CN105734755A - Superfine polyester-nylon colored fiber and preparation method thereof - Google Patents
Superfine polyester-nylon colored fiber and preparation method thereof Download PDFInfo
- Publication number
- CN105734755A CN105734755A CN201610209695.3A CN201610209695A CN105734755A CN 105734755 A CN105734755 A CN 105734755A CN 201610209695 A CN201610209695 A CN 201610209695A CN 105734755 A CN105734755 A CN 105734755A
- Authority
- CN
- China
- Prior art keywords
- filament
- chinlon
- colored fibre
- terylene
- wash
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a superfine polyester-nylon colored fiber which comprises a skeleton shaped like a Chinese character Mi and a filling part filled in peripheral gaps of the skeleton shaped like the Chinese character Mi, wherein a component of the skeleton shaped like the Chinese character Mi is nylon, a component of the filling part is polyester, and the nylon and/or the polyester adopt/adopts colored yarn bodies. The invention further discloses a preparation method for the superfine polyester-nylon colored fiber. According to the superfine polyester-nylon colored fiber and the preparation method thereof, dyeing is not required during after-finishing of the fiber, so that water, electricity, gas and labor force are greatly saved, and significance for environmental protection and energy saving is achieved.
Description
Technical field
The application belongs to spining technology field, particularly relates to a kind of superfine polyamide colored fibre and preparation method thereof.
Background technology
Along with the progress of society, dress is required also more and more higher by people, except to wear comfortable except, also want seeking new thoughts, and the release of fabric lining, just well meet the requirement of masses, but common fiber pull resistance is poor, quality is very unstable.
The fiber of prior art is because diameter of section is relatively big, and contact surface area is less, so amount of cooling water is difficult to quickly enter fibrous inside in cooling procedure, so production efficiency is relatively low；And the fiber of prior art is all solid, so warming effect is poor；And the fiber of prior art does not possess the functions such as deodorization, sterilization, anticorrosion yet.
It addition, more thin fiber is more difficult to painted, and dyeing cost is more high.
Summary of the invention
It is an object of the invention to provide a kind of superfine polyamide colored fibre and preparation method thereof, to overcome deficiency of the prior art.
For achieving the above object, the present invention provides following technical scheme:
The embodiment of the present application discloses a kind of superfine polyamide colored fibre, including M shape skeleton and be filled in the filling part in M shape skeleton surrounding gap, described M shape skeleton component is chinlon, and described filling part component is terylene, and described chinlon and/or terylene are coloured filament.
Preferably, washing in brocade colored fibre above-mentioned, described chinlon is undyed filament, and described terylene is the filament of dyeing.
Preferably, washing in brocade colored fibre above-mentioned, described chinlon and terylene have different colors.
Preferably, washing in brocade colored fibre above-mentioned, described chinlon is the filament of dyeing, and described terylene is undyed filament.
Preferably, washing in brocade colored fibre above-mentioned, the surface of described colored fibre is coated with skid resistant course.
Preferably, washing in brocade colored fibre above-mentioned, described colored fibre surface is additionally provided with one layer of photocatalyst material.
Accordingly, the preparation method that disclosed herein as well is a kind of superfine polyamide colored fibre, including: note color after chinlon 6 filament raw material drying, wash monofilament raw material drying；Spinning；Winding；Add bullet；Inspection；Finished product.
Preferably, in the preparation method of above-mentioned superfine polyamide colored fibre, the parameter of preparation technology meets:
Chinlon 6 filament raw material and the baking temperature washing monofilament raw material are 120～140 DEG C；
Wash the spinning temperature of monofilament: 285～295 DEG C；
The spinning temperature of chinlon 6 filament: 245～255 DEG C；
The speed of winding: 3100～3300 meter per seconds；
Adding bullet: draw ratio: 1.6～1.8 times, heating-up temperature: 160～180 DEG C, D/Y compares: 1.5～1.8, process velocity: 600～700 meter per seconds.
Compared with prior art, it is an advantage of the current invention that:
(1), the present invention adopt the multifilament of compound, improve tensile property.Adding aesthetics to prevent from loosening, filament surface configuration has skid resistant course.
(2), it is additionally provided with one layer of photocatalyst material outside fiber bodies, and photocatalyst material itself possesses the functions such as deodorization, sterilization, anticorrosion.
(3), Final finishing of the present invention need not dye, save a large amount of water, electricity, gas and artificial, and environmental protection and energy saving be of great importance.
