CN105863083B - 一种无机保温墙体 - Google Patents
一种无机保温墙体 Download PDFInfo
- Publication number
- CN105863083B CN105863083B CN201610205930.XA CN201610205930A CN105863083B CN 105863083 B CN105863083 B CN 105863083B CN 201610205930 A CN201610205930 A CN 201610205930A CN 105863083 B CN105863083 B CN 105863083B
- Authority
- CN
- China
- Prior art keywords
- heat insulation
- inorganic heat
- mortar
- layer
- wall
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种无机保温墙体，包括墙体，自墙体外壁向外依次设置界面层、保温层、抗裂防护层和饰面层；界面层由界面砂浆构成，保温层由无机保温砂浆构成，抗裂防护层由抗裂砂浆构成。本发明能够有效解决现有的保温墙体在各方面性能不够好，不能够满足市场需求的问题。
Description
技术领域
发明涉及一种无机保温墙体。
背景技术
近几年来，我国施工了巨大量的外墙外保温***，其中以有机保温材料为主，从建筑节能方面考虑取得了一定的成就。但是，随之而来的接连不断的火灾向人们敲响了警钟，因而建筑防火、特别是外墙外保温的防火问题得到高度重视。2009年9月，公安部、住房和城乡***于发布了《民用建筑外保温***及外墙装饰防火暂行规定》([2009]46号)。2011年3月14日，公安部消防局又下发了《关于进一步明确民用建筑保温材料消防监督管理有关要求的通知》。通知要求“在新标准发布前，从严执行《民用建筑外保温***及外墙装饰防火暂行规定》(公通字[2009]46号)第二条规定，民用建筑外保温材料采用燃烧性能为A级的材料”。
这些文件的强制性规定，使得有机保温材料的使用受到极大约束。因而，人们一方面开始寻找、研制能够达到无机不燃性能要求的保温材料，另一方面，人们对以前应用的能够达到A级不燃材料的外墙外保温***进行进一步的开发应用。在前一种情况下，岩棉板外墙外保温***技术应运而生，迅速得到大量应用，占有一定量的市场份额。在后一种情况下，以前已经具有一定应用范围和市场份额的建筑保温砂浆外墙外保温***得到进一步的应用，所占有的市场份额迅速增大。
2013年1月20日，住房和城乡***下发《关于贯彻落实国务院关于加强和改进消防工作的意见的通知》，规定“民用建筑外保温材料的燃烧性能宜为A级，且不应低于B2级”。这样以来虽然燃烧性能达到B2级的保温材料应用于外墙面，但由于许多地方上的消防部门在竣工验收方面并没有放开，因而能够达到A级不燃的外墙保温材料仍然具有很大的应用市场。
发明内容
发明的目的是提供一种无机保温墙体，解决现有的保温墙体在各方面性 能不够好，不能够满足市场需求的问题。
发明解决其技术问题所采用的技术方案是：一种无机保温墙体，包括墙体，自墙体外壁向外依次设置界面层、保温层、抗裂防护层和饰面层；界面层由界面砂浆构成，保温层由无机保温砂浆构成，抗裂防护层由抗裂砂浆构成；
