CN105820691A - Thin antistatic reflective heat-insulation wall coating - Google Patents
Thin antistatic reflective heat-insulation wall coating Download PDFInfo
- Publication number
- CN105820691A CN105820691A CN201610314514.3A CN201610314514A CN105820691A CN 105820691 A CN105820691 A CN 105820691A CN 201610314514 A CN201610314514 A CN 201610314514A CN 105820691 A CN105820691 A CN 105820691A
- Authority
- CN
- China
- Prior art keywords
- parts
- synthetic resin
- coating
- reflective insulation
- emulsifying agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a thin antistatic reflective heat-insulation wall coating. The thin antistatic reflective heat-insulation wall coating is prepared from, by weight, 5-30 parts of deionized water, 0.1-0.3 part of hydroxyethyl cellulose, 2-5 parts of a conductive emulsifier, 1-40 parts of a packing, 5-30 parts of a cold pigment, 5-20 parts of reflective heat-insulation powder, 5-20 parts of a coating additive and 10-40 parts of synthetic resin emulsion. The coating is characterized in that a coating film of the coating has the function of reflection to solar heat and can further form an electrostatic channel, so that static electricity produced in the coating escapes through the channel and repels dust in the air to achieve an anti-dust-staining function, reflective substances in the coating are not shielded by the dust, the function of reflection to solar heat of the coating can be lasting, the service life of the coating is prolonged, and a real energy-saving effect is achieved.
Description
Technical field
The present invention relates to technical field of fine, particularly to a kind of antistatic reflective insulation thin matter wall covering.
Background technology
Owing to population increases and economic development, the impact producing excessive exploitation and the unreasonable development of resource provides
The series of problems of source quality, these problems the most directly threaten the existence of we and descendants.
The patent of invention of Application No. CN200910244239.2 discloses the making of a kind of flame-retardant thermal-insulating antistatic coating
Technology, it is by epoxy resin, Rutile type titanium dioxide, cenosphere, TDE, antimony oxide, aluminium hydroxide
Be prepared from Deng material, this coating be mainly used under mine rock stratum heat insulation, can slow down high-temperature rock stratum heat transmission, from
And reduce the effect of operating ambient temperature.A kind of color of this coating only white, is unfavorable for colourful decoration needs.
The most this coating is with inflammable and explosive dangerous goods.Make again the coating of carrier as membrane substance with flammable solvent, produce and skill
Will discharge a large amount of harmful gas by process, not only danger is also to environmental injury, it is impossible to meet existing environmental protection policy and safety
The new situations produced, are highly desirable to improve and improve, the coloured reflective insulation of one of Publication No. CN104264924A
Coating, by acrylic emulsion, titanium dioxide, infrared reflecting paint, Paris white, Pulvis Talci, kaolin powder, dispersant, wetting agent,
Defoamer, thickening agent, coalescents, preservative etc. are formed, and this coating, for the application in skin face, can reduce and build
Build the temperature on 10 DEG C-20 DEG C of thing surface, thus save air conditioning energy consumption, can use in hot summer and warm winter zone and the Xia Redong area such as cold, reach
To being not only incubated but also heat insulation effect, product energy-saving effect is notable, the elastic thin layer thermal insulation of Application No. 2006100963300
Coating, discloses the heat insulation silicate cavity filling that a kind of far-infrared radiation ceramic is filler modified, sunlight reflective pigments,
Four layers of coating, gross thickness is less than, equal to 0.6 millimeter in the case of, still have good elasticity, heat preservation and insulation and heat reflectivity
The technology of energy coating, both patented products, compared to having outstanding substantive distinguishing features and marked improvement for prior art.
But owing to earth environment is going from bad to worse, industrial dust and vehicle exhaust, sandstorm make in air containing harmful gas and dust
Density quickly increases, and the Clean after every phase of exterior wall is shortening.Easily by dust and exhaust emission and cover after insulating moulding coating coating
Reflection granules of pigments in coating, causes it to lose reflectance, seriously undermines the heat insulating effect of coating, necessarily to popularization
Application brings resistance.In sum, background technology has plenty of the feature of environmental protection poor, produce and use and will discharge a large amount of nuisance
Body, and some insulating mold coatings ash easy to stick stains, it is impossible to reach the design life of reflective insulation, virtually cause the energy
Waste, it is necessary to reform and raising.
