CN105860843A - Room temperature non-solidified waterproof sealant - Google Patents
Room temperature non-solidified waterproof sealant Download PDFInfo
- Publication number
- CN105860843A CN105860843A CN201610320593.9A CN201610320593A CN105860843A CN 105860843 A CN105860843 A CN 105860843A CN 201610320593 A CN201610320593 A CN 201610320593A CN 105860843 A CN105860843 A CN 105860843A
- Authority
- CN
- China
- Prior art keywords
- room temperature
- waterproof gasket
- gasket cement
- solidified
- uncured
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the field of waterproof sealing materials, in particular to a room temperature non-solidified waterproof sealant. The room temperature non-solidified waterproof sealant comprises the following raw materials in parts by mass: 20 to 40 parts of vegetable asphalt and 5 to 20 parts of elastically polymerized pure acrylic emulsions. The purpose of the invention is to provide the room temperature non-solidified waterproof sealant, so that a coating can be sprayed at room temperature, the 'non-solidified' adhesive-sticker effect of the coating with a formed film is consistent with that of a 'non-solidified rubber asphalt coating', and the room temperature non-solidified waterproof sealant does not flow at the high temperature of 100 DEG C, and further does not harden and crack, and is very convenient to use and good in waterproof effect.
Description
Technical field
The present invention relates to waterproof and sealing material field, particularly relate to a kind of uncured waterproof gasket cement of room temperature.
Background technology
The anti-market for water of domestic construction occurs the most in a large number and is used in the product of one entitled " uncured rubber-asphalt coating " of all kinds of waterproofing work, due to pitch articles at normal temperatures in solid state, enter and need when building site uses to use special electric smelting furnace to heat thawing to liquid；Re-use special spraying equipment and carry out spraying application, and the fusing point of pitch articles is the lowest, typically i.e. start melting trickling at about 60 degree, construction part is easy to occurs that coating runs off and type becomes and causes disabler；For small-sized building site, field without electricity operation, safeguard the engineerings such as repairing will be hope into not and.
Summary of the invention
It is an object of the invention to provide a kind of uncured waterproof gasket cement of room temperature, can construction paint at normal temperatures, " uncured " adhesive sticker effect after coating film forming is consistent with the effect of " uncured rubber-asphalt coating ", do not flow under the high temperature of 100 degrees Celsius, non-sclerous embrittlement in a low temperature of subzero 20 degrees Celsius, very easy to use, waterproof effect is the most excellent.
In order to realize object above, the technical solution used in the present invention is: a kind of uncured waterproof gasket cement of room temperature, and it includes the raw material of following mass fraction: plant asphalt 20-40 part；Flexible polymer pure-acrylic emulsion 5-20 part.
Preferably, described plant asphalt is the bitumen product obtained after Vegetable oil lipoprotein heavy distillate.
Preferably, it also includes esters or the benzene kind solvent of 3-8 part.
Preferably, described esters or benzene kind solvent solvent are lower boiling esters or benzene kind solvent.
Preferably, described esters solvent is ethyl acetate or butyl acetate.
Preferably, described benzene kind solvent is toluene or dimethylbenzene.
Preferably, it also includes the hydroquinone polymerization inhibitor of 0.1-0.3 part.
Preferably, it also includes the OP-10 emulsifying agent of 0.05-0.2 part.
The invention have the benefit that
1, the waterproof gasket cement of the present invention can construction paint at normal temperatures, " uncured " adhesive sticker effect after coating film forming is consistent with the effect of " uncured rubber-asphalt coating ", do not flow under the high temperature of 100 degrees Celsius, non-sclerous embrittlement in a low temperature of subzero 20 degrees Celsius, very easy to use, waterproof effect is the most excellent.
2, the Colophonium that plant asphalt obtains after using Vegetable oil lipoprotein heavy distillate, material is cheap, has good uncured characteristic simultaneously, and in the environment of-20-100 degree Celsius, performance will not change.
3, esters or the interpolation of benzene kind solvent, reduces polymerization viscosity, it is simple to construction.
4, the addition of emulsifying agent, preferably can form homogenizing pasty colloid by plant asphalt and flexible polymer pure-acrylic emulsion.
5, the addition of polymerization inhibitor, can reduce plant asphalt and the response speed of flexible polymer pure-acrylic emulsion further, improves the holding time of product.
Detailed description of the invention
Understandable for enabling the above-mentioned purpose of the present invention, feature and advantage to become apparent from, below the detailed description of the invention of the present invention is elaborated.Elaborate a lot of detail in the following description so that fully understanding the present invention.But the present invention can implement to be much different from other modes described here, those skilled in the art can do similar improvement in the case of intension of the present invention, and therefore the present invention is not limited by following public being embodied as.
