CN105945375B - A kind of filamentary silver volume flower welding method - Google Patents
A kind of filamentary silver volume flower welding method Download PDFInfo
- Publication number
- CN105945375B CN105945375B CN201610496984.6A CN201610496984A CN105945375B CN 105945375 B CN105945375 B CN 105945375B CN 201610496984 A CN201610496984 A CN 201610496984A CN 105945375 B CN105945375 B CN 105945375B
- Authority
- CN
- China
- Prior art keywords
- silver
- parts
- filamentary
- filamentary silver
- cleaning solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to filamentary silvers to compile flower welding production technical field, and especially a kind of filamentary silver compiles flower welding method, by the way that block silver is melted, it is modified, cooling beat, cleaning solution washing, after wire drawing machine wire drawing, cleaning solution tripperfaden, obtain filamentary silver；Using liquid silver as solder, filamentary silver is welded on silverware, baking step so that the surface that filamentary silver is compiled after flower welding is smooth, weld mark is not seen, so that silver jeweleries is specious, and the suppleness of filamentary silver is increased, improves the difficulty that filamentary silver compiles flower, and after soldering, it does not need to higher temperature and carries out baking processing, reduce the energy consumption after welding, reduce silver jeweleries cost of manufacture.
Description
Technical field
The present invention relates to filamentary silvers to compile flower welding production technical field, and especially a kind of filamentary silver compiles flower welding method.
Background technology
Silver jeweleries as a kind of cultural phenomenon in history once by it is many it is national favor, become multiculture exchange carrier it
One, the processing of Miao ethnic group's silver jeweleries is completed with the manual operations in family workshop entirely；As needed, silversmith is first the white of melting
Silvery flakiness, silver bar or filamentary silver, using pressure, it is few, the techniques such as carve, hug, make exquisite grain pattern, then weld or be woven into again
Type, however the silver jeweleries that flower welding method obtains is compiled in existing fine silver wire drawing, has apparent weld mark, welding position surface is not only
Cunning is smooth.
It is studied for this purpose, there is researcher to compile flower welding method to fine silver wire drawing in the prior art, by silver strip or silver bar
Be fabricated to silver powder, and handled with borax, pure water Hybrid Heating tanning, then the filigree accessory of welding is put into immersion, then by its
After drying, welding so that do not see that weld mark, smooth in appearance are smooth in silver jeweleries surface.
However, in the prior art, during compiling flower soldering for filamentary silver, silver jeweleries production cannot still be met
The requirement of product mass production, and after welding, high-temperature baking is needed to handle so that the energy consumption of making is higher, and cost is larger.
It is studied in consideration of it, this is studied by compiling flower welding procedure to filamentary silver, is silver jeweleries production field, for filamentary silver
The method that flower is compiled in welding provides a kind of new approaches.
Invention content
In order to solve the above technical problems existing in the prior art, the present invention provides a kind of filamentary silver volume flower welding method.
It is achieved particular by following technical scheme：
A kind of filamentary silver volume flower welding method, block silver is melted, is modified, cooling is beaten, cleaning solution washs, wire drawing machine wire drawing
Afterwards, cleaning solution tripperfaden obtains filamentary silver；Using liquid silver as solder, filamentary silver is welded on silverware, is dried, you can.
A kind of filamentary silver volume flower welding method, includes the following steps：
(1) block silver is placed in and is melted in pond, after being melted, modifier modification is added and handles 10-20min, then its is cold
But it solidifies, and beats into the thin slice of 0.5-1.3cm thickness；
(2) thin slice in step (1) is placed in cleaning solution and impregnates 2-5min, and use distilled water flushing 2-4 times, then
Wire drawing process on wire drawing machine, and the filamentary silver that drawing is formed is drenched using cleaning solution, in 30-50 DEG C of drying and processing 10-20min, is obtained
Filamentary silver；
(3) filamentary silver is placed in immersion treatment 20-30min in liquid silver, and after being drawn off, using liquid silver as solder,
Filamentary silver is welded on silverware, it is to toast 20-30s at 60-90 DEG C to be placed in temperature, you can.
The modifying agent, material composition in parts by weight be 0.1-0.5 parts of ethyl acetate, 0.1-0.5 parts of styrene,
4-9 parts of mica powder, 1-3 parts of blanc fixe, 0.1-0.4 parts of copper powder, 1-3 parts of aluminium powder, preparation method are to mix above-mentioned raw materials to mix
After even, it is 20-30min to be handled at 60-80 DEG C, then its ground 160-300 mesh is sieved to be placed in temperature.
