CN105907304A - Reflecting release film and preparation method thereof - Google Patents
Reflecting release film and preparation method thereof Download PDFInfo
- Publication number
- CN105907304A CN105907304A CN201610301152.4A CN201610301152A CN105907304A CN 105907304 A CN105907304 A CN 105907304A CN 201610301152 A CN201610301152 A CN 201610301152A CN 105907304 A CN105907304 A CN 105907304A
- Authority
- CN
- China
- Prior art keywords
- parts
- mould release
- reflective
- release membrance
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a reflecting release film, which is characterized by comprising a base film layer, wherein a release layer is arranged on the base film layer; the release layer is formed by coating a release agent; the release agent is prepared from the following ingredients in parts by mass: 20 to 35 parts of reflecting powder, 10 to 40 parts of vinyl organic silicon resin, 5 to 18 parts of butyl acrylate, 2 to 6 parts of titanium dioxide, 0.1 to 3 parts of antioxidant, 1 to 5 parts of coupling agents, 0.5 to 1.5 parts of defoaming agents and 15 to 30 parts of solvents. The reflecting release film has the advantages that adhesion cannot be generated when the obtained release film is separated from a contact adhesion belt or bonding belt; reflecting powder glass microbeads are added, so that the recognition degree of the release film is enhanced at night or in dark lamp light environment; the processing and the use of the release film are convenient.
Description
Technical field
The present invention relates to a kind of mould release membrance, particularly to a kind of reflective mould release membrance and preparation method thereof.
Background technology
Mould release membrance also known as antiadhesion barrier, be with polyethylene terephthalate plastics (be called for short PET),
Bidirectional stretching polypropylene film plastics (being called for short BOPP), vinyon (being called for short PE), carbonic acid
Ester plastics (being called for short PC), polystyrene plastics (being called for short PS), polypropylene plastics (being called for short CPP)
A kind of surface made for base material has the material of characteristic of low-surface-energy.By the viscose of next-door neighbour from release
When face is peeled off, can peel off or pipette separated type material easily, and not injure viscose physical property.Mould release membrance
Feature is surfacing, cleanliness factor height, following process dimensionally stable, and transparency and Color tunable are whole,
The thickness of thin film scope selectable with the kind of base material is wide.Utilize these features of mould release membrance can be to light
The deep processing learning the parts with electronic applications develops, thus it is the most automatic to adapt to this field
Changing production process, at present, mould release membrance can be widely applied for copper-clad plate, printed circuit board (PCB), electricity
The fields such as sub-adhesive.
Mould release membrance comprises base material film and release layer.Base material film surface at least one side is provided with release layer, with
Relatively low surface energy is provided.Base material film many employings paper, plastic sheeting are as material, and release layer is main
Silicon mixture is used to constitute.Typically it is used for industry adhesion zone or adhesive tape etc., to mould release membrance
Performance requirement relatively low, it is only necessary to its have high adherence and remain gluing rate, but be as industry neck
Developing rapidly of territory, the range of mould release membrance is increasingly wider, and there has also been its other performances must
Ask.
But, traditional mould release membrance mostly is transparent, translucent or coloured mould release membrance, due to its transparency
Height, is difficult to identification, at night or in the environment of the light is dusky, can affect processing and the use of mould release membrance.
Accordingly, it would be desirable to a kind of mould release membrance can in the environment of light intensity is more weak with strong reflecting effect, come
Strengthen the resolution of mould release membrance.
Summary of the invention
For solving the problem of above-mentioned existence, it is an object of the invention to provide a kind of reflective mould release membrance.Institute
Stating reflective mould release membrance, each component cooperates so that the release layer obtained can be spread evenly across basement membrane
On layer, and then it is viscous to make the mould release membrance obtained not produce when separating with the adhesion zone contacted or adhesive tape
Even;And it is added with reflective powder glass microballoon, owing to the high refraction action of glass microballoon and optically focused are at glass
On the special reflecting layer of microballon focus, light is reflexed to light source by transparent microballon by reflecting layer again
Near, so very bright reflection light can be seen at light source, at night or the environment that the light is dusky
Under, strengthen the resolution of mould release membrance, it is simple to the processing of mould release membrance and use.
