CN105754263A - High-toughness antibacterial fishing net - Google Patents
High-toughness antibacterial fishing net Download PDFInfo
- Publication number
- CN105754263A CN105754263A CN201610231013.9A CN201610231013A CN105754263A CN 105754263 A CN105754263 A CN 105754263A CN 201610231013 A CN201610231013 A CN 201610231013A CN 105754263 A CN105754263 A CN 105754263A
- Authority
- CN
- China
- Prior art keywords
- fishing net
- toughness
- minutes
- antibacterial
- antibacterial fishing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a high-toughness antibacterial fishing net.The high-toughness antibacterial fishing net comprises ethylene-propylene-diene monomer rubber, polyvinylidene chloride, polyisoprene rubber, rosin, polyphthalamide, polyacrylamide, glass fibers, basalt, nanometer diatomaceous earth, bamboo powder, zinc oxide, plasticizers and auxiliaries.The high-toughness antibacterial fishing net has the advantages that technologies for processing the high-toughness antibacterial fishing net are simple, the ethylene-propylene-diene monomer rubber is pre-treated and is matched with other components in the high-toughness antibacterial fishing net, accordingly, the tensile strength of materials for the high-toughness antibacterial fishing nets can be improved by 41.5%, and the breaking elongation and the toughness can be improved; the auxiliaries and the other components are matched with one another, accordingly, the anti-aging capacity of the manufactured high-toughness antibacterial fishing net can be greatly improved, the compatibility of the various components can be enhanced, the weather fastness can be improved, the antibacterial ability of the high-toughness antibacterial fishing net can be greatly enhanced, and the production cost can be lowered; the glass fibers, the mixed and treated diatomaceous earth, the rosin, the basalt, the zinc oxide and the bamboo powder are matched with one another, accordingly, the toughness of the high-toughness antibacterial fishing net can be improved by 44.9%, the toughness and the antibacterial ability can be enhanced, and the service life of the high-toughness antibacterial fishing net can be prolonged by 29% as compared with ordinary fishing nets.
Description
Technical field
The present invention relates to fishing gear field, particularly relate to a kind of antibacterial fishing net of high tenacity.
Background technology
Fishing net is the net of fishing, and it is numb as raw material that men of old uses coarse cloth to add, makes fishnet by tying the method for volume.Although this fishing net is perishable, toughness is poor, but its fishing efficiency is greatly improved.Along with the development of fishery, the object of fishing and hunting is more than fish, and the instrument fished for also grows with each passing hour.It is numb as raw material that men of old uses coarse cloth to add, by the method tying volume
Make fishnet.Although this fishing net is perishable, toughness is poor, but its fishing efficiency is greatly improved.Along with the development of fishery, the object of fishing and hunting is more than fish, and the instrument fished for also grows with each passing hour.Modern fishing net mainly adopts polyethylene, the raw materials such as nylon are processed, there is longer life cycle, higher catching rate, but the mechanical property of polyethylene itself is general, and hot strength is relatively low, and creep resistance is bad, resulting in the tradition intensity of fishing net, anti-wear performance, poor toughness, the fishing net life-span is short.
Summary of the invention
It is an object of the invention to provide a kind of antibacterial fishing net of high tenacity, be achieved through the following technical solutions:
A kind of antibacterial fishing net of high tenacity, is made up of following component: ethylene propylene diene rubber 0.8, Vingon 126, polyisoprene rubber 0.7, Colophonium 0.5, polyphtalamide 0.7, polyacrylamide 0.8, glass fibre 0.1, basalt 0.1, nano diatomite 0.1, bamboo powder 0.1, zinc oxide 0.1, plasticizer 1, auxiliary agent 0.1 by weight；Described auxiliary agent is the mixed extract of Herba Erodii, Herba Senecionis Scandentis, Fructus Tribuli, Herba pegani harmalae, needs 15 portions of Herba Erodiis, 14 parts of Herba Senecionis Scandentiss, 14 parts of Fructus Tribulis, 12 parts of Herba pegani harmalaes by weight, and preparation method is: will pulverize after selected plant cleaning-drying；Then the plant after pulverizing is put in the solution that hydrochloric acid solution mixes with ethanol, mix homogeneously, the Chlorine in Solution hydrogen that described hydrochloric acid mixes with ethanol: water: the mass ratio of ethanol is 0.2:1.9:10；Said mixture is placed in ultrasonic extraction tank, adopts every 3 minutes of the ultrasound wave of 21.5kHZ, 28kHZ frequency to substitute circulation successively and carries out extracting operation to it, it is possible to improve extraction efficiency and extraction degree greatly, after 30 minutes extracting solution；Gained extracting solution is first adopted in ammonia and hydrochloric acid, then carry out recovered alcohol, remaining solution is carried out process of anhydrating, namely can be made into required auxiliary agent.
