CN105733074A - Automobile air pipe material and preparation method thereof - Google Patents
Automobile air pipe material and preparation method thereof Download PDFInfo
- Publication number
- CN105733074A CN105733074A CN201610171150.8A CN201610171150A CN105733074A CN 105733074 A CN105733074 A CN 105733074A CN 201610171150 A CN201610171150 A CN 201610171150A CN 105733074 A CN105733074 A CN 105733074A
- Authority
- CN
- China
- Prior art keywords
- parts
- automobile air
- air duct
- material according
- density polyethylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an automobile air pipe material, relates to the technical field of high-polymer material processing. The material is prepared from the following raw materials in parts by weight: 70-89 parts of high-density polyethylene reclaimed material, 12-25 parts of toughener, 0.3-1 part of weather resisting agent, 1-3 parts of odor adsorbent, 0.2-0.6 part of antioxidant, 1-3 parts of black color master batch and 0.5-2 parts of lubricant. The preparation method comprises the following steps: proportionally weighing the raw materials, uniformly mixing all the raw materials, adding the mixture into a double screw extruder, granulating, cooling, drying and pelleting to obtain the finished product. The automobile air pipe material has the advantages of low production cost, low odor, favorable impact resistance, favorable rigidity and favorable weather resistance.
Description
Technical field
The present invention relates to processing of high molecular material technical field, especially one automobile air duct material and system thereof
Preparation Method.
Background technology
Automobile air duct is complex-shaped large-sized structural component, it requires possess low abnormal smells from the patient, excellent high/low-temperature impact, rigidity, thermostability, environmental stress resistance, resistance to ag(e)ing and alternating hot and cold performance etc., and requirement can within-50 DEG C to 60 DEG C periods life-time service and occur without exception.High density polyethylene (HDPE) possesses these speciality, and therefore, major part automobile air duct adopts pure high-density polyethylene material to process.
At present, China produces substantial amounts of high density polyethylene (HDPE) non-returnable container material every year, such as, food, beverage, medicine, cosmetic bottle, oil drum etc. and leftover bits thereof, owing to product surface and food hygiene require very strict, this series products is almost single use, is only used for the production of other relatively low side goods after recovery;Prepared automobile air duct material as modifiied by the non-returnable container plastics of these recovery, necessarily achieve the comprehensive utilization of resource.But, have not yet to see the report adopting the high density polyethylene (HDPE) reclaimed to prepare automobile air duct material.
Summary of the invention
An object of the present invention is to provide a kind of automobile air duct material, and it is possible not only to the problem solving to recycle intractable non-returnable container plastics, and resulting materials abnormal smells from the patient is less, resistance to impact, stiff super.
In order to solve the problems referred to above, the technical solution used in the present invention is:
This automobile air duct material is prepared from by the raw material of following parts by weight: high density polyethylene (HDPE) reworked material 70 parts~89 parts, toughener 10 parts~25 parts, weather resisting agent 0.3 part~1 part, odor adsorption agent 1 part~3 parts, 0.2 part~0.6 part of antioxidant, black masterbatch 1 part~3 parts, lubricant 0.5 part~2 parts.
In technique scheme, technical scheme is it may also is that high density polyethylene (HDPE) reworked material is reworked material high-density polyethylene bottle or the bucket of recovery obtained through pulverizing cleaning, extruding pelletization more specifically.
Further, the melting means of high density polyethylene (HDPE) reworked material ranges for 0.2 gram/10 minutes~1 gram/10 minutes.
Further, toughener is one or more in ethylene propylene diene rubber, ethylene-octene copolymer, ethylene-propylene copolymer.
Further, weather resisting agent is one or more in light stabilizer 944, UV791, UV783, UV327.
Further, odor adsorption agent is one or more in activated carbon, porous silica, Woelm Alumina, porous molecular screen, activated zeolite.
Further, antioxidant is the compound that Hinered phenols antioxidant 1010 mixes with the mass ratio of 1:1 with phosphite ester kind antioxidant 168.
Further, color masterbatch be with polyethylene be carrier, carbon black concentration be the black masterbatch of 30%.
Further, lubricant is one or more in white mineral oil, Tissuemat E, calcium stearate, zinc stearate.
It is simple that the two of the purpose of the present invention are to provide a kind of production technology, and the preparation method of the automobile air duct material that efficiency is high comprises the following steps:
A, weigh each raw material according to above-mentioned percentage by weight, then by all raw material mix homogeneously;
B, the mixture obtained by step A put into double screw extruder and carry out pelletize;Wherein, setting the extruder temperature of double screw extruder as 175 DEG C~195 DEG C, main-machine screw rotating speed is 500 revs/min~600 revs/min, and feeding machine frequency is 20 hertz~25 hertz;
Finished product is obtained after C, cooling, dry, pelletizing.