所述界面砂浆的组分按质量百分比包括：胶凝材料45～50％，成品砂47～52％，增稠剂0.5～1.5％，可分散乳胶粉1.5～2.5％；
所述无机保温砂浆的组分按质量百分比包括：胶凝材料48～52％，矿物添加剂4～6％，增粘保水剂0.5～1.5％，高分子增强剂0.25％，短切纤维0.5～1％，膨胀玻化微珠40～45％；
所述抗裂砂浆的组分按质量百分比为：胶凝材料38～42％，矿物添加剂4～6％，增稠剂2～2.5％，成品用砂45～55％，短切纤维0.5～1％，可分散乳胶粉1.5～2.5％。
优选的，胶凝材料为硅酸盐水泥和石膏中的一种或者两种，石膏为α-半水石膏、β-半水石膏和天然建筑石膏中的一种或者多种。
优选的，成品砂的目数为40目。
优选的，增稠剂为聚丙烯酰胺。
优选的，可分散乳胶粉为瓦克可再分散乳胶粉，可分散乳胶粉为瓦克可再分散乳胶粉，其中抗裂砂浆和界面砂浆中的可分散乳胶粉为山西三维集团股份有限公司的SWF-04型乳胶粉，保温砂浆中的可分散乳胶粉为SWF-05型乳胶粉。
优选的，增粘保水剂为羟甲基纤维素。
优选的，高分子增强剂选用短纤维聚丙烯纤维。
优选的，短切纤维为聚丙烯纤维。
为了提高抗裂防护效果，抗裂防护层内设置有耐碱网格布或热镀锌钢丝网。
为了使得无极保温墙体结构更加合理，保温及各方面性能更好，界面层、 保温层、抗裂防护层和饰面层四者间的层厚比为1：4：2：3。
发明的有益效果：涉及的界面砂浆、无机保温砂浆、抗裂砂浆在各方面的功能效果更好，同时该保温墙体相对现有的保温墙体而言，在各方效果及结构合理性上更具优势。
以下将结合附图和实施例，对本发明进行较为详细的说明。
附图说明
图1为发明的结构示意图。
具体实施方式
实施例1，如图1所示的一种无机保温墙体，包括墙体1，自墙体1外壁向外依次设置界面层2、保温层3、抗裂防护层4和饰面层5；界面层2由界面砂浆构成，保温层3由无机保温砂浆构成，抗裂防护层4由抗裂砂浆构成；
所述界面砂浆的组分按质量百分比包括：胶凝材料50％，成品砂47％，增稠剂0.5％，可分散乳胶粉2.5％；
所述无机保温砂浆的组分按质量百分比包括：胶凝材料50％，矿物添加剂5％，增粘保水剂1.5％，高分子增强剂0.5％，短切纤维0.5％，膨胀玻化微珠42.5％；
所述抗裂砂浆的组分按质量百分比为：胶凝材料40％，矿物添加剂5％，增稠剂2.25％，成品用砂50％，短切纤维0.75％，可分散乳胶粉2％。
实施例2，一种无机保温墙体，包括墙体1，自墙体1外壁向外依次设置界面层2、保温层3、抗裂防护层4和饰面层5；界面层2由界面砂浆构成，保温层3由无机保温砂浆构成，抗裂防护层4由抗裂砂浆构成；
所述界面砂浆的组分按质量百分比包括：胶凝材料45％，成品砂52％，增稠剂1.5％，可分散乳胶粉1.5％；
所述无机保温砂浆的组分按质量百分比包括：胶凝材料52％，矿物添加剂6％，增粘保水剂1，高分子增强剂0.25％，短切纤维0.75％，膨胀玻化微珠40％；
所述抗裂砂浆的组分按质量百分比为：胶凝材料38％，矿物添加剂4％， 增稠剂2.5％，成品用砂52％，短切纤维1％，可分散乳胶粉2.5％。
实施例3，一种无机保温墙体，包括墙体1，自墙体1外壁向外依次设置界面层2、保温层3、抗裂防护层4和饰面层5；界面层2由界面砂浆构成，保温层3由无机保温砂浆构成，抗裂防护层4由抗裂砂浆构成；
所述界面砂浆的组分按质量百分比包括：胶凝材料47％，成品砂50％，增稠剂1％，可分散乳胶粉2％；
