CN105595469A - Sterilization and filtration composition for anti-fog-and-haze mouth mask - Google Patents

Sterilization and filtration composition for anti-fog-and-haze mouth mask Download PDF

Info

Publication number
CN105595469A
CN105595469A CN201610030398.2A CN201610030398A CN105595469A CN 105595469 A CN105595469 A CN 105595469A CN 201610030398 A CN201610030398 A CN 201610030398A CN 105595469 A CN105595469 A CN 105595469A
Authority
CN
China
Prior art keywords
mouth mask
parts
haze mouth
haze
cotton gauze
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610030398.2A
Other languages
Chinese (zh)
Inventor
邓新平
聂雄
唐宾
傅小妮
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangxi University
Original Assignee
Guangxi University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guangxi University filed Critical Guangxi University
Priority to CN201610030398.2A priority Critical patent/CN105595469A/en
Publication of CN105595469A publication Critical patent/CN105595469A/en
Pending legal-status Critical Current

Abstract

The invention provides an anti-fog-and-haze mouth mask. A preparation method of the anti-fog-and-haze mouth mask comprises the following steps: 1, immersing activated carbon cloth and purified cotton gauze into a sterilization composition, then taking the activated carbon cloth and the purified cotton gauze out, and conducting drying for use; 2, blending a filter material composition with deionized water according to the weight ratio of 1: 10, stirring the mixture uniformly, heating the mixture to 40 DEG C, and non-woven fabric is placed in the mixture, so that the non-woven fabric is immersed in the liquid for adsorption, and taking the non-woven fabric out for drying; 3, conducting stacking according to the sequence that the non-woven fabric, the purified cotton gauze, the activated carbon cloth, the non-woven fabric and the purified cotton gauze are stacked from outside to inside; 4, conducting sewing, trimming and cutting on a mouth mask, heating the mouth mask in a drying oven, and taking the mouth mask out for cooling, so that the anti-fog-and-haze mouth mask is obtained. According to the anti-fog-and-haze mouth mask, base materials of the mouth mask are subjected to treatment with the sterilization composition, so that the mouth mask has the sterilization function, and wearing safety is improved; the sterilization composition of the anti-fog-and-haze mouth mask contains selected traditional Chinese medicine elements, the sterilization efficacy is achieved, furthermore, peculiar smell can be removed, flower and plant aroma is left, and joy in body and mind generated when a user wears the mouth mask is improved.

