CN105733040A - Automotive high-temperature-resistant rubber - Google Patents
Automotive high-temperature-resistant rubber Download PDFInfo
- Publication number
- CN105733040A CN105733040A CN201610272335.8A CN201610272335A CN105733040A CN 105733040 A CN105733040 A CN 105733040A CN 201610272335 A CN201610272335 A CN 201610272335A CN 105733040 A CN105733040 A CN 105733040A
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber
- temperature
- zinc oxide
- stearic acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Automotive high-temperature-resistant rubber is prepared from, by weight, 80-90 parts of natural rubber, 30-50 parts of silicone rubber, 25-35 parts of butadiene rubber, 10-25 parts of butadiene-acrylonitrile rubber, 20-35 parts of fluororubber, 20-30 parts of ethylene propylene diene monomer, 5-15 parts of aromatic oil, 2-5 parts of stearic acid, 5-6 parts of coupling agent, 4-10 parts of stearic acid, 2-7 parts of zinc oxide, 1-5 parts of nanosilicon dioxide, 1-5 parts of anti-ageing agent, 0.5-5 parts of accelerator, 0.5-3 parts of high-aluminum powder, 10-15 parts of highly-high-temperature-resistant carbon black, 10-15 parts of silica powder, 2-3 parts of sulphur, 0.8-1.5 parts of accelerant, 3-5 parts of zinc oxide, 3-5 parts of anti-ageing agent and 5-10 parts of silane coupling agent. Through the prepared high-temperature-resistant rubber, a quite good high-temperature-resistant effect can be achieved, and meanwhile the rubber has quite good high temperature resistance and heat resistance.
Description
Technical field
The present invention relates to high-temperature resistant rubber production field, a kind of new and effective automobile-used resistance to
Super heated rubber and production method.
Background technology
Rubber industry is one of important foundation industry of national economy.It not only provides day for people
The light industry rubber product such as daily, medical that often life is indispensable, and to digging, traffic,
The heavy industry such as building, machinery, electronics and new industry provide various rubber systems to produce equipment or rubber
Glue component.Visible, the product category of rubber industry is various, and backward industry is the most wide.
In prior art, it is used for manufacturing automobile rubber, generally selects natural rubber, due to sky
So reason of rubber self chemical constitution, its resistance to oxidation decay resistance is poor, thus have impact on
Automobile Rubber Products physical and mechanical properties and service life.Accordingly, it would be desirable at the base of prior art
On plinth, existing elastomeric material is made improvements, improve its oxidation resistent susceptibility, thus improve automobile
The service life of rubber.The rubber that heat-resisting quantity is good, the anti-ageing property of excellent heat resistance, oxytolerant is good
Glue is devoted to the pursuit to rubber always, and the production method of current rubber is a lot, makes rubber production
Reduce cost, improve performance, simplification operation, the focus being to study will be continued.
Summary of the invention
The technical problem that present invention mainly solves be to provide a kind of vehicle high-temperature resistant rubber and
Preparation method.
The present invention solves that the technical scheme that above-mentioned technical problem uses is:
A kind of vehicle high-temperature resistant rubber, by weight component is: natural rubber 80-90 part,
Silicone rubber 30-50 part, butadiene rubber 25-35 part, nitrile rubber 10-25 part, fluorubber
20-35 part, ethylene propylene diene rubber 20-30 part, CSM 40-45 part, chlorine
Hydrin rubber 30-35 part, thiorubber. 25-45 part, aromatic naphtha 5-15 part, stearic acid 2-5
Part, coupling agent 5-6 part, stearic acid 4-10 part, zinc oxide 2-7 part, nano silicon
1-5 part, age resistor 1-5 part, accelerator 0.5-5 part, high-alumina fly 0.5-3 part, Gao Naigao
Temperature carbon black 10-15 part, silicon powder 10-15 part, sulfur 2-3 part, accelerator 0.8-1.5 part,
Zinc oxide 3-5 part, age resistor 3-5 part, silane coupler 5-10 part, zinc oxide 4-5 part,
Stearic acid 1.8 parts, accelerator 2-2.5 part, white carbon black 15-35 part, age resistor 5-6 part,
Paraffin 3-4 part, dithio-bis-benzothiazole 2-10 part, fire retardant 3-5 part, Magnaglo
5-20 part, carborundum 5-9 part, diadust 6-8 part.