For reaching above-mentioned purpose, the technical scheme is that
A kind of reflective mould release membrance, including base membrane layer, described base membrane layer is provided with release layer, described from
Type layer is formed by mould release coating, and described mould release comprises each component of following mass fraction: reflective powder:
20-35 part;Vinyl organosilicon resin: 10-40 part;Butyl acrylate: 5-18 part;Titanium dioxide:
2-6 part;Antioxidant: 0.1-3 part;Coupling agent: 1-5 part;Defoamer: 0.5-1.5 part;Solvent:
15-30 part.
Further, described mould release comprises each component of following weight percent: reflective powder: 24-32
Part;Vinyl organosilicon resin: 20-40 part;Butyl acrylate: 10-18 part;Titanium dioxide: 3-5
Part;Antioxidant: 0.1-1.5 part;Coupling agent: 2-4 part;Defoamer: 1-1.5 part;Solvent: 18-26
Part.
Further, described mould release comprises each component of following weight percent: reflective powder: 28
Part;Vinyl organosilicon resin: 35 parts;Butyl acrylate: 16 parts;Titanium dioxide: 4.5 parts;
Antioxidant: 1.2 parts;Coupling agent: 3 parts;Defoamer: 1.1 parts;Solvent: 25 parts.
Further, described base membrane layer material is in PE, PET, TPX, PMMA, BOPP or PS
Any one.
Separately having, described reflective powder is glass microsphere light-reflecting powder, and the granularity of described glass microsphere light-reflecting powder is
300-500 mesh.
And, described antioxidant is DI-tert-butylphenol compounds or Butylated hydroxyanisole;Described coupling agent is
Silane coupler;Described defoamer is glycol distearate or polyoxyethylene polyoxypropylene glycerin ether.
The preparation method of a kind of reflective mould release membrance, comprises the steps:
(1) weigh needed raw material by mass fraction, vinyl organosilicon resin and butyl acrylate are added
Enter in solvent and stir, add titanium dioxide and reflective powder, 0.5-1.5h is stirred at room temperature, then adds
Enter antioxidant, coupling agent, defoamer, after being warming up to 40-60 DEG C, continue stirring 0.5-1h
(2) gained mixed liquor in the one or both sides coating step (1) of base membrane layer, coating weight is
0.60-0.80g/m2, it is placed in drying baker, at 50-65 DEG C, is dried 6-20min, makes surface the most solid
Change, be finally shaped, rolling, obtain reflective mould release membrance.
The beneficial effects of the present invention is:
The reflective mould release membrance of one that the present invention provides, each component cooperates so that the release layer obtained
Can be spread evenly across on base membrane layer, so make the mould release membrance obtained with the adhesion zone contacted or glue
Adhesive tape does not produce adhesion when separating;And it is added with reflective powder glass microballoon, due to the high folding of glass microballoon
The effect of penetrating and optically focused on the special reflecting layer of glass microballoon focus, reflecting layer by light by transparent micro-
Pearl reflexes near light source again, so can see very bright reflection light at light source, at night
Evening or in the environment of the light is dusky, strengthen the resolution of mould release membrance, it is simple to the processing of mould release membrance and use.
Detailed description of the invention
In order to make the purpose of the present invention, technical scheme and advantage clearer, below in conjunction with enforcement
Example further describes.
Embodiment 1
A kind of reflective mould release membrance, including base membrane layer, described base membrane layer is provided with release layer, described from
Type layer is formed by mould release coating, and described mould release comprises each component of following mass fraction: reflective powder:
20 parts;Vinyl organosilicon resin: 35 parts;Butyl acrylate: 5 parts;Titanium dioxide: 3 parts;
Antioxidant: 0.5 part;Coupling agent: 1 part;Defoamer: 0.6 part;Solvent: 20 parts.
Wherein, described base membrane layer material is PE, and described reflective powder is glass microsphere light-reflecting powder, described glass
The granularity of the reflective powder of glass microballon is 300 mesh, and described antioxidant is DI-tert-butylphenol compounds;Described coupling
Agent is silane coupler;Described defoamer is polyoxyethylene polyoxypropylene glycerin ether.