The cleaning solution, material composition are 1-3 parts of cocoanut fatty acid diethanolamide, acrylic in parts by weight
1-3 parts of benzene, 10-20 parts of distilled water, 0.1-0.7 parts of tall oil, 10-15 parts of mineral oil, 1-3 parts of triethanolamine borate, cottonseed
60-70 parts oily, 5-7 parts of nano-silver powder.
The cleaning solution, preparation method are by cocoanut fatty acid diethanolamide, propenylbenzene, tall oil, mineral
Oil, triethanolamine borate, cottonseed oil are uniformly mixed, and obtain batch mixing a；Nano-silver powder is added in distilled water, using ultrasonic disperse
10-20min is handled, adds in batch mixing a, stirs evenly, you can.
The ultrasonic disperse, supersonic frequency 5-10MHz.
Compared with prior art, technique effect of the invention is embodied in：
By the way that block silver is melted, it is modified, cooling beat, cleaning solution washing, after wire drawing machine wire drawing, cleaning solution tripperfaden, obtain silver-colored
Silk；Using liquid silver as solder, filamentary silver is welded on silverware, baking step so that filamentary silver compiles the surface light after flower welding
It is sliding, do not see weld mark so that silver jeweleries it is specious, and increase the suppleness of filamentary silver, improve filamentary silver and compile flower
Difficulty, and after soldering, do not need to higher temperature and carry out baking processing, the energy consumption after welding is reduced, is reduced
Silver jeweleries cost of manufacture.
Using liquid silver as solder so that in the welding process, liquid silver filamentary silver is firm, seamless can be bonded in
In silver jeweleries, after the drying, do not see the weld seam of welding, and liquid silver is during baking, constantly with filamentary silver device into
Row fusion, improves aesthetics, and the appearance for improving silver jeweleries is beautiful.
Specific implementation mode
It is limited with reference to specific embodiment technical scheme of the present invention is further, but claimed
Range describes made by being not only limited to.
Embodiment 1
A kind of filamentary silver volume flower welding method, includes the following steps：
(1) block silver is placed in and is melted in pond, after being melted, modifier modification is added and handles 10min, then is cooled to coagulate
Gu and beating into the thin slice of 0.5cm thickness；
(2) thin slice in step (1) is placed in cleaning solution and impregnates 2min, and use distilled water flushing 2 times, then in wire drawing
Wire drawing process on machine, and the filamentary silver that drawing is formed is drenched using cleaning solution, in 30 DEG C of drying and processing 10min, obtains filamentary silver；
(3) filamentary silver is placed in immersion treatment 20min in liquid silver, and after being drawn off, it, will be silver-colored using liquid silver as solder
Wire bond is connected on silverware, and it is to toast 20s at 60 DEG C to be placed in temperature, you can.
The modifying agent, material composition by weight be ethyl acetate 0.1kg, styrene 0.1kg, mica powder 4kg,
Blanc fixe 1kg, copper powder 0.1kg, aluminium powder 1kg, preparation method are after mixing above-mentioned raw materials mixing thoroughly, and it is at 60 DEG C to be placed in temperature
20min is handled, then its ground 160 mesh is sieved.
The cleaning solution, material composition are cocoanut fatty acid diethanolamide 1kg, propenylbenzene by weight
1kg, distilled water 10kg, tall oil 0.1kg, mineral oil 10kg, triethanolamine borate 1kg, cottonseed oil 60kg, nano-silver powder
5kg。
The cleaning solution, preparation method are by cocoanut fatty acid diethanolamide, propenylbenzene, tall oil, mineral
Oil, triethanolamine borate, cottonseed oil are uniformly mixed, and obtain batch mixing a；Nano-silver powder is added in distilled water, using ultrasonic disperse
10min is handled, adds in batch mixing a, stirs evenly, you can.The ultrasonic disperse, supersonic frequency 5MHz.
Embodiment 2
A kind of filamentary silver volume flower welding method, includes the following steps：
(1) block silver is placed in and is melted in pond, after being melted, modifier modification is added and handles 20min, then is cooled to coagulate
Gu and beating into the thin slice of 1.3cm thickness；
(2) thin slice in step (1) is placed in cleaning solution and impregnates 5min, and use distilled water flushing 4 times, then in wire drawing
Wire drawing process on machine, and the filamentary silver that drawing is formed is drenched using cleaning solution, in 50 DEG C of drying and processing 20min, obtains filamentary silver；
(3) filamentary silver is placed in immersion treatment 30min in liquid silver, and after being drawn off, it, will be silver-colored using liquid silver as solder
Wire bond is connected on silverware, and it is to toast 30s at 90 DEG C to be placed in temperature, you can.
The modifying agent, material composition by weight be ethyl acetate 0.5kg, styrene 0.5kg, mica powder 9kg,
Blanc fixe 3kg, copper powder 0.4kg, aluminium powder 3kg, preparation method are after mixing above-mentioned raw materials mixing thoroughly, and it is at 80 DEG C to be placed in temperature
30min is handled, then its ground 300 mesh is sieved.
