CN105777177A - Method for preparing aluminum oxide and chrome oxide hybrid aerogel composite - Google Patents
Method for preparing aluminum oxide and chrome oxide hybrid aerogel composite Download PDFInfo
- Publication number
- CN105777177A CN105777177A CN201610066891.XA CN201610066891A CN105777177A CN 105777177 A CN105777177 A CN 105777177A CN 201610066891 A CN201610066891 A CN 201610066891A CN 105777177 A CN105777177 A CN 105777177A
- Authority
- CN
- China
- Prior art keywords
- aluminium oxide
- chromium oxide
- aerogel composite
- preparation
- hybrid aerogel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a method for preparing an aluminum oxide and chrome oxide hybrid aerogel composite.The method includes the steps that prepared hybrid sol is permeated into a processed inorganic fiber material, after sol coagulation and fully aging are conducted, supercritical drying is conducted, and the hybrid aerogel composite is obtained.The method is simple in preparation process and easy to operate, and aluminum oxide and chrome oxide hybrid aerogel which is excellent in performance is prepared for the first time; the aluminum oxide and chrome oxide hybrid aerogel prepared through the method is high in specific surface area, low in density and high in porosity, and the excellent performance includes that the specific surface area is 350-450 m<2>/g, the density is 0.13-0.20 g/m<3>, and the porosity is 80-90%.The heat conductivity of the aerogel composite below 1000 DEG C is smaller than 0.035 w/m.k, and the percentage of contraction is smaller than 3.4%; by means of the method, development and application of an aluminum oxide material are broadened.
Description
Technical field
The preparation method that the present invention relates to a kind of aeroge, specifically, relates to a kind of aluminium oxide and the preparation method of chromium oxide aerogel composite.
Background technology
Aeroge refers to that the nanoporous network mutually assembling composition with nano-particle is skeleton, and is full of the lightweight nano solid material of gaseous state disperse medium in network skeleton hole.Aeroge is as a kind of nano material, except the characteristic with nano material, also there are other excellent properties, as: high porosity, high-specific surface area, extremely low density, low thermal conductivity and low sound transmission speed etc., in catalysis, space flight, medicine, the energy, building and metallurgy etc., there is huge application prospect.
Meanwhile, aeroge kind have also been obtained extreme enrichment, and such as metal aerogel, organic aerogel and carbon aerogels, so far increasing Novel air gel is progressively developed.
Aluminium oxide can be widely used for making chemical catalyst, medical industry, PET resin, electronic device etc.;Such as, salic glass has higher refractive index and dispersion, can as pantoscope and microscope camera lens.In order to expand the development of aeroge further, the present invention will set forth have the aluminium oxide of unique texture and performance and the preparation method of chromium oxide hybrid aerogel composite first, can better promote development and the application of such material, widen the kind of aeroge simultaneously, promote the development of aeroge science and technology.
Summary of the invention
The preparation method that it is an object of the invention to provide the little aluminium oxide of a kind of high-specific surface area, low-density, high porosity, low heat conduction and shrinkage factor and chromium oxide hybrid aerogel composite;Technical scheme processing technology provided by the invention simply, easily operate, and prepares aluminium oxide and the chromium oxide hybrid aerogel of excellent performance first.
