CN105694706A - 一种新型除甲醛抗菌水性uv漆 - Google Patents
一种新型除甲醛抗菌水性uv漆 Download PDFInfo
- Publication number
- CN105694706A CN105694706A CN201610256053.9A CN201610256053A CN105694706A CN 105694706 A CN105694706 A CN 105694706A CN 201610256053 A CN201610256053 A CN 201610256053A CN 105694706 A CN105694706 A CN 105694706A
- Authority
- CN
- China
- Prior art keywords
- aqueous
- paint
- water
- novel formaldehyde
- removing antibiotic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种新型除甲醛抗菌水性UV漆及其制备方法,该漆由以下质量组分的原料构成:水性UV聚氨酯丙烯酸酯乳液30-60份,水性润湿分散剂5-10份,水性消泡剂0.3-0.5份,助溶剂5-10份,水性光引发剂1.5-2.5份,胺中和剂0.3-0.5份,去离子水15-20份,水性增稠剂2-3份,纳米硅粉10-40份,几丁聚糖0.5-1份;本发明具有改进涂层环保性能、抗菌、除甲醛、净化空气、增强涂膜抗划伤、高效利用、节能、绿色环保、可机械涂装作业、高生产效率的优点。
Description
技术领域
本发明属于涂料技术领域,尤其涉及一种除甲醛抗菌的水性UV漆。
背景技术
家具板材含有大量的甲醛释放空气中,甲醛是一种致癌物质,对居住在这样环境中的人身体带来严重的伤害,家具行业长期使用的油漆主要是传统溶剂型涂料,在用油漆给这些板材所做成的家具喷涂时,更会有大量的甲醛产生;并且传统溶剂型着色剂通过喷涂施工,效率低,成本高、污染环境,影响施工人员的健康;制作溶剂型涂料原料中含有大量易燃有机挥发物溶剂如甲苯、丙酮、醋酸乙酯固化剂等易燃易爆危险品,溶剂型涂料成膜后的产品也不具有防火阻燃效果,遇火花极易燃烧造成火灾危害。
水性UV油漆因其不含有机溶剂、无VOC挥发,不会对空气和操作工人带来危害受到人们喜爱,但水性UV漆的技术含量较高,生产困难较大,且涂膜表面表现出来的效果略差于PU面漆产品;
随着人们对良好居住氛围的重视,除了环保利于身心健康的要求之外,同时还对油漆的涂抹效果、抗菌杀菌作用均要求越来越高,尤其对有小孩子的家庭,如何保证油漆环保性能的同时又具有良好的杀菌性能,是水性UV漆中急需解决的问题。
发明内容
为了解决上述问题,本发明提供了一种绿色环保,涂装效果好,具有抗菌除甲醛效果的水性UV漆;本发明是通过以下技术方案实现的:
一种新型除甲醛抗菌水性UV漆,由以下质量组分的原料构成:水性UV聚氨酯丙烯酸酯乳液30-60份,水性润湿分散剂5-10份,水性消泡剂0.3-0.5份,助溶剂5-10份,水性光引发剂1.5-2.5份,胺中和剂0.3-0.5份,去离子水15-20份,水性增稠剂2-3份,纳米硅粉10-40份,几丁聚糖0.5-1份;
所述纳米硅粉为直径小于5纳米的晶体硅颗粒,纳米硅粉具有纯度高,粒径小,分布均匀等特点,表面积大,高表面活性,松装密度低,无毒,无味,活性好,具有独特的光催化作用和自洁功能,可防霉杀菌,净化空气;