Description

A kind of anti-haze mouth mask disinfection filtering composition
Technical field
The present invention relates to dust control technology field, specifically a kind of anti-haze mouth mask disinfection filtering composition.
Background technology
In recent years, again and again produce haze weather in many big and medium-sized cities of China, the serious threat people's bodyBody health and lives. The mechanism that haze weather produces is very complicated, and its chemical composition is also very complicated, Ke NengyinSend out various diseases. Meanwhile, virus, germ etc. may be attached on the particle of atmosphere, spread disease.PM2.5 is the particle to harm maximum in atmosphere pollution, and this particle diameter is equal to or less than2.5 microns, be medically called pellet. Various places monitoring PM2.5 usually exceeds standard seriously.
General mouth mask cannot filter PM2.5, and dragons and fishes jumbled together for current multiple anti-haze mouth mask on the market,Also all can not effectively stop PM2.5. And blocking effect is good, mouth mask as that in N95, cost is tooHeight, and gas permeability is poor, can not use for a long time. Therefore need to develop one and there is excellent absorption propertyAnd anti-microbial property, gas permeability is better, can effectively stop the atmosphere pollutions such as PM2.5, and preparation workSkill is simple, filtering material with low cost.
The information that is disclosed in this background technology part is only intended to increase the reason to general background of the present inventionSeparate, and should not be regarded as admitting or imply that in any form this information structure has been this area general technologyThe prior art that personnel are known.
Summary of the invention
For the deficiencies in the prior art, the object of the present invention is to provide and a kind ofly can effectively filter PM2.5'sMouth mask filter material, and there is the anti-haze mouth mask bactericidal composition of sterilizing function.
Technical scheme provided by the invention is:
A kind of anti-haze mouth mask, selects active carbon cloth, cotton gauze and nonwoven as base material, its preparationMethod comprises the steps:
(1) active carbon cloth, cotton gauze are immersed in bactericidal composition, the time is 2-3h, then willIt takes out dry for standby;
(2) filter material composition and deionized water are pressed to 1:10 weight proportion, stir, heat to 40 DEG C,Insert nonwoven, it is immersed in liquid, after absorption 6h, take out dry, for subsequent use;
(3) mouth mask body is according to being respectively from outside to inside nonwoven, cotton gauze, active carbon cloth, nonwovenCloth, cotton gauze totally five layers stack in order;
(4) mouth mask is carried out sewing, prunes, cut, the 30min that heats in the baking oven of 60-80 DEG C, getsGo out coolingly, obtain described anti-haze mouth mask.
As preferably, described bactericidal composition comprises following component by weight: 30 parts of deionized waters,5 parts of wormwoods, 3 parts of pomelo peels, 2 parts of kuh-sengs, 2 parts of Tea Polyphenols, 3 parts of honeysuckles, 3 parts of lavenders,Pivot holds 3 parts of 2 parts and peppermints.
As preferably, the preparation method of described bactericidal composition, comprises the steps:
(1) wormwood, kuh-seng, honeysuckle, lavender are mixed, be placed in marmite and add pure water and do not have medicineFace, soaks 3min, and big fire renews and decocts 30min after boiling, and decocts altogether 2 times, filters, and merges and decocts for 2 timesBoil liquid, obtain solution A;
(2) pomelo peel, Tea Polyphenols, pivot are held, peppermint mixes, and adds deionized water to soak after 20min,Big fire is boiled to renew and is decocted 3min, and Guan Huo filters, and obtains solution B;
(3) step (1) gained solution A and step (2) gained solution B are mixed, obtain instituteThe bactericidal composition of stating.
As preferably, described filter material composition comprises following component by weight: NACF30-40 part, sodium carbonate 10-15 part, vitamin C 3-5 part, diatomite 5-10 part, mulberry bark extract10-15 part, luffa are concocted thing 10-15 part and Graphene 0.8-1.0 part.
As preferably, described filter material composition comprises following component by weight: NACF 38Part, 12 parts, sodium carbonate, 4 parts of vitamin Cs, 8 parts, diatomite, 10 parts of mulberry bark extracts, sponge gourd0.8 part of 10 parts of network process of preparing Chinese medicine things and Graphene.
As preferably, the specific area of described NACF is 950-1550m2/ g, micro-pore diameter is5-100A。
As preferably, the preparation method of described mulberry bark extract is: get the root bark of white mulberry clean, dry in the shade,Pulverize; Add the organic solution of equivalent, the lixiviate that refluxes in water-bath, then soak, takes out with Buchner funnelFilter, fully obtains filtrate after washing; Filtrate Vacuum Concentration is obtained to concentrate, concentrate is dry in drying boxDry, obtaining solid content is mulberry bark extract.
As preferably, the preparation method that described luffa is concocted thing is: luffa is cleaned and dried, cutBecome segment, stir to yellow degree of being with wheat bran, luffa takes out, and sieve removes wheat bran, obtains described sponge gourdNetwork is concocted thing.
As preferably, the specific area 2630m of described Graphene2/ g, fracture strength 130GPa, heat conductionCoefficient 5000W/mK.
Compared with prior art, the present invention has following beneficial effect:
