CN105799279A - Ultraviolet-proof jean fabric with waterproof and oilproof functions - Google Patents
Ultraviolet-proof jean fabric with waterproof and oilproof functions Download PDFInfo
- Publication number
- CN105799279A CN105799279A CN201610149239.4A CN201610149239A CN105799279A CN 105799279 A CN105799279 A CN 105799279A CN 201610149239 A CN201610149239 A CN 201610149239A CN 105799279 A CN105799279 A CN 105799279A
- Authority
- CN
- China
- Prior art keywords
- layer
- ultraviolet
- jean
- thickness
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides ultraviolet-proof jean fabric with waterproof and oilproof functions.The ultraviolet-proof jean fabric comprises a jean layer, the inner surface of the jean layer is compounded with a pearl fiber layer through a bonding layer, an ultraviolet-proof layer is arranged on the outer surface of the jean fabric, an antifungal layer is arranged on the ultraviolet-proof layer, and an oilproof and water repellent layer is arranged on the antifungal layer.The oilproof and water repellent layer is prepared from, by weight, 20-25 parts of polyurethane, 25-30 parts of a three-proof finishing agent, 2-5 parts of a softening agent, 4-6 parts of an antibacterial agent, 2-5 parts of an antistatic agent, 2-4 parts of a crosslinking agent, 5-10 parts of activated carbon, 2-4 parts of a fixing agent and is 0.02-0.05 mm thick.The thickness of the pearl fiber layer is 0.05-0.15 mm, and the ultraviolet-proof layer is a nanometer titanium dioxide coating and is 0.01-0.05 mm thick.The ultraviolet-proof layer is compounded to the outer surface of the jean layer, the pearl fiber layer is compounded to the inner surface of the jean layer, and the ultraviolet-proof effect of the fabric is better than that of common ultraviolet-proof fabric by 150-180%.
Description
Technical field
The present invention relates to a kind of jean, a kind of anti-ultraviolet jean with waterproof oil resistant function.
Background technology
Fashionable denim apparel for many years is because its mode of wearing not being restricted to one pattern has catered to the aesthetic consciousness of several generations and advocates freely
Psychological need, adds it and synchronizes constantly bringing forth new ideas of fashion so that it " is shown special preference to " by people.This dress ornament is the most
Popular more than 100 years, particularly in American-European countries, deeply liked by men and women, old and young, sell well.In China from 20th century 80
Since age jeans come into vogue, owing to its feel is abundant, bright in colour, lines clear, and have good hygroscopicity and
Conformality, the feature such as comfortable and easy to wear, simple and easy, also liked by different consumption stratas, the crowd that wear is more and more, makes
Denim is rapidly developed in China.Experience development and the innovation of more than 30 year, jean no matter from color, quality,
Sight, style, or all there occurs very from aspects such as raw material selection, yarn types, fabric construction, or Final finishing processing technique
Big change.Meanwhile, along with the design of forward position fashion and mutually merging and using of advanced technologies, jean is not with
Same technique, different fashion style show its fashion and variation, define all kinds of jean and fall over each other to struggle against gorgeous multicoloured
The world.
It is well known that, jean is unsuitable for often cleaning, and otherwise can affect the attractive in appearance of fabric, but jean is most
Being made up of cotton, antifouling capacity is poor, and in real life, jean often must clean because rubbing greasy dirt, and this is just
Easily causing the aging of jean, practicality is the highest.
Summary of the invention
Goal of the invention: for the problems referred to above, it is an object of the invention to provide a kind of anti-ultraviolet cowboy with waterproof and oilproof function
Fabric.
Technical scheme: for realizing object above, a kind of anti-ultraviolet jean with waterproof oil resistant function that the present invention provides, bag
Including cowboy's layer of cloth, the inner face of described cowboy's layer of cloth is combined with pearl fiber layer mutually by adhesive layer;The outside of described cowboy's layer of cloth sets
There is ultraviolet resistant layer;Described ultraviolet resistant layer is provided with antibiotic layer;Described antibiotic layer is provided with grease proofing water repellent layer;Described grease proofing refuse
Water layer is made up of the material of following components by weight percent: polyurethane 20-25 part, three-proof finishing agent 25-30, softening agent 2-5 part, anti-
Microbial inoculum 4-6 part, antistatic agent 2-5 part, cross-linking agent 2-4 part, activated carbon 5-10 part, color fixing agent 2-4 part;Its thickness
For 0.02-0.05mm;The thickness of described pearl fiber layer is 0.05-0.15mm;Described ultraviolet resistant layer is nano titanium oxide
Dope layer, its thickness is 0.01-0.05mm.