所述几丁聚糖为阳离子聚合物,化学稳定性好,约185℃分解,加入到本系列的水性UV漆中,能够与聚氨酯相结合形成薄膜封闭甲醛,本身无毒还可以吸附甲醛等有毒物质,而且对于重金属如镉、汞、铅等也具有良好的吸收作用。
作为优选,所述水性UV聚氨酯丙烯酸酯乳液为美国氰特化工产品,固含量为40%,外观乳状透明液体,分子量为5500道尔顿具有;有卓越的附着力、木材的润湿性佳、低粘度的特点,可机械循环涂装施工、光固化前可乳化、漆膜柔韧性好。
作为优选,所述水性润湿分散剂为迪高Dispers760w;用于水性印刷油墨和涂料体系的润湿分散剂,35%活性含量的含高颜料亲和基团聚合物和表面活性物的水溶液,呈透明到轻微浑浊液体;适用用于水性配方,能够强烈降低研磨粘度;而且具有优异的着色力。
作为优选,所述水性消泡剂为迪高Foamex3062;用于水性体系的消泡剂,轻微浑浊液体;为聚醚硅氧烷共聚物,含气相二氧化硅,在研磨阶段消泡效果优异。
作为优选,所述水性助溶剂为丙二醇甲醚醋酸酯;是性能优良的低毒高级工业溶剂,分子量132.16,透明液体,对极性和非极性的物质均有很强的溶解能力,挥发性慢,还可以提高漆膜的流平性、光泽和丰满度。
作为优选,所述水性光引发剂为汽巴化学819DW;为白色或浅黄色分散液,用于不饱和树脂体系的高效自由基聚合光引发剂,它尤其适用于UV水性聚氨酯分散体系的固化,同时还可用于UV水性聚氨酯分散体的日光固化体系和UV水性的厚涂层固化体系。
作为优选,所述水性胺中和剂为台湾德谦化学MA-95;具有低气味和低挥发性特点,有效调节体系PH值,并赋予体系很好的PH值稳定性;同时有良好的助颜料分散性,可促进漆膜光泽的展现及遮盖力的提高;并且有效提高漆液冻融稳定性及罐内防腐蚀性能。
作为优选,所述水性增稠剂为科宁化学3551;为超强非离子缔合型增稠剂,不含有机溶剂,使适用于聚氨酯树脂体系中,还可以改善涂料的施工和贮存性能。
一种新型除甲醛抗菌水性UV漆的制备方法,包括以下步骤:
(1)按照以下质量组分称取原料:水性UV聚氨酯丙烯酸酯乳液30-60份,水性润湿分散剂5-10份,水性消泡剂0.3-0.5份,助溶剂5-10份,水性光引发剂1.5-2.5份,胺中和剂0.3-0.5份,去离子水15-20份,水性增稠剂2-3份,纳米硅粉10-40份,几丁聚糖0.5-1份;
(2)先将助溶剂丙二醇甲醚醋酸酯加入容器中,再缓慢加入819DW光引发剂,继续加入水性760W分散剂和水性消泡剂Foamex3062,滴入MA-9,稀释搅拌均匀;再缓慢滴入水性聚氨酯丙烯酸酯,以500r/min的转速在容器中搅拌,搅拌均匀后加入去离子水和增稠剂稀释搅拌,接下来缓慢滴入几丁聚糖,搅拌30分钟;再缓慢加入纳米硅粉,以800r/min搅拌40分钟后,再进行研磨至细度达到25um以下,即得到一种新型除甲醛抗菌水性UV漆;
(3)加入完后控制转速800r/min分散30分钟、检测漆液粒径细度≤25um,漆液粘度:旋转粘度计4#针测试粘度为:600±100maps/25℃;乳液紫外线光固化能量:波长280-450nm,固化能量为250-350mj/cm2。
本发明的有益效果在于:该水性UV漆可以有效吸收家具本身所释放的甲醛,并且对于空气中的甲醛及重金属离子也有良好的吸收作用,净化效率高、效果持久;可以有效地杀死空气中的霉菌和其他细菌,具有改进涂层环保抗菌、净化空气的作用;另一方面可采用辊涂、淋涂、喷涂、擦涂多种涂装方式,形成的涂膜抗划伤里强,附着力好,光泽性好,可机械涂装循环涂装作业、提高企业生产效率,同时避免有机挥发物对大气的污染和影响人体的健康。。
