oenotherae erythrosepalae oil 15-25 part, oxirane
11-17 part, Oleum Arachidis hypogaeae semen 8-10 part, diallyl succinate 8-10 part, dehydrated alcohol 50-60 part, help profit
Agent 10-18 part;
The described profit agent that helps is made up of the raw material of following weight portion: polyamidoimide 22-31 part, sorbitol
Acid anhydride fatty acid ester 22-31 part, Oleum Ricini 22-31 part, isopropyl myristate 22-31 part, acenaphthylene 5-13
Part, Crataegolic acid 5-13 part, 4,4 '-benzidine ether 5-13 part, 2-Pyrrolidone 5-13 part, γ-
Butyrolactone 15-17 part, propylgallate 15-17 part, b-sitosterol 15-17 part, aliphatic acid polyethenoxy
Ester 15-17 part, sorbitan carboxylic esters 5-6 part, 4-benzylaminoquinoline 5-6 part, maleic anhydride
5-6 part;Preparation method is, is sufficiently mixed by each raw material, processes 2 hours, process in joining pressure cooker
Temperature is 90-105 DEG C, and processing pressure is 0.5-0.8MPa.
With lubricator, preparation method is as follows for a kind of oil resistant dipping lacquer envelope curve:
(1) dehydrated alcohol is put into 0 DEG C of Cold storage in the refrigerator 1 hour, after taking-up, together put into container with paraffin
Interior heating, until paraffin all melts;
(2) by docosahexenoic acid, sodium stearate, Radix Oenotherae erythrosepalae oil, oxirane, Oleum Arachidis hypogaeae semen, amber
Amber diallyl phthalate joins mix homogeneously in said vesse, is then placed in-8 DEG C of freezers freezing 20 minutes,
Taking-up post-heating is to 80 DEG C, and keeps 80 DEG C of temperature 5 minutes;
(3) profit agent will be helped to join in step (2) gained mixture, stir 10 minutes, after cooling i.e.
Obtain lubricant.
The invention has the beneficial effects as follows: lubricant of the present invention does not results in enamel-covered wire fracture when using, accelerate
Coiling payingoff speed, lubricant of the present invention is particularly suitable for oil resistant dipping lacquer envelope curve lubrication and uses, can temperature enamel-cover
Linear matter, extends enamel-covered wire service life, and meanwhile, lubricant is high temperature resistant, resistance to low temperature the best.
Detailed description of the invention
For the technological means making the present invention realize, creation characteristic, reach purpose and effect and be readily apparent from
Solve, below in conjunction with specific embodiment, the present invention is expanded on further.
Embodiment 1
A kind of oil resistant dipping lacquer envelope curve with lubricator, is made up of the raw material of following weight portion: 54 parts of paraffin, two
Dodecahexaene acid 35 parts, sodium stearate 20 parts, Radix Oenotherae erythrosepalae oil 20 parts, 14 parts of oxirane, Oleum Arachidis hypogaeae semen 9
Part, diallyl succinate 9 parts, dehydrated alcohol 55 parts, help profit agent 14 parts;
The described profit agent that helps is made up of the raw material of following weight portion: polyamidoimide 26 parts, sorbitol anhydride
Fatty acid ester 26 parts, Oleum Ricini 26 parts, isopropyl myristate 26 parts, acenaphthylene 9 parts, Crataegolic acid 9
Part, 4,9 parts of 4 '-benzidine ether, 2-Pyrrolidone 9 parts, gamma-butyrolacton 16 parts, gallic acid
Propyl ester 16 parts, b-sitosterol 16 parts, polyoxyethylene carboxylate 16 parts, sorbitan carboxylic esters 5 parts,
4-benzylaminoquinoline 5 parts, maleic anhydride 5 parts;Preparation method is, is sufficiently mixed by each raw material,
Processing 2 hours in joining pressure cooker, treatment temperature is 90-105 DEG C, and processing pressure is 0.5-0.8MPa.