Described adhesive layer is made up of the material of following composition by weight: polyetheramine 35-45 part, octamethylcy-clotetrasiloxane 10-15 part,
Softening agent 3-5 part, silane coupler 3-8 part, antibacterial 4-6 part, antistatic additive 1-3 part;Nano titanium oxide 2-3
Part, antioxidant 5-8 part, remainder is deionized water, and the thickness of described adhesive layer is 0.5-1mm.
Described cowboy's layer of cloth is contained within being uniformly distributed zinc oxide ceramics powder, and its particle diameter is 10-15nm.
Described pearl fiber layer thickness is 0.1-0.3mm.
Described ultraviolet resistant layer is nanometer titanium dioxide layer, and its thickness is 0.03-0.08mm.
Described antibiotic layer is chitosan layer, and its thickness is 0.02-0.08mm.
Described waterproof oil reservoir of refusing is provided with scratch-resistant layer, and the thickness of described scratch-resistant layer is 0.1-0.3mm.
Described scratch-resistant layer is aqueous polyurethane acrylate coating.
Described softening agent is stearic acid triethanolamine ester quaternary;Antibacterial is chitosan;Antioxidant is acrylic resin.
Beneficial effect: compared with prior art, the invention have the advantages that
1. preventing ultraviolet effect is good: the present invention is fine by Composite ultraviolet-proof layer outside cowboy's layer of cloth, inner face compound pearl
Dimension layer, described ultraviolet resistant layer, pearl fiber layer are provided with the anti-ultraviolet function of excellence, are conducive to improving cattle
The ability and ultraviolet resistance of young fabric, again owing to adding zinc oxide ceramics powder in cowboy's layer of cloth, strengthens further
The ability and ultraviolet resistance of jean facing material, fabric preventing ultraviolet effect is higher than common ultraviolet-resistant fabric
150%-180%;
2. grease-proof and waterproof is effective: the present invention, by composite oil-proof water repellent layer in ultraviolet resistant layer, can realize the waterproof of fabric
Oil-resistant function, is effectively improved fabric practicality;
3. aging resistance: the present invention, by scratch-resistant layer compound on grease proofing water repellent layer, makes fabric possess preferable scratch-resistant layer ability, is prevented effectively from
Fabric is corroded by external environment, and increase the service life 35%-45%.
Accompanying drawing explanation
Fig. 1 is present configuration schematic diagram;
Wherein: 1. cowboy's layer of cloth, 2. adhesive layer, 3. pearl fiber layer, 4. ultraviolet resistant layer, 5. antibiotic layer, the most grease proofing water repellent
Layer, 7. scratch-resistant layer.
Detailed description of the invention
Below in conjunction with the accompanying drawings and specific embodiment, it is further elucidated with the present invention, it should be understood that these embodiments are merely to illustrate the present invention
Rather than restriction the scope of the present invention, after having read the present invention, those skilled in the art's shape various of equal value to the present invention
The amendment of formula all falls within the application claims limited range.
Embodiment 1
A kind of anti-ultraviolet jean with waterproof oil resistant function as shown in Figure 1, including cowboy's layer of cloth 1, described denim
The inner face of layer 1 is combined with pearl fiber layer 3 phase by adhesive layer 2;The outside of described cowboy's layer of cloth is provided with ultraviolet resistant layer 4;
Described ultraviolet resistant layer 4 is provided with antibiotic layer 5;Described antibiotic layer 5 is provided with grease proofing water repellent layer 6;Described grease proofing water repellent layer 6 by
The material composition of following components by weight percent: polyurethane 20 parts, three-proof finishing agent 25, softening agent 2 parts, antibacterial 4 parts, anti-
Electrostatic agent 2 parts, cross-linking agent 2 parts, activated carbon 5 parts, 2 parts of color fixing agent;Its thickness is 0.02mm;Described softening agent
For stearic acid triethanolamine ester quaternary;Antibacterial is chitosan;Antioxidant is acrylic resin.