Summary of the invention
It is an object of the invention to: for technical problem present in prior art, it is provided that a kind of antistatic reflective insulation
Thin matter wall covering.
The present invention is achieved by the following technical solutions:
A kind of antistatic reflective insulation thin matter wall covering, it is characterised in that: formed by following parts by weight, including: go from
Sub-water 5-30 part, hydroxyethyl cellulose 0.1-0.3 part, conduction emulsifying agent 2-5 part, filler 1-40 part, cold pigment 1-30 part, anti-
Penetrate heat-insulating powder 5-20 part, coating additive 5-20 part and synthetic resin emulsion 10-40 part.
Further, described conduction emulsifying agent is by anionic electroconductive emulsifying agent, ionic conductivity emulsifying agent, conducting polymer breast
Agent and one or more in cationic electroconductive emulsifying agent are formed.
Further, described cold pigment is by rutile, light spar, the metal-oxide of hematite structure and ferrum oxide
Red, iron oxide yellow, chrome oxide green and titanium ultramarine and other have in the pigment of reflection function one or more formed.
Further, described coating additive is industry versatile material, and the those skilled in the art of the industry both know about its usage
And consumption, do not repeat.
Further, described synthetic resin emulsion is synthesized by acrylic acid synthetic resin emulsion, silicon the third synthetic resin emulsion, phenylpropyl alcohol
Resin emulsion, fluorine the third synthetic resin emulsion, acrylic acid synthetic resin elastic emulsion, silicon the third synthetic resin elastic emulsion, phenylpropyl alcohol closes
Resin elastic emulsion, one or more in fluorine the third synthetic resin elastic emulsion and their derivant thereof are formed.
Further, described coating additive is killed agent, coalescents, pH nertralizer, froth breaking by bentonite, Ludox, mildew-resistant
Two or more in agent and thickening agent is formed.
Formula one, is formed by following parts by weight, including: deionized water 10 parts, hydroxyethyl cellulose 0.1 part, conduction
Emulsifying agent 3 parts, filler 20 parts, cold pigment 20 parts, 10 parts of reflective insulation powder, coating additive 15 parts and synthetic resin emulsion 40 parts.
Formula two, is formed by following parts by weight, including: deionized water 15 parts, hydroxyethyl cellulose 0.2 part, conduction
Emulsifying agent 3.8 parts, filler 10 parts, cold dispersible pigment color paste 18 parts, 15 parts of reflective insulation powder, coating additive 20 parts and synthetic resin emulsion
35 parts.
Formula three, is formed by following parts by weight, including: deionized water 20 parts, hydroxyethyl cellulose 0.3 part, conduction
Emulsifying agent 5 parts, filler 10 parts, cold pigment 15 parts, 15 parts of reflective insulation powder, coating additive 9 parts and synthetic resin emulsion 35 parts.
Manufacture method one: deionized water, hydroxyethyl cellulose etc. are put in dispersion cylinder successively and carries out high speed dispersion, then
Add conduction emulsifying agent, bentonite, wide spectrum antimildew disinfectant, filler, cold pigment, reflective insulation powder, carry out high speed dispersion to scraping
When plate fineness reaches more than 60, with adding Ludox after the pH=9 in nertralizer adjustment system, carry out moderate-speed mixer, the most successively
Add coalescents and the synthetic resin emulsion of neutralized dose of adjusted pH=9, then adjust color stirring all with cold dispersible pigment color paste
Even, in the case of stirring at low speed, then add defoamer froth breaking and adjust denseness with levelling agent or thickening agent, making coating property reach
To the requirement of standard GB/T/T31389-2015, coating surface resistance should reach 1 × 104-1×1011 Ω, qualified rear packaging
Warehouse-in.
