CN105771091A - 一种负离子贴组合物 - Google Patents
一种负离子贴组合物 Download PDFInfo
- Publication number
- CN105771091A CN105771091A CN201610268569.5A CN201610268569A CN105771091A CN 105771091 A CN105771091 A CN 105771091A CN 201610268569 A CN201610268569 A CN 201610268569A CN 105771091 A CN105771091 A CN 105771091A
- Authority
- CN
- China
- Prior art keywords
- anion
- light shale
- patch
- parts
- powder body
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种负离子贴组合物,该组合物由10~50份的轻质页岩粉体、60~80份的胶体和5~20份的粘合剂制成,其中,所述轻质页岩粉体由轻质页岩矿进行破碎、清洗、磨细和筛分制得,所述胶体包括田菁胶、瓜尔胶、胡麻胶、香豆角和石花胶,所述胶体还包括羟甲基纤维素、聚乙烯醇、甲基纤维素、羟乙基纤维素,所述粘合剂选自胶原蛋白、蜂蜜、淀粉、聚环氧乙烷和聚丙烯酸钠中的一种或几种。所述组合物以及由该组合物制成的负离子贴能够释放负离子,发射生物波和远红外,达到预防和治疗感冒的用途,并且所述负离子贴组合物的制备方法简单,易于大规模生产应用。
Description
技术领域
本发明涉及膏药领域,尤其涉及一种负离子贴组合物,特别地,涉及一种用于治疗感冒的负离子贴组合物。
背景技术
在一般疾病中,感冒的发病率较高,成人每年发生2~4次,儿童每年6~8次,全年皆可发病,冬春季较多。一般治疗感冒的方式是输液、***或吃药,但是上三种方式治疗不方便、治疗时间长,尤其对于儿童而言,不宜实施。内病外治是我国中医治疗疾病的基本理论之一,而外治的主要方法通常是采用膏药敷贴的方式,这样,直接将膏药贴于肚脐或其它位置即可,不会出现***疼痛或吃药难的情况,并且,膏药敷贴的方式实施方便。
中国专利CN00120658公开了一种感冒贴膏,其中,以三节剑、固不婆律、薄荷、芝麻油、木焦脂和松香为原料,经熬制、搅拌制得。
中国专利CN201510813908公开了一种风热感冒贴,其中,将黄柏、苦参、龙胆草和白英粉碎成细粉,添加苯磺酸钠,并与练蜜混合均匀,固定于胶粘材料上,再贴上表面封纸,得到风热感冒贴。
上述两篇专利采用外治的方式治疗感冒,治疗方法简单、易于实施,但是,其均采用药物为原材料,俗话说,是药三分毒,其对人体或多或少都会造成伤害。因此,亟需一种不以药物为原材料的用于治疗感冒的外敷膏药。
发明内容
为了解决上述问题,本发明人进行了锐意研究,结果发现:由轻质页岩粉体、天然植物胶和粘合剂制成的负离子贴组合物能够有效预防并治疗感冒,其中,所述负离子贴组合物能够释放负离子,抑制细菌病毒的滋生,并达到杀菌的目的,这样,感冒病毒入侵人体后的滋生环境就受到极大的限制,并且,所用原料不属于药物,无毒,不会对人体造成伤害,从而完成本发明。
本发明的目的之一在于提供一种负离子贴组合物,具体体现在以下几方面:
(1)一种负离子贴组合物,其中,所述负离子贴组合物由包括以下重量配比的原料制成:
轻质页岩粉体10~50份,
胶体60~80份,
粘合剂5~20份;
(2)根据上述(1)所述的负离子贴组合物,其中,所述负离子贴组合物由包括以下重量配比的原料制成:
轻质页岩粉体20~40份,
胶体65~75份,
粘合剂10~15份;
优选地:
轻质页岩粉体30份,