Owing to have employed technique scheme, the present invention compared with prior art has the advantages that
Automobile air duct material of the present invention is prepared from by high density polyethylene (HDPE) reworked material, toughener, weather resisting agent, odor adsorption agent, antioxidant, black masterbatch and lubricant compound, production cost is low, resulting materials abnormal smells from the patient is less, and resistance to impact, rigidity and weather resistance are excellent;Wherein, adopt the reworked material of high-density polyethylene bottle or the bucket reclaimed as the main base material preparing automobile exterior air inlet, abundance, with low cost, it is possible not only to reduce environmental pollution, more can realize recycling of resource;Adopt one or more in activated carbon, porous silica, Woelm Alumina, porous molecular screen, activated zeolite as odor adsorption agent, the multi-cellular structure that these materials have can effectively adsorb toxic and harmful molecule, thus eliminating the abnormal flavour of material itself;Adopt the cooperative effect that weather resisting agent and antioxidant are composite formed, it is possible to promote the weather resistance of material, with less addition, the weather-proof requirement of automobile air duct can be met.
Detailed description of the invention
Below in conjunction with embodiment, the invention will be further described:
Embodiment 1
The present embodiment automobile air duct material is prepared from by the raw material of following parts by weight: high density polyethylene (HDPE) reworked material 89 parts, ethylene propylene diene rubber 12 parts, and light stabilizer 944 is 0.8 part, porous silica 2 parts, 0.2 part of antioxidant, black masterbatch 2.5 parts, zinc stearate 1 part.
The present embodiment high density polyethylene (HDPE) reworked material is the high-density polyethylene bottle of recovery to be passed through the melting means that pulverizing is cleaned, extruding pelletization obtains range for the reworked material of 0.2 gram/10 minutes.
The present embodiment black masterbatch be with polyethylene be carrier, carbon black concentration be the black masterbatch of 30%.
The present embodiment antioxidant is Hinered phenols antioxidant 1010 and the phosphite ester kind antioxidant 168 1:1 in mass ratio compound mixed.
The preparation method of the present embodiment automobile air duct material is:
A, weigh each raw material according to above-mentioned parts by weight, then by all raw material mix homogeneously;
B, the mixture obtained by step A put into double screw extruder and carry out pelletize;Setting the extruder temperature of double screw extruder as 190 DEG C, main-machine screw rotating speed is 580 revs/min, and feeding machine frequency is 20 hertz;
Finished product is obtained after C, cooling, dry, pelletizing.
Embodiment 2
The present embodiment automobile air duct material is prepared from by the raw material of following parts by weight: high density polyethylene (HDPE) reworked material 84 parts, ethylene-propylene copolymer 18 parts, and UV327 is 0.5 part, Woelm Alumina 1 part, 0.3 part of antioxidant, black masterbatch 3 parts, calcium stearate 2 parts.
The present embodiment high density polyethylene (HDPE) reworked material is the high-density polyethylene drum of recovery to be passed through the melting means that pulverizing is cleaned, extruding pelletization obtains range for the reworked material of 1 gram/10 minutes.
The present embodiment black masterbatch be with polyethylene be carrier, carbon black concentration be the black masterbatch of 30%.
The present embodiment antioxidant is Hinered phenols antioxidant 1010 and the phosphite ester kind antioxidant 168 1:1 in mass ratio compound mixed.
The preparation method of the present embodiment automobile air duct material is:
A, weigh each raw material according to above-mentioned parts by weight, then by all raw material mix homogeneously;
B, the mixture obtained by step A put into double screw extruder and carry out pelletize;Setting the extruder temperature of double screw extruder as 175 DEG C, main-machine screw rotating speed is 520 revs/min, and feeding machine frequency is 25 hertz;
Finished product is obtained after C, cooling, dry, pelletizing.
Embodiment 3
The present embodiment automobile air duct material is prepared from by the raw material of following parts by weight: high density polyethylene (HDPE) reworked material 80 parts, ethylene-octene copolymer 20 parts, and UV791 is 0.3 part, porous molecular screen 3 parts, 0.5 part of antioxidant, black masterbatch 2 parts, calcium stearate 1.5 parts.
The present embodiment high density polyethylene (HDPE) reworked material is the high-density polyethylene bottle of recovery to be passed through the melting means that pulverizing is cleaned, extruding pelletization obtains range for the reworked material of 0.5 gram/10 minutes.
The present embodiment black masterbatch be with polyethylene be carrier, carbon black concentration be the black masterbatch of 30%.
The present embodiment antioxidant is Hinered phenols antioxidant 1010 and the phosphite ester kind antioxidant 168 1:1 in mass ratio compound mixed.
The preparation method of the present embodiment automobile air duct material is:
A, weigh each raw material according to above-mentioned parts by weight, then by all raw material mix homogeneously;
B, the mixture obtained by step A put into double screw extruder and carry out pelletize;Setting the extruder temperature of double screw extruder as 180 DEG C, main-machine screw rotating speed is 600 revs/min, and feeding machine frequency is 22 hertz;
Finished product is obtained after C, cooling, dry, pelletizing.
Embodiment 4
The present embodiment automobile air duct material is prepared from by the raw material of following parts by weight: high density polyethylene (HDPE) reworked material 75 parts, ethylene-octene copolymer 22 parts, and UV783 is 1 part, activated carbon 1.5 parts, 0.6 part of antioxidant, black masterbatch 1.5 parts, Tissuemat E 0.5 part.
