CN105648764A - Anti-mite finishing method for silk fabrics - Google Patents
Anti-mite finishing method for silk fabrics Download PDFInfo
- Publication number
- CN105648764A CN105648764A CN201610141606.6A CN201610141606A CN105648764A CN 105648764 A CN105648764 A CN 105648764A CN 201610141606 A CN201610141606 A CN 201610141606A CN 105648764 A CN105648764 A CN 105648764A
- Authority
- CN
- China
- Prior art keywords
- parts
- aqueous solution
- mite
- fabrics
- silk
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an anti-mite finishing method for silk fabrics. The anti-mite finishing method includes steps of adding finishing agents into water to prepare aqueous solution; spraying the aqueous solution on the surfaces of the fabrics by the aid of high-pressure spraying processes; drying the fabrics. The finishing agents comprise, by weight, 5-6 parts of sodium alginate, 4-8 parts of trimethoxysilyl propyl methacrylate, 5-10 parts of vinyl versatate, 3-6 parts of silicon dioxide, 2-4 parts of benzyltrimethylammonium chloride, 4-8 parts of sodium citrate, 2-6 parts of potassium oxalate, 3-7 parts of didecyl dimethyl ammonium chloride, 2-6 parts of sodium xylene sulfonate, 7-11 parts of vinyl trimethoxy silane, 10-12 parts of talc powder and 15-20 parts of 2-methyl-4-isothiazolines biocide-3-ketone. The anti-mite finishing method has the advantages that the silk fabrics finished by the aid of the anti-mite finishing method are excellent in avoidance performance for dust mites, gamasid mites and chigger mites; the fabrics are safe and are free of allergy even if the fabrics are in contact with the skin surfaces of users for a long time, and accordingly comfortable family life environments can be created for people.
Description
Technical field
The invention belongs to textile technology field, be specifically related to a kind of silk fabric anti-mite method.
Background technology
Silk fabric is to be made into silkworm silk or synthetic fibers, staple fibre, short silk etc.; General name with the pure fabric knitted or be interwoven of silkworm silk or artificial silk. Through effort for many years, China strives again the leading position on silk market, the world, and silk industry becomes the pillar industry of earning foreign exchange of country, builds up more complete silk industry system, and silk product has been on sale throughout countries and regions, more than 100, the whole world.
Silk broadcloth is made up of azelon, has fabulous biocompatibility with human body, in addition smooth surface, and the friction of human body is stimulated coefficient to be minimum in each fibrid by it, is only 7.4%. Moisture adsorption and releasing are good. Fibroin fiber is enriched the hydrophilic radicals such as many amidos (-CONH), amino (-NH2), again due to its porous, it is easy to water diffusion, so it can absorb moisture in atmosphere or distribute moisture, and keeps certain moisture. Under normal temperature, it can help skin to possess certain moisture, does not make skin excessively dry; Wear in summer, sweat and the heat that human body is discharged can be distributed rapidly again, make people feel nice and cool incomparable. Silk not only has good heat dispersion, also has good warmth retention property. Its heat insulating ability has benefited from its multi-void fiber structure. In a silk fiber, there are many superfine little fibers, and these tiny fibers are made up of more tiny fiber. Therefore, the silkworm silk seeming solid actually has 38% to be above hollow, there is substantial amounts of air in these spaces, and these air prevent distributing of heat, make silk have good warmth retention property. Sound-absorbing, dust suction, fire-retardant. Real silk fabric has higher voidage, thus has good sound absorption properties with inspiratory, thus except making clothing, it may also be used for interior decoration, such as real silk carpet, tapestry, curtain, wall paper etc. Owing to silkworm silk has moisture absorption, moisture releasing performance and moisture retention, inspiratory and porous, can also adjust indoor temperature and humidity, and harmful gas, dust, microorganism can be sopped up.It addition, the thermal denaturation of cocoon fiber is little, relatively heat-resisting. It is when being heated to 100 DEG C, and only about 5��8% is brittle, and the hot variation of most of synthetic fibers than real silk big 4��5 times. The ignition temperature of silkworm silk, at 300��400 DEG C, belongs to flame retardant fibre, and the ignition temperature of synthetic fibers is at 200��260 DEG C, namely inflammable, meltable. Therefore, adopt silk fiber as the raw material of interior decoration, not only can play sound-absorbing, dust suction, insulation effect, also have and play anti-flaming function. The health care of cocoon fiber is irreplaceable, wherein contains 18 seed amino acid necessary to human body, very nearly the same with the aminoacid contained by human body skin, therefore has again the laudatory title of " Second Skin " of the mankind. Wear real silk clothes, not only can prevent ultraviolet radiation, defence harmful gas from invading and also can also the vigor of reinforcement table Skin Cell, promote the metabolism of Skin Cell, some dermatosis had good auxiliary therapeutic action simultaneously.