胶体70份,
粘合剂12份;
(3)根据上述(1)或(2)所述的负离子贴组合物,其中,
所述轻质页岩粉体由轻质页岩矿经破碎、清洗、磨细和筛分制得,和/或
所述轻质页岩粉体的粒径为150目~20nm,优选为1000目~200nm,更优选为2000目~500nm;
(4)根据上述(1)至(3)之一所述的负离子贴组合物,其中,所述轻质页岩矿的内部具有毛孔状微孔间隙,所述微孔的孔径为5~20nm;
(5)根据上述(1)至(4)之一所述的负离子贴组合物,所述胶体包括田菁胶、瓜尔胶、胡麻胶、香豆角和石花胶,优选包括田菁胶、瓜尔胶和石花胶;
所述胶体还包括羟甲基纤维素、聚乙烯醇、甲基纤维素、羟乙基纤维素,优选包括羟甲基纤维素和聚乙烯醇;
(6)根据上述(1)至(5)之一所述的负离子贴组合物,其中,所述粘合剂选自胶原蛋白、蜂蜜、淀粉、聚环氧乙烷和聚丙烯酸钠中的一种或几种,优选选自胶原蛋白、蜂蜜和聚环氧乙烷中的一种或几种,更优选选自蜂蜜;
(7)根据上述(1)至(6)之一所述的负离子贴组合物,其中,所述负离子贴组合物由包含以下步骤的方法制得:
步骤1、将轻质页岩矿进行破碎、清洗、磨细和筛分,得轻质页岩粉体;
步骤2、将轻质页岩粉体、胶体、粘合剂和水混合,得混合料;
步骤3、将混合料进行加热并搅拌,然后冷却,得负离子贴组合物;
(8)根据上述(1)至(7)之一所述的负离子贴组合物,其中,
在步骤2中,基于轻质页岩粉体、胶体和粘合剂的重量和,水的用量为5~30wt%,优选为10~20wt%,更优选为15wt%;和/或
在步骤3中,所述加热于30~90℃下进行,优选于50~70℃下进行,更优选于60℃下进行;和/或
在步骤3中,所述搅拌进行10~60min,优选20~40min,更优选30min;
(9)根据上述(1)至(8)之一所述的负离子贴组合物,其中,在步骤3之后进行步骤4,其中,
步骤4、取适量负离子贴组合物粘附于牛皮纸或无纺布上,压片成型,得到负离子贴。
本发明的目的之二在于提供一种上述(1)至(9)之一所述的负离子贴组合物或负离子贴用于预防和治疗感冒的用途。
具体实施方式
下面通过对本发明进行详细说明,本发明的特点和优点将随着这些说明而变得更为清楚、明确。
根据本发明的一方面,提供了一种负离子贴组合物,所述负离子贴组合物由轻质页岩粉体、胶体和粘合剂制成。
根据本发明一种优选的实施方式,轻质页岩粉体的用量为10~50份。
在进一步优选的实施方式中,轻质页岩粉体的用量为20~40份。
在更进一步优选的实施方式中,轻质页岩粉体的用量为30份。
根据本发明一种优选的实施方式,所述轻质页岩粉体由轻质页岩矿进行破碎、清洗、磨细和筛分制得。
根据本发明一种优选的实施方式,所述轻质页岩矿的内部具有毛孔状微孔间隙,所述微孔的孔径为5~20nm,其内部的纳米微孔结构赋予轻质页岩矿纳米效应,其中,上述引自“刘新建,李青山.一种天然纳米材料的发现与应用研究.E纳米材料”。
在本发明中,所述轻质页岩矿选自内蒙古莫旗额尔和乡境内的蛋白页岩矿。其中,蛋白页岩矿是由火山爆发形成的火山灰在空气中灼烧成细小炽热体后经落入湖底沉积而形成。
其中,所述轻质页岩矿是一种天然纳米材料,具有页状层理、粒度细小均匀、结构输送多孔等特征,其内部含有大量孔隙,使其比表面积可达277.3cm2/g,具有很强的吸附性。上述有关轻质页岩颗粒的数据引自“刘新建,李青山.一种天然纳米材料的发现与应用研究.E纳米材料”。
在本发明中,所述轻质页岩矿能够释放负离子,发射生物波和远红外。
根据本发明一种优选的实施方式,所述轻质页岩粉体的粒径为150目~20nm,优选为1000目~200nm,更优选为2000目~500nm。
根据本发明一种优选的实施方式,所述胶体的用量为60~80份。
在进一步优选的实施方式中,所述胶体的用量为65~75份。
