CN105906942A - Novel low-temperature-resisting medical polypropylene film formula - Google Patents
Novel low-temperature-resisting medical polypropylene film formula Download PDFInfo
- Publication number
- CN105906942A CN105906942A CN201610440142.9A CN201610440142A CN105906942A CN 105906942 A CN105906942 A CN 105906942A CN 201610440142 A CN201610440142 A CN 201610440142A CN 105906942 A CN105906942 A CN 105906942A
- Authority
- CN
- China
- Prior art keywords
- parts
- polypropylene
- novel low
- low temperature
- vinyl acetate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a novel low-temperature-resisting medical polypropylene film formula. The medical polypropylene film is prepared from, by weight, 100-110 parts of polypropylene, 12-18 parts of glycerol-phthalic resin, 5-9 parts of trimethylolpropane triacrylate, 4-8 parts of potassium persulfate, 50 parts of vinyl acetate, 10-15 parts of glycerinum, 12-18 parts of linear low density polyethylene, 10-15 parts of polyethylene wax, 15-20 parts of Artemisia glue and 12-18 parts of hydroxy propyl cellulose. The novel low-temperature-resisting medical polypropylene film has the advantages of restraining bacteria, killing the bacteria, being environmentally friendly and the like, and is good in low temperature resisting performance and good in strength, toughness and heat resisting performance, and the effect is not influenced after long-time use.
Description
Technical field
The invention belongs to polymeric material field, be specifically related to a kind of novel low temperature resistant medical poly-third
Alkene film formulation.
Background technology
The yield of Chinese Plastics film accounts for the 20% of plastic products total output, is in plastic products
Increase of production one of classification faster.From China's plastic sheeting (thickness is 0.06mm~0.26mm)
Application see, consumption is maximum, kind is most, most widely used is packaging industry, and it disappears
Expense accounts for 2/3, next to that agricultural accounts for 30%, then to have be exactly functional membrane, such as microporous barrier, screen
Cover film, geomembrane etc..If adding suitable plastic additive in resin matrix, it is possible to preparation
Go out required various functional films.Production method on plastic film industry has rolling process and squeezes
Going out method, wherein extrusion molding is divided into again extrusion blown film, extrusion curtain coating, extrusion stretching (also known as secondary
Shaping) etc..
Along with development and the adjustment of the structure of rural undertaking of China's economic, China's all trades and professions pair
The market demand of plastic sheeting constantly rises.Predict global plastic sheetings in 2015 and sheet material city
Field consumption figure is expected to reach 50,700,000 tons, and wherein the Asian-Pacific area is anticipated will become fastest-rising
Regional markets.Chinese Plastics film industry is currently in a flourish stage,
2001-2011 market scale average annual growth rate reaches more than 18%, it is contemplated that within 2012, be up to
350000000000 yuan.
Chinese Plastics film industry is in a flourish stage, it is reported, Chinese Plastics
The demand of film every year by with more than 9% speed increment.And along with various new materials,
New equipment and new technology are constantly emerged in large numbers, and the plastic sheeting of China will be promoted towards numerous in variety
Change, customizations and possess multi-functional composite membrane direction and develop.
Plastic sheeting, is used for packing, and is used as coating layer.Plastics package and plastics package are produced
The commercially shared share of product is increasing, particularly composite plastic flexible package, the most extensively
Be applied to the fields such as food, medicine, chemical industry, maximum with packaging for foodstuff proportion the most again,
Such as beverage packaging, quick-frozen food packaging, cooking food packaging, fast food packaging etc., this
A little products all bring great convenience to people's life.
Medical devices packaging film has a bigger market potential, and the requirement that medical devices is to packaging film
Higher, its not only need ensure the pliability of film, mouldability and with good heat sealing strength etc.,
It is also contemplated that it intercepts bacterium, puncture resistance and guarantees that in low temperature environment content is stable, heat-resisting
And the sanitation performances such as nuisance migration, also environment friendly will not be produced.Also need to simultaneously
Medical film has good lower temperature resistance, so could meet cryopreservation requirement.
In sum, the deficiency solving prior art existence has become the skill that this area is urgently to be resolved hurrily
Art problem.
Summary of the invention
It is an object of the invention to provide a kind of novel low temperature resistant polypropylene for medical article film formulation.
