CN105860930B - Vehicle glass antirain agent and preparation method thereof when a kind of long-acting - Google Patents
Vehicle glass antirain agent and preparation method thereof when a kind of long-acting Download PDFInfo
- Publication number
- CN105860930B CN105860930B CN201610204984.4A CN201610204984A CN105860930B CN 105860930 B CN105860930 B CN 105860930B CN 201610204984 A CN201610204984 A CN 201610204984A CN 105860930 B CN105860930 B CN 105860930B
- Authority
- CN
- China
- Prior art keywords
- modified
- solution
- acting
- long
- vehicle glass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention belongs to technical field of fine, vehicle glass antirain agent and preparation method thereof when specially a kind of long-acting.The glass antirain agent is made up of the raw material of following weight percent:Modified manometer silicon dioxide colloidal sol 10 20%, modified polypropene acid solution 1 2%, modified sorbitol solution 5% 10%, sodium alginate 0.1 0.5%, poly-vinyl alcohol solution 1% 5%, polysorbate60 0.5 1%, lauryl sodium sulfate 0.5 1%, glycerine 5 10%, propane diols 5 10%, water surplus, gross mass percentage composition sum is 100%.As a result of modified super hydrophilic nano silicon in the present invention, its rainproof effect is greatly enhanced.As a result of the preferable modified polypropene acid solution of adhesion, super hydrophilic nano-particle and surface active agent composition can be made to be attached on without coming off on glass, so as to more enhance the durability of rain-proof product.The rainproof effect of 15 days can be kept.
Description
Technical field
The invention belongs to technical field of fine, vehicle glass antirain agent and its preparation side when specially a kind of long-acting
Method.
Background technology
At present, with rapid economic development, the car ownership of China has broken through 100,000,000.And also in sustainable growth.
Automobile greatly facilitates the life of people, still, and it also brings a series of traffic safety hidden danger, according to the statistics made by the departments concerned,
Great motor traffic accidents has 70% generation in rainy day and night.Driving in the rain, it is maximum potential safety hazard that sight, which is not known,.
Greatly in the rain, even if rain brush high speed swinging, the rainwater on glass still can not be cleaned, the moisture film folding at this moment formed on glass
Penetrate, you can be made can not to see front clearly;When the oversize vehicle particularly travelled with opposite crosses, the water that cart wheel is splash can splash
Onto vehicle window, at this moment waiting, outer situation is just unclear, and potential safety hazard is high.The concrete reason for causing not seeing Chu is:Rainwater
When splashing on glass, the angle between water droplet and glass surface forms moisture film at 15 degree or so, and on glass, makes sight mould
Paste, cause you can not in time to glass outside situation grasp.So in rainy day, particularly reversing process, vehicle glass
And adhere to many droplets on rearview mirror, influence driving sight, it is impossible to see the barrier of after car and car side clearly from rearview mirror.
Rain because sight difference has become a very important traffic safety problem.At present on the market with the presence of glass antirain agent, but
Being specific to the antirain agent of vehicle glass does not almost have.
The content of the invention
The present invention exactly has efficient, lasting water-resistant performance and green ring for above technical problem there is provided a kind of
Vehicle glass antirain agent of guarantor and preparation method thereof.
The concrete technical scheme of the present invention is as follows:
Vehicle glass antirain agent is made up of the raw material of following weight percent when a kind of long-acting:
Modified manometer silicon dioxide colloidal sol 10-20%
Modified polypropene acid solution 1-2%
Modified sorbitol solution 5%-10%
Sodium alginate 0.1-0.5%
Poly-vinyl alcohol solution 1%-5%
Tween-60 0.5-1%
Lauryl sodium sulfate 0.5-1%
Glycerine 5-10%
Propane diols 5-10%
Water surplus
Gross mass percentage composition sum is 100%.
The concentration control of the modified manometer silicon dioxide colloidal sol is 30wt%.
The concentration of the modified polypropene acid solution is 8wt%.
The concentration of the modified sorbitol solution is controlled in 15wt%.
The concentration of the poly-vinyl alcohol solution is controlled in 3wt%.
The preparation method of the modified manometer silicon dioxide colloidal sol comprises the following steps:
(1) each raw material, is weighed in proportion, then in the 250ml there-necked flasks with thermometer and agitator, adds 18g
Nano silicon and 78.8g absolute ethyl alcohols, after being stirred 10 minutes under conditions of 40 DEG C, add the ethoxy of 0.2g vinyl three
Radical siloxane, is again stirring for 30 minutes;
(2) 0.5g maleic anhydrides, 1g acrylic acid, 0.5g methacrylic acids, 0.5g propylene, are sequentially added into there-necked flask again
Sour hydroxyl ethyl ester, was sufficiently stirred for after 10 minutes, adds 0.1g dibenzoyl peroxides, is warming up to boiling;
(3), boiling reaction 3h, is incubated 30 minutes, adds polyvinyl alcohol 0.1g and sorbierite 0.3g, stirs to completely molten
Solution, that is, be made modified manometer silicon dioxide colloidal sol.