Realize the object of the invention technical scheme as follows:
The preparation method of a kind of aluminium oxide and chromium oxide hybrid aerogel composite, described composite includes aluminium oxide and chromium oxide hybrid aerogel, inorganic fibers, and described preparation method comprises the steps:
1) process of inorganic fibers: at 150~200 DEG C, dry inorfil 4~6 hours;After inorfil is immersed the surface treatment agent solution by inorfil, distilled water, surfactant and proportions that coupling agent weight ratio is 1:2~4:0.004~0.008:0.012~0.02, dry 1~3 hour at 160~220 DEG C, cool down to obtain inorfil after surface treatment;
Wherein, described inorfil is mullite fiber, and described mullite fiber includes following component by mass percentage: Brown Alundum, 34~45%;Bauxite chamotte, 15~20%;Fused mullite, 13~27%;Electrofused mullite, 5~9%;Silicon powder, 2~6%;Coagulant, 1~15%;
2) preparation of aluminium oxide and chromium oxide hybrid collosol: by aluminum chloride, Chlorizate chromium, alcohols material, deionized water, expoxy propane and catalyst according to the proportions mixed liquor that mol ratio is 0.5~1:0.5~2:10~50:10~40:0.05~0.5:10-4~10-2, stirring 10~20min obtains aluminium oxide and chromium oxide hybrid collosol after standing;
3) infiltration: by step 2) aluminium oxide and chromium oxide hybrid collosol infiltrate through step 1) process after inorganic fibers;
4) prepare aluminium oxide and chromium oxide hybrid aerogel composite: at 50~80 DEG C, make step 3) gained infiltration thing in aluminium oxide and chromium oxide hybrid collosol generation gelling, obtain aluminium oxide and chromium oxide hybrid gel;After 20~50 DEG C of aging 20~50h, after ethanol or carbon dioxide supercritical fluid drying;Under inert gas shielding, aluminium oxide and chromium oxide hybrid aerogel composite are carried out high-temperature calcination, obtain aluminium oxide and chromium oxide hybrid aerogel composite.
Further, described step 4) in noble gas be nitrogen, helium or neon.Described step 4) in high-temperature calcination temperature be 600~1200 DEG C.
Further, described alcohols material is methanol, ethanol, propanol or butanol.Described catalyst is hydrochloric acid, sulphuric acid, phosphoric acid, formic acid, acetic acid, ethanedioic acid or Fluohydric acid..Described coupling agent is gamma-aminopropyl-triethoxy-silane, N-β-aminoethyl-γ-aminopropyltriethoxy dimethoxysilane, MTMS or vinyltrimethoxy silane.Described surfactant is dodecyl dimethyl benzyl ammonium chloride, dodecylbenzene sodium sulfonate, dimethyl dodecyl amine oxide, dodecyl-dimethyl amine second lactone or glycerin polyoxyethylene ether.
Further, the aluminium oxide that prepared by described method and chromium oxide hybrid gel specific surface area 350~450m2/ g, porosity 80~90%.Aluminium oxide that described method is prepared and chromium oxide hybrid aerogel composite thermal conductivity at 1000 DEG C are less than 0.035w/m k, and shrinkage factor is less than 3.4%.
With immediate prior art ratio, technical scheme provided by the invention has following excellent effect:
1, technical scheme preparation technology provided by the invention is simply, easily operate, and is suitable for large-scale production, and prepares aluminium oxide and the chromium oxide hybrid aerogel of excellent performance first.
2, technical scheme provided by the invention prepares high-specific surface area, low-density, the aluminium oxide of high porosity and chromium oxide hybrid aerogel, and its excellent properties is specific surface area 350~450m2/ more than g, density 0.13~0.20g/m3, porosity 80~90%.
3, technical scheme provided by the invention is prepared aluminium oxide and chromium oxide hybrid aerogel composite thermal conductivity at 1000 DEG C are less than 0.035w/m k, and shrinkage factor is less than 3.4%.
4, technical scheme provided by the invention, has widened development and the application of alumina material.
Detailed description of the invention
Further technical scheme is clearly and completely described below in conjunction with the embodiment of the present invention, it is clear that described embodiment is only a part of embodiment of the present invention, rather than whole embodiments.Based on the embodiment in the present invention, the every other embodiment that those of ordinary skill in the art obtain, broadly fall into the scope of protection of the invention.
Embodiment 1
1) process of inorganic fibers: at 200 DEG C, dry inorfil 6 hours;After inorfil is immersed the surface treatment agent solution by inorfil, distilled water, surfactant and proportions that coupling agent weight ratio is 1:4:0.008:0.02, dry 1 hour at 220 DEG C, cool down to obtain inorfil after surface treatment;
Wherein, inorfil is mullite fiber;
2) preparation of aluminium oxide and chromium oxide hybrid collosol: be 1:0.5:10:10:0.05:10 according to mol ratio by aluminum chloride, Chlorizate chromium, alcohols material, deionized water, expoxy propane and catalyst-4Proportions mixed liquor, stirring 20min stand after, obtain aluminium oxide and chromium oxide hybrid collosol;
3) infiltration: by step 2) aluminium oxide and chromium oxide hybrid collosol infiltrate through step 1) process after inorganic fibers;
4) prepare aluminium oxide and chromium oxide hybrid aerogel composite: at 80 DEG C, make step 3) gained infiltration thing in aluminium oxide and chromium oxide hybrid collosol generation gelling, obtain aluminium oxide and chromium oxide hybrid gel;After 50 DEG C of aging 20h, after supercritical drying;Under inert nitrogen gas is protected, aluminium oxide and chromium oxide hybrid aerogel composite are carried out 600 DEG C of high-temperature calcinations, obtains aluminium oxide and chromium oxide hybrid aerogel composite.
