CN105926295A - 一种用于牛仔服饰压皱整理的整理液 - Google Patents

一种用于牛仔服饰压皱整理的整理液 Download PDF

Info

Publication number
CN105926295A
CN105926295A CN201610369403.2A CN201610369403A CN105926295A CN 105926295 A CN105926295 A CN 105926295A CN 201610369403 A CN201610369403 A CN 201610369403A CN 105926295 A CN105926295 A CN 105926295A
Authority
CN
China
Prior art keywords
parts
agent
arrangement
crumpling
crumple
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610369403.2A
Other languages
English (en)
Inventor
张红桥
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hongqiao Taicang Garments Co Ltd
Original Assignee
Hongqiao Taicang Garments Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hongqiao Taicang Garments Co Ltd filed Critical Hongqiao Taicang Garments Co Ltd
Priority to CN201610369403.2A priority Critical patent/CN105926295A/zh
Publication of CN105926295A publication Critical patent/CN105926295A/zh
Pending legal-status Critical Current

Abstract

本发明提供一种用于牛仔服饰压皱整理的整理液，包括重量组分为：5‑25份的硬挺剂，25‑45份的压皱树脂，3‑6份的催化剂，10‑15份的强力保护剂，2‑5份的渗透剂，2‑3份的交联剂，45‑65份的水。采用本发明的整理液，可以提高牛仔的弹性恢复性能及抗皱性能；赋予压皱整理后的牛仔服饰具有立体感和持久性；手感柔软，并且断裂强力和撕破强力良好，性价比高，具有广泛的工业化应用前景和市场价值。

Description

一种用于牛仔服饰压皱整理的整理液
技术领域
本发明涉及纺织面料及纺织品后整理技术领域，特别涉及一种用于牛仔服饰压皱整理的整理液。
背景技术
牛仔压皱整理是近年来较流行的一种整理工艺，它是在服装的裤筒、裤身等部位整理产生出的扁平和圆形自然折皱，并将其折皱形态稳定下来的水洗工艺。牛仔压皱树脂作用原理与免烫整理类似，通过活性基团与纤维素长链分子中的羟基发生共价交联反应，将纤维素纤维相邻的分子链联结起来，限制其之间的相对滑动，从而保证牛仔布上的褶皱不会消失，即具有形态记忆功能。
牛仔服饰经整理液整理压皱后需要保持良好的弹性恢复性能，以及良好的抗皱性能，并需要具有立体感和持久性以及良好的保色性能及干湿磨擦牢度，手感柔软。
为解决上述问题，中国专利201310464023.3公开了用于牛仔服饰压皱整理的硬挺剂及树脂整理液。用于牛仔服饰压皱整理的硬挺剂，包括以下重量百分比含量或重量含量的组分：聚乙烯醇乳液60％～67％、聚亚胺酯乳液33％～40％、重量是聚乙烯醇乳液和聚亚胺酯乳液总重量0.006倍的缓冲体系。用于牛仔服饰压皱整理的树脂整理液，包括以下重量百分比含量或重量含量的组分:硬挺剂3～6％、压皱树脂6～18％、用量为所述压皱树脂的1/5～1/4的催化剂、余量是水，采用本发明的硬挺剂及树脂整理液，可以提高牛仔的弹性恢复性能及抗皱性能；赋予压皱猫须、3D猫须立体感，持久性；提高其保色性能及干湿磨擦牢度，手感柔软性价比高，满足牛仔服饰时尚元素的要求。虽然此种整理液提高了弹性恢复性能及抗皱性能，但其断裂强力、耐磨性和撕破强力性能较差。
因此，为了满足人们日益增长的服饰需要，研究出一种压皱整理液，使牛仔服饰的弹性恢复性能以及抗皱性能良好，并且断裂强力和撕破强力性能良好。
发明内容
本发明的目的是提供一种用于牛仔服饰压皱整理的整理液，通过使用此整理液提高牛仔的弹性恢复性能，赋予压皱整理后的牛仔服饰具有立体感和持久性；并且断裂强力和撕破强力性能良好，手感柔软。
为解决上述问题，本发明通过以下技术方案实现:
一种用于牛仔服饰压皱整理的整理液，其特征在于：以质量份数计，包括5-25份的硬挺剂，25-45份的压皱树脂，3-6份的催化剂，强力保护剂10-15，渗透剂2-5份，交联剂2-3份，45-65份的水。
优选地，以质量份数计，包括10-15份的硬挺剂，30-40份的压皱树脂，3-5份的催化剂，强力保护剂12-15份，渗透剂2-5份，交联剂2-3份，48-60份的水。
优选地，所述硬挺剂为聚丙烯酸酯和聚乙烯乙酸酯或三聚氰胺树脂或聚丙烯酰胺。
优选地，所述催化剂为亚磷酸碱金属盐。
优选地，所述亚磷酸碱金属盐为次磷酸铵。
优选地，所述压皱树脂为2D树脂或改性2D树脂。
优选地，所述强力保护剂为聚乙烯乳液。
优选地，所述渗透剂为琥珀酸烷基酯磺酸钠、烷基酚聚氧乙烯醚、烷基硫酸酯钠、烷基苯磺酸钠的一种或几种。
优选地，所述交联剂为1，2，3，4-四羧酸丁烷。
本发明的有益效果在于：(1)经过本发明整理液压皱整理后的牛仔服饰保持有良好的弹性恢复性能，以及良好的抗皱性能，并具有立体感和持久性以及良好的保色性能及干湿磨擦牢度，手感柔软。(2)整理处理过的牛仔服饰还具有良好的断裂强力和撕破强力性能。(3)整理工艺操作简单，设备简单，环保节能。
具体实施方式
下面通过具体实施例对本发明做进一步的说明，但实施例并不限制本发明的保护范围。
实施例1
本实施例的压皱整理液，以质量份数计，包括5份的聚丙烯酸酯硬挺剂，25份的2D压皱树脂，3份的次磷酸铵催化剂，10份的聚乙烯乳液强力保护剂，2份的琥珀酸烷基酯磺酸钠渗透剂，2份的1，2，3，4-四羧酸丁烷交联剂，45份的水。
实施例2
本实施例的压皱整理液，以质量份数计，包括10份的聚乙烯乙酸酯硬挺剂，30份的2D压皱树脂，5份的次磷酸铵催化剂，13份的聚乙烯乳液强力保护剂，3份的烷基酚聚氧乙烯醚渗透剂，3份的1，2，3，4-四羧酸丁烷交联剂，50份的水。
实施例3
本实施例的压皱整理液，以质量份数计，包括15份的聚乙烯乙酸酯硬挺剂，35份的改性2D压皱树脂，5份的次磷酸铵催化剂，15份的聚乙烯乳液强力保护剂，4份的烷基硫酸酯钠渗透剂，3份的1，2，3，4-四羧酸丁烷交联剂，60份的水。
实施例4
本实施例的压皱整理液，以质量份数计，包括25份的三聚氰胺树脂硬挺剂，30份的2D压皱树脂，6份的次磷酸铵催化剂，10聚乙烯乳液强力保护剂，5份的烷基苯磺酸钠渗透剂，3份的1，2，3，4-四羧酸丁烷交联剂，65份的水。
实施例5
本实施例的压皱整理液，以质量份数计，包括20份的聚丙烯酰胺硬挺剂，35份的改性2D压皱树脂，6份的次磷酸铵催化剂，12份的聚乙烯乳液强力保护剂，5份的烷基酚聚氧乙烯醚渗透剂，2份的1，2，3，4-四羧酸丁烷交联剂，65份的水。
牛仔服饰压皱整理工艺流程：
浸轧整理液→脱液→烘干→压皱→烘培→出箱→水洗。
性能测试：
(1)压皱效果
参照GB/T3819-1997《纺织品织物折痕回复性的测定回复角法》测试整理后织物的折皱回复角，并结合目测评判压皱效果。
(2)撕破强力
参照GB/T3917.2-1997《纺织品织物撕破性能第2部分：舌形试样撕破强力的测定》测试。
(3)断裂强力：用GB/T3923-1998《纺织品-织物拉伸性能》
实施例1-5压皱整理后的牛仔服饰性能测试结果如下表：
需要说明的是，以上实施例仅用以说明本发明的技术方案而非限制。尽管参照较佳实施例对本发明进行了详细说明，本领域的普通技术人员应当理解，可以对发明的技术方案进行修改或者等同替换，而不脱离本发明技术方案的范围，其均应涵盖在本发明的权利要求范围中。