The present embodiment high density polyethylene (HDPE) reworked material is the high-density polyethylene bottle of recovery to be passed through the melting means that pulverizing is cleaned, extruding pelletization obtains range for the reworked material of 0.8 gram/10 minutes.
The present embodiment black masterbatch be with polyethylene be carrier, carbon black concentration be the black masterbatch of 30%.
The present embodiment antioxidant is Hinered phenols antioxidant 1010 and the phosphite ester kind antioxidant 168 1:1 in mass ratio compound mixed.
The preparation method of the present embodiment automobile air duct material is:
A, weigh each raw material according to above-mentioned parts by weight, then by all raw material mix homogeneously;
B, the mixture obtained by step A put into double screw extruder and carry out pelletize;Setting the extruder temperature of double screw extruder as 195 DEG C, main-machine screw rotating speed is 550 revs/min, and feeding machine frequency is 25 hertz;
Finished product is obtained after C, cooling, dry, pelletizing.
Embodiment 5
The present embodiment automobile air duct material is prepared from by the raw material of following parts by weight: high density polyethylene (HDPE) reworked material 70 parts, ethylene propylene diene rubber 25 parts, and UV791 is 0.6 part, activated zeolite 2.5 parts, 0.4 part of antioxidant, black masterbatch 1 part, white mineral oil 1 part.
The present embodiment high density polyethylene (HDPE) reworked material is the high-density polyethylene bottle of recovery to be passed through the melting means that pulverizing is cleaned, extruding pelletization obtains range for the reworked material of 1 gram/10 minutes.
The present embodiment black masterbatch be with polyethylene be carrier, carbon black concentration be the black masterbatch of 30%.
The present embodiment antioxidant is Hinered phenols antioxidant 1010 and the phosphite ester kind antioxidant 168 1:1 in mass ratio compound mixed.
The preparation method of the present embodiment automobile air duct material is:
A, weigh each raw material according to above-mentioned parts by weight, then by all raw material mix homogeneously;
B, the mixture obtained by step A put into double screw extruder and carry out pelletize;Setting the extruder temperature of double screw extruder as 175 DEG C, main-machine screw rotating speed is 500 revs/min, and feeding machine frequency is 20 hertz;
Finished product is obtained after C, cooling, dry, pelletizing.
Being tested by the physical and chemical performance of above-described embodiment resulting materials, test result is in Table 1:
Table 1
As seen from the results in Table 1, prepared by the present invention, automobile air duct material abnormal smells from the patient is less, and resistance to impact, rigidity and ageing-resistant performance are excellent.
Claims (10)
1. an automobile air duct material, it is characterized in that including the raw material of following weight portion: high density polyethylene (HDPE) reworked material 70 parts~89 parts, toughener 12 parts~25 parts, weather resisting agent 0.3 part~1 part, odor adsorption agent 1 part~3 parts, 0.2 part~0.6 part of antioxidant, black masterbatch 1 part~3 parts, lubricant 0.5 part~2 parts.
2. automobile air duct material according to claim 1, it is characterised in that described high density polyethylene (HDPE) reworked material is the reworked material obtained through pulverizing cleaning, extruding pelletization by the high density polyethylene (HDPE) non-returnable container material of recovery.
3. automobile air duct material according to claim 2, it is characterised in that: the melting means of described high density polyethylene (HDPE) reworked material ranges for 0.2 gram/10 minutes~1 gram/10 minutes.
4. automobile air duct material according to claim 1, it is characterised in that: described toughener is one or more in ethylene propylene diene rubber, ethylene-octene copolymer, ethylene-propylene copolymer.
5. automobile air duct material according to claim 1, it is characterised in that: described weather resisting agent is one or more in light stabilizer 944, UV791, UV783, UV327.
6. automobile air duct material according to claim 1, it is characterised in that: described odor adsorption agent is one or more in activated carbon, porous silica, Woelm Alumina, porous molecular screen, activated zeolite.
7. automobile air duct material according to claim 1, it is characterised in that: described antioxidant is the compound that Hinered phenols antioxidant 1010 mixes with the mass ratio of 1:1 with phosphite ester kind antioxidant 168.
8. automobile air duct material according to claim 1, it is characterised in that: described color masterbatch be with polyethylene be carrier, carbon black concentration be the black masterbatch of 30%.
9. automobile air duct material according to claim 1, it is characterised in that: described lubricant is one or more in white mineral oil, Tissuemat E, calcium stearate, zinc stearate.
10. the preparation method of the automobile air duct material as described in claim 1 or 2 or 3 or 4 or 5 or 6 or 7 or 8 or 9, it is characterised in that comprise the following steps:
A, weigh each raw material according to above-mentioned percentage by weight, then by all raw material mix homogeneously;
B, the mixture obtained by step A put into double screw extruder and carry out pelletize;Wherein, setting the extruder temperature of double screw extruder as 175 DEG C~195 DEG C, main-machine screw rotating speed is 500 revs/min~600 revs/min, and feeding machine frequency is 20 hertz~25 hertz;
Finished product is obtained after C, cooling, dry, pelletizing.