Further, described ethylene propylene diene rubber is through pretreatment: by weight is ethylene propylene diene rubber 1/19th calcium sulfate crystal whiskers mix at 210 DEG C with ethylene propylene diene rubber, after being incubated 15 minutes, carry out post vulcanization process.
Further, described plasticizer is epoxy tetrahydro-2-ethylhexyl phthalate and di-2-ethylhexyl maleate composite elasticizer, wherein epoxy tetrahydro-2-ethylhexyl phthalate is 2:1 with the composite quality ratio of di-2-ethylhexyl maleate, combined temp is between 79-80 DEG C, the plasticizer that thus compound goes out, plasticization effect is more preferably notable, and can also improve the toughness of fishing lines.
Further, described basalt is through 450 DEG C of calcinings, and calcination time is 30 minutes, and it is 5500-5600 order that basalt grinds to form granularity, and basalt surface processes through Silane coupling reagent KH-570.
Further, the granularity of described nano diatomite is 23-27nm, nano diatomite and Colophonium are through mixing pretreatment: by nano diatomite and Colophonium Homogeneous phase mixing to together with, mixture is added in the fumaric acid solution that mass fraction is 11.5%, hermetic container heats to 71-75 DEG C, and stir with 900r/min speed, after 40 minutes, remove fumaric acid, and be dried.
Further, described glass fibre is short glass fiber, and glass fibre is through pretreatment: adopt the methacryloxypropyl silane of glass fibre 1/40th weight, at 125 DEG C, glass fibre is carried out surface treatment 30 minutes.
Further, described zinc oxide is that to adopt zinc sulphate heptahydrate and sodium bicarbonate be the nano zine oxide that raw material is prepared, granularity is 18.5-20nm, and nano zine oxide is through surface modification treatment: mix airtight at 61-63 DEG C to nano zine oxide and liquid treating agent, and stir with 1100r/min speed, after 50 minutes, filter, dry；Described liquid treating agent is made up of 0.5% oleic acid, 11% titanate esters and 88.5% water by mass percentage.
Further, the granularity of described bamboo powder is 5000-5200 order, and bamboo powder is through pretreatment: after the fumaric acid that bamboo powder adopts mass concentration be 1.5% soaks 30 minutes at 5-6 DEG C, filters, and dries.
The preparation method of the antibacterial fishing net of a kind of high tenacity: by weight by ethylene propylene diene rubber, Vingon, polyisoprene rubber, polyphtalamide, polyacrylamide gel is put in the container that temperature is 100-108 DEG C and is mixed 40 minutes, when internal tank temperature is adjusted to 70-72 DEG C, the Colophonium of corresponding weight portion it is sequentially added in container, basalt, glass fibre, nano diatomite, bamboo powder, zinc oxide is stirred, the speed of stirring is 700r/min, after stirring 10 minutes, add plasticizer and the auxiliary agent of corresponding weight portion again, stir 15 minutes with 1000r/min speed, finally add extruder to and carry out pelletize, then injection machine injection moulding is used, then spray webbing machine spray webbing is used, finally weave, obtain described high intensity fishing net.
The invention has the beneficial effects as follows: the fishing net processing technique that the present invention makes is simple, by adopting, ethylene propylene diene rubber is carried out other composition in the pretreatment cooperation present invention, fishing net tensile strength of material can improve 41.5%, and improve the comprehensive mechanical property of fishing net, elongation at break and toughness can be improved, the ageing resistance coordinating the fishing net that can greatly improve making by auxiliary agent with other composition, improve the compatibility between each composition, improve weatherability, and can greatly improve the antibacterial ability of fishing net, reduce production cost；By glass fibre, cooperate through kieselguhr and Colophonium, basalt, zinc oxide, the bamboo powder of mixed processing, the elastic modelling quantity of fishing net improves 100.1%, fishing net toughness can improve 44.9%, the ageing resistace of fishing net can be strengthened, improve its mechanical property, strengthen toughness and antibacterial ability, greatly improve anti-tensile degree, the life-span of fishing net of the present invention improves 29% than common fishing net, extremely durable, is especially suitable for fisherman and uses.