Embodiment 2
A kind of reflective mould release membrance, including base membrane layer, described base membrane layer is provided with release layer, described from
Type layer is formed by mould release coating, and described mould release comprises each component of following mass fraction: reflective powder:
25 parts;Vinyl organosilicon resin: 10 parts;Butyl acrylate: 8 parts;Titanium dioxide: 2 parts;
Antioxidant: 1.5 parts;Coupling agent: 3 parts;Defoamer: 1 part;Solvent: 18 parts.
Wherein, described base membrane layer material is PMMA, and described reflective powder is glass microsphere light-reflecting powder, institute
The granularity stating glass microsphere light-reflecting powder is 400 mesh, and described antioxidant is DI-tert-butylphenol compounds;Described
Coupling agent is silane coupler;Described defoamer is glycol distearate.
Embodiment 3
A kind of reflective mould release membrance, including base membrane layer, described base membrane layer is provided with release layer, described from
Type layer is formed by mould release coating, and described mould release comprises each component of following weight percent: anti-
Light powder: 28 parts;Vinyl organosilicon resin: 35 parts;Butyl acrylate: 16 parts;Titanium dioxide:
4.5 part;Antioxidant: 1.2 parts;Coupling agent: 3 parts;Defoamer: 1.1 parts;Solvent: 25 parts.
Wherein, described base membrane layer material is BOPP, and described reflective powder is glass microsphere light-reflecting powder, institute
The granularity stating glass microsphere light-reflecting powder is 400 mesh, and described antioxidant is Butylated hydroxyanisole;Institute
Stating coupling agent is silane coupler;Described defoamer is glycol distearate.
Embodiment 4
A kind of reflective mould release membrance, including base membrane layer, described base membrane layer is provided with release layer, described from
Type layer is formed by mould release coating, and described mould release comprises each component of following mass fraction: reflective powder:
30 parts;Vinyl organosilicon resin: 32 parts;Butyl acrylate: 18 parts;Titanium dioxide: 5 parts;
Antioxidant: 2.8 parts;Coupling agent: 5 parts;Defoamer: 1.5 parts;Solvent: 26 parts.
Wherein, described base membrane layer material is TPX, and described reflective powder is glass microsphere light-reflecting powder, described
The granularity of glass microsphere light-reflecting powder is 500 mesh, and described antioxidant is Butylated hydroxyanisole;Described
Coupling agent is silane coupler;Described defoamer is glycol distearate.
Embodiment 5
A kind of reflective mould release membrance, including base membrane layer, described base membrane layer is provided with release layer, described from
Type layer is formed by mould release coating, and described mould release comprises each component of following mass fraction: reflective powder:
35 parts;Vinyl organosilicon resin: 40 parts;Butyl acrylate: 12 parts;Titanium dioxide: 6 parts;
Antioxidant: 3 parts;Coupling agent: 3.5 parts;Defoamer: 1.2 parts;Solvent: 30 parts.
Wherein, described base membrane layer material is PET, and described reflective powder is glass microsphere light-reflecting powder, described
The granularity of glass microsphere light-reflecting powder is 500 mesh, and described antioxidant is DI-tert-butylphenol compounds;Described idol
Connection agent is silane coupler;Described defoamer is polyoxyethylene polyoxypropylene glycerin ether.
The preparation method of above-mentioned reflective mould release membrance, comprises the steps:
(1) weigh needed raw material by mass fraction, vinyl organosilicon resin and butyl acrylate are added
Enter in solvent and stir, add titanium dioxide and reflective powder, 0.5-1.5h is stirred at room temperature, then adds
Enter antioxidant, coupling agent, defoamer, after being warming up to 40-60 DEG C, continue stirring 0.5-1h
(2) gained mixed liquor in the one or both sides coating step (1) of base membrane layer, coating weight is
0.60-0.80g/m2, it is placed in drying baker, at 50-65 DEG C, is dried 6-20min, makes surface the most solid
Change, be finally shaped, rolling, obtain reflective mould release membrance.