The preparation method of the modified polypropene acid solution comprises the following steps:
In there-necked flask, acrylic acid 2g, maleic anhydride 3g, methacrylic acid 3g, water 92g, potassium peroxydisulfate 0.5g are added, is mixed
Close and react 3h after 85 DEG C, that is, modified polyacrylate solution is made.
The preparation method of the modified sorbitol solution comprises the following steps:Take the sorbierite 18g after drying and dewatering, Malaysia
Acid anhydrides 30g, is heated to 80 DEG C, stirring reaction 2h adds water the solution for being configured to 15wt%, and pH=7 are neutralized to NaOH, that is, is made
Modified sorbitol solution.
The preparation method of vehicle glass antirain agent comprises the following steps when long-acting:
(1)Each raw material is weighed in proportion, then at room temperature, to addition modified manometer silicon dioxide colloidal sol in a reservoir,
Water, glycerine, propane diols, modified polypropene acid solution, modified sorbitol solution, poly-vinyl alcohol solution, sodium alginate, stirring is equal
It is even;
(2) lauryl sodium sulfate, is added into container again, then Tween-60 emulsifying agent stirs, that is, length is made
Glass antirain agent during effect.
The positive effect of the present invention is embodied in:
(One), the rain-proof duration can reach 15 days, it is easy to use, be sprayed on glass, without wiping, natural sagging, which is dried, is
Can.As a result of modified super hydrophilic nano silicon, its rainproof effect is greatly enhanced.
(Two), as a result of the preferable modified polypropene acid solution of adhesion, super hydrophilic nano-particle and surface can be made
Active agent component is attached on without coming off on glass, so as to more enhance the durability of rain-proof product.It can keep 15 days
Rainproof effect.
(Three), it is the application environmental protection, pollution-free, easy to clean, it is corrosion-free to glass.
Embodiment
In order to make the purpose , technical scheme and advantage of the present invention be clearer, with reference to embodiment pair
The present invention is described in further detail, but this should not be interpreted as to the scope of above-mentioned theme of the invention is only limitted to following implementations
Example.
In all examples below, unless stated otherwise, its raw material used is satisfied by following condition:
The concentration control of described modified manometer silicon dioxide colloidal sol is 30wt%.
The concentration of the modified polypropene acid solution is 8wt%.
The concentration of the modified sorbitol solution is controlled in 15wt%.
The concentration of the poly-vinyl alcohol solution is controlled in 3wt%.
The preparation method of the modified manometer silicon dioxide colloidal sol comprises the following steps:
(1) each raw material, is weighed in proportion, then in the 250ml there-necked flasks with thermometer and agitator, adds 18g
Nano silicon and 78.8g absolute ethyl alcohols, after being stirred 10 minutes under conditions of 40 DEG C, add the ethoxy of 0.2g vinyl three
Radical siloxane, is again stirring for 30 minutes;
(2) 0.5g maleic anhydrides, 1g acrylic acid, 0.5g methacrylic acids, 0.5g propylene, are sequentially added into there-necked flask again
Sour hydroxyl ethyl ester, was sufficiently stirred for after 10 minutes, adds 0.1g dibenzoyl peroxides, is warming up to boiling;
(3), boiling reaction 3h, is incubated 30 minutes, adds polyvinyl alcohol 0.1g and sorbierite 0.3g, stirs to completely molten
Solution, that is, be made modified manometer silicon dioxide colloidal sol.
The preparation method of the modified polypropene acid solution comprises the following steps:
In there-necked flask, acrylic acid 2g, maleic anhydride 3g, methacrylic acid 3g, water 92g, potassium peroxydisulfate 0.5g are added, is mixed
Close and react 3h after 85 DEG C, that is, modified polyacrylate solution is made.
The preparation method of the modified sorbitol solution comprises the following steps:Take the sorbierite 18g after drying and dewatering, Malaysia
Acid anhydrides 30g, is heated to 80 DEG C, stirring reaction 2h adds water the solution for being configured to 15wt%, and pH=7 are neutralized to NaOH, that is, is made
Modified sorbitol solution.
Embodiment 1:
Vehicle glass antirain agent when a kind of long-acting, includes the raw material of following weight/mass percentage composition:
Modified manometer silicon dioxide colloidal sol 10%
Modified polypropene acid solution 1%
Modified sorbitol solution 5%
Sodium alginate 0.1%
Poly-vinyl alcohol solution 1%
Tween-60 0.5%
Lauryl sodium sulfate 0.5%
Glycerine 5%
Propane diols 5%
Water surplus,
Gross mass percentage composition sum is 100%.
The specific preparation process of vehicle glass antirain agent is when this is long-acting:
(1), at room temperature, modified manometer silicon dioxide colloidal sol 10g, water 72g, glycerine 5g, the third two are first added in a reservoir
Alcohol 5g, modified polypropene acid solution 1g, modified sorbitol solution 5g, poly-vinyl alcohol solution 1g, sodium alginate 0.1 stir.
(2), again into container add lauryl sodium sulfate 0.5g, Tween-60 emulsifying agent 0.5g, then stir,
Glass antirain agent when being made long-acting.
