CN105733533B - The thin pons hematoma agent of the molten type mineral fibres of acid and leakage-stop liquid and preparation method thereof - Google Patents
The thin pons hematoma agent of the molten type mineral fibres of acid and leakage-stop liquid and preparation method thereof Download PDFInfo
- Publication number
- CN105733533B CN105733533B CN201610155606.1A CN201610155606A CN105733533B CN 105733533 B CN105733533 B CN 105733533B CN 201610155606 A CN201610155606 A CN 201610155606A CN 105733533 B CN105733533 B CN 105733533B
- Authority
- CN
- China
- Prior art keywords
- parts
- level
- acid
- agent
- stirring
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
It is a kind of thin pons hematoma agent of the molten type mineral fibres of acid and leakage-stop liquid and preparation method thereof the present invention relates to oilfield exploration drilling auxiliary agent technical field;The grain size of lime stone is 0.045mm to 2.5mm in the thin pons hematoma agent raw material of the molten type mineral fibres of the acid, the grain size of mica is 1.4mm to 2.5mm, the grain size of vermiculite is 0.3mm to 2.0mm.The molten thin pons hematoma agent of type mineral fibres of acid of the invention can keep drilling fluid proper flow performance after leak stopping slurry is added under deep-well, ultradeep well, high temperature, high density, high-pressure situations;There is high acid-soluble ratio simultaneously, the acid-soluble ratio of Yin Qigao when strong acid is injected in oil-gas mining is carried out after leak stopping and is dissolved, to ensure oil gas smoothly pollution-free exploitation;The leakage-stop liquid obtained using the molten thin pons hematoma agent of type mineral fibres of acid is suitable for various drop plies, and plugging effect is good.
Description
Technical field
The present invention relates to oilfield exploration drilling auxiliary agent technical fields, are a kind of molten thin pons hematomas of type mineral fibres of acid
Agent and leakage-stop liquid and preparation method thereof.
Background technology
The generation of leakage brings extreme difficulties to the exploration and development of petroleum resources, it can not only expend drilling time, loss
Mud, and be possible to cause a series of complex situation such as bit freezing, blowout, well slough, wellbore can be caused to scrap when serious, cause weight
Big economic loss.Leakage can be summarized as to being endangered caused by oil-gas exploration, drilling well and development operation:1. leakage delay is bored
The well operations time extends drilling period;2. leakage directly contributes huge goods and materials and economic loss;3. reservoir leakage can damage production
Layer;4. interfering geological logging work;5. leakage interferes the conventional maintenance processing of mud property;6. leakage can cause underground complexity feelings
Condition.And leakage prevents mainly to use five class measures:Rational well structure design;Reduce wellbore pressure;Wellbore pressure is reduced to swash
It is dynamic;Drilling fluid following drill leakproof;Under balance pressure drilling.Rational well structure design is to prevent the most important link of leakage.Planned well
When body structure, it is necessary to according to formation pore pressure, fracture pressure, caving pressure and leakage pressure section, make as far as possible same naked
Equivalent drilling fluid density meets blowout prevention, anti-collapse, leakproof requirement simultaneously needed for eye well section.Due to being limited by casing program, when
When above-mentioned condition can not meet simultaneously, then setting of casing is answered to separate on low fracture pressure stratum with high pressure zone so that same open hole well
Duan Suoxu drilling fluid highest equal yield densities are less than formation fracture pressure, prevent the generation of pressure break leakage.Because of bridging materials used
Difference, so there are many bridge joint sealing agent preparation method, presently describe several common bridge plug agent:
1. shell slag-polyacrylamide drilling fluid:It can leak stopping, and de-plugging can be acidified, be conducive to protect oil-gas Layer,
Good effect is achieved in the biogenic limestone of fracture development.Gluey polyacrylamide dosage be drilling fluid volume 1% to
1.5%, cement (or other polyvalent metal compounds) dosage is the 0.5% to 1% of drilling fluid volume.Shell slag (removes after shell roasting
Removing the residue of firing fine powder) dosage is the 3% to 5% of drilling fluid volume, size distribution is:0.075mm to 0.5mm accounts for 20%,
0.5mm to 5mm accounts for 20%, 5mm to 15mm and accounts for 60%, when preparation, first in polyacrylamide and cement addition drilling fluid, uses drilling well
Liquid rifle is made a spurt or is stirred with blender, is uniformly mixed, drilling fluid viscosity is made to rise to 50s or more, shell slag is then added, then mix
Uniform, injection drop ply position is closed, with the leakage of drilling fluid, visible plugging effect soon.
2. flexible leak stoppage agent:The compoundings such as rubber granule and modified asbestos, scurf are added in drilling fluid, and wherein micelle, which rises, builds bridge
Effect, modified asbestos and scurf play filling and solidification, because rubber granule density is in 1.17 g/cm3To 1.27g/cm3Between, energy
It is enough evenly dispersed in drilling fluid, and the substances such as the clay in drilling fluid can be adsorbed and form one layer of adsorbed film, have centainly
Cementation.Micelle is flexible, is easily accessible smaller crack, and micelle is in irregular polyhedron, can be generated with slotted wall compared with
Big frictional force, it is very effective that this sealing agent tackles fractured leakage.When use, micelle granularity should be selected according to fracture width,
Micelle more than slit width should account for 40% to 50%, and the micelle for being equivalent to 1 to 1/2 times of fracture width accounts for 10% to 20%, less than splitting
It is proper that the micelle that 1/2 times of slit width degree, which accounts for 30% to 40%, it, which is formed by tamper not only, certain intensity, and
It is dense.In addition there is a kind of sealing agent of asphalt type, name of product is OP-1, and 160 DEG C of softening point, particle is irregular
Body, can account for 90% by the particle that 60 mesh are sieved to 200 mesh, not soluble in water, but can be dispersed in water well.OP-1 particles are soft
Change or less has certain intensity, into after drop ply, forms bridge joint skeleton, and then form bed course and mud cake, plays filling and bridge
The effect of leak stopping layer.OP-1 blocking agents have plasticity, can enter the crack less than particle size, when downhole temperature is close to softening point,
Particle deformation, it is coatable on the borehole wall, fine and close and tough and tensile mud cake is formed, not only can be with leakproof, but also it can be anti-collapse.