The cleaning solution, material composition are cocoanut fatty acid diethanolamide 3kg, propenylbenzene by weight
3kg, distilled water 20kg, tall oil 0.7kg, mineral oil 15kg, triethanolamine borate 3kg, cottonseed oil 70kg, nano-silver powder
7kg。
The cleaning solution, preparation method are by cocoanut fatty acid diethanolamide, propenylbenzene, tall oil, mineral
Oil, triethanolamine borate, cottonseed oil are uniformly mixed, and obtain batch mixing a；Nano-silver powder is added in distilled water, using ultrasonic disperse
20min is handled, adds in batch mixing a, stirs evenly, you can.
The ultrasonic disperse, supersonic frequency 10MHz.
Embodiment 3
A kind of filamentary silver volume flower welding method, includes the following steps：
(1) block silver is placed in and is melted in pond, after being melted, modifier modification is added and handles 15min, then is cooled to coagulate
Gu and beating into the thin slice of 0.9cm thickness；
(2) thin slice in step (1) is placed in cleaning solution and impregnates 3min, and use distilled water flushing 3 times, then in wire drawing
Wire drawing process on machine, and the filamentary silver that drawing is formed is drenched using cleaning solution, in 40 DEG C of drying and processing 15min, obtains filamentary silver；
(3) filamentary silver is placed in immersion treatment 25min in liquid silver, and after being drawn off, it, will be silver-colored using liquid silver as solder
Wire bond is connected on silverware, and it is to toast 25s at 80 DEG C to be placed in temperature, you can.
The modifying agent, material composition by weight be ethyl acetate 0.4kg, styrene 0.3kg, mica powder 7kg,
Blanc fixe 2kg, copper powder 0.3kg, aluminium powder 2kg, preparation method are after mixing above-mentioned raw materials mixing thoroughly, and it is at 70 DEG C to be placed in temperature
25min is handled, then its ground 200 mesh is sieved.
The cleaning solution, material composition are cocoanut fatty acid diethanolamide 2kg, propenylbenzene by weight
2kg, distilled water 15kg, tall oil 0.6kg, mineral oil 13kg, triethanolamine borate 2kg, cottonseed oil 65kg, nano-silver powder
6kg。
The cleaning solution, preparation method are by cocoanut fatty acid diethanolamide, propenylbenzene, tall oil, mineral
Oil, triethanolamine borate, cottonseed oil are uniformly mixed, and obtain batch mixing a；Nano-silver powder is added in distilled water, using ultrasonic disperse
15min is handled, adds in batch mixing a, stirs evenly, you can.
The ultrasonic disperse, supersonic frequency 8MHz.
Embodiment 4
A kind of filamentary silver volume flower welding method, includes the following steps：
(1) block silver is placed in and is melted in pond, after being melted, modifier modification is added and handles 15min, then is cooled to coagulate
Gu and beating into the thin slice of 1cm thickness；
(2) thin slice in step (1) is placed in cleaning solution and impregnates 4min, and use distilled water flushing 3 times, then in wire drawing
Wire drawing process on machine, and the filamentary silver that drawing is formed is drenched using cleaning solution, in 30 DEG C of drying and processing 20min, obtains filamentary silver；
(3) filamentary silver is placed in immersion treatment 20min in liquid silver, and after being drawn off, it, will be silver-colored using liquid silver as solder
Wire bond is connected on silverware, and it is to toast 30s at 90 DEG C to be placed in temperature, you can.
The modifying agent, material composition by weight be ethyl acetate 0.1kg, styrene 0.5kg, mica powder 4kg,
Blanc fixe 3kg, copper powder 0.1kg, aluminium powder 3kg, preparation method are after mixing above-mentioned raw materials mixing thoroughly, and it is at 60 DEG C to be placed in temperature
30min is handled, then its ground 160 mesh is sieved.
The cleaning solution, material composition are cocoanut fatty acid diethanolamide 1kg, propenylbenzene by weight
2kg, distilled water 10kg, tall oil 0.6kg, mineral oil 14kg, triethanolamine borate 1kg, cottonseed oil 60kg, nano-silver powder
7kg。
The cleaning solution, preparation method are by cocoanut fatty acid diethanolamide, propenylbenzene, tall oil, mineral
Oil, triethanolamine borate, cottonseed oil are uniformly mixed, and obtain batch mixing a；Nano-silver powder is added in distilled water, using ultrasonic disperse
17min is handled, adds in batch mixing a, stirs evenly, you can.
The ultrasonic disperse, supersonic frequency 5MHz.