具体实施方式
下面结合具体实施例,对本发明做详细说明。
实施例1
(1)按照以下质量组分共称取原料100kg;其中:水性UV聚氨酯丙烯酸酯乳液35kg,水性润湿分散剂5kg,水性消泡剂0.4kg,助溶剂5.6kg,水性光引发剂2kg,胺中和剂0.5kg,去离子水18kg,水性增稠剂3kg,纳米粉30kg,几丁聚糖0.5kg;
(2)先将助溶剂丙二醇甲醚醋酸酯加入容器中,再缓慢加入819DW光引发剂,继续加入水性760W分散剂,水性消泡剂Foamex3062,滴入MA-9,将以上原料先搅拌均匀;再缓慢滴入水性聚氨酯丙烯酸酯,以500r/min的转速在容器中搅拌,搅拌均匀后加入去离子水和增稠剂稀释搅拌,接下来缓慢滴入几丁聚糖,搅拌30分钟;再缓慢加入纳米硅粉,以800r/min搅拌40分钟后,再进行研磨至细度达到25um以下,即得到一种新型除甲醛抗菌水性UV漆;
(3)加入完后控制转速800r/min分散30分钟,检测漆液粒径细度≤25um,漆液粘度:旋转粘度计4#针测试粘度为600±100maps/25℃;乳液紫外线光固化能量:波长280-450nm,固化能量为250-350mj/cm2。
实施例2
(1)按照以下质量组分共称取原料100kg;其中:水性UV聚氨酯丙烯酸酯乳液50kg,水性润湿分散剂7kg,水性消泡剂0.5kg,助溶剂7kg,水性光引发剂1.6kg,胺中和剂0.4kg,去离子水15kg,水性增稠剂2kg,纳米粉15kg,几丁聚糖0.5kg;
(2)先将助溶剂丙二醇甲醚醋酸酯加入容器中,再缓慢加入819DW光引发剂,继续加入水性760W分散剂,水性消泡剂Foamex3062,滴入MA-9,将以上原料先搅拌均匀;再缓慢滴入水性聚氨酯丙烯酸酯,以500r/min的转速在容器中搅拌,搅拌均匀后加入去离子水和增稠剂稀释搅拌,接下来缓慢滴入几丁聚糖,搅拌30分钟;再缓慢加入纳米硅粉,以800r/min搅拌40分钟后,再进行研磨至细度达到25um以下,即得到一种新型除甲醛抗菌水性UV漆;
(3)加入完后控制转速800r/min分散30分钟,检测漆液粒径细度≤25um,漆液粘度:旋转粘度计4#针测试粘度为600±100maps/25℃;乳液紫外线光固化能量:波长280-450nm,固化能量为250-350mj/cm2。
通过实施例1和实施例2制备得到的新型除甲醛抗菌水性UV漆,进行夹板铁木皮素板实验辊涂涂装工艺,工序如下表:
序号 | 工序 | 说明 |
1 | 基材除尘 | 砂纸:180# |
2 | 水性UV着色剂辊涂着色 | IR红外干燥60℃15m/min |
3 | 紫外线光固化 | 固化能量:≥260mj/cm |
4 | 辊涂水性UV透明腻子底漆 | 涂布量:30g/m2 |
5 | 汞灯半灯半固化 | 固化能量:≥60mj/cm 免砂光 |
6 | 辊涂水性UV透明底漆 | 涂布量:15g/m2 |
7 | 汞灯1灯固化 | 固化能量:≥120mj/cm 240#砂纸砂光 |
8 | 辊涂水性UV透明底漆 | 涂布量:15g/m2 |
9 | 汞灯半灯固化 | 固化能量:≥60mj/cm 免砂光 |
10 | 辊涂水性除甲醛抗菌水性UV漆 | 涂布量:15g/m2 |