3. intumescent sealing agent:Type is also very much, and onsite application is mainly the following:
(1) polyurethane foam varicosity sealing agent:The characteristics of polyurethane foam varicosity (PAT) particle sealing agent be water suction after from
Body product can expand rapidly.Observe under the microscope, PAT be netted connectivity structure, grid by 0.1~0.2mm of diameter twine
It constitutes, eye diameter is 0.4~0.5mm, has good elasticity and intensity.Due to its heap in hole, one is formed
Infiltrative interval, while its grid can trap various particles and form fine and close mud cake therebetween and leak stopping work to fill
With.(2) TP-1090:TP-1090 is reacted with polyacrylamide by inorganic metal salt, is solid granular object, normal
Under temperature, 40 minutes start water swelling, after 6 hours, may expand up to 50 times.After the blocking agent enters drop ply, water swelling
Block drop ply.(3) SYZ dilatancy sealing agent:It is a kind of high molecular polymer, there is very strong water swellability, can absorb certainly
The water that 50~60 times of body weight, water swellability occur mainly in first 30 minutes after being contacted with water, therefore are leaked entering
Before layer, the agent cannot be allowed to be in direct contact with water, that is, which cannot directly be carried with water-base drilling fluid.Use the agent
Shi Bixu takes a three-stage approach, the first step, and it is in place to drop ply to carry the agent with water-in-oil emulsion;Second step is injected containing demulsifier
Liquid passes through leakage channel, and the intrapore water-in-oil emulsion of bridge plug is displaced.In order to give full play to the work of demulsifier
With answering intermittent driving, demulsifier and water-in-oil emulsion made to have sufficient time of contact and contact area.Third walks, and is inhaled in SYZ
It after water expansion, then is squeezed and is blocked up with drilling fluid, solid colmatation zone can be formed.
Compound leakage stop agent:I.e. by the rigid particles of different-grain diameter, flexible particle, fibrous matter, flaky substance by certain ratio
Example mixing is added high glue and cuts in the drilling fluid of high dehydration, is pumped to drop ply position leak stopping.Because after leakage, we are difficult to determine
The property of drop ply, if fractured leakage, fracture width will not be uniform, and the applicable model of mixed type sealing agent
It is that comparison is extensive to enclose, and rigid particles are first in duct bridging, followed by fibrous matter, flaky substance and special small clay particles
It is filled, forms solid blocking substance.Typical compound leakage stop agent can be enumerated following several:(1) rubber granule is compound stifled
Leak agent:Rubber granule 35%, walnut shell 20%, oyster shell whiting 15%, sawdust 10%, cotton seed hulls 12%, peanut shell 5%, straw 3%.(2) HD bridges
Connect sealing agent:Walnut shell:Mica:Rubber granule:Monofilament:Vermiculite:Cotton seed hulls:Sawdust=3:2:3:0.1:2:1:1.(3) FDJ is compound
Sealing agent:Be using inertia hard blocking material as primary raw material, using inorganic salts as reinforcing agent, using polymer as synergistic agent, optimum ratio
It forms.The agent is divided into three kinds:There is the FDJ-1 for adapting to small leakage speed, the FDJ-2 of speed is leaked in adaptation and adapts to the FDJ-3 of big leakage speed.Add
The FDJ-1 for entering 5% to 8% (weight and volume ratio) can block up the cracks below 2mm, and 5% to 10% FDJ-2 is added and can block up 2mm to 5mm
Crack, 5% to 12% FDJ-3, which is added, can block up the crack of 5mm to 10mm.(4) 915,917 compound leakage stop agents:915 compound leak stopping
Agent by 30% walnut shell, 45% cotton seed hulls and sawdust, 25% vermiculite and mica sheet assemble.917 compound leakage stop agents by
20% walnut shell, 15% rubber granule, 15% cotton seed hulls, 20% sawdust, 15% vermiculite, 15% mica sheet assemble.
(5) cotton seed hulls ball sealing agent:By 50% cotton seed meal, 31% cotton seed hulls, 1% velveteen, 18% bentonite and 0.1% surface
Activating agent (such as trimethyl ether of ethylene oxide, propylene oxide, polyethylene glycol) is uniformly mixed, and is heated with steam in tube furnace
To 100 DEG C to 160 DEG C, then the mixture after heating is compressed, diameter 6.3mm, long 6.3mm are squeezed into extremely with pellet processing machine
The pill of 25.4mm, in case using.When boring chance lost-circulation zone, 10% to 25% cotton seed hulls ball is added in drilling fluid, is pumped into drop ply,
After a period of time, cotton seed hulls ball absorbs a large amount of moisture content, causes to expand and divide, blocks drop ply.Though the above pons hematoma agent
Can also so be played in drilling well prevents leakage, but it prepares complicated, takes time and effort, can not general warranty high temperature resistant, high pressure and
High acid-soluble ratio.
Invention content
The present invention provides a kind of thin pons hematoma agent of the molten type mineral fibres of acid and leakage-stop liquids and preparation method thereof, overcome
The deficiency of the above-mentioned prior art, can effectively solve existing pons hematoma agent prepare it is complicated, take time and effort, can not general warranty it is resistance to
The problem of high temperature, high pressure and high acid-soluble ratio and plugging effect difference.
One of technical scheme of the present invention is realized by following measures:A kind of molten thin bridge plug of type mineral fibres of acid is stifled
Agent is leaked, raw material contains 30 parts to 40 parts of lime stone, 18 parts to 30 parts of mica, 10 parts to 20 parts of asbestos, 3 parts of vermiculite in parts by weight
To 15 parts, 1 part to 5 parts of velveteen, 1 part to 15 parts of acidificable fiber, 1 part to 10 parts of uniaxial pressure sealer, 1 part of delayed expansion agent
To 5 parts, 0.1 part to 2 parts of thinner;Wherein:The grain size of lime stone is 0.045mm to 2.5mm, the grain size of mica be 1.4mm extremely
2.5mm, vermiculite grain size be 0.3mm to 2.0mm.