Further, described age resistor is 2,2,4-trimethyls 1,2-dihydro quinoline polymer.
Further, the preparation method of described high-temperature resistant rubber is as follows:
A. by natural rubber, silicone rubber, butadiene rubber, nitrile rubber, fluorubber, ternary second
Third rubber puts into the 5-8min that plasticates in banbury, makes temperature reach 90-100 DEG C, continuously adds
Aromatic naphtha, stearic acid, coupling agent, carry out mixing, cools down after mixing 20-25min,
Obtain premixing glue;
B. the premixing glue obtained in step a is added in mill, at a temperature of 60-80 DEG C
Stearic acid, zinc oxide, nano silicon, age resistor, promotion is added after mill 8-10min
Agent, high-alumina fly, high high temperature resistant carbon black, silicon powder, sulfur, accelerator, zinc oxide, anti-old
Agent, silane coupler, zinc oxide, stearic acid, accelerator, white carbon black, age resistor, paraffin,
Dithio-bis-benzothiazole, fire retardant, Magnaglo, carborundum, diadust, continue
Mill, binder removal when temperature is raised to 140-160 DEG C, room temperature is placed 10-12h, is obtained epoxy glue
Body;
C. by colloid mixture in two-roll mill mixing, and add sulfur, mixing uniformly after give
Enter double screw extruder hopper, carry out extruding pelletization;
D. putting in vulcanizing press by the rubber grain obtained, controlling curing temperature is
145-155 DEG C, control sulfide stress is 10-14MPa, and control cure time is 20-30min,
In calorstat, place 30-40h after sulfuration, to obtain final product.
The invention have the benefit that
By by natural rubber, silicone rubber, butadiene rubber, nitrile rubber, fluorubber, ternary
EP rubbers, CSM, chlorohydrin rubber, the mixed smelting of thiorubber. are logical
Cross the characteristic between each rubber complementary, the natural of each rubber can be avoided to lack with high degree
Fall into, comprehensive and give full play to good characteristics and the performance that each rubber has, each rubber this
Body also possesses extraordinary heat-resisting quantity, makes premixing glue have an excellent heat-resisting quantity, oil resistivity,
Oxidative resistance, anti-aging.
By adding stearic acid, zinc oxide, nano silicon, age resistor, accelerator, height
Aluminium powder, high high temperature resistant carbon black, silicon powder, sulfur, accelerator, zinc oxide, age resistor, silicon
Alkane coupling agent, zinc oxide, stearic acid, accelerator, white carbon black, age resistor, paraffin, dithio
Bisbenzothiazole, fire retardant, Magnaglo, carborundum, diadust, it is ensured that pre-
The heat-resisting quantity of premixing glue is further enhanced in the performance that mixed glue is excellent.
By stearic acid, zinc oxide, nano silicon, age resistor, accelerator, high-alumina fly,
High high temperature resistant carbon black, silicon powder, sulfur, accelerator, zinc oxide, the addition of age resistor, can
To promote non-oxidizability and the intensity of rubber, coordinate dithio-bis-benzothiazole, fire retardant etc.,
Can further promote the heat-resisting quantity of rubber itself and corrosion-resistant, wearability.
The high-temperature resistant rubber prepared by the present invention, not only cost is relatively low, and fabrication cycle is short, and
And the high-temperature resistant rubber yields that obtains is high, service life is long.