Manufacture method two: by deionized water, hydroxyethyl cellulose etc. puts in dispersion cylinder successively and carries out high speed dispersion, then
Add conduction emulsifying agent, bentonite, antimildew disinfectant, filler, cold pigment, carry out high speed dispersion and reach more than 60 to Hegman fineness grind
Time, with adding Ludox, reflective insulation powder after the pH=9 in nertralizer adjustment system, carry out moderate-speed mixer, and be sequentially added into into
Film auxiliary agent and the synthetic resin emulsion of the neutralized dose of pH=9 adjusted, then adjust after color stirs low with cold dispersible pigment color paste
Add defoamer froth breaking under speed stirring state, and adjust denseness and levelability with levelling agent or thickening agent, make coating property reach
To the requirement of standard GB/T/T31389-2015, coating surface resistance reaches 1 × 104-1×1011After Ω requires, it is packaged into
Storehouse.
In sum, owing to have employed technique scheme, the invention has the beneficial effects as follows: the feature of the coating of the present invention
It is that its paint film not only has the function of heat reflection to the sun, self can also form electrostatic passage, make generation in coating
Electrostatic passes through this passage loss, repels the dust in air, reaches antidusting and resists the function being stained with ash, so that in coating
Reflective substance do not covered by dust, make coating that the reflection function of solar heat to be sustained its quality through age, extend coating service life,
Reach real energy-saving effect;And the present invention is using water-soluble emulsion as film forming matter, environmentally friendly, meet the sustainable of country
Development policies;The present invention abandon do the thinking of reflection isolation hot material with glass microballoon and with fine reflective insulation powder body conduct
Functional material, can be made into shades of colour, and spreading rate is high, low cost, can keep the reflection function of insulating moulding coating and anlistatig
Dual-use function, and length in service life, integrated cost is low, material is easy to get, it is simple to make, energy-saving effect is notable, it is easy to promote.
Detailed description of the invention
All features disclosed in this specification, or disclosed all methods or during step, except mutually exclusive
Feature and/or step beyond, all can combine by any way.
Any feature disclosed in this specification (including any accessory claim and summary), unless specifically stated otherwise, all
Can be by other equivalences or there is the alternative features of similar purpose replaced.I.e., unless specifically stated otherwise, each feature is one to be
An example in row equivalence or similar characteristics.
Specific embodiment 1, a kind of antistatic reflective insulation thin matter wall covering, following parts by weight form, including:
Deionized water 10 parts, hydroxyethyl cellulose 0.1 part, conduction emulsifying agent 3 parts, filler 20 parts, cold pigment 20 parts, reflective insulation powder
10 parts, coating additive 10 parts and synthetic resin emulsion 40 parts;
Specifically, described conduction emulsifying agent is made up of anionic conduction emulsifying agent and ionic conductivity emulsifying agent.
Specifically, described cold pigment 20 parts, it is made up of Rutile type titanium dioxide.
Specifically, described reflective insulation powder by possessing the white powder of function of heat reflection to sunlight, by Shanghai generation exhibitionization
The TK501W powder body of work is formed.
Specifically, described coating additive by bentonite 2 parts, Ludox 5 parts, antimildew disinfectant 0.2 part, coalescents 2 parts,
PH nertralizer 0.5 part, defoamer 0.3 part, levelling agent and thickening agent form in right amount.
Specifically, described synthetic resin emulsion is silicon the third synthetic resin emulsion 30 parts, 10 parts of institutes of phenylpropyl alcohol synthetic resin emulsion
Composition..
Manufacture method: deionized water, hydroxyethyl cellulose etc. are put in dispersion cylinder successively and carries out high speed dispersion, then add
Enter by anionic conduction emulsifying agent and the conduction emulsifying agent that forms of ionic conductivity emulsifying agent, bentonite and antimildew disinfectant,
Filler, cold pigment carry out high speed dispersion to Hegman fineness grind when reaching more than 60, add with after the pH=9 in nertralizer adjustment system
Ludox, reflective insulation powder, carry out moderate-speed mixer, be then sequentially added into coalescents and the silicon of neutralized dose of adjusted pH=9
Third synthetic resin emulsion, then adds defoamer froth breaking in the case of stirring at low speed and adjusts denseness with levelling agent and thickening agent,
Making coating property be up to state standards the requirement of GB/T31389-2015, coating surface resistance should reach 1 × 104-1×1011Ω
Requirement, qualified after pack warehouse-in.