(1) anti-haze mouth mask of the present invention, by the base material of mouth mask is adopted to bactericidal composition processing, makes mouthCover has sterilizing function, improves the security while wearing.
(2) in anti-haze mouth mask of the present invention, bactericidal composition includes selected traditional Chinese medicine ingredients, not only toolThere is biocidal efficacies, and can dispelling abnormal flavor, leave over flowers and plants fragrance, improve the joyful sense of body and mind while wearing.
(3) in anti-haze mouth mask of the present invention filter material composition selected multiple can increase adsorbingMaterial, makes mouth mask have better filter effect and gas permeability.
(4) anti-haze mouth mask preparation process technique of the present invention is simple, with low cost, have good canProcessability, can filter the air pollutants such as PM2.5 effectively, also can be applicable to dyestuff, greasy dirt suction simultaneouslyBe accompanied by and the field such as air filter.
Detailed description of the invention
Below in conjunction with embodiment, the specific embodiment of the present invention is described in detail, but is to be understood that thisThe protection domain of invention is not subject to the restriction of detailed description of the invention.
Unless separately there is other clearly to represent, otherwise in whole description and claims, term " bagDraw together " or its conversion element of stating being understood to include as " comprising " or " including " etc. orPart, and do not get rid of other element or other part.
Embodiment 1：
A kind of anti-haze mouth mask, selects active carbon cloth, cotton gauze and nonwoven as base material, its preparationMethod comprises the steps:
(1) active carbon cloth, cotton gauze are immersed in bactericidal composition, the time is 2h, then by itTake out dry for standby; Described bactericidal composition comprises following component by weight: 30 parts of deionized waters,5 parts of wormwoods, 3 parts of pomelo peels, 2 parts of kuh-sengs, 2 parts of Tea Polyphenols, 3 parts of honeysuckles, 3 parts of lavenders,Pivot holds 3 parts of 2 parts and peppermints; The preparation method of described bactericidal composition, comprises the steps: Chinese mugwortGrass, kuh-seng, honeysuckle, lavender mix, and are placed in marmite and add pure water and do not have powder, soak 3min,Big fire renews and decocts 30min after boiling, and decocts altogether 2 times, filters, and merges 2 times decoction liquor, obtains solution A;By pomelo peel, Tea Polyphenols, pivot hold, peppermint mixes, and adds deionized water to soak after 20min, big fire is boiledBoil to renew and decoct 3min, Guan Huo, filters, and obtains solution B; By step (1) gained solution A and step (2)Gained solution B mixes, and obtains described bactericidal composition;
(2) filter material composition and deionized water are pressed to 1:10 weight proportion, stir, heat to 40 DEG C,Insert nonwoven, it is immersed in liquid, after absorption 6h, take out dry, for subsequent use; Described filter materialComposition comprises following component by weight: 30 parts of NACFs, 10 parts, sodium carbonate, vitamin C3 parts, 5 parts, diatomite, 10 parts of mulberry bark extracts, luffa are concocted 0.8 part of 10 parts of things and Graphene;The specific area of described NACF is 1550m2/ g, micro-pore diameter is 100A; The described root bark of white mulberryThe preparation method of extract is: get the root bark of white mulberry and clean, dry in the shade, pulverize; Add the organic solution of equivalent,The lixiviate that refluxes in water-bath, then soak, uses Buchner funnel suction filtration, fully after washing filtrate; To filterLiquid Vacuum Concentration obtains concentrate, and by concentrate, at drying box inner drying, obtaining solid content is mulberry bark extract;The preparation method that described luffa is concocted thing is: luffa is cleaned and dried, be cut into segment, use wheat branStirring to yellow is to spend, and luffa takes out, and sieve removes wheat bran, obtains described luffa process of preparing Chinese medicine thing; DescribedThe specific area 2630m of Graphene2/ g, fracture strength 130GPa, thermal conductivity factor 5000W/mK;
(3) mouth mask body is according to being respectively from outside to inside nonwoven, cotton gauze, active carbon cloth, nonwovenCloth, cotton gauze totally five layers stack in order;
(4) mouth mask is carried out sewing, prunes, cut, the 30min that heats in the baking oven of 60 DEG C, takes outCooling, obtain described anti-haze mouth mask.
Embodiment 2：
A kind of anti-haze mouth mask, selects active carbon cloth, cotton gauze and nonwoven as base material, its preparationMethod comprises the steps:
(1) active carbon cloth, cotton gauze are immersed in bactericidal composition, the time is 3h, then by itTake out dry for standby; Described bactericidal composition comprises following component by weight: 30 parts of deionized waters,5 parts of wormwoods, 3 parts of pomelo peels, 2 parts of kuh-sengs, 2 parts of Tea Polyphenols, 3 parts of honeysuckles, 3 parts of lavenders,Pivot holds 3 parts of 2 parts and peppermints; The preparation method of described bactericidal composition, comprises the steps: Chinese mugwortGrass, kuh-seng, honeysuckle, lavender mix, and are placed in marmite and add pure water and do not have powder, soak 3min,Big fire renews and decocts 30min after boiling, and decocts altogether 2 times, filters, and merges 2 times decoction liquor, obtains solution A;By pomelo peel, Tea Polyphenols, pivot hold, peppermint mixes, and adds deionized water to soak after 20min, big fire is boiledBoil to renew and decoct 3min, Guan Huo, filters, and obtains solution B; By step (1) gained solution A and step (2)Gained solution B mixes, and obtains described bactericidal composition;