Embodiment 2
1) process of inorganic fibers: at 150 DEG C, dry inorfil 6 hours;After inorfil is immersed the surface treatment agent solution by inorfil, distilled water, surfactant and proportions that coupling agent weight ratio is 1:2:0.004:0.012, dry 3 hours at 160 DEG C, cool down to obtain inorfil after surface treatment;
Wherein, inorfil is mullite fiber;
2) preparation of aluminium oxide and chromium oxide hybrid collosol: be 0.5:2:50:40:0.5:10 according to mol ratio by aluminum chloride, Chlorizate chromium, alcohols material, deionized water, expoxy propane and catalyst-2Proportions mixed liquor, stirring 15min stand after, obtain aluminium oxide and chromium oxide hybrid collosol;
3) infiltration: by step 2) aluminium oxide and chromium oxide hybrid collosol infiltrate through step 1) process after inorganic fibers;
4) prepare aluminium oxide and chromium oxide hybrid aerogel composite: at 50 DEG C, make step 3) gained infiltration thing in aluminium oxide and chromium oxide hybrid collosol generation gelling, obtain aluminium oxide and chromium oxide hybrid gel;After 20 DEG C of aging 50h, after ethanol or carbon dioxide supercritical fluid drying;Under noble gas neon is protected, aluminium oxide and chromium oxide hybrid aerogel composite are carried out 1200 DEG C of high-temperature calcinations, obtains aluminium oxide and chromium oxide hybrid aerogel composite.
Embodiment 3
1) process of inorganic fibers: at 180 DEG C, dry inorfil 5 hours;After inorfil is immersed the surface treatment agent solution by inorfil, distilled water, surfactant and proportions that coupling agent weight ratio is 1:3:0.006:0.016, dry 2 hours at 200 DEG C, cool down to obtain inorfil after surface treatment;
Wherein, inorfil is mullite fiber;
2) preparation of aluminium oxide and chromium oxide hybrid collosol: be 1::30:20:0.1:10 according to mol ratio by aluminum chloride, Chlorizate chromium, alcohols material, deionized water, expoxy propane and catalyst-3Proportions mixed liquor, stirring 20min stand after, obtain aluminium oxide and chromium oxide hybrid collosol;
3) infiltration: by step 2) aluminium oxide and chromium oxide hybrid collosol infiltrate through step 1) process after inorganic fibers;
4) prepare aluminium oxide and chromium oxide hybrid aerogel composite: at 70 DEG C, make step 3) gained infiltration thing in aluminium oxide and chromium oxide hybrid collosol generation gelling, obtain aluminium oxide and chromium oxide hybrid gel;After 40 DEG C of aging 35h, after ethanol or carbon dioxide supercritical fluid drying;Under inert gas helium is protected, aluminium oxide and chromium oxide hybrid aerogel composite are carried out 800 DEG C of high-temperature calcinations, obtains aluminium oxide and chromium oxide hybrid aerogel composite.