With lubricator, preparation method is as follows for a kind of oil resistant dipping lacquer envelope curve:
(1) dehydrated alcohol is put into 0 DEG C of Cold storage in the refrigerator 1 hour, after taking-up, together put into container with paraffin
Interior heating, until paraffin all melts;
(2) by docosahexenoic acid, sodium stearate, Radix Oenotherae erythrosepalae oil, oxirane, Oleum Arachidis hypogaeae semen, amber
Amber diallyl phthalate joins mix homogeneously in said vesse, is then placed in-8 DEG C of freezers freezing 20 minutes,
Taking-up post-heating is to 80 DEG C, and keeps 80 DEG C of temperature 5 minutes;
(3) profit agent will be helped to join in step (2) gained mixture, stir 10 minutes, after cooling i.e.
Obtain lubricant.
Embodiment 2
A kind of oil resistant dipping lacquer envelope curve with lubricator, is made up of the raw material of following weight portion: 48 parts of paraffin, two
Dodecahexaene acid 32 parts, sodium stearate 15 parts, Radix Oenotherae erythrosepalae oil 15 parts, 11 parts of oxirane, Oleum Arachidis hypogaeae semen 8
Part, diallyl succinate 8 parts, dehydrated alcohol 50 parts, help profit agent 10 parts;
The described profit agent that helps is made up of the raw material of following weight portion: polyamidoimide 22 parts, sorbitol anhydride
Fatty acid ester 22 parts, Oleum Ricini 22 parts, isopropyl myristate 22 parts, acenaphthylene 5 parts, Crataegolic acid 5
Part, 4,5 parts of 4 '-benzidine ether, 2-Pyrrolidone 5 parts, gamma-butyrolacton 15 parts, gallic acid
Propyl ester 15 parts, b-sitosterol 15 parts, polyoxyethylene carboxylate 15 parts, sorbitan carboxylic esters 5 parts,
4-benzylaminoquinoline 5 parts, maleic anhydride 5 parts;Preparation method is, is sufficiently mixed by each raw material,
Processing 2 hours in joining pressure cooker, treatment temperature is 90-105 DEG C, and processing pressure is 0.5-0.8MPa.
With lubricator, preparation method is as follows for a kind of oil resistant dipping lacquer envelope curve:
(1) dehydrated alcohol is put into 0 DEG C of Cold storage in the refrigerator 1 hour, after taking-up, together put into container with paraffin
Interior heating, until paraffin all melts;
(2) by docosahexenoic acid, sodium stearate, Radix Oenotherae erythrosepalae oil, oxirane, Oleum Arachidis hypogaeae semen, amber
Amber diallyl phthalate joins mix homogeneously in said vesse, is then placed in-8 DEG C of freezers freezing 20 minutes,
Taking-up post-heating is to 80 DEG C, and keeps 80 DEG C of temperature 5 minutes;
(3) profit agent will be helped to join in step (2) gained mixture, stir 10 minutes, after cooling i.e.
Obtain lubricant.