Embodiment 5
A kind of filamentary silver volume flower welding method, includes the following steps：
(1) block silver is placed in and is melted in pond, after being melted, modifier modification is added and handles 20min, then is cooled to coagulate
Gu and beating into the thin slice of 0.5cm thickness；
(2) thin slice in step (1) is placed in cleaning solution and impregnates 5min, and use distilled water flushing 2 times, then in wire drawing
Wire drawing process on machine, and the filamentary silver that drawing is formed is drenched using cleaning solution, in 50 DEG C of drying and processing 10min, obtains filamentary silver；
(3) filamentary silver is placed in immersion treatment 30min in liquid silver, and after being drawn off, it, will be silver-colored using liquid silver as solder
Wire bond is connected on silverware, and it is to toast 20s at 60 DEG C to be placed in temperature, you can.
The modifying agent, material composition by weight be ethyl acetate 0.1kg, styrene 0.4kg, mica powder 8kg,
Blanc fixe 2kg, copper powder 0.2kg, aluminium powder 1kg, preparation method are after mixing above-mentioned raw materials mixing thoroughly, and it is at 60 DEG C to be placed in temperature
30min is handled, then its ground 240 mesh is sieved.
The cleaning solution, material composition are cocoanut fatty acid diethanolamide 1kg, propenylbenzene by weight
3kg, distilled water 15kg, tall oil 0.1kg, mineral oil 13kg, triethanolamine borate 2kg, cottonseed oil 60kg, nano-silver powder
7kg。
The cleaning solution, preparation method are by cocoanut fatty acid diethanolamide, propenylbenzene, tall oil, mineral
Oil, triethanolamine borate, cottonseed oil are uniformly mixed, and obtain batch mixing a；Nano-silver powder is added in distilled water, using ultrasonic disperse
20min is handled, adds in batch mixing a, stirs evenly, you can.The ultrasonic disperse, supersonic frequency 5MHz.
Claims (5)
1. a kind of filamentary silver compiles flower welding method, which is characterized in that melt block silver, is modified, cooling is beaten, cleaning solution washing, is drawn
Silk machine wire drawing after, cleaning solution tripperfaden, obtain filamentary silver；Using liquid silver as solder, filamentary silver is welded on silverware, is dried, you can；
Above-mentioned filamentary silver compiles flower welding method, includes the following steps：
(1) block silver is placed in and is melted in pond, after being melted, modifier modification is added and handles 10-20min, then is cooled to coagulate
Gu and beating into the thin slice of 0.5-1.3cm thickness；
(2) thin slice in step (1) is placed in cleaning solution and impregnates 2-5min, and use distilled water flushing 2-4 times, then in wire drawing
Wire drawing process on machine, and the filamentary silver that drawing is formed is drenched using cleaning solution, in 30-50 DEG C of drying and processing 10-20min, obtains filamentary silver；
(3) filamentary silver is placed in immersion treatment 20-30min in liquid silver, and after being drawn off, it, will be silver-colored using liquid silver as solder
Wire bond is connected on silverware, and it is to toast 20-30s at 60-90 DEG C to be placed in temperature, you can.
2. the filamentary silver stated such as claim 1 compiles flower welding method, which is characterized in that the modifying agent, material composition is with weight
Amount part is calculated as 0.1-0.5 parts of ethyl acetate, 0.1-0.5 parts of styrene, 4-9 parts of mica powder, 1-3 parts of blanc fixe, copper powder 0.1-
0.4 part, 1-3 parts of aluminium powder, preparation method are after mixing above-mentioned raw materials mixing thoroughly, and it is to handle 20- at 60-80 DEG C to be placed in temperature
30min, then its ground 160-300 mesh is sieved.
3. filamentary silver as described in claim 1 compiles flower welding method, which is characterized in that the cleaning solution, material composition with
Parts by weight are calculated as 1-3 parts of cocoanut fatty acid diethanolamide, 1-3 parts of propenylbenzene, 10-20 parts of distilled water, tall oil 0.1-
0.7 part, 10-15 parts of mineral oil, 1-3 parts of triethanolamine borate, 60-70 parts of cottonseed oil, 5-7 parts of nano-silver powder.
4. the filamentary silver as described in claim 1 or 3 compiles flower welding method, which is characterized in that the cleaning solution, preparation method are
Cocoanut fatty acid diethanolamide, propenylbenzene, tall oil, mineral oil, triethanolamine borate, cottonseed oil are mixed equal
It is even, obtain batch mixing a；Nano-silver powder is added in distilled water, 10-20min is handled using ultrasonic disperse, is added in batch mixing a, is stirred
Uniformly, you can.
5. filamentary silver as claimed in claim 4 compiles flower welding method, which is characterized in that the ultrasonic disperse, supersonic frequency are
5-10MHz。