Claims (9)

1.一种用于牛仔服饰压皱整理的整理液，其特征在于：以质量份数计，包括5-25份的硬挺剂，25-45份的压皱树脂，3-6份的催化剂，10-15份的强力保护剂，2-5份的渗透剂，2-3份的交联剂，45-65份的水。
2.根据权利要求1所述的一种用于牛仔服饰压皱整理的整理液，其特征在于：以质量份数计，包括10-15份的硬挺剂，30-40份的压皱树脂，3-5份的催化剂，12-15份的强力保护剂，2-5份的渗透剂，2-3份的交联剂，48-60份的水。
3.根据权利要求1所述的一种用于牛仔服饰压皱整理的整理液，其特征在于：所述硬挺剂为聚丙烯酸酯和聚乙烯乙酸酯或三聚氰胺树脂或聚丙烯酰胺。
4.根据权利要求1所述的一种用于牛仔服饰压皱整理的整理液，其特征在于：所述催化剂为亚磷酸碱金属盐。
5.根据权利要求4所述的一种用于牛仔服饰压皱整理的整理液，其特征在于：所述亚磷酸碱金属盐为次磷酸铵。
6.根据权利要求1所述的一种用于牛仔服饰压皱整理的整理液，其特征在于，所述压皱树脂为2D树脂或改性2D树脂。
7.根据权利要求1所述的一种用于牛仔服饰压皱整理的整理液，其特征在于，所述强力保护剂为聚乙烯乳液。
8.根据权利要求1所述的一种用于牛仔服饰压皱整理的整理液，其特征在于，所述渗透剂为琥珀酸烷基酯磺酸钠、烷基酚聚氧乙烯醚、烷基硫酸酯钠、烷基苯磺酸钠的一种或几种。
9.根据权利要求1所述的一种用于牛仔服饰压皱整理的整理液，其特征在于，所述交联剂为1，2，3，4-四羧酸丁烷。
CN201610369403.2A 2016-05-30 2016-05-30 一种用于牛仔服饰压皱整理的整理液 Pending CN105926295A (zh)