Detailed description of the invention
A kind of antibacterial fishing net of high tenacity, is made up of following component: ethylene propylene diene rubber 0.8, Vingon 126, polyisoprene rubber 0.7, Colophonium 0.5, polyphtalamide 0.7, polyacrylamide 0.8, glass fibre 0.1, basalt 0.1, nano diatomite 0.1, bamboo powder 0.1, zinc oxide 0.1, plasticizer 1, auxiliary agent 0.1 by weight；Described auxiliary agent is the mixed extract of Herba Erodii, Herba Senecionis Scandentis, Fructus Tribuli, Herba pegani harmalae, needs 15 portions of Herba Erodiis, 14 parts of Herba Senecionis Scandentiss, 14 parts of Fructus Tribulis, 12 parts of Herba pegani harmalaes by weight, and preparation method is: will pulverize after selected plant cleaning-drying；Then the plant after pulverizing is put in the solution that hydrochloric acid solution mixes with ethanol, mix homogeneously, the Chlorine in Solution hydrogen that described hydrochloric acid mixes with ethanol: water: the mass ratio of ethanol is 0.2:1.9:10；Said mixture is placed in ultrasonic extraction tank, adopts every 3 minutes of the ultrasound wave of 21.5kHZ, 28kHZ frequency to substitute circulation successively and carries out extracting operation to it, it is possible to improve extraction efficiency and extraction degree greatly, after 30 minutes extracting solution；Gained extracting solution is first adopted in ammonia and hydrochloric acid, then carry out recovered alcohol, remaining solution is carried out process of anhydrating, namely can be made into required auxiliary agent.
Further, described ethylene propylene diene rubber is through pretreatment: by weight is ethylene propylene diene rubber 1/19th calcium sulfate crystal whiskers mix at 210 DEG C with ethylene propylene diene rubber, after being incubated 15 minutes, carry out post vulcanization process.
Further, described plasticizer is epoxy tetrahydro-2-ethylhexyl phthalate and di-2-ethylhexyl maleate composite elasticizer, wherein epoxy tetrahydro-2-ethylhexyl phthalate is 2:1 with the composite quality ratio of di-2-ethylhexyl maleate, combined temp is between 79-80 DEG C, the plasticizer that thus compound goes out, plasticization effect is more preferably notable, and can also improve the toughness of fishing lines.
Further, described basalt is through 450 DEG C of calcinings, and calcination time is 30 minutes.
Further, the granularity of described nano diatomite is 23-27nm, nano diatomite and Colophonium are through mixing pretreatment: by nano diatomite and Colophonium Homogeneous phase mixing to together with, mixture is added in the fumaric acid solution that mass fraction is 11.5%, hermetic container heats to 71-75 DEG C, and stir with 900r/min speed, after 40 minutes, remove fumaric acid, and be dried.
Further, described glass fibre is short glass fiber, and glass fibre is through pretreatment: adopt the methacryloxypropyl silane of glass fibre 1/40th weight, at 125 DEG C, glass fibre is carried out surface treatment 30 minutes.
Further, described zinc oxide is that to adopt zinc sulphate heptahydrate and sodium bicarbonate be the nano zine oxide that raw material is prepared, granularity is 18.5-20nm, and nano zine oxide is through surface modification treatment: mix airtight at 61-63 DEG C to nano zine oxide and liquid treating agent, and stir with 1100r/min speed, after 50 minutes, filter, dry；Described liquid treating agent is made up of 0.5% oleic acid, 11% titanate esters and 88.5% water by mass percentage.
Further, the granularity of described bamboo powder is 5000-5200 order, and bamboo powder is through pretreatment: after the fumaric acid that bamboo powder adopts mass concentration be 1.5% soaks 30 minutes at 5-6 DEG C, filters, and dries.
The preparation method of the antibacterial fishing net of a kind of high tenacity: by weight by ethylene propylene diene rubber, Vingon, polyisoprene rubber, polyphtalamide, polyacrylamide gel is put in the container that temperature is 100-108 DEG C and is mixed 40 minutes, when internal tank temperature is adjusted to 70-72 DEG C, the Colophonium of corresponding weight portion it is sequentially added in container, basalt, glass fibre, nano diatomite, bamboo powder, zinc oxide is stirred, the speed of stirring is 700r/min, after stirring 10 minutes, add plasticizer and the auxiliary agent of corresponding weight portion again, stir 15 minutes with 1000r/min speed, finally add extruder to and carry out pelletize, then injection machine injection moulding is used, then spray webbing machine spray webbing is used, finally weave, obtain described high intensity fishing net.