The high-temperature resistant rubber prepared by the present invention, can obtain extraordinary high-temperature resistant result,
The heat-resisting quantity of rubber, thermostability also have the best performance simultaneously.
Detailed description of the invention
Below in conjunction with detailed description of the invention, the invention will be further described.
Embodiment 1:
Component by weight takes: natural rubber 80 parts, 30 parts of silicone rubber, butadiene rubber 25
Part, nitrile rubber 10 parts, fluorubber 20 parts, ethylene propylene diene rubber 20 parts, aromatic naphtha 5
Part, stearic acid 2 parts, coupling agent 5 parts, stearic acid 4 parts, zinc oxide 2 parts, nano-silica
SiClx 1 part, 1 part of age resistor, accelerator 0.5 part, high-alumina fly 0.5 part, high high temperature resistant carbon
Black 10 parts, silicon powder 10 parts, 2 parts of sulfur, accelerator 0.8 part, zinc oxide 3 parts, anti-
Old agent 3 parts, silane coupler 5 parts, zinc oxide 4 parts, stearic acid 1.8 parts, accelerator 2
Part, white carbon black 15 parts, 5 parts of age resistor, 3 parts of paraffin, dithio-bis-benzothiazole 2 parts,
Fire retardant 3 parts, Magnaglo 5 parts, carborundum 5 parts, diadust 6 parts.
Age resistor is 2,2,4-trimethyls 1,2-dihydro quinoline polymer.
The step preparing high-temperature resistant rubber is as follows:
A. by natural rubber, silicone rubber, butadiene rubber, nitrile rubber, fluorubber, ternary second
Third rubber puts into the 5-8min that plasticates in banbury, makes temperature reach 90-100 DEG C, continuously adds
Aromatic naphtha, stearic acid, coupling agent, carry out mixing, cools down after mixing 20-25min,
Obtain premixing glue;
B. the premixing glue obtained in step a is added in mill, at a temperature of 60-80 DEG C
Stearic acid, zinc oxide, nano silicon, age resistor, promotion is added after mill 8-10min
Agent, high-alumina fly, high high temperature resistant carbon black, silicon powder, sulfur, accelerator, zinc oxide, anti-old
Agent, silane coupler, zinc oxide, stearic acid, accelerator, white carbon black, age resistor, paraffin,
Dithio-bis-benzothiazole, fire retardant, Magnaglo, carborundum, diadust, continue
Mill, binder removal when temperature is raised to 140-160 DEG C, room temperature is placed 10-12h, is obtained epoxy glue
Body;
C. by colloid mixture in two-roll mill mixing, and add sulfur, mixing uniformly after give
Enter double screw extruder hopper, carry out extruding pelletization;
D. putting in vulcanizing press by the rubber grain obtained, controlling curing temperature is
145-155 DEG C, control sulfide stress is 10-14MPa, and control cure time is 20-30min,
In calorstat, place 30-40h after sulfuration, to obtain final product.
Embodiment 2:
Component by weight takes: natural rubber 90 parts, 50 parts of silicone rubber, butadiene rubber 35
Part, nitrile rubber 25 parts, fluorubber 35 parts, ethylene propylene diene rubber 30 parts, aromatic naphtha 15
Part, stearic acid 5 parts, coupling agent 6 parts, stearic acid 10 parts, zinc oxide 7 parts, nanometer two
Silicon oxide 5 parts, 5 parts of age resistor, accelerator 5 parts, high-alumina fly 3 parts, high high temperature resistant carbon black
15 parts, silicon powder 15 parts, 3 parts of sulfur, accelerator 1.5 parts, zinc oxide 5 parts, anti-old
Agent 5 parts, silane coupler 10 parts, zinc oxide 5 parts, stearic acid 1.8 parts, accelerator 2.5
Part, white carbon black 35 parts, 6 parts of age resistor, 4 parts of paraffin, dithio-bis-benzothiazole 10 parts,
Fire retardant 5 parts, Magnaglo 20 parts, carborundum 9 parts, diadust 8 parts.