Here is the further optimization and/or improvements to one of foregoing invention technical solution:
The thin pons hematoma agent of the above-mentioned molten type mineral fibres of acid obtains as follows:The first step, by the desired amount of lime stone,
Mica, asbestos, vermiculite, velveteen, acidificable fiber, uniaxial pressure sealer, delayed expansion agent and thinner are added in mixing machine
Level-one stirring is carried out, the batch mixing that fiber is floated on surface is obtained after level-one stirring;Second step, by a batch mixing in mixing machine
Two level stirring is carried out, small wind is sent into when two level stirs into mixing machine with wind turbine simultaneously, rerolling is obtained after two level stirring, the
Rerolling in mixing machine is carried out three-level stirring, strong wind is sent into mixing machine with wind turbine simultaneously when three-level stirs by three steps,
The molten thin pons hematoma agent of type mineral fibres of acid is obtained after three-level stirring.
The rotating speed of above-mentioned level-one stirring is 40rpm to 60rpm, and the time of level-one stirring is 20min to 40min;Two level is stirred
The rotating speed mixed is 60rpm to 100rpm, and time of two level stirring is 20min to 40min, the wind speed of small wind be 5.5 m/s extremely
7.9m/s;The rotating speed of three-level stirring is 80rpm to 100rpm, and the time of three-level stirring is 20min to 40min, the wind speed of strong wind
For 8.0m/s to 10.7m/s.
Technical scheme of the present invention second is that being realized by following measures:A kind of molten thin bridge plug of type mineral fibres of acid is stifled
The preparation method for leaking agent, carries out as follows:The first step, by the desired amount of lime stone, mica, asbestos, vermiculite, velveteen, can
It is acidified fiber, uniaxial pressure sealer, delayed expansion agent and thinner and progress level-one stirring in mixing machine is added, after level-one stirring
Obtain the batch mixing that fiber is floated on surface;Batch mixing is carried out two level stirring, when two level stirs by second step in mixing machine
It is sent into small wind into mixing machine with wind turbine simultaneously, rerolling, third step, by rerolling in mixing machine is obtained after two level stirring
Middle progress three-level stirring is sent into strong wind into mixing machine with wind turbine simultaneously when three-level stirs, the molten type mine of acid is obtained after three-level stirring
The thin pons hematoma agent of fibres.
Here is two further optimization and/or improvements to foregoing invention technical solution:
The rotating speed of above-mentioned level-one stirring is 40rpm to 60rpm, and the time of level-one stirring is 20min to 40min;Two level is stirred
The rotating speed mixed is 60rpm to 100rpm, and time of two level stirring is 20min to 40min, the wind speed of small wind be 5.5 m/s extremely
7.9m/s;The rotating speed of three-level stirring is 80rpm to 100rpm, and the time of three-level stirring is 20min to 40min, the wind speed of strong wind
For 8.0m/s to 10.7m/s.
The three of technical scheme of the present invention are realized by following measures:It is a kind of to use the molten thin bridge of type mineral fibres of acid
Fill in the leakage-stop liquid of sealing agent, raw material is pressed per containing the thin pons hematoma agent 1Kg to 8Kg of the molten type mineral fibres of acid, extraordinarily thick in square mud
Vermiculite 0 is to 4Kg, thick shell 0 to 10Kg, middle shell 2Kg to 10Kg, thin shell 4Kg to 10Kg, cotton seed hulls 0 to 4Kg, sawdust 2Kg
To thick pons hematoma agent 3Kg in 4Kg, the molten type mineral fibres of acid to 10Kg, JYW-1 0 to 2Kg.
Here is three further optimization and/or improvements to foregoing invention technical solution:
The above-mentioned leakage-stop liquid using the molten thin pons hematoma agent of type mineral fibres of acid obtains as follows:By the desired amount of acid
The thin pons hematoma agent of molten type mineral fibres, extraordinarily thick vermiculite, thick shell, middle shell, thin shell, cotton seed hulls, sawdust, the molten type mineral of acid
Thick pons hematoma agent and JYW-1 are added in the desired amount of mud after mixing in fiber, obtain leakage-stop liquid.
The grain size of above-mentioned extraordinarily thick vermiculite is 4mm to 8mm, the grain size of thick shell is 4.2mm to 8mm, the grain size of middle shell is
2.5mm to 4.2mm, thin shell grain size be 0.1mm to 2.5mm, the grain size of cotton seed hulls is 2mm to 6mm, the grain size of sawdust is
0.1mm to 3.1mm.
Thick pons hematoma agent obtains as follows in the above-mentioned molten type mineral fibres of acid:The first step, by the desired amount of lime
Mixing machine is added in stone, mica, asbestos, vermiculite, velveteen, acidificable fiber, uniaxial pressure sealer, delayed expansion agent and thinner
Middle progress level-one stirring obtains the batch mixing that fiber is floated on surface after level-one stirring;Second step, by a batch mixing in mixing machine
Middle progress two level stirring is sent into small wind into mixing machine with wind turbine, rerolling is obtained after two level stirring simultaneously when two level stirs,
Third walks, and rerolling is carried out three-level stirring in mixing machine, is sent into simultaneously into mixing machine greatly with wind turbine when three-level stirs
Wind obtains thick pons hematoma agent in the molten type mineral fibres of acid after three-level stirring;Thick pons hematoma agent in the molten type mineral fibres of the acid
Raw material contains 30 parts to 40 parts of lime stone, 20 parts to 35 parts of mica, 15 parts to 20 parts of asbestos, 5 parts to 15 of vermiculite in parts by weight
Part, 2 parts to 5 parts of velveteen, 3 parts to 15 parts of acidificable fiber, 3 parts to 10 parts of uniaxial pressure sealer, 1 part to 5 of delayed expansion agent
Part, 0.1 part to 2 parts of thinner;Wherein:The grain size of lime stone is 2.5mm to 4.2mm, the grain size of mica be 2.5mm to 4.2mm,
The grain size of vermiculite is 2.0mm to 4.0mm.
The rotating speed of above-mentioned level-one stirring is 40rpm to 60rpm, and the time of level-one stirring is 20min to 40min;Two level is stirred
The rotating speed mixed is 60rpm to 100rpm, and time of two level stirring is 20min to 40min, the wind speed of small wind be 5.5 m/s extremely
7.9m/s;The rotating speed of three-level stirring is 80rpm to 100rpm, and the time of three-level stirring is 20min to 40min, the wind speed of strong wind
For 8.0m/s to 10.7m/s.