Specific embodiment 2, a kind of antistatic reflective insulation thin matter wall covering, following parts by weight form, including:
Deionized water 15 parts, hydroxyethyl cellulose 0.2 part, conduction emulsifying agent 3.8 parts, filler 20
Part, cold dispersible pigment color paste 19 parts, 15 parts of reflective insulation powder, coating additive 20 parts and synthetic resin emulsion 38 parts.
Specifically, described conduction emulsifying agent is made up of ionic conductivity emulsifying agent and conducting polymer emulsifying agent.
Specifically, described cold pigment is by Rutile type titanium dioxide mill base 16 parts, iron oxide yellow mill base 2 parts and chrome oxide green
Mill base 1 part is formed.
Specifically, described synthetic resin emulsion is by acrylic acid synthetic resin elastic emulsion 30 parts and silicon the third synthetic resin emulsion
8 parts are formed.
Specifically, described reflective insulation powder is made up of Britain's Hensel Altiris550 powder body produced advanced in years.
Specifically, described coating additive is killed agent 1.5 parts, coalescents 2 by bentonite 1 part, Ludox 10.5 parts, mildew-resistant
Part, propylene glycol 2 parts, nertralizer 1 part, defoamer 1 part, thickening agent are formed in right amount.
Manufacture method: deionized water, hydroxyethyl cellulose etc. are put in dispersion cylinder successively and carries out high speed dispersion, then add
Enter the conduction emulsifying agent being made up of ionic conductivity emulsifying agent and conducting polymer emulsifying agent, bentonite and antimildew disinfectant, fill out
Material, reflective insulation powder carry out high speed dispersion to Hegman fineness grind when reaching more than 60, add after the pH=9 in nertralizer adjustment system
Enter Ludox, carry out moderate-speed mixer, be then sequentially added into the phenylpropyl alcohol synthesis tree of coalescents and neutralized dose of adjusted pH=9
Fat liquor and silicon the third synthetic resin elastic emulsion, then stir, then in the case of stirring at low speed with the toning of cold dispersible pigment color paste
Add defoamer froth breaking and by levelling agent and thickening agent adjustment denseness, make coating property be up to state standards GB/T31389-2015
Requirement, coating surface resistance should reach 1 × 104-1×1011Ω requirement, qualified after pack warehouse-in.
Specific embodiment 3, a kind of antistatic reflective insulation thin matter wall covering, following parts by weight form, including:
Deionized water 12 parts, hydroxyethyl cellulose 15 parts, conduction emulsifying agent 3 parts, filler 10 parts, cold pigment 15 parts, reflective insulation powder 15
Part, coating additive 9 parts and synthetic resin emulsion 35 parts.
Specifically, described conduction emulsifying agent is the mixture of ionic conductivity emulsifying agent and anion emulsifier.
Specifically, described cold pigment is by Rutile type titanium dioxide mill base 10 parts, iron oxide red mill base 4 parts, titanium
Ultramarine mill base 1 part is formed, and upper is formed.
Specifically, described synthetic resin emulsion, by fluorine the third synthetic resin 9 parts of liquid acrylic acid synthetic resin elastic emulsions 26 of breast
Part is formed.
Specifically, described coating additive by bentonite 1 part, Ludox 4 parts, mildew-resistant kill agent 1 part, coalescents 1.8 parts,
PH nertralizer 0.7 part, defoamer and levelling agent thickening agent are formed in right amount.
Specifically, the Altiris800 powder body that institute's reflective insulation powder is produced by Huntsman Corporation of Britain is formed.