In order to the off-type force of reflective mould release membrance a kind of in embodiment 1-5 is tested, use
FINAT-10, the index zone of the wide 50mm × long 175mm of attachment on each embodiment mould release membrance
(TESA7475-acryloyl chloride class).Then, FINAT-10 test roller (2Kg load) is utilized,
Come and go twice index zone with the speed of 10mm/sec to compress, clamp release with two pieces of smooth metallic plates
Film, plus 70g/cm2Pressure, at a temperature of about 25 DEG C keep 20h.Afterwards, lay down
Pressure, is fixed to tool mould release membrance after 4h, by index zone from the direction of 180 ° according to 300mm/min
Speed peel off, test, repeatedly test average for 5 times, the results are shown in Table 1.
The off-type force test result of mould release membrance in table 1 embodiment 1-5
As can be known from the above table, in embodiment 1-5, mould release membrance has preferable off-type force, each component phase interworking
Close so that the release layer obtained can be spread evenly across on base membrane layer, and then makes the mould release membrance obtained exist
Adhesion is not produced with the adhesion zone contacted or adhesive tape when separating;And it is added with reflective powder glass microballoon,
Due to the high refraction action of glass microballoon, optically focused is on the special reflecting layer of glass microballoon focus, reflection
Light is reflexed near light source again, so can see very at light source by layer by transparent microballon
Bright reflection light, at night or in the environment of the light is dusky, strengthens the resolution of mould release membrance, it is simple to
The processing of mould release membrance and use.
It should be noted that above example is only in order to illustrate technical scheme and unrestricted.
Although being described in detail the present invention with reference to preferred embodiment, those of ordinary skill in the art should
Work as understanding, the technical scheme of invention can be modified or equivalent, without deviating from the present invention
The scope of technical scheme, it all should be contained in scope of the presently claimed invention.
Claims (7)
1. a reflective mould release membrance, it is characterised in that include base membrane layer, described base membrane layer is provided with release layer, and described release layer is formed by mould release coating, and described mould release comprises each component of following mass fraction: reflective powder: 20-35 part;Vinyl organosilicon resin: 10-40 part;Butyl acrylate: 5-18 part;Titanium dioxide: 2-6 part;Antioxidant: 0.1-3 part;Coupling agent: 1-5 part;Defoamer: 0.5-1.5 part;Solvent: 15-30 part.
The reflective mould release membrance of one the most according to claim 1, it is characterised in that described mould release comprises each component of following weight percent: reflective powder: 24-32 part;Vinyl organosilicon resin: 20-40 part;Butyl acrylate: 10-18 part;Titanium dioxide: 3-5 part;Antioxidant: 0.1-1.5 part;Coupling agent: 2-4 part;Defoamer: 1-1.5 part;Solvent: 18-26 part.
The reflective mould release membrance of one the most according to claim 1, it is characterised in that described mould release comprises each component of following weight percent: reflective powder: 28 parts;Vinyl organosilicon resin: 35 parts;Butyl acrylate: 16 parts;Titanium dioxide: 4.5 parts;Antioxidant: 1.2 parts;Coupling agent: 3 parts;Defoamer: 1.1 parts;Solvent: 25 parts.
The reflective mould release membrance of one the most according to claim 1, it is characterised in that described base membrane layer material is any one in PE, PET, TPX, PMMA, BOPP or PS.
The reflective mould release membrance of one the most according to claim 1, it is characterised in that described reflective powder is glass microsphere light-reflecting powder, the granularity of described glass microsphere light-reflecting powder is 300-500 mesh.
The reflective mould release membrance of one the most according to claim 1, it is characterised in that described antioxidant is DI-tert-butylphenol compounds or Butylated hydroxyanisole;Described coupling agent is silane coupler;Described defoamer is glycol distearate or polyoxyethylene polyoxypropylene glycerin ether.
7. the preparation method of a reflective mould release membrance, it is characterised in that comprise the steps:
(1) needed raw material is weighed by mass fraction, vinyl organosilicon resin and butyl acrylate are added in solvent and stirs, add titanium dioxide and reflective powder, 0.5-1.5h is stirred at room temperature, it is subsequently adding antioxidant, coupling agent, defoamer, after being warming up to 40-60 DEG C, continues stirring 0.5-1h;
(2) gained mixed liquor in the one or both sides coating step (1) of base membrane layer, coating weight is 0.60-0.80g/m2, it is placed in drying baker, at 50-65 DEG C, is dried 6-20min, makes surface be fully cured, be finally shaped, rolling, obtain reflective mould release membrance.