Embodiment 4
1) process of inorganic fibers: at 180 DEG C, dry inorfil 4 hours;After inorfil is immersed the surface treatment agent solution by inorfil, distilled water, surfactant and proportions that coupling agent weight ratio is 1:3:0.007:0.014, dry 3 hours at 180 DEG C, cool down to obtain inorfil after surface treatment;
Wherein, inorfil is mullite fiber;
2) preparation of aluminium oxide and chromium oxide hybrid collosol: be 0.5:1:40:30:0.2:10 according to mol ratio by aluminum chloride, Chlorizate chromium, alcohols material, deionized water, expoxy propane and catalyst-4Proportions mixed liquor, stirring 15min stand after, obtain aluminium oxide and chromium oxide hybrid collosol;
3) infiltration: by step 2) aluminium oxide and chromium oxide hybrid collosol infiltrate through step 1) process after inorganic fibers;
4) prepare aluminium oxide and chromium oxide hybrid aerogel composite: at 65 DEG C, make step 3) gained infiltration thing in aluminium oxide and chromium oxide hybrid collosol generation gelling, obtain aluminium oxide and chromium oxide hybrid gel;After 45 DEG C of aging 30h, after ethanol or carbon dioxide supercritical fluid drying;Under inert nitrogen gas is protected, aluminium oxide and chromium oxide hybrid aerogel composite are carried out 900 DEG C of high-temperature calcinations, obtains aluminium oxide and chromium oxide hybrid aerogel composite.
Embodiment 5
1) process of inorganic fibers: at 175 DEG C, dry inorfil 4 hours;After inorfil is immersed the surface treatment agent solution by inorfil, distilled water, surfactant and proportions that coupling agent weight ratio is 1:4:0.007:0.018, dry 2 hours at 220 DEG C, cool down to obtain inorfil after surface treatment;
Wherein, inorfil is mullite fiber;
2) preparation of aluminium oxide and chromium oxide hybrid collosol: be 1:2:35:25:0.4:10 according to mol ratio by aluminum chloride, Chlorizate chromium, alcohols material, deionized water, expoxy propane and catalyst-2Proportions mixed liquor, stirring 18min stand after, obtain aluminium oxide and chromium oxide hybrid collosol;
3) infiltration: by step 2) aluminium oxide and chromium oxide hybrid collosol infiltrate through step 1) process after inorganic fibers;
4) prepare aluminium oxide and chromium oxide hybrid aerogel composite: at 75 DEG C, make step 3) gained infiltration thing in aluminium oxide and chromium oxide hybrid collosol generation gelling, obtain aluminium oxide and chromium oxide hybrid gel;After 40 DEG C of aging 45h, after ethanol or carbon dioxide supercritical fluid drying;Under noble gas neon is protected, aluminium oxide and chromium oxide hybrid aerogel composite are carried out 1000 DEG C of high-temperature calcinations, obtains aluminium oxide and chromium oxide hybrid aerogel composite.
Embodiment 6
1) process of inorganic fibers: at 200 DEG C, dry inorfil 5 hours;After inorfil is immersed the surface treatment agent solution by inorfil, distilled water, surfactant and proportions that coupling agent weight ratio is 1:3:0.006:0.016, dry 3 hours at 200 DEG C, cool down to obtain inorfil after surface treatment;
Wherein, inorfil is mullite fiber;
2) preparation of aluminium oxide and chromium oxide hybrid collosol: be 1:2:35:40:0.5:10 according to mol ratio by aluminum chloride, Chlorizate chromium, alcohols material, deionized water, expoxy propane and catalyst-3Proportions mixed liquor, stirring 14min stand after, obtain aluminium oxide and chromium oxide hybrid collosol;
3) infiltration: by step 2) aluminium oxide and chromium oxide hybrid collosol infiltrate through step 1) process after inorganic fibers;
4) prepare aluminium oxide and chromium oxide hybrid aerogel composite: at 65 DEG C, make step 3) gained infiltration thing in aluminium oxide and chromium oxide hybrid collosol generation gelling, obtain aluminium oxide and chromium oxide hybrid gel;After 25 DEG C of aging 35h, after ethanol or carbon dioxide supercritical fluid drying;Under inert gas helium is protected, aluminium oxide and chromium oxide hybrid aerogel composite are carried out 1100 DEG C of high-temperature calcinations, obtains aluminium oxide and chromium oxide hybrid aerogel composite.
The raw materials used kind of the various embodiments described above and ratio thereof, as shown in table 1.
Table 1
In embodiment, gained properties of sample is listed in the table below 2.
Table 2
Above example is only in order to illustrate that technical scheme is not intended to limit; those of ordinary skill in the field are to be understood that; the specific embodiment of the present invention can being modified with reference to above-described embodiment or equivalent replacement, these are all being applied within the claims awaited the reply without departing from any amendment or equivalent replacement of spirit and scope of the invention.