Accompanying drawing explanation
In order to be illustrated more clearly that the embodiment of the present application or technical scheme of the prior art, the accompanying drawing used required in embodiment or description of the prior art will be briefly described below, apparently, the accompanying drawing that the following describes is only some embodiments recorded in the application, for those of ordinary skill in the art, under the premise not paying creative work, it is also possible to obtain other accompanying drawing according to these accompanying drawings.
Fig. 1 show in the specific embodiment of the invention to wash the sectional view of brocade colored fibre.
Detailed description of the invention
Below in conjunction with the accompanying drawing in the embodiment of the present invention, the technical scheme in the embodiment of the present invention is described in detail, it is clear that described embodiment is only a part of embodiment of the present invention, rather than whole embodiments.Based on the embodiment in the present invention, the every other embodiment that those of ordinary skill in the art obtain under the premise not making creative work, broadly fall into the scope of protection of the invention.
Shown in Fig. 1, superfine polyamide colored fibre, including M shape skeleton 1 and be filled in the filling part 2 in M shape skeleton surrounding gap, M shape skeleton 1 component is chinlon, and filling part 2 component is terylene, chinlon and/or terylene is coloured filament.
In a preferred embodiment, chinlon is undyed filament, and terylene is the filament of dyeing.
In other embodiments, chinlon and terylene can have different colors.
In one embodiment, chinlon is the filament of dyeing, and terylene is undyed filament.
Further, the surface of fiber is coated with skid resistant course.
In this technical scheme, adopt the monofilament of compound, improve tensile property.In order to prevent loosening, fiber surface is provided with skid resistant course.
Further, fiber surface is additionally provided with one layer of photocatalyst material.
In this technical scheme, outside fiber bodies, it is additionally provided with one layer of photocatalyst material, and photocatalyst material itself possesses the functions such as deodorization, sterilization, anticorrosion.
The preparation method of superfine polyamide colored fibre, including: note color after chinlon 6 filament raw material drying, wash monofilament raw material drying；Spinning；Winding；Add bullet；Inspection；Finished product.
The parameter of preparation technology meets:
Chinlon 6 filament raw material and the baking temperature washing monofilament raw material are 120～140 DEG C；
Wash the spinning temperature of monofilament: 285～295 DEG C；
The spinning temperature of chinlon 6 filament: 245～255 DEG C；
The speed of winding: 3100～3300 meter per seconds；
Adding bullet: draw ratio: 1.6～1.8 times, heating-up temperature: 160～180 DEG C, D/Y compares: 1.5～1.8, process velocity: 600～700 meter per seconds.
By this technological means, Final finishing need not dye, and saves a large amount of water, electricity, gas and artificial, and environmental protection and energy saving are of great importance.
Finally, it can further be stated that, term " includes ", " comprising " or its any other variant are intended to comprising of nonexcludability, so that include the process of a series of key element, method, article or equipment not only include those key elements, but also include other key elements being not expressly set out, or also include the key element intrinsic for this process, method, article or equipment.
Claims (8)
1. a superfine polyamide colored fibre, it is characterized in that, including M shape skeleton and be filled in the filling part in M shape skeleton surrounding gap, described M shape skeleton component is chinlon, described filling part component is terylene, and described chinlon and/or terylene are coloured filament.
2. according to claim 1 wash brocade colored fibre, it is characterised in that: described chinlon is undyed filament, described terylene be dyeing filament.
3. according to claim 1 wash brocade colored fibre, it is characterised in that: described chinlon and terylene have different colors.
4. according to claim 1 wash brocade colored fibre, it is characterised in that: described chinlon be dyeing filament, described terylene is undyed filament.
5. according to claim 1 wash brocade colored fibre, it is characterised in that: the surface of described colored fibre is coated with skid resistant course.
6. according to claim 1 wash brocade colored fibre, it is characterised in that: described colored fibre surface is additionally provided with one layer of photocatalyst material.
7. the preparation method of the arbitrary described superfine polyamide colored fibre of claim 1 to 6, it is characterised in that including: note color after chinlon 6 filament raw material drying, wash monofilament raw material drying；Spinning；Winding；Add bullet；Inspection；Finished product.
8. the preparation method of superfine polyamide colored fibre according to claim 7, it is characterised in that: the parameter of preparation technology meets:
Chinlon 6 filament raw material and the baking temperature washing monofilament raw material are 120～140 DEG C；
The spinning temperature of chinlon 6 filament: 245～255 DEG C；
Wash the spinning temperature of monofilament: 285～295 DEG C；
The speed of winding: 3100～3300 meter per seconds；
Adding bullet: draw ratio: 1.6～1.8 times, heating-up temperature: 160～180 DEG C, D/Y compares: 1.5～1.8, process velocity: 600～700 meter per seconds.