在更进一步优选的实施方式中,所述胶体的用量为70份。
根据本发明一种优选的实施方式,所述胶体包括田菁胶、瓜尔胶、胡麻胶、香豆角和石花胶,优选包括田菁胶、瓜尔胶和石花胶。
在进一步优选的实施方式中,所述胶体还包括羟甲基纤维素、聚乙烯醇、甲基纤维素、羟乙基纤维素,优选包括羟甲基纤维素和聚乙烯醇。
其中,本发明使用的胶体是天然的植物胶和生物相容性的胶体,无毒,适合人体敷用。
根据本发明一种优选的实施方式,所述粘合剂的用量为5~20份。
在进一步优选的实施方式中,所述粘合剂的用量为10~15份。
在更进一步优选的实施方式中,所述粘合剂的用量为12份。
根据本发明一种优选的实施方式中,所述粘合剂选自胶原蛋白、蜂蜜、淀粉、聚环氧乙烷和聚丙烯酸钠中的一种或几种。
在进一步优选的实施方式中,所述粘合剂选自胶原蛋白、蜂蜜和聚环氧乙烷中的一种或几种。
在更进一步优选的实施方式中,所述粘合剂选自蜂蜜。
其中,粘合剂的选择原则也是具有生物相容性和无毒性,同时,蜂蜜和胶原蛋白对皮肤还具有一定的滋养作用,由于成本原因,优选蜂蜜。
在发明中,所提供的负离子贴组合物中含有轻质页岩粉体,因此,所述负离子贴组合物:
(1)能够释放负离子:其一,所述负离子可以抑制细菌病毒的滋生,其中,负离子具有较高的活性,能破坏细菌的细胞膜原生质活性酶的活性,且负离子与细菌结合后可使细菌病毒产生结构的改变或能量的转换,导致细菌病毒的死亡,不再形成新的菌落,达到杀菌的目的,可以治疗感冒;其二,所述负离子可以促进人体内绒毛运动,易于排除废物,增加抵抗力及免疫力,减少疾病的感染,可以预防感冒;
其中,使用该负离子贴组合物制成的负离子贴,对于7cm×11cm的负离子贴,1~3秒可释放3万个以上的负离子(采用日本ARSINC公司AK-103型Dr.ION负离子测定仪测试得到);
(2)能够发射人体所需的6μm~14μm长的生物波,所述生物波可以活化组织细胞,使细胞再生能力提高,血清中的溶血素含量降低,吞噬细胞吞噬能力增强,因而可以增强人体的细胞免疫和体液免疫能力,进而有效预防感冒;
其中,生物波也是物质的属性之一,人体也具有生物波场,现已发现人脑、心脏、皮肤和其它器官的微电流活动都是生物波场,甚至连头发上也有生物波场。近年来由于生物学的发展,出现了生物波学的边缘学科,现已获知,生物波场对生物的生理机能都有一定的作用和影响,这种作用和影响叫做生物波场的效应;
(3)能够发射远红外,其一,远红外能够激活生物大分子的活性,使生物体的分子能级被激发而处于较高振动能级,这边激活了核酸蛋白质等生物大分子的活性,从而发挥了生物大分子调节机体代谢免疫等活动的功能,有利于人体机能的恢复和平衡,达到防病、治病的目的,例如感冒;其二,远红外能够提高巨噬细胞的吞噬功能,调节人体细胞和体液的免疫功能,可以预防感冒。
根据本发明一种优选的实施方式,所述负离子贴组合物由包含以下步骤的方法制得:
步骤1、将轻质页岩矿进行破碎、清洗、磨细和筛分,得轻质页岩粉体。
根据本发明一种优选的实施方式,破碎后得轻质页岩碎石,其粒径为10~100mm。
在进一步优选的实施方式中,所述轻质页岩碎石的粒径为20~80mm。
在更进一步优选的实施方式中,所述轻质页岩碎石的粒径为40~60mm。
根据本发明一种优选的实施方式,所述清洗采用水力洗矿筛、筒形洗矿筛、圆筒擦洗机或槽型洗矿机进行,主要是清除轻质页岩碎石表面的泥土或其它杂质。
根据本发明一种优选的实施方式,所述磨细优选为球磨,更优选为高能球磨。
根据本发明一种优选的实施方式,所述轻质页岩粉体的粒径为150目~20nm,优选为1000目~200nm,更优选为2000目~500nm。
步骤2、将轻质页岩粉体、胶体、粘合剂和水混合,得混合料。