Claims (9)
1. the antibacterial fishing net of high tenacity, it is characterized in that, be made up of following component by weight: ethylene propylene diene rubber 0.8, Vingon 126, polyisoprene rubber 0.7, Colophonium 0.5, polyphtalamide 0.7, polyacrylamide 0.8, glass fibre 0.1, basalt 0.1, nano diatomite 0.1, bamboo powder 0.1, zinc oxide 0.1, plasticizer 1, auxiliary agent 0.1；Described auxiliary agent is the mixed extract of Herba Erodii, Herba Senecionis Scandentis, Fructus Tribuli, Herba pegani harmalae, needs 15 portions of Herba Erodiis, 14 parts of Herba Senecionis Scandentiss, 14 parts of Fructus Tribulis, 12 parts of Herba pegani harmalaes by weight, and preparation method is: will pulverize after selected plant cleaning-drying；Then the plant after pulverizing is put in the solution that hydrochloric acid solution mixes with ethanol, mix homogeneously, the Chlorine in Solution hydrogen that described hydrochloric acid mixes with ethanol: water: the mass ratio of ethanol is 0.2:1.9:10；Being placed in ultrasonic extraction tank by said mixture, the ultrasound wave of employing 21.5kHZ, 28kHZ frequency substitutes circulation for every 3 minutes successively to carry out extracting operation to it, obtains extracting solution after 30 minutes；Gained extracting solution is first adopted in ammonia and hydrochloric acid, then carry out recovered alcohol, remaining solution is carried out process of anhydrating, namely can be made into required auxiliary agent.
2. a kind of antibacterial fishing net of high tenacity according to claim 1, it is characterized in that, described ethylene propylene diene rubber is through pretreatment: by weight is ethylene propylene diene rubber 1/19th calcium sulfate crystal whiskers mix at 210 DEG C with ethylene propylene diene rubber, after being incubated 15 minutes, carry out post vulcanization process.
3. a kind of antibacterial fishing net of high tenacity according to claim 1, it is characterized in that, described plasticizer is epoxy tetrahydro-2-ethylhexyl phthalate and di-2-ethylhexyl maleate composite elasticizer, wherein epoxy tetrahydro-2-ethylhexyl phthalate is 2:1 with the composite quality ratio of di-2-ethylhexyl maleate, and combined temp is between 79-80 DEG C.
4. a kind of antibacterial fishing net of high tenacity according to claim 1, it is characterised in that described basalt is through 450 DEG C of calcinings, and calcination time is 30 minutes, and it is 5500-5600 order that basalt grinds to form granularity, and basalt surface processes through Silane coupling reagent KH-570.
5. a kind of antibacterial fishing net of high tenacity according to claim 1, it is characterized in that, the granularity of described nano diatomite is 23-27nm, nano diatomite and Colophonium are through mixing pretreatment: by nano diatomite and Colophonium Homogeneous phase mixing to together with, mixture is added in the fumaric acid solution that mass fraction is 11.5%, heats in hermetic container to 71-75 DEG C, and stir with 900r/min speed, after 40 minutes, remove fumaric acid, and be dried.
6. a kind of antibacterial fishing net of high tenacity according to claim 1, it is characterized in that, described glass fibre is short glass fiber, and glass fibre is through pretreatment: adopt the methacryloxypropyl silane of glass fibre 1/40th weight, at 125 DEG C, glass fibre is carried out surface treatment 30 minutes.
7. a kind of antibacterial fishing net of high tenacity according to claim 1, it is characterized in that, described zinc oxide is that to adopt zinc sulphate heptahydrate and sodium bicarbonate be the nano zine oxide that raw material is prepared, granularity is 18.5-20nm, and nano zine oxide is through surface modification treatment: mix airtight at 61-63 DEG C to nano zine oxide and liquid treating agent, and stir with 1100r/min speed, after 50 minutes, filter, dry；Described liquid treating agent is made up of 0.5% oleic acid, 11% titanate esters and 88.5% water by mass percentage.
8. a kind of antibacterial fishing net of high tenacity according to claim 1, it is characterized in that, the granularity of described bamboo powder is 5000-5200 order, and bamboo powder is through pretreatment: after the fumaric acid that bamboo powder adopts mass concentration be 1.5% soaks 30 minutes at 5-6 DEG C, filter, dry.
null9. the preparation method of the antibacterial fishing net of a kind of high tenacity according to any one of claim 1-8，It is characterized in that，By weight by ethylene propylene diene rubber、Vingon、Polyisoprene rubber、Polyphtalamide、Polyacrylamide gel is put in the container that temperature is 100-108 DEG C and is mixed 40 minutes，When internal tank temperature is adjusted to 70-72 DEG C，The Colophonium of corresponding weight portion it is sequentially added in container、Basalt、Glass fibre、Nano diatomite、Bamboo powder、Zinc oxide is stirred，The speed of stirring is 700r/min，After stirring 10 minutes，Add plasticizer and the auxiliary agent of corresponding weight portion again，Stir 15 minutes with 1000r/min speed，Finally add extruder to and carry out pelletize，Then injection machine injection moulding is used，Then spray webbing machine spray webbing is used，Finally weave，Obtain described high intensity fishing net.