所述无机保温砂浆的组分按质量百分比包括：胶凝材料48％，矿物添加剂4％，增粘保水剂0.5％，高分子增强剂1.5％，短切纤维1％，膨胀玻化微珠45％；
所述抗裂砂浆的组分按质量百分比为：胶凝材料42％，矿物添加剂6％，增稠剂2％，成品用砂48％，短切纤维0.5％，可分散乳胶粉1.5％。
实施例4，基于实施例1至3所述的无机保温墙体，胶水凝材料为硅酸盐水泥和石膏中的一种或者两种，石膏为α-半水石膏、β-半水石膏和天然建筑石膏中的一种或者多种。成品砂的目数为40目。增稠剂为聚丙烯酰胺。可分散乳胶粉为瓦克可再分散乳胶粉。增粘保水剂为羟甲基纤维素。高分子增强剂选用短纤维聚丙烯纤维。短切纤维为聚丙烯纤维。抗裂防护层4内设置有耐碱网格布6或热镀锌钢丝网。界面层2、保温层3、抗裂防护层4和饰面层5四者间的层厚比为1：4：2：3。
水泥作为无机保温砂浆的胶结材料，其28d强度应不低于32.5MPa，即强度等级不应低于32.5级。我公司使用的是铜陵海螺水泥有限公司生产的32.5级复合硅酸盐水泥，品质优良，性能可靠。
该水泥的的3天抗压强度达到18.5MPa；28天抗压强度达到138.1MPa；3天抗折强度达到4.0MPa；28天抗折强度达到7.4MPa。
可再分散乳胶粉掺加到无机保温砂浆、界面砂浆、抗裂砂浆中，能够起到两种作用，一是残留于乳胶粉中的表面活性剂能够起到强烈的减水作用，因降低砂浆的水灰比而提高强度；二是乳胶粉能够弥补水泥石中的微观缺陷而提高砂浆的韧性和黏结强度。生产中使用的是山西三维集团股份有限公司 的SWF-04型乳胶粉(用于生产抗裂砂浆和界面砂浆)和SWF-05型乳胶粉(用于生产保温砂浆)，其技术性能如表1和表2所示。
表1三维公司SWF-04型乳胶粉的技术性能
表2三维公司SWF-05型乳胶粉的技术性能
使用粉煤灰可以取得一定的技术经济效益。首先，粉煤灰能够提高产品的强度，能够改善水泥基材料中的矿物结构，提高致密性。粉煤灰还能够改善保温砂浆的施工性能，使砂浆呈现极好的和易性。其次，粉煤灰的成本很低，即使包装良好的Ⅰ级商品粉煤灰，价格也只有一百多元一吨，比水泥的价格低得多，可以用于取代部分水泥。
粉煤灰在水泥基材料中应用的最大性能优势还在于其后期水化性能。这 既能够提高水泥基材料的强度，又能够改善水泥基材料中的矿物结构，提高抗冻融耐久性。粉煤灰在水泥水化的后龄期，在水泥水化产生的氢氧化钙的激发作用下开始水化，由于这时水泥已经进行了充分的水化，在结构中存在着大量毛细孔隙，粉煤灰的水化产物能够堵塞结构中的这些毛细孔隙，提高烟道结构的密实性。
因而，在无机建筑保温砂浆生产中使用粉煤灰能够增加浆体含量，改善浆体的和易性，降低保温砂浆的干密度，使保温砂浆的结构更加密实，强度更高。相反，如果不是使用粉煤灰，而是通过增大水泥用量来提高砂浆拌合物的和易性，则会增大制品的干密度，降低保温砂浆的热工性能。
本发明中使用的是发电厂的干排灰，产品质量为Ⅰ级。性能符合国家标准GB/T1596—1991《用于水泥和混凝土中的粉煤灰的规定》的要求。
本发明中中使用的粉煤灰为黄山鑫泰工贸公司供应的商品粉煤灰，供应商提供的九江粉煤灰利用有限公司对该粉煤灰烧失量的检测结果为3.68％。
膨胀玻化微珠是一种新型的无机轻质骨料及绝热材料，其颗粒呈不规则球状，其内部为多孔的空腔结构，而外表面封闭、光滑，具有质轻、绝热、防火、耐高温、耐老化、吸水率低等优异性能。膨胀玻化微珠是膨胀玻化微珠无机保温砂浆的主体保温材料，其性能直接关系到膨胀玻化微珠无机保温砂浆的产品质量，包括物理力学强度、干密度和保温隔热性能。因而，应注意采用优质产品。