Age resistor is 2,2,4-trimethyls 1,2-dihydro quinoline polymer.
The step preparing high-temperature resistant rubber is as follows:
A. by natural rubber, silicone rubber, butadiene rubber, nitrile rubber, fluorubber, ternary second
Third rubber puts into the 5-8min that plasticates in banbury, makes temperature reach 90-100 DEG C, continuously adds
Aromatic naphtha, stearic acid, coupling agent, carry out mixing, cools down after mixing 20-25min,
Obtain premixing glue;
B. the premixing glue obtained in step a is added in mill, at a temperature of 60-80 DEG C
Stearic acid, zinc oxide, nano silicon, age resistor, promotion is added after mill 8-10min
Agent, high-alumina fly, high high temperature resistant carbon black, silicon powder, sulfur, accelerator, zinc oxide, anti-old
Agent, silane coupler, zinc oxide, stearic acid, accelerator, white carbon black, age resistor, paraffin,
Dithio-bis-benzothiazole, fire retardant, Magnaglo, carborundum, diadust, continue
Mill, binder removal when temperature is raised to 140-160 DEG C, room temperature is placed 10-12h, is obtained epoxy glue
Body;
C. by colloid mixture in two-roll mill mixing, and add sulfur, mixing uniformly after give
Enter double screw extruder hopper, carry out extruding pelletization;
D. putting in vulcanizing press by the rubber grain obtained, controlling curing temperature is
145-155 DEG C, control sulfide stress is 10-14MPa, and control cure time is 20-30min,
In calorstat, place 30-40h after sulfuration, to obtain final product.
Embodiment 3:
Natural rubber 80 parts, 50 parts of silicone rubber, butadiene rubber 25 parts, nitrile rubber 25
Part, fluorubber 20 parts, ethylene propylene diene rubber 30 parts, aromatic naphtha 5 parts, stearic acid 5 parts,
Coupling agent 5 parts, stearic acid 10 parts, zinc oxide 2 parts, nano silicon 5 parts, anti-old
Agent 1 part, accelerator 5 parts, high-alumina fly 0.5 part, high high temperature resistant carbon black 15 parts, silicon powder
10 parts, 3 parts of sulfur, accelerator 0.8 part, zinc oxide 5 parts, 3 parts of age resistor, silane
Coupling agent 10 parts, zinc oxide 4 parts, stearic acid 1.8 parts, accelerator 2 parts, white carbon black 35 parts,
5 parts of age resistor, 4 parts of paraffin, dithio-bis-benzothiazole 2 parts, fire retardant 5 parts, magnetic
5 parts of powder of property, carborundum 9 parts, diadust 6 parts.
Age resistor is 2,2,4-trimethyls 1,2-dihydro quinoline polymer.
The step preparing high-temperature resistant rubber is as follows:
A. by natural rubber, silicone rubber, butadiene rubber, nitrile rubber, fluorubber, ternary second
Third rubber puts into the 5-8min that plasticates in banbury, makes temperature reach 90-100 DEG C, continuously adds
Aromatic naphtha, stearic acid, coupling agent, carry out mixing, cools down after mixing 20-25min,
Obtain premixing glue;
B. the premixing glue obtained in step a is added in mill, at a temperature of 60-80 DEG C
Stearic acid, zinc oxide, nano silicon, age resistor, promotion is added after mill 8-10min
Agent, high-alumina fly, high high temperature resistant carbon black, silicon powder, sulfur, accelerator, zinc oxide, anti-old
Agent, silane coupler, zinc oxide, stearic acid, accelerator, white carbon black, age resistor, paraffin,
Dithio-bis-benzothiazole, fire retardant, Magnaglo, carborundum, diadust, continue
Mill, binder removal when temperature is raised to 140-160 DEG C, room temperature is placed 10-12h, is obtained epoxy glue
Body;
C. by colloid mixture in two-roll mill mixing, and add sulfur, mixing uniformly after give
Enter double screw extruder hopper, carry out extruding pelletization;
D. putting in vulcanizing press by the rubber grain obtained, controlling curing temperature is
145-155 DEG C, control sulfide stress is 10-14MPa, and control cure time is 20-30min,
In calorstat, place 30-40h after sulfuration, to obtain final product.