The thickness of described pearl fiber layer 3 is 0.05mm;
Described ultraviolet resistant layer 4 is nanometer titania coating layer, and its thickness is 0.01mm.
Described adhesive layer 2 is made up of the material of following composition by weight: polyetheramine 35 parts, octamethylcy-clotetrasiloxane 10 parts, softness
Agent 3 parts, silane coupler 3 parts, antibacterial 4 parts, 1 part of antistatic additive;Nano titanium oxide 2 parts, remainder is
Deionized water, the thickness of described adhesive layer 2 is 0.5mm.
Described cowboy's layer of cloth 1 is contained within being uniformly distributed zinc oxide ceramics powder, and its particle diameter is 10nm.
Described pearl fiber layer 3 thickness is 0.1mm.
Described ultraviolet resistant layer 4 is nanometer titanium dioxide layer, and its thickness is 0.03mm.
Described antibiotic layer 5 is chitosan layer, and its thickness is 0.02mm.
Described waterproof oil reservoir 6 of refusing is provided with scratch-resistant layer 7, and the thickness of described scratch-resistant layer 7 is 0.1mm.
Described scratch-resistant layer 7 is aqueous polyurethane acrylate coating.
Embodiment 2
A kind of anti-ultraviolet jean with waterproof oil resistant function as shown in Figure 1, including cowboy's layer of cloth 1, described denim
The inner face of layer 1 is combined with pearl fiber layer 3 phase by adhesive layer 2;The outside of described cowboy's layer of cloth is provided with ultraviolet resistant layer 4;
Described ultraviolet resistant layer 4 is provided with antibiotic layer 5;Described antibiotic layer 5 is provided with grease proofing water repellent layer 6;Described grease proofing water repellent layer 6 by
The material composition of following components by weight percent: polyurethane 23 parts, three-proof finishing agent 28, softening agent 3 parts, antibacterial 5 parts, anti-
Electrostatic agent 3 parts, cross-linking agent 3 parts, activated carbon 7 parts, 3 parts of color fixing agent;Its thickness is 0.03mm;Described softening agent
For stearic acid triethanolamine ester quaternary;Antibacterial is chitosan;Antioxidant is acrylic resin.
The thickness of described pearl fiber layer 3 is 0.08mm;
Described ultraviolet resistant layer 4 is nanometer titania coating layer, and its thickness is 0.03mm.
Described adhesive layer 2 is made up of the material of following composition by weight: polyetheramine 45 parts, octamethylcy-clotetrasiloxane 13 parts, softness
Agent 4 parts, silane coupler 6 parts, antibacterial 5 parts, 2 parts of antistatic additive;Nano titanium oxide 2 parts, remainder
For deionized water, the thickness of described adhesive layer 2 is 0.8mm.
Described cowboy's layer of cloth 1 is contained within being uniformly distributed zinc oxide ceramics powder, and its particle diameter is 13nm.
Described pearl fiber layer 3 thickness is 0.2mm.
Described ultraviolet resistant layer 4 is nanometer titanium dioxide layer, and its thickness is 0.05mm.
Described antibiotic layer 5 is chitosan layer, and its thickness is 0.05mm.
Described waterproof oil reservoir 6 of refusing is provided with scratch-resistant layer 7, and the thickness of described scratch-resistant layer 7 is 0.2mm.
Described scratch-resistant layer 7 is aqueous polyurethane acrylate coating.
Embodiment 3
A kind of anti-ultraviolet jean with waterproof oil resistant function as shown in Figure 1, including cowboy's layer of cloth 1, described denim
The inner face of layer 1 is combined with pearl fiber layer 3 phase by adhesive layer 2;The outside of described cowboy's layer of cloth is provided with ultraviolet resistant layer 4;
Described ultraviolet resistant layer 4 is provided with antibiotic layer 5;Described antibiotic layer 5 is provided with grease proofing water repellent layer 6;Described grease proofing water repellent layer 6 by
The material composition of following components by weight percent: polyurethane 25 parts, three-proof finishing agent 30, softening agent 5 parts, antibacterial 6 parts, anti-
Electrostatic agent 5 parts, cross-linking agent 4 parts, activated carbon 10 parts, 4 parts of color fixing agent;Its thickness is 0.05mm;Described softening agent is
Stearic acid triethanolamine ester quaternary;Antibacterial is chitosan;Antioxidant is acrylic resin.