Manufacture method: deionized water, hydroxyethyl cellulose etc. are put in dispersion cylinder successively and carries out high speed dispersion, then add
Enter to conduct electricity emulsifying agent, bentonite, antimildew disinfectant, filler, cold pigment, carry out high speed dispersion and reach more than 60 to Hegman fineness grind
Time, with adding coating additive and reflective insulation powder after the pH=9 in nertralizer adjustment system, carrying out moderate-speed mixer, and it is sequentially added into
The synthetic resin emulsion of the pH=9 of coalescents and neutralized dose of adjustment and Ludox, after stirring in the case of stirring at low speed
Add defoamer froth breaking and adjust denseness and levelability with levelling agent and thickening agent, making coating property be up to state standards GB/
T31389-2015 requirement, coating surface resistance can reach 1 × 104-1×1011After Ω, packaging warehouse-in.
It is embodied as case 4, a kind of antistatic reflective insulation thin matter wall covering, following parts by weight forms, bag
Include deionized water 18 parts, hyetellose 0.3 part, conduction emulsifying agent 3.5 parts, filler 10 parts, cold pigment 20 parts, reflective insulation powder
10 parts, coating additive 10 parts and synthetic resin emulsion 40 parts;
Specifically, described conduction emulsifying agent is made up of anionic conduction emulsifying agent and ionic conductivity emulsifying agent.
Specifically, described cold pigment is rutile-type R-258 titanium dioxide mill base 17 parts, and titanium ultramarine mill base 3 parts is formed.
Specifically, described reflective insulation powder by possessing the white powder of function of heat reflection to sunlight, such as Shanghai generation exhibitionization
The TK501W of work.
Specifically, described coating additive is by bentonite 2 parts, Ludox 5 parts, antimildew disinfectant 0.2 part.
Coalescents 2 parts, pH nertralizer 0.5 part, defoamer 0.3 part, levelling agent and thickening agent forms in right amount,
Specifically, described synthetic resin emulsion is silicon the third synthetic resin emulsion 8 parts, pure acrylic acid synthetic resin elastic emulsion 32 parts
Formed.
Manufacture method: deionized water, hydroxyethyl cellulose etc. are put in dispersion cylinder successively and carries out high speed dispersion, then add
Enter the conduction emulsifying agent 3 parts being made up of anionic conduction emulsifying agent and ionic conductivity emulsifying agent, bentonite and antimycotic antiseptic
Agent, filler, cold pigment carries out high speed dispersion to scraper plate when reaching more than 60, with in add after pH=9 in mixture adjustment system
Ludox, reflective insulation powder, carry out moderate-speed mixer, be then sequentially added into the silicon of the adjusted pH=9 of mixture in coalescents and warp
Third synthetic resin emulsion and elastic pure acrylic acid emulsion, then add defoamer froth breaking in the case of stirring at low speed and use levelling
Agent or thickening agent adjust denseness, make coating property reach the requirement of GB/T31389-2015, and coating surface resistance can should reach 1 ×
104-1×1011Ω requirement, qualified after pack warehouse-in.
Specific embodiment 5, a kind of antistatic reflective insulation thin matter wall covering, following parts by weight form, including:
Deionized water 15 parts, hydroxyethyl cellulose 0.2 part, conduction emulsifying agent 4 parts, filler 8 parts, cold dispersible pigment color paste 14 parts, reflective insulation
15 parts of powder, coating additive 18 parts and synthetic resin emulsion 32 parts.
Specifically, described conduction emulsifying agent is made up of ionic conductivity emulsifying agent and conducting polymer emulsifying agent.
Specifically, described cold pigment by Du Pont R-706 Rutile type titanium dioxide mill base 9 parts, iron oxide yellow mill base 3 parts,
Iron oxide red mill base 2 parts is formed.
Specifically, described synthetic resin emulsion is by phenylpropyl alcohol synthetic resin emulsion 6 parts and 26 parts of institutes of silicon the third synthetic resin emulsion
Composition.
Specifically, described coating additive by swollen intercalation native 1 part, Ludox 10.5 parts, antimildew disinfectant 1.5 parts, film forming help
Agent 1.6 parts, propylene glycol 1 part, nertralizer 1 part, defoamer 1 part, thickening agent form in right amount.