The four of technical scheme of the present invention are realized by following measures:It is a kind of to use the molten thin bridge of type mineral fibres of acid
The preparation method for filling in the leakage-stop liquid of sealing agent, carries out as follows:By the molten thin pons hematoma of type mineral fibres of the desired amount of acid
In agent, extraordinarily thick vermiculite, thick shell, middle shell, thin shell, cotton seed hulls, sawdust, the molten type mineral fibres of acid thick pons hematoma agent and
JYW-1 is added in the desired amount of mud after mixing, obtains leakage-stop liquid.
Here is four further optimization and/or improvements to foregoing invention technical solution:
The grain size of above-mentioned extraordinarily thick vermiculite is 4mm to 8mm, the grain size of thick shell is 4.2mm to 8mm, the grain size of middle shell is
2.5mm to 4.2mm, thin shell grain size be 0.1mm to 2.5mm, the grain size of cotton seed hulls is 2mm to 6mm, the grain size of sawdust is
0.1mm to 3.1mm.
Thick pons hematoma agent obtains as follows in the above-mentioned molten type mineral fibres of acid:The first step, by the desired amount of lime
Mixing machine is added in stone, mica, asbestos, vermiculite, velveteen, acidificable fiber, uniaxial pressure sealer, delayed expansion agent and thinner
Middle progress level-one stirring obtains the batch mixing that fiber is floated on surface after level-one stirring;Second step, by a batch mixing in mixing machine
Middle progress two level stirring is sent into small wind into mixing machine with wind turbine, rerolling is obtained after two level stirring simultaneously when two level stirs,
Third walks, and rerolling is carried out three-level stirring in mixing machine, is sent into simultaneously into mixing machine greatly with wind turbine when three-level stirs
Wind obtains thick pons hematoma agent in the molten type mineral fibres of acid after three-level stirring;Thick pons hematoma agent in the molten type mineral fibres of the acid
Raw material contains 30 parts to 40 parts of lime stone, 20 parts to 35 parts of mica, 15 parts to 20 parts of asbestos, 5 parts to 15 of vermiculite in parts by weight
Part, 2 parts to 5 parts of velveteen, 3 parts to 15 parts of acidificable fiber, 3 parts to 10 parts of uniaxial pressure sealer, 1 part to 5 of delayed expansion agent
Part, 0.1 part to 2 parts of thinner;Wherein:The grain size of lime stone is 2.5mm to 4.2mm, the grain size of mica be 2.5mm to 4.2mm,
The grain size of vermiculite is 2.0mm to 4.0mm.
The rotating speed of above-mentioned level-one stirring is 40rpm to 60rpm, and the time of level-one stirring is 20min to 40min;Two level is stirred
The rotating speed mixed is 60rpm to 100rpm, and time of two level stirring is 20min to 40min, the wind speed of small wind be 5.5 m/s extremely
7.9m/s;The rotating speed of three-level stirring is 80rpm to 100rpm, and the time of three-level stirring is 20min to 40min, the wind speed of strong wind
For 8.0m/s to 10.7m/s.
The molten thin pons hematoma agent of type mineral fibres of acid of the invention is in deep-well, ultradeep well, underground high temperature, high density, high pressure feelings
The proper flow performance of drilling fluid can be kept by being added under condition after leak stopping is starched;There is high acid-soluble ratio simultaneously, oil gas is carried out after leak stopping and is opened
It adopts the acid-soluble ratio of Yin Qigao when injecting strong acid and dissolves, to ensure oil gas smoothly pollution-free exploitation;It is fine using the molten type mineral of acid
It ties up the leakage-stop liquid that thin pons hematoma agent obtains and is suitable for various drop plies, plugging effect is good.
Specific implementation mode
The present invention is not limited by following embodiments, can be determined according to the technique and scheme of the present invention with actual conditions specific
Embodiment.
Embodiment 1, the thin pons hematoma agent of the molten type mineral fibres of the acid, raw material contain lime stone 30 parts to 40 in parts by weight
Part, 18 parts to 30 parts of mica, 10 parts to 20 parts of asbestos, 3 parts to 15 parts of vermiculite, 1 part to 5 parts of velveteen, 1 part to 15 of acidificable fiber
Part, 1 part to 10 parts of uniaxial pressure sealer, 1 part to 5 parts of delayed expansion agent, 0.1 part to 2 parts of thinner;Wherein:Lime stone
Grain size is 0.045mm to 2.5mm, the grain size of mica is 1.4mm to 2.5mm, the grain size of vermiculite is 0.3mm to 2.0mm.
Embodiment 2, the thin pons hematoma agent of the molten type mineral fibres of the acid, raw material contain 30 parts of lime stone or 40 in parts by weight
Part, 18 parts or 30 parts of mica, 10 parts or 20 parts of asbestos, 3 parts or 15 parts of vermiculite, 1 part or 5 parts of velveteen, 1 part of acidificable fiber or 15
Part, 1 part or 10 parts of uniaxial pressure sealer, 1 part or 5 parts of delayed expansion agent, 0.1 part or 2 parts of thinner;Wherein:Lime stone
Grain size is 0.045mm to 2.5mm, the grain size of mica is 1.4mm to 2.5mm, the grain size of vermiculite is 0.3mm to 2.0mm.
Embodiment 3, the thin pons hematoma agent of the molten type mineral fibres of the acid are obtained by following preparation methods:The first step, will be required
Lime stone, mica, asbestos, vermiculite, velveteen, acidificable fiber, uniaxial pressure sealer, delayed expansion agent and the thinner of amount add
Enter progress level-one stirring in mixing machine, the batch mixing that fiber is floated on surface is obtained after level-one stirring;Second step, by a batch mixing
Two level stirring is carried out in mixing machine, is sent into small wind when two level stirs into mixing machine with wind turbine simultaneously, is obtained after two level stirring
Rerolling in mixing machine is carried out three-level stirring, uses wind turbine to mixing machine simultaneously when three-level stirs by rerolling, third step
Middle feeding strong wind obtains the molten thin pons hematoma agent of type mineral fibres of acid after three-level stirring.