The thickness of described pearl fiber layer 3 is 0.05-0.15mm;
Described ultraviolet resistant layer 4 is nanometer titania coating layer, and its thickness is 0.05mm.
Described adhesive layer 2 is made up of the material of following composition by weight: polyetheramine 45 parts, octamethylcy-clotetrasiloxane 15 parts, softness
Agent 5 parts, silane coupler 8 parts, antibacterial 6 parts, 3 parts of antistatic additive;Nano titanium oxide 3 parts, remainder
For deionized water, the thickness of described adhesive layer 2 is 1mm.
Described cowboy's layer of cloth 1 is contained within being uniformly distributed zinc oxide ceramics powder, and its particle diameter is 15nm.
Described pearl fiber layer 3 thickness is 0.3mm.
Described ultraviolet resistant layer 4 is nanometer titanium dioxide layer, and its thickness is 0.08mm.
Described antibiotic layer 5 is chitosan layer, and its thickness is 0.08mm.
Described waterproof oil reservoir 6 of refusing is provided with scratch-resistant layer 7, and the thickness of described scratch-resistant layer 7 is 0.3mm.
Described scratch-resistant layer 7 is aqueous polyurethane acrylate coating.
Claims (9)
1. there is an anti-ultraviolet jean for waterproof oil resistant function, including cowboy's layer of cloth (1), it is characterised in that: the inner face of described cowboy's layer of cloth (1) is combined with pearl fiber layer (3) mutually by adhesive layer (2);
The outside of described cowboy's layer of cloth is provided with ultraviolet resistant layer (4);
Described ultraviolet resistant layer (4) is provided with antibiotic layer (5);
Described antibiotic layer (5) is provided with grease proofing water repellent layer (6);
Described grease proofing water repellent layer (6) is made up of the material of following components by weight percent: polyurethane 20-25 part, three-proof finishing agent 25-30, softening agent 2-5 part, antibacterial 4-6 part, antistatic agent 2-5 part, cross-linking agent 2-4 part, activated carbon 5-10 part, color fixing agent 2-4 part;Its thickness is 0.02-0.05mm;
The thickness of described pearl fiber layer (3) is 0.05-0.15mm;
Described ultraviolet resistant layer (4) is nanometer titania coating layer, and its thickness is 0.01-0.05mm.
The anti-ultraviolet jean with waterproof oil resistant function the most according to claim 1, it is characterised in that: described adhesive layer (2) is made up of the material of following composition by weight: polyetheramine 35-45 part, octamethylcy-clotetrasiloxane 10-15 part, softening agent 3-5 part, silane coupler 3-8 part, antibacterial 4-6 part, antistatic additive 1-3 part;Nano titanium oxide 2-3 part, remainder is deionized water, and the thickness of described adhesive layer (2) is 0.5-1mm.
The anti-ultraviolet jean with waterproof oil resistant function the most according to claim 1, it is characterised in that: described cowboy's layer of cloth (1) is contained within being uniformly distributed zinc oxide ceramics powder, and its particle diameter is 10-15nm.
The anti-ultraviolet jean with waterproof oil resistant function the most according to claim 1, it is characterised in that: described pearl fiber layer (3) thickness is 0.1-0.3mm.
The anti-ultraviolet jean with waterproof oil resistant function the most according to claim 1, it is characterised in that: described ultraviolet resistant layer (4) is nanometer titanium dioxide layer, and its thickness is 0.03-0.08mm.
The anti-ultraviolet jean with waterproof oil resistant function the most according to claim 1, it is characterised in that: described antibiotic layer (5) is chitosan layer, and its thickness is 0.02-0.08mm.
The anti-ultraviolet jean with waterproof oil resistant function the most according to claim 1, it is characterised in that: described waterproof oil reservoir (6) of refusing is provided with scratch-resistant layer (7), and the thickness of described scratch-resistant layer (7) is 0.1-0.3mm.
The anti-ultraviolet jean with waterproof oil resistant function the most according to claim 7, it is characterised in that: described scratch-resistant layer (7) is aqueous polyurethane acrylate coating.
The anti-ultraviolet jean with waterproof oil resistant function the most according to claim 1, it is characterised in that: described softening agent is stearic acid triethanolamine ester quaternary;Antibacterial is chitosan;Antioxidant is acrylic resin.