根据本发明一种优选的实施方式,基于轻质页岩粉体、胶体和粘合剂的重量和,水的用量为5~30wt%,优选为10~20wt%,更优选为15wt%。
其中,水的用量不易太多,太多使得组合物偏稀,不能形成膏状,水的用量也不易太少,太少使得原料不能混合均匀。
步骤3、将混合料进行加热并搅拌,然后冷却,得负离子贴组合物。
根据本发明一种优选的实施方式,在步骤3中,所述加热于30~90℃下进行。
在进一步优选的实施方式中,在步骤3中,所述加热于50~70℃下进行。
在更进一步优选的实施方式中,在步骤3中,所述加热于60℃下进行。
根据本发明一种优选的实施方式,在步骤3中,所述搅拌进行10~60min。
在进一步优选的实施方式中,在步骤3中,所述搅拌进行20~40min。
在更进一步优选的实施方式中,在步骤3中,所述搅拌进行30min。
其中,加热搅拌的目的是使混合物混合均匀,由于体系中含有水,因此加热温度不易太高。
根据本发明一种优选的实施方式中,所述冷却为低温下冷却或室温下冷却。
在进一步优选的实施方式中,所述冷却为室温下冷却。
其中,所述室温为10~30℃,所述低温为5℃左右。
根据本发明一种优选的实施方式,在步骤3之后进行步骤4。
步骤4、取适量负离子贴组合物粘附于牛皮纸或无纺布上,压片成型,得到负离子贴。
根据本发明一种优选的实施方式,所述负离子贴制作成圆形。
在进一步优选的实施方式中,所述圆形负离子贴的直径为2~8cm,优选为3~7cm,更优选为5cm。
其中,上述尺寸跟形状(圆形)的负离子贴适合用于太阳穴,也可贴于别处。
根据本发明另一种优选的实施方式,所述负离子贴制作成长方形。
在进一步优选的实施方式中,所述长方形负离子贴的宽为(4~10)cm,长为(6~14)cm,例如5cm×8cm和8cm×12cm。
其中,上述尺寸跟形状(长方形)的负离子贴适合用于肚脐,也可贴于别处。
根据本发明的另一方面,提供了一种上述负离子贴组合物或负离子贴用于治疗感冒的用途,所述感冒包括风寒性感冒和风热性感冒。
本发明所具有的有益效果包括:
(1)本发明所述负离子贴组合物能够释放负离子,并远红外和生物波,可用于预防和治疗感冒;
(2)本发明所述负离子贴组合物原料简单,价格低廉,具有生物相容性且无毒;
(3)本发明所述负离子贴组合物的制备方法简单,易于大规模生产应用。
实施例
以下通过具体实例进一步描述本发明。不过这些实例仅仅是范例性的,并不对本发明的保护范围构成任何限制。
其中,所用轻质页岩矿选自内蒙古莫旗额尔和乡境内的蛋白页岩矿。
实施例1负离子贴组合物的制备
将轻质页岩矿进行破碎,于槽型洗矿机中清洗,晾干,再次磨细并过筛,得轻质页岩粉体。
将10kg轻质页岩粉体、60kg田菁胶、5kg胶原蛋白和4kg水混合,得混合料。
将混合料于30℃搅拌10min,然后于室温下冷却,得负离子贴组合物。
实施例2负离子贴组合物的制备
将轻质页岩矿进行破碎,于槽型洗矿机中清洗,晾干,再次磨细并过筛,得轻质页岩粉体。
将20kg轻质页岩粉体、65kg瓜尔胶、10kg聚环氧乙烷和9.5kg水混合,得混合料。
将混合料于50℃搅拌20min,然后于室温下冷却,得负离子贴组合物。
实施例3负离子贴组合物的制备
将轻质页岩矿进行破碎,于槽型洗矿机中清洗,晾干,再次磨细并过筛,得轻质页岩粉体。
将30kg轻质页岩粉体、70kg石花胶、12kg蜂蜜和17kg水混合,得混合料。
将混合料于60℃搅拌30min,然后于室温下冷却,得负离子贴组合物。
实施例4负离子贴组合物的制备
将轻质页岩矿进行破碎,于槽型洗矿机中清洗,晾干,再次磨细并过筛,得轻质页岩粉体。
将40kg轻质页岩粉体、75kg羟甲基纤维素、15kg蜂蜜和26kg水混合,得混合料。
将混合料于70℃搅拌40min,然后于室温下冷却,得负离子贴组合物。
实施例5负离子贴组合物的制备