Cellulose contained in natural fiber in silk fabric and protein, become the nutrient source of the microorganisms such as acarid, acarid can on fabric survival and reproduction, modern study shows, acarid is to cause the various dermopathic main cause of the mankind. Acarid is a kind of very strong anaphylactogen, brings harm can to the life of people and health. Wherein the distribution of dust mite is the widest, have the greatest impact, the corpse of acarid, secretions and Excreta are all anaphylactogens, can make people that the diseases such as allergic dermatitis, asthma, bronchitis, nephritis, allergic rhinitis occur, the medium of the pathophoresiss such as acarid or antibacterial, virus, chlamydia, therefore acarid serious harm health. Along with improving constantly of people's living standard, more note the living environment self lived, in industry, expert advice uses the textile with mite-proofing and antimicrobial function, it is possible not only to press down demodicid mite, drive demodicid mite, effectively prevent the various diseases relevant with dust mite, can also be antibacterial, it is suppressed that the breeding of antibacterial, reach the purpose bettered people's living environment. But the anti-demodicid mite effect of use tradition anti-mite finishing agent is poor, has toxicity, property safe to the human body is unreliable, and durability and washability are not high. Therefore how overcoming the deficiencies in the prior art is the problem that current field of textiles needs solution badly.
Summary of the invention
To achieve these goals, the invention provides a kind of silk fabric anti-mite method.
It is an object of the invention to be achieved through the following technical solutions:
A kind of silk fabric anti-mite method, the method has following steps: first being added water by finishing agent is configured to aqueous solution, then adopts the technique of high pressure painting that aqueous solution is sprayed on fabric face, finally dries; Described finishing agent is made up of the component of following parts by weight: sodium alginate 5-6 part, methacryloxypropyl trimethoxy silane 4-8 part, tertiary ethylene carbonate 5-10 part, silicon dioxide 3-6 part, benzyltrimethylammonium chloride 2-4 part, sodium citrate 4-8 part, potassium oxalate 2-6 part, DDAC 3-7 part, sodium xylene sulfonate 2-6 part, vinyltrimethoxy silane 7-11 part, Pulvis Talci 10-12 part, MIT 15-20 part.
The preparation technology of finishing agent is common process, and those of ordinary skill in the art can skillfully grasp.
In described spraying process, the temperature of aqueous solution is 70-80 DEG C, and spray time is 5-10min.
Described drying temperature is 80-90 DEG C, and the time is 30s.
The concentration of described aqueous solution is 800-1000ppm.
The method have the advantages that silk fabric anti-mite method of the present invention, safely and effectively, the inventive method is used to arrange the silk fabric prepared, dust mite, gamasid and trombiculid are respectively provided with and good walk quickly and keep away performance, fabric and skin surface Long Term Contact, safe and non-stimulating, for the family life environment of people's Creating Comfort.
Detailed description of the invention
The following stated is only the preferred embodiments of the present invention, it is not limited to the present invention, although the present invention being described in detail with reference to previous embodiment, for a person skilled in the art, technical scheme described in foregoing embodiments still can be modified by it, or wherein portion of techniques feature carries out equivalent replacement. All within the spirit and principles in the present invention, any amendment of making, equivalent replacement, improvement etc., should be included within protection scope of the present invention.