11 | 汞灯2灯全固化 | 固化能量:≥200mj/cm |
以上辊涂涂装后送国家检测甲醛实验做以下除甲醛测试:
(1)除菌特点:该漆可以有效地分解空气中及家具本身所释放的甲醛,净化效率高、效果持久;经过国家建筑材料测试中心检测:净化效率达92.8%,净化持久效果达到88.0%;该漆可以有效地杀死空气中的霉菌和其他细菌,经过国家建筑材料测试中心检测:抗菌效果能达到99.9%以上;
(2)技术创新:通过反复的调配和测试,终于率先取得行业突破,该涂料在光照作用下可催化甲醛发生分解反应,生成无公害的二氧化碳和水,真正的绿色环保;涂料中含有杀菌作用的纳米材料,能持久抗菌。
应当理解的是,对本领域普通技术人员来说,可以根据上述说明加以改进或变换,而所有这些改进和变换都应属于本发明所附权利要求的保护范围。
Claims (10)
1.一种新型除甲醛抗菌水性UV漆,由以下质量组分的原料构成:
水性UV聚氨酯丙烯酸酯乳液30-60份,水性润湿分散剂5-10份,水性消泡剂0.3-0.5份,助溶剂5-10份,水性光引发剂1.5-2.5份,胺中和剂0.3-0.5份,去离子水15-20份,水性增稠剂2-3份,纳米硅粉10-40份,几丁聚糖0.5-1份。
2.如权利要求1所述的新型除甲醛抗菌水性UV漆,其特征在于,所述水性UV聚氨酯丙烯酸酯乳液为美国氰特化工产品,固含量为40%,外观乳状透明液体,分子量为5500道尔顿。
3.如权利要求1所述的新型除甲醛抗菌水性UV漆,其特征在于,所述水性润湿分散剂为迪高Dispers760w。
4.如权利要求1所述的新型除甲醛抗菌水性UV漆,其特征在于,所述水性消泡剂为迪高Foamex3062。
5.如权利要求1所述的新型除甲醛抗菌水性UV漆,其特征在于,所述水性助溶剂为丙二醇甲醚醋酸酯。
6.如权利要求1所述的新型除甲醛抗菌水性UV漆,其特征在于,所述水性光引发剂为汽巴化学819DW。
7.如权利要求1所述的新型除甲醛抗菌水性UV漆,其特征在于,所述水性胺中和剂为台湾德谦化学MA-95。
8.如权利要求1所述的新型除甲醛抗菌水性UV漆,其特征在于,所述去离子水为纯净水去离子后得到。
9.如权利要求1所述的新型除甲醛抗菌水性UV漆,其特征在于,水性增稠剂为科宁化学3551。
10.一种新型除甲醛抗菌水性UV漆的制备方法,其特征在于,包括以下步骤:
(1)按照以下质量组分称取原料:水性UV聚氨酯丙烯酸酯乳液30-60份,水性润湿分散剂5-10份,水性消泡剂0.3-0.5份,助溶剂5-10份,水性光引发剂1.5-2.5份,胺中和剂0.3-0.5份,去离子水15-20份,水性增稠剂2-3份,纳米硅粉10-40份,几丁聚糖0.5-1份;
(2)先将助溶剂丙二醇甲醚醋酸酯加入容器中,再缓慢加入819DW光引发剂,继续加入水性760W分散剂和水性消泡剂Foamex3062,滴入MA-9,稀释搅拌均匀;再缓慢滴入水性聚氨酯丙烯酸酯,以500r/min的转速在容器中搅拌,搅拌均匀后加入去离子水和增稠剂稀释搅拌,接下来缓慢滴入几丁聚糖,搅拌30分钟;再缓慢加入纳米硅粉,以800r/min搅拌40分钟后,再进行研磨至细度达到25um以下,即得到一种新型除甲醛抗菌水性UV漆;
(3)加入完后控制转速800r/min分散30分钟、检测漆液粒径细度≤25um,漆液粘度:旋转粘度计4#针测试粘度为:600±100maps/25℃;乳液紫外线光固化能量:波长280-450nm,固化能量为250-350mj/cm2。