CN105622028B - A kind of compound porous sewage treating material of organic-inorganic and preparation method thereof - Google Patents
A kind of compound porous sewage treating material of organic-inorganic and preparation method thereof Download PDFInfo
- Publication number
- CN105622028B CN105622028B CN201510985485.9A CN201510985485A CN105622028B CN 105622028 B CN105622028 B CN 105622028B CN 201510985485 A CN201510985485 A CN 201510985485A CN 105622028 B CN105622028 B CN 105622028B
- Authority
- CN
- China
- Prior art keywords
- parts
- weight
- sewage treating
- treating material
- inorganic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
Detection project | Embodiment 1 | Embodiment 2 | Embodiment 3 | Embodiment 4 | Embodiment 5 |
Adsorption capacity/(mg/g) | 650 | 654 | 642 | 680 | 678 |
Bending strength/(Mpa) | 33 | 35.2 | 37.5 | 35.8 | 36.2 |
Coefficient of permeability/(mm/s) | 18.5 | 18.4 | 19.5 | 18.6 | 18.7 |
Claims (1)
- A kind of 1. compound porous sewage treating material of organic-inorganic, it is characterised in that:By the raw material system for including following parts by weight Into:The parts by weight of hydraulic cementing materials 40~50,The parts by weight of aggregate 80~90,The parts by weight of macroporous absorbent resin 10~20,The parts by weight of fibrous material 2~6,The parts by weight of agriculture and forestry organic waste material 2~5,The parts by weight of clay mineral 8~10,2~3 parts of auxiliary agent;Wherein described hydraulic cementing materials is at least one of portland cement, aluminate cement, sulphate aluminium cement; Described aggregate is at least one of cobble, rubble, waste residue, and its particle diameter is 3~8mm;Described macroporous absorbent resin is D- 101 type macroporous absorbent resins, DA-201 types macroporous absorbent resin, HPD-100 types macroporous absorbent resin, H-103 type macroporous absorptions At least one of resin;Described fibrous material is wood fibre, polyvinyl chloride fibre, polyvinylidene fluoride, poly- second At least one of enol fiber;The agriculture and forestry organic waste material is bagasse, straw, corncob, at least one of peanut shell, its Draw ratio is more than 60;The clay mineral is in bentonite, montmorillonite, sepiolite, attapulgite, medical stone, natural zeolite At least one, and 20~30 μm are refined in eddy airstream refining machine;The auxiliary agent includes retardation water reducing agent, swelling agent, table From one kind in sugar calcium, calcium lignosulfonate, wooden sodium, parts by weight are 0.5~0.8 part for face activator, dispersant, wherein retardation water reducing agent; For swelling agent from one kind in calcium sulphoaluminate class, magnesia class, calcium oxide, parts by weight are 0.4~0.6 part;Surfactant For calcium stearate;For dispersant from least one of calgon, borax, sodium tripolyphosphate, parts by weight are 0.8~1.1 Part;The compound porous sewage treating material of a kind of organic-inorganic, is prepared by the following method:(1)10~20 parts by weight macroporous absorbent resins are added in retort, soaked 5~10 minutes with 95% ethanol, then use hydrogen Sodium oxide molybdena, salt acid elution 3~5 minutes are to neutral standby;(2)8~10 parts by weight clay mineral are added in high-temperature reactor after 5% salt low-kappa number, at 150~200 DEG C It is lower addition 0.3~0.5 parts by weight surfactant, 0.8~1.1 parts per weight dispersing agent be calcined 30~40 minutes it is standby;(3)By the parts by weight of hydraulic cementing materials 40~50, the parts by weight of aggregate 80~90, and the product obtained by step (1), The parts by weight of fibrous material 2~6, the parts by weight of agriculture and forestry organic waste material 2~5 are added to Rotary Type Twin-shaft Paddle Mixer, blade rotating speed For 300~400 revs/min, 8~12 revs/min of reversal rate, mix 8~10 minutes, obtain uniform mixture;(4)Step(2)The product and step of gained(3)The retardation water reducing agent of the mixture of gained and 0.5~0.8 parts by weight, 0.4~0.6 parts by weight swelling agent, 0.3~0.5 parts by weight surfactant are added to dispersing mixer, temperature control 40~ 50 DEG C, mixed 8~10 minutes with 800~1200 revs/min of Rate Dispersions, finally imported into mould, by levelling, maintenance, taken off Mould obtains the compound porous sewage treating material of organic-inorganic of bulk.