Embodiment 1
A kind of silk fabric anti-mite method, it has following steps: first being added water by finishing agent is configured to aqueous solution, then adopts the technique of high pressure painting that aqueous solution is sprayed on fabric face, finally dries; Described finishing agent is made up of the component of following parts by weight: sodium alginate 5 parts, methacryloxypropyl trimethoxy silane 4 parts, tertiary ethylene carbonate 5 parts, silicon dioxide 3 parts, benzyltrimethylammonium chloride 2 parts, sodium citrate 4 parts, potassium oxalate 2 parts, DDAC 3 parts, sodium xylene sulfonate 2 parts, vinyltrimethoxy silane 7 parts, Pulvis Talci 10 parts, MIT 15 parts.
In described spraying process, the temperature of aqueous solution is 70-80 DEG C, and spray time is 5-10min.
Described drying temperature is 80-90 DEG C, and the time is 30s.
The concentration of described aqueous solution is 800-1000ppm.
Embodiment 2
A kind of silk fabric anti-mite method, it has following steps: first being added water by finishing agent is configured to aqueous solution, then adopts the technique of high pressure painting that aqueous solution is sprayed on fabric face, finally dries; Described finishing agent is made up of the component of following parts by weight: sodium alginate 6 parts, methacryloxypropyl trimethoxy silane 8 parts, tertiary ethylene carbonate 10 parts, silicon dioxide 6 parts, benzyltrimethylammonium chloride 4 parts, sodium citrate 8 parts, potassium oxalate 6 parts, DDAC 7 parts, sodium xylene sulfonate 6 parts, vinyltrimethoxy silane 11 parts, Pulvis Talci 12 parts, MIT 20 parts.
In described spraying process, the temperature of aqueous solution is 70-80 DEG C, and spray time is 5-10min.
Described drying temperature is 80-90 DEG C, and the time is 30s.
The concentration of described aqueous solution is 800-1000ppm.
Embodiment 3
A kind of silk fabric anti-mite method, it has following steps: first being added water by finishing agent is configured to aqueous solution, then adopts the technique of high pressure painting that aqueous solution is sprayed on fabric face, finally dries; Described finishing agent is made up of the component of following parts by weight: sodium alginate 5 parts, methacryloxypropyl trimethoxy silane 6 parts, tertiary ethylene carbonate 7 parts, silicon dioxide 5 parts, benzyltrimethylammonium chloride 3 parts, sodium citrate 6 parts, potassium oxalate 4 parts, DDAC 5 parts, sodium xylene sulfonate 4 parts, vinyltrimethoxy silane 9 parts, Pulvis Talci 11 parts, MIT 17 parts.
In described spraying process, the temperature of aqueous solution is 70-80 DEG C, and spray time is 5-10min.
Described drying temperature is 80-90 DEG C, and the time is 30s.
The concentration of described aqueous solution is 800-1000ppm.
Claims (4)
1. a silk fabric anti-mite method, it is characterised in that described method has following steps: first being added water by finishing agent is configured to aqueous solution, then adopts the technique of high pressure painting that aqueous solution is sprayed on fabric face, finally dries; Described finishing agent is made up of the component of following parts by weight: sodium alginate 5-6 part, methacryloxypropyl trimethoxy silane 4-8 part, tertiary ethylene carbonate 5-10 part, silicon dioxide 3-6 part, benzyltrimethylammonium chloride 2-4 part, sodium citrate 4-8 part, potassium oxalate 2-6 part, DDAC 3-7 part, sodium xylene sulfonate 2-6 part, vinyltrimethoxy silane 7-11 part, Pulvis Talci 10-12 part, MIT 15-20 part.
2. a kind of silk fabric anti-mite method according to claim 1, it is characterised in that in described spraying process, the temperature of aqueous solution is 70-80 DEG C, and spray time is 5-10min.
3. a kind of silk fabric anti-mite method according to claim 1, it is characterised in that described drying temperature is 80-90 DEG C, and the time is 30s.
4. a kind of silk fabric anti-mite method according to claim 1, it is characterised in that the concentration of described aqueous solution is 800-1000ppm.