CN105734231A - 一种h13钢热处理工艺 - Google Patents

一种h13钢热处理工艺 Download PDF

Info

Publication number
CN105734231A
CN105734231A CN201410744177.2A CN201410744177A CN105734231A CN 105734231 A CN105734231 A CN 105734231A CN 201410744177 A CN201410744177 A CN 201410744177A CN 105734231 A CN105734231 A CN 105734231A
Authority
CN
China
Prior art keywords
temperature
tempering
hardness
conducted
heat treatment
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410744177.2A
Other languages
English (en)
Inventor
刘万明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Chongqing Jinguo Kaichang Machine Tool Factory
Original Assignee
Chongqing Jinguo Kaichang Machine Tool Factory
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Chongqing Jinguo Kaichang Machine Tool Factory filed Critical Chongqing Jinguo Kaichang Machine Tool Factory
Priority to CN201410744177.2A priority Critical patent/CN105734231A/zh
Publication of CN105734231A publication Critical patent/CN105734231A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种工序合理、制造成本低的H13钢热处理工艺，包括如下步骤：1）、预先热处理，首先进行重新退火；2）、等温球化退火，等温球化退火工艺为：860～890℃加热保温2h，降温到740～760℃等温4h，炉冷到500℃左右出炉；3）、淬火及回火，加热温度1020～1050℃，油冷或空冷，硬度54～58HRC；要求热硬性为主的模具淬火工艺规范、加热温度1050～1080℃，油冷，硬度56～58HRC；回火应进行两次，在500℃回火时，出现回火二次硬化峰，回火硬度最高，峰值在55HRC左右，回火工艺应避开500℃左右为宜。淬火加热应进行两次预热（600～650℃，800～850℃）； 4）、化学热处理，H13钢若进行气体渗氮或氮碳共渗使模具进一步强化，但其氮化温度不应高于回火温度。

Description

一种H13钢热处理工艺
技术领域
本发明涉及一种H13钢热处理工艺。
背景技术
现有的H13钢热处理工艺存在工序安排不合理、工序繁多，工艺参数选择不合理，各工艺参数搭配不合理，且对操作者经验要求较高，使得生产成本偏高、产品质量偏低、成品率不高。
发明内容
有鉴于现有技术的上述缺陷，本发明所要解决的技术问题是提供一种工序合理、制造成本低的H13钢热处理工艺。
为实现上述目的，本发明提供了一种H13钢热处理工艺，包括如下步骤：
1）、预先热处理，首先进行进行重新退火；
2）、等温球化退火，等温球化退火工艺为：860～890℃加热保温2h，降温到740～760℃等温4h，炉冷到500℃左右出炉；
3）、淬火及回火，加热温度1020～1050℃，油冷或空冷，硬度54～58HRC；要求热硬性为主的模具淬火工艺规范、加热温度1050～1080℃，油冷，硬度56～58HRC；
回火应进行两次，在500℃回火时，出现回火二次硬化峰，回火硬度最高，峰值在55HRC左右，回火工艺应避开500℃左右为宜。淬火加热应进行两次预热（600～650℃，800～850℃），以减少加热过程产生热应力；
4）、化学热处理，H13钢若进行气体渗氮或氮碳共渗使模具进一步强化，但其氮化温度不应高于回火温度。
进一步，所述的回火温度为：530～560℃，硬度48～52HRC。
进一步，所述的回火温度为：回火温度560～580℃；硬度47～49HRC。
进一步，所述的回火温度为：540～620℃。
本发明的有益效果是：本发明工序合理，制造成本低，各参数搭配合理协调，能够有效地提高产品质量和生产效率。
具体实施方式
下面结合实施例对本发明作进一步说明：
一种H13钢热处理工艺，包括如下步骤：
1）、预先热处理，首先进行进行重新退火。
2）、等温球化退火，等温球化退火工艺为：860～890℃加热保温2h，降温到740～760℃等温4h，炉冷到500℃左右出炉。
3）、淬火及回火，加热温度1020～1050℃，油冷或空冷，硬度54～58HRC；要求热硬性为主的模具淬火工艺规范、加热温度1050～1080℃，油冷，硬度56～58HRC。
推荐回火温度：530～560℃，硬度48～52HRC；回火温度560～580℃；硬度47～49HRC。
回火应进行两次。在500℃回火时，出现回火二次硬化峰，回火硬度最高，峰值在55HRC左右，但韧性最差。因此，回火工艺应避开500℃左右为宜。根据模具的使用需要，在540～620℃范围内回火较好。
淬火加热应进行两次预热（600～650℃，800～850℃），以减少加热过程产生热应力。
4）、化学热处理H13钢若进行气体渗氮或氮碳共渗可使模具进一步强化，但其氮化温度不应高于回火温度，以保证心部强度不降低，从而提高模具的使用寿命。

Claims (4)

1.一种H13钢热处理工艺，其特征是：包括如下步骤：
1)、预先热处理，首先进行进行重新退火；
2)、等温球化退火，等温球化退火工艺为：860～890℃加热保温2h，降温到740～760℃等温4h，炉冷到500℃左右出炉；
3)、淬火及回火，加热温度1020～1050℃，油冷或空冷，硬度54～58HRC；要求热硬性为主的模具淬火工艺规范、加热温度1050～1080℃，油冷，硬度56～58HRC；
回火应进行两次，在500℃回火时，出现回火二次硬化峰，回火硬度最高，峰值在55HRC左右，回火工艺应避开500℃左右为宜，淬火加热应进行两次预热(600～650℃，800～850℃)，以减少加热过程产生热应力；
4)、化学热处理，H13钢若进行气体渗氮或氮碳共渗使模具进一步强化，但其氮化温度不应高于回火温度。
2.如权利要求1所述的一种H13钢热处理工艺，其特征是：所述的回火温度为：530～560℃，硬度48～52HRC。
3.如权利要求1所述的一种H13钢热处理工艺，其特征是：所述的回火温度为：回火温度560～580℃；硬度47～49HRC。
4.如权利要求1所述的一种H13钢热处理工艺，其特征是：所述的回火温度为：540～620℃。
CN201410744177.2A 2014-12-09 2014-12-09 一种h13钢热处理工艺 Pending CN105734231A (zh)