The molten thin pons hematoma agent of type mineral fibres of acid of the invention is encountering deep-well(5000m or more), ultradeep well(8000m is extremely
10000m), underground high temperature(200℃)High density(1.5g/m3 to 3.0g/m3), high pressure(180Mpa)In the case of leak stopping is added
The proper flow performance of drilling fluid can be kept after slurry;There is high acid-soluble ratio simultaneously, acid-soluble ratio >=80%, water content≤5%, institute is aqueous
Insoluble matter≤5%, magma wastage after leak stopping(ml)≤ 40, i.e., in drilling process after leak stopping, carries out oil-gas mining and inject strong acid
When Yin Qigao acid-soluble ratio and dissolve, to ensure oil gas smoothly pollution-free exploitation;The success rate of leak stopping not by geological condition and
The influence of drilling speed, as deep-well, the increase of ultra-deep well depth and temperature, the increase of strata pressure are without influencing plugging effect.
Embodiment 4, the thin pons hematoma agent of the molten type mineral fibres of the acid are obtained by following preparation methods:The first step, will be required
Lime stone, mica, asbestos, vermiculite, velveteen, acidificable fiber, uniaxial pressure sealer, delayed expansion agent and the thinner of amount add
Enter progress level-one stirring in mixing machine, the batch mixing that fiber is floated on surface is obtained after level-one stirring;Second step, by a batch mixing
Two level stirring is carried out in mixing machine, is sent into small wind when two level stirs into mixing machine with wind turbine simultaneously, is obtained after two level stirring
Rerolling in mixing machine is carried out three-level stirring, uses wind turbine to mixing machine simultaneously when three-level stirs by rerolling, third step
Middle feeding strong wind obtains the molten thin pons hematoma agent of type mineral fibres of acid after three-level stirring;Wherein:The molten thin bridge plug of type mineral fibres of acid
Sealing agent raw material contains 35 parts of lime stone, 20 parts of mica, 19 parts of asbestos, 5 parts of vermiculite, 2 parts of velveteen, theobromine chemical fibre in parts by weight
9 parts of dimension, 6 parts of uniaxial pressure sealer, 3 parts of delayed expansion agent, 1 part of thinner;The grain size of lime stone be 0.045mm to 2.5mm,
The grain size of mica is 1.4mm to 2.5mm, the grain size of vermiculite is 0.3mm to 2.0mm.
When the molten thin pons hematoma agent of type mineral fibres of acid that the present embodiment obtains is primarily directed to oilfield exploration drilling,
It is not influenced by geological condition and drilling speed, is only changed, drilling well shared by the increase with density according to different the case where well depth
The ratio of liquid and reduce.It is that 5000m is below in well depth, the molten thin pons hematoma agent of type mineral fibres of acid is in drilling fluid
Middle proportion is 28%, and leak stopping success rate can reach 96%.
Embodiment 5, the thin pons hematoma agent of the molten type mineral fibres of the acid are obtained by following preparation methods:The first step, will be required
Lime stone, mica, asbestos, vermiculite, velveteen, acidificable fiber, uniaxial pressure sealer, delayed expansion agent and the thinner of amount add
Enter progress level-one stirring in mixing machine, the batch mixing that fiber is floated on surface is obtained after level-one stirring;Second step, by a batch mixing
Two level stirring is carried out in mixing machine, is sent into small wind when two level stirs into mixing machine with wind turbine simultaneously, is obtained after two level stirring
Rerolling in mixing machine is carried out three-level stirring, uses wind turbine to mixing machine simultaneously when three-level stirs by rerolling, third step
Middle feeding strong wind obtains the molten thin pons hematoma agent of type mineral fibres of acid after three-level stirring;Wherein:The molten thin bridge plug of type mineral fibres of acid
Sealing agent raw material contains 32 parts of lime stone, 23 parts of mica, 11 parts of asbestos, 7 parts of vermiculite, 4 parts of velveteen, theobromine chemical fibre in parts by weight
13 parts of dimension, 6 parts of uniaxial pressure sealer, 3.5 parts of delayed expansion agent, 0.5 part of thinner;The grain size of lime stone be 0.045mm extremely
2.5mm, mica grain size be 1.4mm to 2.5mm, the grain size of vermiculite is 0.3mm to 2.0mm.
When the molten thin pons hematoma agent of type mineral fibres of acid that the present embodiment obtains is directed to oilfield exploration drilling, not by
The influence of geological condition and drilling speed only changes, the ratio of drilling fluid shared by the increase with density according to different the case where well depth
Example and reduce.Well depth be 5000m to 8000 meters in the case of, the molten thin pons hematoma agent of type mineral fibres of acid is in drilling fluid
Proportion is 20%, and the leak stopping success rate of the sealing agent can reach 98%.
Embodiment 6, the thin pons hematoma agent of the molten type mineral fibres of the acid are obtained by following preparation methods:The first step, will be required
Lime stone, mica, asbestos, vermiculite, velveteen, acidificable fiber, uniaxial pressure sealer, delayed expansion agent and the thinner of amount add
Enter progress level-one stirring in mixing machine, the batch mixing that fiber is floated on surface is obtained after level-one stirring;Second step, by a batch mixing
Two level stirring is carried out in mixing machine, is sent into small wind when two level stirs into mixing machine with wind turbine simultaneously, is obtained after two level stirring
Rerolling in mixing machine is carried out three-level stirring, uses wind turbine to mixing machine simultaneously when three-level stirs by rerolling, third step
Middle feeding strong wind obtains the molten thin pons hematoma agent of type mineral fibres of acid after three-level stirring;Wherein:The molten thin bridge plug of type mineral fibres of acid
Sealing agent raw material contains 39 parts of lime stone, 27 parts of mica, 16 parts of asbestos, 10 parts of vermiculite, 3 parts of velveteen, acidificable in parts by weight
2 parts of fiber, 1 part of uniaxial pressure sealer, 1.75 parts of delayed expansion agent, 0.25 part of thinner;The grain size of lime stone is 0.045mm
Grain size to 2.5mm, mica is 1.4mm to 2.5mm, the grain size of vermiculite is 0.3mm to 2.0mm.