The high-temperature resistant rubber prepared by the present invention, not only cost is relatively low, and fabrication cycle is short, and
And the high-temperature resistant rubber yields that obtains is high, service life is long.
The high-temperature resistant rubber prepared by the present invention, can obtain extraordinary high-temperature resistant result,
The heat-resisting quantity of rubber, thermostability also have the best performance simultaneously.
Claims (3)
1. a vehicle high-temperature resistant rubber, it is characterised in that component by weight is: natural rubber
Glue 80-90 part, silicone rubber 30-50 part, butadiene rubber 25-35 part, nitrile rubber 10-25
Part, fluorubber 20-35 part, ethylene propylene diene rubber 20-30 part, CSM
40-45 part, chlorohydrin rubber 30-35 part, thiorubber. 25-45 part, aromatic naphtha 5-15 part,
Stearic acid 2-5 part, coupling agent 5-6 part, stearic acid 4-10 part, zinc oxide 2-7 part, nanometer
Silica 1-5 parts, age resistor 1-5 part, accelerator 0.5-5 part, high-alumina fly 0.5-3 part,
High high temperature resistant carbon black 10-15 part, silicon powder 10-15 part, sulfur 2-3 part, accelerator 0.8-1.5
Part, zinc oxide 3-5 part, age resistor 3-5 part, silane coupler 5-10 part, zinc oxide 4-5
Part, stearic acid 1.8 parts, accelerator 2-2.5 part, white carbon black 15-35 part, age resistor 5-6
Part, paraffin 3-4 part, dithio-bis-benzothiazole 2-10 part, fire retardant 3-5 part, magnetic
Powder 5-20 part, carborundum 5-9 part, diadust 6-8 part.
Vehicle high-temperature resistant rubber the most according to claim 1, it is characterised in that described anti-
Old agent is 2,2,4-trimethyls 1,2-dihydro quinoline polymer.
Vehicle high-temperature resistant rubber the most according to claim 1, it is characterised in that described resistance to
The preparation method of super heated rubber is as follows:
A. by natural rubber, silicone rubber, butadiene rubber, nitrile rubber, fluorubber, ternary second
Third rubber puts into the 5-8min that plasticates in banbury, makes temperature reach 90-100 DEG C, continuously adds
Aromatic naphtha, stearic acid, coupling agent, carry out mixing, cools down after mixing 20-25min,
Obtain premixing glue;
B. the premixing glue obtained in step a is added in mill, at a temperature of 60-80 DEG C
Stearic acid, zinc oxide, nano silicon, age resistor, promotion is added after mill 8-10min
Agent, high-alumina fly, high high temperature resistant carbon black, silicon powder, sulfur, accelerator, zinc oxide, anti-old
Agent, silane coupler, zinc oxide, stearic acid, accelerator, white carbon black, age resistor, paraffin,
Dithio-bis-benzothiazole, fire retardant, Magnaglo, carborundum, diadust, continue
Mill, binder removal when temperature is raised to 140-160 DEG C, room temperature is placed 10-12h, is obtained epoxy glue
Body;
C. by colloid mixture in two-roll mill mixing, and add sulfur, mixing uniformly after give
Enter double screw extruder hopper, carry out extruding pelletization;
D. putting in vulcanizing press by the rubber grain obtained, controlling curing temperature is
145-155 DEG C, control sulfide stress is 10-14MPa, and control cure time is 20-30min,
In calorstat, place 30-40h after sulfuration, to obtain final product.