The following is specific embodiment
Embodiment 1:
A kind of uncured waterproof gasket cement of room temperature, it includes the raw material of following mass fraction: obtain plant asphalt 20 parts after Vegetable oil lipoprotein heavy distillate；Flexible polymer pure-acrylic emulsion 20 parts.
Application: plant asphalt and flexible polymer pure-acrylic emulsion are separated packaging, then enters with twin-tub high-pressure slip-casting and become uncured wall leakage grouting glue in building cracks defect；Use now with the current.
Embodiment 2:
A kind of uncured waterproof gasket cement of room temperature, it includes the raw material of following mass fraction: obtain plant asphalt 40 parts after Vegetable oil lipoprotein heavy distillate；Flexible polymer pure-acrylic emulsion 5 parts；Ethyl acetate 3 parts；0.3 part of hydroquinone polymerization inhibitor；0.05 part of OP-10 emulsifying agent.
Embodiment 3:
A kind of uncured waterproof gasket cement of room temperature, it includes the raw material of following mass fraction: obtain plant asphalt 20 parts after Vegetable oil lipoprotein heavy distillate；Flexible polymer pure-acrylic emulsion 20 parts；Butyl acetate 8 parts；0.1 part of hydroquinone polymerization inhibitor；0.15 part of OP-10 emulsifying agent.
Embodiment 4:
A kind of uncured waterproof gasket cement of room temperature, it includes the raw material of following mass fraction: obtain plant asphalt 30 parts after Vegetable oil lipoprotein heavy distillate；Flexible polymer pure-acrylic emulsion 10 parts；Second toluene 5 parts；0.2 part of hydroquinone polymerization inhibitor；0.1 part of OP-10 emulsifying agent.
Embodiment 5:
A kind of uncured waterproof gasket cement of room temperature, it includes the raw material of following mass fraction: obtain plant asphalt 22 parts after Vegetable oil lipoprotein heavy distillate；Flexible polymer pure-acrylic emulsion 15 parts；Dimethylbenzene 4 parts；0.15 part of hydroquinone polymerization inhibitor；0.1 part of OP-10 emulsifying agent.
The making of embodiment 2-5 and application, first raw material is mixed to get a kind of pasty colloid material in high-temperature stirring state, is mainly used in painting and scrapes after building surface air-dries film forming, in a kind of elastic permanent property non-drying glue layer, can be also used for the film foil material of the various material of paving, strengthen waterproof effect.
Embodiment 6:
Colloidal materials embodiment 2-5 prepared adds the dusty material (calcium phosphate powder or Pulvis Talci) that mass fraction is its half, can serve as the caulking material in various construction gap, can play good sealed waterproof effect.
It should be noted that, in this article, term " includes ", " comprising " or its any other variant are intended to comprising of nonexcludability, so that include that the process of a series of key element, method, article or equipment not only include those key elements, but also include other key elements being not expressly set out, or also include the key element intrinsic for this process, method, article or equipment.
Principle and the embodiment of the present invention are set forth by specific case used herein, and the explanation of above example is only intended to help to understand method and the core concept thereof of the present invention.The above is only the preferred embodiment of the present invention, should be understood that, finiteness due to literal expression, and objectively there is unlimited concrete structure, for those skilled in the art, under the premise without departing from the principles of the invention, it is also possible to make some improvement, retouch or change, it is also possible to above-mentioned technical characteristic is combined by rights；These improve retouching, change or combine, or the most improved design by invention and technical scheme directly apply to other occasion, are regarded as protection scope of the present invention.
Claims (8)
1. the uncured waterproof gasket cement of room temperature, it is characterised in that it includes the raw material of following mass fraction: plant asphalt 20-40 part；Flexible polymer pure-acrylic emulsion 5-20 part.
A kind of uncured waterproof gasket cement of room temperature the most according to claim 1, it is characterised in that described plant asphalt is the bitumen product obtained after Vegetable oil lipoprotein heavy distillate.
A kind of uncured waterproof gasket cement of room temperature the most according to claim 1 and 2, it is characterised in that it also includes esters or the benzene kind solvent of 3-8 part.
A kind of uncured waterproof gasket cement of room temperature the most according to claim 3, it is characterised in that described esters or benzene kind solvent solvent are lower boiling esters or benzene kind solvent.
A kind of uncured waterproof gasket cement of room temperature the most according to claim 4, it is characterised in that described esters solvent is ethyl acetate or butyl acetate.
A kind of uncured waterproof gasket cement of room temperature the most according to claim 4, it is characterised in that described benzene kind solvent is toluene or dimethylbenzene.
A kind of uncured waterproof gasket cement of room temperature the most according to claim 3, it is characterised in that it also includes the hydroquinone polymerization inhibitor of 0.1-0.3 part.
A kind of uncured waterproof gasket cement of room temperature the most according to claim 3, it is characterised in that it also includes the OP-10 emulsifying agent of 0.05-0.2 part.