(3), this product is sprayed at glass surface with 10mL/m2, wiped without towel, allow its natural sagging, natural drying is
Can, the glass has lasting rainproof effect.
Embodiment 2:
Vehicle glass antirain agent when a kind of long-acting, includes the raw material of following weight/mass percentage composition:
Modified manometer silicon dioxide colloidal sol(Wt30% liquid) 15%
Modified polypropene acid solution(wt8%) 1.5%
Modified sorbitol solution (wt15%) 7%
Sodium alginate 0.3%
Poly-vinyl alcohol solution(wt3%) 3%
Tween-60 0.7%
Lauryl sodium sulfate 0.7%
Glycerine 7%
Propane diols 7%
Water surplus
Gross mass percentage composition sum is 100%.
Described preparation method is with example 1.
Embodiment 3:
Vehicle glass antirain agent when a kind of long-acting, includes the raw material of following weight/mass percentage composition:
Modified manometer silicon dioxide colloidal sol(Wt30% liquid) 20%
Modified polypropene acid solution(wt8%) 2%
Modified sorbitol solution (wt15%) 10%
Sodium alginate 0.5%
Poly-vinyl alcohol solution(wt3%) 5%
Tween-60 1%
Lauryl sodium sulfate 1%
Glycerine 10%
Propane diols 10%
Water surplus
Gross mass percentage composition sum is 100%.
Described preparation method is with example 1.
Claims (8)
1. vehicle glass antirain agent when a kind of long-acting, it is characterised in that be made up of the raw material of following weight percent:
Modified manometer silicon dioxide colloidal sol 10-20%
Modified polypropene acid solution 1-2%
Modified sorbitol solution 5%-10%
Sodium alginate 0.1-0.5%
Poly-vinyl alcohol solution 1%-5%
Tween-60 0.5-1%
Lauryl sodium sulfate 0.5-1%
Glycerine 5-10%
Propane diols 5-10%
Water surplus
Gross mass percentage composition sum is 100%;
The preparation method of the modified manometer silicon dioxide colloidal sol comprises the following steps:
(1) each raw material, is weighed in proportion, then in the 250ml there-necked flasks with thermometer and agitator, adds 18g nanometers
Silica and 78.8g absolute ethyl alcohols, after being stirred 10 minutes under conditions of 40 DEG C, add 0.2g vinyl triethoxyl silicon
Oxygen alkane, is again stirring for 30 minutes;
(2) 0.5g maleic anhydrides, 1g acrylic acid, 0.5g methacrylic acids, 0.5g acrylic acid hydroxyls, are sequentially added into there-necked flask again
Ethyl ester, was sufficiently stirred for after 10 minutes, adds 0.1g dibenzoyl peroxides, is warming up to boiling;
(3), boiling reaction 3h, is incubated 30 minutes, adds polyvinyl alcohol 0.1g and sorbierite 0.3g, stirring to being completely dissolved,
Modified manometer silicon dioxide colloidal sol is made.
2. vehicle glass antirain agent when according to claim 1 long-acting, it is characterised in that:The modified manometer silicon dioxide
The concentration control of colloidal sol is 30wt%.
3. vehicle glass antirain agent when according to claim 1 long-acting, it is characterised in that:The modified polypropene acid solution
Concentration be 8wt%.
4. vehicle glass antirain agent when according to claim 1 long-acting, it is characterised in that:The modified sorbitol solution
Concentration is controlled in 15wt%.
5. vehicle glass antirain agent when according to claim 1 long-acting, it is characterised in that:The poly-vinyl alcohol solution it is dense
Degree control is in 3wt%.
6. vehicle glass antirain agent during long-acting according to any one claim in claim 1-5, it is characterised in that
The preparation method of the modified polypropene acid solution comprises the following steps:
In there-necked flask, acrylic acid 2g, maleic anhydride 3g, methacrylic acid 3g, water 92g, potassium peroxydisulfate 0.5g, after mixing are added
3h is reacted in 85 DEG C, that is, modified polyacrylate solution is made.
7. vehicle glass antirain agent during long-acting according to any one claim in claim 1-5, it is characterised in that
The preparation method of the modified sorbitol solution comprises the following steps:The sorbierite 18g after drying and dewatering, maleic anhydride 30g are taken,
80 DEG C are heated to, stirring reaction 2h adds water the solution for being configured to 15wt%, and pH=7 are neutralized to NaOH, that is, modified sorb is made
Alcoholic solution.
8. the preparation method of vehicle glass antirain agent when long-acting according to claim 1, it is characterised in that comprise the following steps:
(1)Each raw material is weighed in proportion, and then at room temperature, to modified manometer silicon dioxide colloidal sol is added in a reservoir, water is sweet
Oil, propane diols, modified polypropene acid solution, modified sorbitol solution, poly-vinyl alcohol solution, sodium alginate stirs;
(2) lauryl sodium sulfate, is added into container again, then Tween-60 emulsifying agent stirs, that is, when being made long-acting
Glass antirain agent.