Claims (9)
1. the preparation method of an aluminium oxide and chromium oxide hybrid aerogel composite, it is characterised in that described composite includes aluminium oxide and chromium oxide hybrid aerogel, inorganic fibers, and described preparation method comprises the steps:
1) process of inorganic fibers: at 150~200 DEG C, dry inorfil 4~6 hours;Inorfil is immersed after processing by weight the surface treatment agent solution for the preparation of the inorfil of ratio of 1:2~4:0.004~0.008:0.012~0.02, distilled water, surfactant and coupling agent, dry 1~3 hour at 160~220 DEG C, cooling;
Wherein, described inorfil is mullite fiber, and described mullite fiber includes following component by mass percentage: Brown Alundum, 34~45%;Bauxite chamotte, 15~20%;Fused mullite, 13~27%;Electrofused mullite, 5~9%;Silicon powder, 2~6%;Coagulant, 1~15%;
2) preparation of aluminium oxide and chromium oxide hybrid collosol: be 0.5~1:0.5~2:10~50:10~40:0.05~0.5:10 according to mol ratio by aluminum chloride, Chlorizate chromium, alcohols material, deionized water, expoxy propane and catalyst-4~10-2Proportions mixed liquor, stirring 10~20min stand after, obtain aluminium oxide and chromium oxide hybrid collosol;
3) infiltration: by step 2) aluminium oxide and chromium oxide hybrid collosol infiltrate through step 1) process after inorganic fibers;
4) prepare aluminium oxide and chromium oxide hybrid aerogel composite: at 50~80 DEG C, make step 3) gained infiltration thing in aluminium oxide and chromium oxide hybrid collosol generation gelling, obtain aluminium oxide and chromium oxide hybrid gel;At 20~50 DEG C after aging 20~50h, after ethanol or carbon dioxide supercritical fluid drying;Under inert gas shielding, aluminium oxide and chromium oxide hybrid aerogel composite are carried out high-temperature calcination, obtain aluminium oxide and chromium oxide hybrid aerogel composite.
2. the preparation method of a kind of aluminium oxide as claimed in claim 1 and chromium oxide hybrid aerogel composite, it is characterised in that described step 4) in noble gas be nitrogen, helium or neon.
3. the preparation method of a kind of aluminium oxide as claimed in claim 1 and chromium oxide hybrid aerogel composite, it is characterised in that described step 4) in high-temperature calcination temperature be 600~1200 DEG C.
4. the preparation method of a kind of aluminium oxide as claimed in claim 1 and chromium oxide hybrid aerogel composite, it is characterised in that described alcohols material is methanol, ethanol, propanol or butanol.
5. the preparation method of a kind of aluminium oxide as claimed in claim 1 and chromium oxide hybrid aerogel composite, it is characterised in that described catalyst is hydrochloric acid, sulphuric acid, phosphoric acid, formic acid, acetic acid, ethanedioic acid or Fluohydric acid..
6. the preparation method of a kind of aluminium oxide as claimed in claim 1 and chromium oxide hybrid aerogel composite, it is characterized in that, described coupling agent is gamma-aminopropyl-triethoxy-silane, N-β-aminoethyl-γ-aminopropyltriethoxy dimethoxysilane, MTMS or vinyltrimethoxy silane.
7. the preparation method of a kind of aluminium oxide as claimed in claim 1 and chromium oxide hybrid aerogel composite, it is characterized in that, described surfactant is dodecyl dimethyl benzyl ammonium chloride, dodecylbenzene sodium sulfonate, dimethyl dodecyl amine oxide, dodecyl-dimethyl amine second lactone or glycerin polyoxyethylene ether.
8. such as the preparation method of the claim 1~7 aluminium oxide as described in any one and chromium oxide hybrid aerogel composite, it is characterised in that aluminium oxide prepared by described method and chromium oxide hybrid gel specific surface area 350~450m2/ g, porosity 80~90%.
9. such as the preparation method of the claim 1~7 aluminium oxide as described in any one and chromium oxide hybrid aerogel composite, it is characterized in that, aluminium oxide that described method is prepared and chromium oxide hybrid aerogel composite thermal conductivity at 1000 DEG C are less than 0.035w/m k, and shrinkage factor is less than 3.4%.