When the molten thin pons hematoma agent of type mineral fibres of acid that the present embodiment obtains is directed to oilfield exploration drilling, not by
The influence of geological condition and drilling speed only changes, the ratio of drilling fluid shared by the increase with density according to different the case where well depth
Example and reduce.Well depth be 8000 meters to ten thousand metres in the case of, the molten thin pons hematoma agent of type mineral fibres of acid is in drilling fluid
Proportion is 11%, and the leak stopping success rate of the sealing agent can reach 99%.
Embodiment 7, as the optimization of above-described embodiment, the rotating speed of level-one stirring is 40rpm to 60rpm, level-one stirring
Time is 20min to 40min;Two level stirring rotating speed be 60rpm to 100rpm, two level stirring time be 20min extremely
The wind speed of 40min, small wind are 5.5 m/s to 7.9m/s;Three-level stirring rotating speed be 80rpm to 100rpm, three-level stirring when
Between be 20min to 40min, the wind speed of strong wind is 8.0m/s to 10.7m/s.
Embodiment 8, the leakage-stop liquid using the molten thin pons hematoma agent of type mineral fibres of acid, raw material in every side's mud by containing
The thin pons hematoma agent 1Kg to 8Kg of the molten type mineral fibres of acid, extraordinarily thick vermiculite 0 to 4Kg, thick shell 0 to 10Kg, middle shell 2Kg are extremely
Thick pons hematoma agent in 10Kg, thin shell 4Kg to 10Kg, cotton seed hulls 0 to 4Kg, sawdust 2Kg to 4Kg, the molten type mineral fibres of acid
3Kg is to 10Kg, JYW-1 0 to 2Kg.JYW-1 is existing public product, and JYW-1 is that the last powder particles of thin grass add polymer particles
Grain, grain size are 0.07mm to 0.9mm.
Embodiment 9, the leakage-stop liquid using the molten thin pons hematoma agent of type mineral fibres of acid are obtained by following preparation methods:It will
The thin pons hematoma agent of the desired amount of molten type mineral fibres of acid, extraordinarily thick vermiculite, thick shell, middle shell, thin shell, cotton seed hulls, sawdust,
Thick pons hematoma agent and JYW-1 are added in the desired amount of mud after mixing in the molten type mineral fibres of acid, obtain leakage-stop liquid.
Embodiment 10, the leakage-stop liquid using the molten thin pons hematoma agent of type mineral fibres of acid are obtained by following preparation methods:
By the thin pons hematoma agent of the molten type mineral fibres of the desired amount of acid, extraordinarily thick vermiculite, thick shell, middle shell, thin shell, cotton seed hulls, saw
Thick pons hematoma agent and JYW-1 are added in the desired amount of mud after mixing in end, the molten type mineral fibres of acid, obtain leak stopping
Liquid;Wherein:Contain the thin pons hematoma agent 6Kg to 8Kg of the molten type mineral fibres of acid, extraordinarily thick vermiculite 3Kg to 4Kg, thick in per side's mud
Shell 8Kg to 10Kg, middle shell 8Kg to 10Kg, thin shell 8Kg to 10Kg, cotton seed hulls 2Kg to 4Kg, sawdust 2Kg to 4Kg, acid
Thick pons hematoma agent 8Kg is to 10Kg, JYW-1 1Kg in molten type mineral fibres.The leakage-stop liquid that the present embodiment obtains can be used for seriously
The large fracture solution cavity drop ply and cobblestone drop ply of leakage degree, leak stopping success rate can reach 97%.
Embodiment 11, the leakage-stop liquid using the molten thin pons hematoma agent of type mineral fibres of acid are obtained by following preparation methods:
The thin pons hematoma agent of the molten type mineral fibres of the desired amount of acid, extraordinarily thick vermiculite, thick shell, middle shell, thin shell, sawdust, acid is molten
Thick pons hematoma agent and JYW-1 are added in the desired amount of mud after mixing in type mineral fibres, obtain leakage-stop liquid;Its
In:Contain the thin pons hematoma agent 6Kg to 8Kg of the molten type mineral fibres of acid, extraordinarily thick vermiculite 2 Kg to 3Kg, thick shell in per side's mud
Thick bridge plug is stifled in 6Kg to 8Kg, middle shell 6Kg to 8Kg, thin shell 6Kg to 8Kg, sawdust 2Kg to 4Kg, the molten type mineral fibres of acid
Agent 6Kg is leaked to 8Kg, JYW-1 1Kg.The leakage-stop liquid that the present embodiment obtains can be used for leaking speed and be more than 50m3The big of/h leaks the big of degree
Crack drop ply, cobblestone drop ply and gritstone drop ply, leak stopping success rate can reach 98%.
Embodiment 12, the leakage-stop liquid using the molten thin pons hematoma agent of type mineral fibres of acid are obtained by following preparation methods:
By the thin pons hematoma agent of the molten type mineral fibres of the desired amount of acid, extraordinarily thick vermiculite, thick shell, middle shell, thin shell, cotton seed hulls, saw
Thick pons hematoma agent and JYW-1 are added in the desired amount of mud after mixing in end, the molten type mineral fibres of acid, obtain leak stopping
Liquid;Wherein:Contain the thin pons hematoma agent 6Kg to 8Kg of the molten type mineral fibres of acid, extraordinarily thick vermiculite 2Kg to 3Kg, thick in per side's mud
Shell 6Kg to 8Kg, middle shell 6Kg to 8Kg, thin shell 4Kg to 6Kg, cotton seed hulls 2Kg to 4Kg, sawdust 2Kg to 4Kg, the molten type of acid
Thick pons hematoma agent 6Kg is to 8Kg, JYW-1 1Kg to 2Kg in mineral fibres.The leakage-stop liquid that the present embodiment obtains can be used for leaking speed
For 20m3/ h to 50m3Middle crack drop ply, pebblestone drop ply and the cobblestone drop ply of the middle leakage degree of/h, leak stopping success rate can reach
97%。
Embodiment 13, the leakage-stop liquid using the molten thin pons hematoma agent of type mineral fibres of acid are obtained by following preparation methods:
By the thin pons hematoma agent of the molten type mineral fibres of the desired amount of acid, thick shell, middle shell, thin shell, sawdust, the molten type mineral fibres of acid
In thick pons hematoma agent and JYW-1 be added in the desired amount of mud after mixing, obtain leakage-stop liquid;Wherein:Per side's mud
In contain the thin pons hematoma agent 4Kg to 6Kg of the molten type mineral fibres of acid, thick shell 4Kg to 6Kg, middle shell 4Kg to 6Kg, thin shell
Thick pons hematoma agent 4Kg is to 6Kg, JYW-1 1Kg to 2Kg in 4Kg to 6Kg, sawdust 2Kg to 4Kg, the molten type mineral fibres of acid.This
It is 10m that the leakage-stop liquid that embodiment obtains, which can be used for leaking speed,3/ h to 20m3Small crack drop ply, the granule rock drop ply of the small leakage degree of/h
With cobblestone drop ply, leak stopping success rate can reach 98%.