Embodiment 3
A kind of oil resistant dipping lacquer envelope curve with lubricator, is made up of the raw material of following weight portion: 60 parts of paraffin, two
Dodecahexaene acid 39 parts, sodium stearate 25 parts, Radix Oenotherae erythrosepalae oil 25 parts, 17 parts of oxirane, Oleum Arachidis hypogaeae semen
10 parts, diallyl succinate 10 parts, dehydrated alcohol 60 parts, help profit agent 18 parts;
The described profit agent that helps is made up of the raw material of following weight portion: polyamidoimide 31 parts, sorbitol anhydride
Fatty acid ester 31 parts, Oleum Ricini 31 parts, isopropyl myristate 31 parts, acenaphthylene 13 parts, Crataegolic acid
13 parts, 4,13 parts of 4 '-benzidine ether, 2-Pyrrolidone 13 parts, gamma-butyrolacton 17 parts, no food
Sub-propyl propionate 17 parts, b-sitosterol 17 parts, polyoxyethylene carboxylate 17 parts, sorbitan carboxylic esters 6
Part, 4-benzylaminoquinoline 6 parts, maleic anhydride 6 parts;Preparation method is, by the most mixed for each raw material
Closing, process 2 hours in joining pressure cooker, treatment temperature is 90-105 DEG C, and processing pressure is
0.5-0.8MPa。
With lubricator, preparation method is as follows for a kind of oil resistant dipping lacquer envelope curve:
(1) dehydrated alcohol is put into 0 DEG C of Cold storage in the refrigerator 1 hour, after taking-up, together put into container with paraffin
Interior heating, until paraffin all melts;
(2) by docosahexenoic acid, sodium stearate, Radix Oenotherae erythrosepalae oil, oxirane, Oleum Arachidis hypogaeae semen, amber
Amber diallyl phthalate joins mix homogeneously in said vesse, is then placed in-8 DEG C of freezers freezing 20 minutes,
Taking-up post-heating is to 80 DEG C, and keeps 80 DEG C of temperature 5 minutes;
(3) profit agent will be helped to join in step (2) gained mixture, stir 10 minutes, after cooling i.e.
Obtain lubricant.
The ultimate principle of the present invention and principal character and advantages of the present invention have more than been shown and described.One's own profession
Skilled person will appreciate that of industry, the present invention is not restricted to the described embodiments, above-described embodiment and explanation
The principle that the present invention is simply described described in book, without departing from the spirit and scope of the present invention,
The present invention also has various changes and modifications, and these changes and improvements both fall within claimed invention model
In enclosing.Claimed scope is defined by appending claims and equivalent thereof.
Claims (2)
1. an oil resistant dipping lacquer envelope curve is with lubricator, it is characterised in that be made up of the raw material of following weight portion:
Paraffin 48-60 part, docosahexenoic acid 32-39 part, sodium stearate 15-25 part, Radix Oenotherae erythrosepalae oil 15-25
Part, oxirane 11-17 part, Oleum Arachidis hypogaeae semen 8-10 part, diallyl succinate 8-10 part, dehydrated alcohol 50-60
Part, help profit agent 10-18 part;
The described profit agent that helps is made up of the raw material of following weight portion: polyamidoimide 22-31 part, sorbitol
Acid anhydride fatty acid ester 22-31 part, Oleum Ricini 22-31 part, isopropyl myristate 22-31 part, acenaphthylene 5-13
Part, Crataegolic acid 5-13 part, 4,4 '-benzidine ether 5-13 part, 2-Pyrrolidone 5-13 part, γ-
Butyrolactone 15-17 part, propylgallate 15-17 part, b-sitosterol 15-17 part, aliphatic acid polyethenoxy
Ester 15-17 part, sorbitan carboxylic esters 5-6 part, 4-benzylaminoquinoline 5-6 part, maleic anhydride
5-6 part;Preparation method is, is sufficiently mixed by each raw material, processes 2 hours, process in joining pressure cooker
Temperature is 90-105 DEG C, and processing pressure is 0.5-0.8MPa.
2. a kind of oil resistant dipping lacquer envelope curve as claimed in claim 1 is with lubricator, it is characterised in that preparation
Method is as follows:
(1) dehydrated alcohol is put into 0 DEG C of Cold storage in the refrigerator 1 hour, after taking-up, together put into container with paraffin
Interior heating, until paraffin all melts;
(2) by docosahexenoic acid, sodium stearate, Radix Oenotherae erythrosepalae oil, oxirane, Oleum Arachidis hypogaeae semen, amber
Amber diallyl phthalate joins mix homogeneously in said vesse, is then placed in-8 DEG C of freezers freezing 20 minutes,
Taking-up post-heating is to 80 DEG C, and keeps 80 DEG C of temperature 5 minutes;
(3) profit agent will be helped to join in step (2) gained mixture, stir 10 minutes, after cooling i.e.
Obtain lubricant.