To achieve these goals, the invention provides a kind of novel low temperature resistant polypropylene for medical article thin
Film formulation, is prepared by the raw material of following weight portion: polypropylene 100-110 part, alkyd resin
12-18 part, trimethylolpropane trimethacrylate 5-9 part, potassium peroxydisulfate 4-8 part, acetic acid
Ethene 50 parts, glycerine 10-15 part, LLDPE 12-18 part, Tissuemat E
10-15 part, Artemisia Glue 15-20 part, hydroxypropyl cellulose 12-18 part.
Preferred version is to be prepared by the raw material of following weight portion: polypropylene 100 parts, alkyd resin
12 parts, trimethylolpropane trimethacrylate 5 parts, potassium peroxydisulfate 4 parts, vinyl acetate 50
Part, glycerine 10 parts, LLDPE 12 parts, Tissuemat E 10 parts, Artemisia Glue
15 parts, hydroxypropyl cellulose 12 parts.
Preferred version is to be prepared by the raw material of following weight portion: polypropylene 110 parts, alkyd resin
18 parts, trimethylolpropane trimethacrylate 9 parts, potassium peroxydisulfate 8 parts, vinyl acetate 50
Part, glycerine 15 parts, LLDPE 18 parts, Tissuemat E 15 parts, Artemisia Glue
20 parts, hydroxypropyl cellulose 18 parts.
Preferred version is to be prepared by the raw material of following weight portion: polypropylene 102 parts, alkyd resin
14 parts, trimethylolpropane trimethacrylate 6 parts, potassium peroxydisulfate 5 parts, vinyl acetate 50
Part, glycerine 12 parts, LLDPE 13 parts, Tissuemat E 12 parts, Artemisia Glue
16 parts, hydroxypropyl cellulose 13 parts.
Preferred version is to be prepared by the raw material of following weight portion: polypropylene 108 parts, alkyd resin
17 parts, trimethylolpropane trimethacrylate 8 parts, potassium peroxydisulfate 7 parts, vinyl acetate 50
Part, glycerine 14 parts, LLDPE 17 parts, Tissuemat E 14 parts, Artemisia Glue
17 parts, hydroxypropyl cellulose 17 parts.
Its preparation method is: weigh each component by weight ratio, puts in reactor,
Adding thermal response in nitrogen atmosphere, be then fed into double screw extruder, twin-screw extrusion batten is through water
Cold, air-dried, pelletizing, obtains master batch, and master batch is finally put into plastic film blowing machine extrusion blown film,
I.e. obtain finished product.
The method have the advantages that the present invention low temperature resistant polypropylene for medical article film has to press down
Bacterium processed, killing the advantage such as bacterium and environmental protection, resistance to low temperature is good, and after Long-Time Service, effect is not
Impacted, and its intensity, toughness, fine heat-resisting performance.
Detailed description of the invention
Embodiment 1
The novel low temperature resistant polypropylene for medical article film formulation of one of the present embodiment, by following weight portion
Raw material prepare: polypropylene 100 parts, alkyd resin 12 parts, trimethylolpropane tris propylene
Acid esters 5 parts, potassium peroxydisulfate 4 parts, vinyl acetate 50 parts, glycerine 10 parts, linea low density
Polyethylene 12 parts, Tissuemat E 10 parts, Artemisia Glue 15 parts, hydroxypropyl cellulose 12 parts.
Preparation method is: weigh each component by weight ratio, puts in reactor, at nitrogen
Gas atmosphere adds thermal response, is then fed into double screw extruder, twin-screw extrusion batten is water cooled,
Air-dried, pelletizing, obtains master batch, master batch is finally put into plastic film blowing machine extrusion blown film, to obtain final product
To finished product.
Embodiment 2
The novel low temperature resistant polypropylene for medical article film formulation of one of the present embodiment, by following weight portion
Raw material prepare: polypropylene 110 parts, alkyd resin 18 parts, trimethylolpropane tris propylene
Acid esters 9 parts, potassium peroxydisulfate 8 parts, vinyl acetate 50 parts, glycerine 15 parts, linea low density
Polyethylene 18 parts, Tissuemat E 15 parts, Artemisia Glue 20 parts, hydroxypropyl cellulose 18 parts.
Preparation method is: weigh each component by weight ratio, puts in reactor, at nitrogen
Gas atmosphere adds thermal response, is then fed into double screw extruder, twin-screw extrusion batten is water cooled,
Air-dried, pelletizing, obtains master batch, master batch is finally put into plastic film blowing machine extrusion blown film, to obtain final product
To finished product.