本发明中使用的膨胀玻化微珠为河南信阳华新建材有限公司的产品，系采用煤气供热式玻化微珠膨化炉生产的产品。其膨化工艺可靠，产品质量稳定。该玻化微珠产品属于市场上质量比较好的，价格稍高些。该膨胀玻化微珠的性能如表3所示。
表3膨胀玻化微珠的技术性能
由于甲基开投料。聚丙烯纤维难于分散，在投料时可采取特殊措施处理，助其分散。纤维素醚、粉煤灰、聚丙烯纤维、某些添加剂和乳胶粉等数量小，应该在投料时和水泥叉。
在水泥和甲基纤维素醚、粉煤灰、聚丙烯纤维、添加剂、乳胶粉等混合均匀后，投入玻化微珠搅拌混合均匀，得到成品膨胀玻化微珠无机保温砂浆。
界面砂浆、抗裂砂浆的生产过程基本类似。在生产过程中还应注意先打开除尘机的开关，做好除尘。
本发明涉及的无机保温墙体的性能与现有保温墙体的性能的比较见表4。
表4本无机保温墙体性能与现有技术的比较
本发明涉及的无机保温砂浆性能与现有技术的比较见表5。
表5本发明涉及的无机保温砂浆与现有技术的比较
界面砂浆性能对外墙外保温***的性能会产生重要影响，也应该给予高度重视，本发明涉及的界面砂浆性能十分优异。本发明公开的界面砂浆性能与现有产品的比较参见表6。
表6本发明涉及的界面砂浆性能与现有先进产品的比较
本发明涉及的抗裂砂浆的性能和现有产品性能水平的比较详见表7。
表7本发明涉及的抗裂砂浆性能与现有产品的比较
Claims (9)
1.一种无机保温墙体，其特征在于：包括墙体(1)，自墙体(1)外壁向外依次设置界面层(2)、保温层(3)、抗裂防护层(4)和饰面层(5)；界面层(2)由界面砂浆构成，保温层(3)由无机保温砂浆构成，抗裂防护层(4)由抗裂砂浆构成；
所述界面砂浆的组分按质量百分比包括：胶凝材料45～50％，成品砂47～52％，增稠剂0.5～1.5％，可分散乳胶粉1.5～2.5％；
所述无机保温砂浆的组分按质量百分比包括：胶凝材料48～52％，矿物添加剂4～6％，增粘保水剂0.5～1.5％，高分子增强剂0.25％，短切纤维0.5～1％，膨胀玻化微珠40～45％；
所述抗裂砂浆的组分按质量百分比为：胶凝材料38～42％，矿物添加剂4～6％，增稠剂2～2.5％，成品用砂45～55％，短切纤维0.5～1％，可分散乳胶粉1.5～2.5％；
胶凝材料为硅酸盐水泥和石膏中的一种或者两种，石膏为α-半水石膏、β-半水石膏和天然建筑石膏中的一种或者多种。
2.根据权利要求1所述的无机保温墙体，其特征在于：成品砂的目数为40目。
3.根据权利要求1所述的无机保温墙体，其特征在于：增稠剂为聚丙烯酰胺。
4.根据权利要求1所述的无机保温墙体，其特征在于：可分散乳胶粉为瓦克可再分散乳胶粉，其中抗裂砂浆和界面砂浆中的可分散乳胶粉为山西三维集团股份有限公司的SWF-04型乳胶粉，保温砂浆中的可分散乳胶粉为SWF-05型乳胶粉。
5.根据权利要求1所述的无机保温墙体，其特征在于：增粘保水剂为羟甲基纤维素。
6.根据权利要求1所述的无机保温墙体，其特征在于：高分子增强剂选用短纤维聚丙烯纤维。
7.根据权利要求1所述的无机保温墙体，其特征在于：短切纤维为聚丙烯纤维。
8.根据权利要求1至7任意一项所述的无机保温墙体，其特征在于：抗裂防护层(4)内设置有耐碱网格布或热镀锌钢丝网。
9.根据权利要求1至7任意一项所述的无机保温墙体，其特征在于：界面层(2)、保温层(3)、抗裂防护层(4)和饰面层(5)四者间的层厚比为1：4：2：3。