将轻质页岩矿进行破碎,于槽型洗矿机中清洗,晾干,再次磨细并过筛,得轻质页岩粉体。
将50kg轻质页岩粉体、80kg聚乙烯醇、20kg蜂蜜和45kg水混合,得混合料。
将混合料于90℃搅拌60min,然后于室温下冷却,得负离子贴组合物。
实施例6负离子贴的制备
取适量实施例3制得的负离子贴组合物粘附于5cm×8cm的具有粘性的牛皮纸上,然后贴上隔粘纸,进行压片成型,得到负离子贴。
试验例
共200例感冒患者,根据其症状大概可以分为三类患者:第一类患者有67例,表现为鼻塞、流涕、打喷嚏;第二类患者有67例,表现为发烧、畏寒、头疼,食欲不振;第三类患者有66例,表现为咳嗽、咽炎。该200名患者均使用实施例6制得的负离子贴,使用时将隔粘纸撕去,直接贴于肚脐,并且三天一换,其治疗结果见表1。
表1感冒治疗效果
从表1中可以看出,患者在使用实施例6所制负离子贴5天后大部分已经康复,其中,治疗率达到95%,并且,使用后并无副作用产生。
上结合具体实施方式和范例性实例对本发明进行了详细说明,不过这些说明并不能理解为对本发明的限制。本领域技术人员理解,在不偏离本发明精神和范围的情况下,可以对本发明技术方案及其实施方式进行多种等价替换、修饰或改进,这些均落入本发明的范围内。本发明的保护范围以所附权利要求为准。
Claims (10)
1.一种负离子贴组合物,其特征在于,所述负离子贴组合物由包括以下重量配比的原料制成:
轻质页岩粉体10~50份,
胶体60~80份,
粘合剂5~20份。
2.根据权利要求1所述的负离子贴组合物,其特征在于,所述负离子贴组合物由包括以下重量配比的原料制成:
轻质页岩粉体20~40份,
胶体65~75份,
粘合剂10~15份;
优选地:
轻质页岩粉体30份,
胶体70份,
粘合剂12份。
3.根据权利要求1或2所述负离子贴组合物,其特征在于,
所述轻质页岩粉体由轻质页岩矿进行破碎、清洗、磨细和筛分制得;和/或
所述轻质页岩粉体的粒径为150目~20nm,优选为1000目~200nm,更优选为2000目~500nm。
4.根据权利要求1至3之一所述的负离子贴组合物,其特征在于,所述轻质页岩矿的内部具有毛孔状微孔间隙,所述微孔的孔径为5~20nm。
5.根据权利要求1至4之一所述的负离子贴组合物,其特征在于,所述胶体包括田菁胶、瓜尔胶、胡麻胶、香豆角和石花胶,优选包括田菁胶、瓜尔胶和石花胶;
所述胶体还包括羟甲基纤维素、聚乙烯醇、甲基纤维素、羟乙基纤维素,优选包括羟甲基纤维素和聚乙烯醇。
6.根据权利要求1至5之一所述的负离子贴组合物,其特征在于,所述粘合剂选自胶原蛋白、蜂蜜、淀粉、聚环氧乙烷和聚丙烯酸钠中的一种或几种,优选选自胶原蛋白、蜂蜜和聚环氧乙烷中的一种或几种,更优选选自蜂蜜。
7.根据权利要求1至6之一所述的负离子贴组合物,其特征在于,所述负离子贴组合物由包含以下步骤的方法制得:
步骤1、将轻质页岩矿进行破碎、清洗、磨细和筛分,得轻质页岩粉体;
步骤2、将轻质页岩粉体、胶体、粘合剂和水混合,得混合料;
步骤3、将混合料进行加热并搅拌,然后冷却,得负离子贴组合物。
8.根据权利要求1至7之一所述的负离子贴组合物,其特征在于,
在步骤2中,基于轻质页岩粉体、胶体和粘合剂的重量和,水的用量为5~30wt%,优选为10~20wt%,更优选为15wt%;和/或
在步骤3中,所述加热于30~90℃下进行,优选于50~70℃下进行,更优选于60℃下进行;和/或
在步骤3中,所述搅拌进行10~60min,优选20~40min,更优选30min。
9.根据权利要求1至8之一所述的负离子贴组合物,其特征在于,在步骤3之后进行步骤4,其中,
步骤4、取适量负离子贴组合物粘附于牛皮纸或无纺布上,压片成型,得到负离子贴。
10.根据权利要求1至9之一所述的负离子贴组合物或负离子贴用于预防和治疗感冒的用途。