Embodiment 3
The novel low temperature resistant polypropylene for medical article film formulation of one of the present embodiment, by following weight portion
Raw material prepare: polypropylene 102 parts, alkyd resin 14 parts, trimethylolpropane tris propylene
Acid esters 6 parts, potassium peroxydisulfate 5 parts, vinyl acetate 50 parts, glycerine 12 parts, linea low density
Polyethylene 13 parts, Tissuemat E 12 parts, Artemisia Glue 16 parts, hydroxypropyl cellulose 13 parts.
Preparation method is: weigh each component by weight ratio, puts in reactor, at nitrogen
Gas atmosphere adds thermal response, is then fed into double screw extruder, twin-screw extrusion batten is water cooled,
Air-dried, pelletizing, obtains master batch, master batch is finally put into plastic film blowing machine extrusion blown film, to obtain final product
To finished product.
Embodiment 4
The novel low temperature resistant polypropylene for medical article film formulation of one of the present embodiment, by following weight portion
Raw material prepare: polypropylene 108 parts, alkyd resin 17 parts, trimethylolpropane tris propylene
Acid esters 8 parts, potassium peroxydisulfate 7 parts, vinyl acetate 50 parts, glycerine 14 parts, linea low density
Polyethylene 17 parts, Tissuemat E 14 parts, Artemisia Glue 17 parts, hydroxypropyl cellulose 17 parts.
Preparation method is: weigh each component by weight ratio, puts in reactor, at nitrogen
Gas atmosphere adds thermal response, is then fed into double screw extruder, twin-screw extrusion batten is water cooled,
Air-dried, pelletizing, obtains master batch, master batch is finally put into plastic film blowing machine extrusion blown film, to obtain final product
To finished product.
Claims (5)
1. a novel low temperature resistant polypropylene for medical article film formulation, it is characterised in that include following
The raw material of weight portion: polypropylene 100-110 part, alkyd resin 12-18 part, trihydroxy methyl third
Alkane triacrylate 5-9 part, potassium peroxydisulfate 4-8 part, vinyl acetate 50 parts, glycerine 10-15
Part, LLDPE 12-18 part, Tissuemat E 10-15 part, Artemisia Glue 15-20
Part, hydroxypropyl cellulose 12-18 part.
The novel low temperature resistant polypropylene for medical article film of one the most according to claim 1 is joined
Side, it is characterised in that prepared by the raw material of following weight portion: polypropylene 100 parts, alkyd resin
12 parts, trimethylolpropane trimethacrylate 5 parts, potassium peroxydisulfate 4 parts, vinyl acetate 50
Part, glycerine 10 parts, LLDPE 12 parts, Tissuemat E 10 parts, Artemisia Glue
15 parts, hydroxypropyl cellulose 12 parts.
The novel low temperature resistant polypropylene for medical article film of one the most according to claim 1 is joined
Side, it is characterised in that prepared by the raw material of following weight portion: polypropylene 110 parts, alkyd resin
18 parts, trimethylolpropane trimethacrylate 9 parts, potassium peroxydisulfate 8 parts, vinyl acetate 50
Part, glycerine 15 parts, LLDPE 18 parts, Tissuemat E 15 parts, Artemisia Glue
20 parts, hydroxypropyl cellulose 18 parts.
The novel low temperature resistant polypropylene for medical article film of one the most according to claim 1 is joined
Side, it is characterised in that prepared by the raw material of following weight portion: polypropylene 102 parts, alkyd resin
14 parts, trimethylolpropane trimethacrylate 6 parts, potassium peroxydisulfate 5 parts, vinyl acetate 50
Part, glycerine 12 parts, LLDPE 13 parts, Tissuemat E 12 parts, Artemisia Glue
16 parts, hydroxypropyl cellulose 13 parts.
The novel low temperature resistant polypropylene for medical article film of one the most according to claim 1 is joined
Side, it is characterised in that prepared by the raw material of following weight portion: polypropylene 108 parts, alkyd resin
17 parts, trimethylolpropane trimethacrylate 8 parts, potassium peroxydisulfate 7 parts, vinyl acetate 50
Part, glycerine 14 parts, LLDPE 17 parts, Tissuemat E 14 parts, Artemisia Glue
17 parts, hydroxypropyl cellulose 17 parts.