Embodiment 14, the leakage-stop liquid using the molten thin pons hematoma agent of type mineral fibres of acid are obtained by following preparation methods:
By thick bridge in the thin pons hematoma agent of the molten type mineral fibres of the desired amount of acid, middle shell, thin shell, sawdust, the molten type mineral fibres of acid
Plug sealing agent and JYW-1 are added in the desired amount of mud after mixing, obtain leakage-stop liquid;Wherein:Contain in per side's mud
The thin pons hematoma agent 3Kg to 4Kg of the molten type mineral fibres of acid, middle shell 2Kg to 4Kg, thin shell 4Kg to 6Kg, sawdust 2Kg are extremely
Thick pons hematoma agent 4Kg is to 6Kg, JYW-1 1Kg to 2Kg in 4Kg, the molten type mineral fibres of acid.The leakage-stop liquid that the present embodiment obtains
It can be used for leaking speed and be less than 10m3Microcrack drop ply, cobblestone drop ply and the pebblestone drop ply of micro- leakage degree of/h, leak stopping success rate
It can reach 99%.
Embodiment 15, as the optimization of above-described embodiment, the grain size of extraordinarily thick vermiculite is 4mm to 8mm, the grain size of thick shell is
4.2mm to 8mm, middle shell grain size be 2.5mm to 4.2mm, the grain size that the grain size of thin shell is 0.1mm to 2.5mm, cotton seed hulls
Grain size for 2mm to 6mm, sawdust is 0.1mm to 3.1mm.
Embodiment 16, as the optimization of above-described embodiment, in the molten type mineral fibres of acid, thick pons hematoma agent is as follows
It obtains:The first step by the desired amount of lime stone, mica, asbestos, vermiculite, velveteen, acidificable fiber, uniaxial pressure sealer, is prolonged
Slow swelling agent and thinner, which are added in mixing machine, carries out level-one stirring, and surface is obtained after level-one stirring and floats the primary mixed of fiber
Material;Batch mixing in mixing machine is carried out two level stirring, is sent into simultaneously into mixing machine with wind turbine when two level stirs by second step
Small wind, obtains rerolling after two level stirring, rerolling is carried out three-level stirring, three-level stirring by third step in mixing machine
When be sent into strong wind into mixing machine with wind turbine simultaneously, thick pons hematoma agent in the molten type mineral fibres of acid is obtained after three-level stirring;It should
Thick pons hematoma agent raw material contains 30 parts to 40 parts of lime stone, 20 parts to 35 of mica in parts by weight in the molten type mineral fibres of acid
Part, the closing of 15 parts to 20 parts of asbestos, 5 parts to 15 parts of vermiculite, 2 parts to 5 parts of velveteen, 3 parts to 15 parts of acidificable fiber, uniaxial pressure
3 parts to 10 parts of agent, 1 part to 5 parts of delayed expansion agent, 0.1 part to 2 parts of thinner;Wherein:The grain size of lime stone be 2.5mm extremely
4.2mm, mica grain size be 2.5mm to 4.2mm, the grain size of vermiculite is 2.0mm to 4.0mm.
Embodiment 17, as the optimization of above-described embodiment, the rotating speed of level-one stirring is 40rpm to 60rpm, level-one stirring
Time is 20min to 40min;Two level stirring rotating speed be 60rpm to 100rpm, two level stirring time be 20min extremely
The wind speed of 40min, small wind are 5.5 m/s to 7.9m/s;Three-level stirring rotating speed be 80rpm to 100rpm, three-level stirring when
Between be 20min to 40min, the wind speed of strong wind is 8.0m/s to 10.7m/s.
In conclusion the present invention molten thin pons hematoma agent of type mineral fibres of acid is in deep-well, ultradeep well, underground high temperature, highly dense
The proper flow performance of drilling fluid can be kept by being added under degree, high-pressure situations after leak stopping is starched;Have high acid-soluble ratio, leak stopping laggard simultaneously
Row oil-gas mining inject strong acid when Yin Qigao acid-soluble ratio and dissolve, to ensure oil gas smoothly pollution-free exploitation;It is molten using acid
The leakage-stop liquid that the thin pons hematoma agent of type mineral fibres obtains is suitable for various drop plies, and plugging effect is good.
The above technical characteristic constitutes the embodiment of the present invention, can basis with stronger adaptability and implementation result
Actual needs increases and decreases non-essential technical characteristic, to meet the needs of different situations.
Claims (9)
1. a kind of thin pons hematoma agent of molten type mineral fibres of acid, it is characterised in that raw material contains 30 parts of lime stone extremely in parts by weight
40 parts, 18 parts to 30 parts of mica, 10 parts to 20 parts of asbestos, 3 parts to 15 parts of vermiculite, 1 part to 5 parts of velveteen, 1 part of acidificable fiber extremely
15 parts, 1 part to 10 parts of uniaxial pressure sealer, 1 part to 5 parts of delayed expansion agent, 0.1 part to 2 parts of thinner;Wherein:Lime stone
Grain size be 0.045mm to 2.5mm, the grain size of mica is 1.4mm to 2.5mm, the grain size of vermiculite is 0.3mm to 2.0mm;The acid
The molten thin pons hematoma agent of type mineral fibres obtains as follows:The first step, by the desired amount of lime stone, mica, asbestos, leech
Stone, velveteen, acidificable fiber, uniaxial pressure sealer, delayed expansion agent and thinner, which are added in mixing machine, carries out level-one stirring,
The batch mixing that fiber is floated on surface is obtained after level-one stirring;Batch mixing is carried out two level stirring by second step in mixing machine,
It is sent into small wind when two level stirs into mixing machine with wind turbine simultaneously, rerolling is obtained after two level stirring, third step will be secondary mixed
Material carries out three-level stirring in mixing machine, and strong wind is sent into mixing machine with wind turbine simultaneously when three-level stirs, after three-level stirring
To the molten thin pons hematoma agent of type mineral fibres of acid.