Manufacture method: deionized water, hydroxyethyl cellulose etc. are put in dispersion cylinder successively and disperses, be subsequently adding by
Ionic conductivity emulsifying agent and the conduction emulsifying agent of conducting polymer emulsifying agent composition, bentonite and antimildew disinfectant, filler, anti-
Penetrate heat-insulating powder and carry out high speed dispersion to Hegman fineness grind when reaching more than 60, molten with adding silicon after the pH=9 in nertralizer adjustment system
Glue, implementation moderate-speed mixer, the phenylpropyl alcohol synthetic resin being then sequentially added into coalescents and neutralized dose of adjusted pH=9 is elastic
Emulsion and silicon the third synthetic resin emulsion, then carry out toning with cold dispersible pigment color paste and stir, then add in the case of stirring at low speed
Enter defoamer froth breaking and adjust denseness with levelling agent or thickening agent, making coating property be up to state standards GB/T31389-2015's
Requirement, coating surface resistance can should reach 1 × 104-1×1011Ω requirement, qualified after pack warehouse-in.
Particular embodiments described above, has been carried out the purpose of the present invention, technical scheme and beneficial effect the most in detail
Describe in detail bright, be it should be understood that the specific embodiment that the foregoing is only the present invention, be not limited to the present invention.This
Invention expands to any new feature disclosed in this manual or any new combination, and the arbitrary new method that discloses or
The step of process or any new combination.
Claims (9)
1. an antistatic reflective insulation thin matter wall covering, it is characterised in that: formed by following parts by weight, including: go
Ionized water 5-30 part, hydroxyethyl cellulose 0.1-0.3 part, conduction emulsifying agent 2-5 part, filler 1-40 part, cold pigment 5-30 part,
Reflective insulation powder 5-20 part, coating additive 5-20 part and synthetic resin emulsion 10-40 part.
Antistatic reflective insulation the most according to claim 1 thin matter wall covering, it is characterised in that described conduction emulsifying agent
By anionic electroconductive emulsifying agent, ionic conductivity emulsifying agent, conducting polymer emulsifying agent and in cationic electroconductive emulsifying agent
Plant or more than one are formed.
The most according to claim 1, it is characterised in that described reflective insulation powder is that commercially available sunlight reflects powder body such as Shanghai generation
The TK501W of exhibition chemical industry, Altirs550 and Altirs800 etc. that Britain's Hensel steps.
Antistatic reflective insulation the most according to claim 1 thin matter wall covering, it is characterised in that described cold pigment by
Rutile type titanium dioxide, light spar, the metal-oxide of hematite structure and iron oxide red, iron oxide yellow, chrome oxide green and
Titanium ultramarine and other have in the pigment of reflective insulation function one or more formed.
Antistatic reflective insulation the most according to claim 1 thin matter wall covering, it is characterised in that described synthetic resin
Emulsion by acrylic acid synthetic resin emulsion, silicon the third synthetic resin emulsion, phenylpropyl alcohol synthetic resin emulsion, fluorine the third synthetic resin emulsion,
Acrylic acid synthetic resin elastic emulsion, silicon the third synthetic resin elastic emulsion, phenylpropyl alcohol synthetic resin elastic emulsion, fluorine the third synthetic resin
One or more in elastic emulsion and their derivant thereof are formed.
Antistatic reflective insulation the most according to claim 1 thin matter wall covering, it is characterised in that described coating additive
By bentonite 1-10 part, Ludox 0-20 part, antimildew disinfectant 0.1-5 part, coalescents 5-20 part, propylene glycol 0.1-5 part, pH
Nertralizer is appropriate, defoamer 1-3 part, levelling agent 0-5 part, two or more in thickening agent 0.1-5 part are formed.
7. according to the antistatic reflective insulation thin matter wall covering described in claim 1 and 3, it is characterised in that cold pigment is powdery
Thing or slurry.
8. according to described in claim 1 and 3, it is characterised in that described filler is industry common used material, such as calcium carbonate, Talcum
Powder, Kaolin, barium sulfate etc., its fineness is more than 300 mesh.
9. an antistatic reflective insulation thin matter wall covering, it is characterised in that the properties of the film formed by it should reach
The requirement of standard GB/T/T31389-2015, coating surface resistance should reach 1 × 104-1×1011Ω requirement.