2. the thin pons hematoma agent of the molten type mineral fibres of acid according to claim 1, it is characterised in that the rotating speed of level-one stirring
Time for 40rpm to 60rpm, level-one stirring is 20min to 40min;Two level stirring rotating speed be 60rpm to 100rpm, two
The time of grade stirring is 20min to 40min, and the wind speed of small wind is 5.5 m/s to 7.9m/s;The rotating speed of three-level stirring is 80rpm
To 100rpm, the time of three-level stirring is 20min to 40min, and the wind speed of strong wind is 8.0m/s to 10.7m/s.
3. a kind of preparation method of the thin pons hematoma agent of molten type mineral fibres of acid according to claim 1 or 2, feature exist
In carrying out as follows:The first step, by the desired amount of lime stone, mica, asbestos, vermiculite, velveteen, acidificable fiber, unidirectional
Pressure seal agent, delayed expansion agent and thinner, which are added in mixing machine, carries out level-one stirring, and obtaining surface after level-one stirring floats
Batch mixing of fiber;Batch mixing is carried out two level stirring by second step in mixing machine, when two level stirs simultaneously with wind turbine to
It is sent into small wind in mixing machine, rerolling is obtained after two level stirring, rerolling is carried out three-level in mixing machine and stirred by third step
It mixes, is sent into strong wind into mixing machine with wind turbine simultaneously when three-level stirs, the molten thin bridge plug of type mineral fibres of acid is obtained after three-level stirring
Sealing agent.
4. a kind of leakage-stop liquid using the thin pons hematoma agent of the molten type mineral fibres of acid according to claim 1 or 2, feature
It is raw material by containing the thin pons hematoma agent 1Kg to 8Kg of the molten type mineral fibres of acid, extraordinarily thick vermiculite 0 to 4Kg, thick in every side's mud
Shell 0 is to 10Kg, middle shell 2Kg to 10Kg, thin shell 4Kg to 10Kg, cotton seed hulls 0 to 4Kg, sawdust 2Kg to 4Kg, the molten type of acid
Thick pons hematoma agent 3Kg is to 10Kg, JYW-1 0 to 2Kg in mineral fibres.
5. leakage-stop liquid according to claim 4, it is characterised in that obtain as follows:By the molten type mineral of the desired amount of acid
It is thick in the agent of fiber finer pons hematoma, extraordinarily thick vermiculite, thick shell, middle shell, thin shell, cotton seed hulls, sawdust, the molten type mineral fibres of acid
Pons hematoma agent and JYW-1 are added in the desired amount of mud after mixing, obtain leakage-stop liquid.
6. leakage-stop liquid according to claim 4 or 5, it is characterised in that the grain size of extraordinarily thick vermiculite is 4mm to 8mm, thick shell
Grain size be 4.2mm to 8mm, the grain size of middle shell is 2.5mm to 4.2mm, the grain size of thin shell is 0.1mm to 2.5mm, cottonseed
The grain size of shell is 2mm to 6mm, the grain size of sawdust is 0.1mm to 3.1mm.
7. the leakage-stop liquid according to claim 4 or 5 or described in 6, it is characterised in that thick pons hematoma agent in the molten type mineral fibres of acid
It obtains as follows:The first step, by the desired amount of lime stone, mica, asbestos, vermiculite, velveteen, acidificable fiber, unidirectional pressure
Force-closed dose, delayed expansion agent and thinner, which are added in mixing machine, carries out level-one stirring, and obtaining surface after level-one stirring floats fibre
Batch mixing of dimension;Batch mixing is carried out two level stirring by second step in mixing machine, simultaneously with wind turbine to mixed when two level stirs
It mixes and is sent into small wind in device, rerolling is obtained after two level stirring, rerolling is carried out three-level in mixing machine and stirred by third step
It mixes, is sent into strong wind into mixing machine with wind turbine simultaneously when three-level stirs, thick bridge in the molten type mineral fibres of acid is obtained after three-level stirring
Fill in sealing agent;Thick pons hematoma agent raw material contains 30 parts to 40 parts of lime stone, cloud in parts by weight in the molten type mineral fibres of the acid
20 parts to 35 parts female, 15 parts to 20 parts of asbestos, 5 parts to 15 parts of vermiculite, 2 parts to 5 parts of velveteen, 3 parts to 15 parts of acidificable fiber, list
To 3 parts to 10 parts of pressure seal agent, 1 part to 5 parts of delayed expansion agent, 0.1 part to 2 parts of thinner;Wherein:The grain size of lime stone is
2.5mm to 4.2mm, mica grain size be 2.5mm to 4.2mm, the grain size of vermiculite is 2.0mm to 4.0mm.
8. leakage-stop liquid according to claim 7, it is characterised in that the rotating speed of level-one stirring is 40rpm to 60rpm, and level-one is stirred
The time mixed is 20min to 40min;Two level stirring rotating speed be 60rpm to 100rpm, two level stirring time be 20min extremely
The wind speed of 40min, small wind are 5.5 m/s to 7.9m/s;Three-level stirring rotating speed be 80rpm to 100rpm, three-level stirring when
Between be 20min to 40min, the wind speed of strong wind is 8.0m/s to 10.7m/s.
9. the leakage-stop liquid of the molten thin pons hematoma agent of type mineral fibres of acid described in a kind of according to claim 4 or 5 or 6 or 7 or 8
Preparation method, it is characterised in that carry out as follows:By the thin pons hematoma agent of the molten type mineral fibres of the desired amount of acid, extraordinarily thick leech
Thick pons hematoma agent and JYW-1 are added in stone, thick shell, middle shell, thin shell, cotton seed hulls, sawdust, the molten type mineral fibres of acid
In the desired amount of mud after mixing, leakage-stop liquid is obtained.