(2) filter material composition and deionized water are pressed to 1:10 weight proportion, stir, heat to 40 DEG C,Insert nonwoven, it is immersed in liquid, after absorption 6h, take out dry, for subsequent use; Described filter materialComposition comprises following component by weight: 40 parts of NACFs, 15 parts, sodium carbonate, vitamin C5 parts, 10 parts, diatomite, 15 parts of mulberry bark extracts, luffa are concocted 15 parts of things and Graphene 1.0Part; The specific area of described NACF is 950m2/ g, micro-pore diameter is 5A; Described Sang BaiThe preparation method of bark extract is: get the root bark of white mulberry and clean, dry in the shade, pulverize; Add the organic solution of equivalent,The lixiviate that refluxes in water-bath, then soak, uses Buchner funnel suction filtration, fully after washing filtrate; To filterLiquid Vacuum Concentration obtains concentrate, and by concentrate, at drying box inner drying, obtaining solid content is mulberry bark extract;The preparation method that described luffa is concocted thing is: luffa is cleaned and dried, be cut into segment, use wheat branStirring to yellow is to spend, and luffa takes out, and sieve removes wheat bran, obtains described luffa process of preparing Chinese medicine thing; DescribedThe specific area 2630m of Graphene2/ g, fracture strength 130GPa, thermal conductivity factor 5000W/mK;
(3) mouth mask body is according to being respectively from outside to inside nonwoven, cotton gauze, active carbon cloth, nonwovenCloth, cotton gauze totally five layers stack in order;
(4) mouth mask is carried out sewing, prunes, cut, the 30min that heats in the baking oven of 80 DEG C, takes outCooling, obtain described anti-haze mouth mask.
Embodiment 3：
A kind of anti-haze mouth mask, selects active carbon cloth, cotton gauze and nonwoven as base material, its preparationMethod comprises the steps:
(1) active carbon cloth, cotton gauze are immersed in bactericidal composition, the time is 2.5h, then willIt takes out dry for standby; Described bactericidal composition comprises following component by weight: deionized water 30Part, 5 parts of wormwoods, 3 parts of pomelo peels, 2 parts of kuh-sengs, 2 parts of Tea Polyphenols, 3 parts of honeysuckles, lavender 3Fen, pivot holds 3 parts of 2 parts and peppermints; The preparation method of described bactericidal composition, comprises the steps:Wormwood, kuh-seng, honeysuckle, lavender are mixed, be placed in marmite and add pure water and do not have powder, soak3min, big fire renews and decocts 30min after boiling, and decocts altogether 2 times, filters, and merges 2 times decoction liquor, obtains moltenLiquid A; By pomelo peel, Tea Polyphenols, pivot hold, peppermint mixes, and adds deionized water to soak after 20min,Big fire is boiled to renew and is decocted 3min, and Guan Huo filters, and obtains solution B; By step (1) gained solution A andStep (2) gained solution B mixes, and obtains described bactericidal composition;
(2) filter material composition and deionized water are pressed to 1:10 weight proportion, stir, heat to 40 DEG C,Insert nonwoven, it is immersed in liquid, after absorption 6h, take out dry, for subsequent use; Described filter materialComposition comprises following component by weight: 35 parts of NACFs, 13 parts, sodium carbonate, vitamin C4 parts, 8 parts, diatomite, 12 parts of mulberry bark extracts, luffa are concocted 0.9 part of 13 parts of things and Graphene;The specific area of described NACF is 1200m2/ g, micro-pore diameter is 50A; The described root bark of white mulberryThe preparation method of extract is: get the root bark of white mulberry and clean, dry in the shade, pulverize; Add the organic solution of equivalent,The lixiviate that refluxes in water-bath, then soak, uses Buchner funnel suction filtration, fully after washing filtrate; To filterLiquid Vacuum Concentration obtains concentrate, and by concentrate, at drying box inner drying, obtaining solid content is mulberry bark extract;The preparation method that described luffa is concocted thing is: luffa is cleaned and dried, be cut into segment, use wheat branStirring to yellow is to spend, and luffa takes out, and sieve removes wheat bran, obtains described luffa process of preparing Chinese medicine thing; DescribedThe specific area 2630m of Graphene2/ g, fracture strength 130GPa, thermal conductivity factor 5000W/mK;
(3) mouth mask body is according to being respectively from outside to inside nonwoven, cotton gauze, active carbon cloth, nonwovenCloth, cotton gauze totally five layers stack in order;
(4) mouth mask is carried out sewing, prunes, cut, the 30min that heats in the baking oven of 70 DEG C, takes outCooling, obtain described anti-haze mouth mask.
Embodiment 4: the effect measuring of anti-haze mouth mask of the present invention
For checking anti-haze mouth mask air filtration effect of the present invention, by mouth prepared above-described embodiment 1-3The rectangle of cover material cutting growth 15cm × wide 10cm, will detect the air box (green grass or young crops of air qualityAir-conditioner Co., Ltd of island Haier, KZW-A01U1) be placed in closed container, by above-mentioned mask material envelopeLive opening; Experiment, adopts common cotton cloth respirator to seal opening in contrast, then container is placed in and is full ofIn the environment of cigarette flue dust, the results are shown in Table 1.
The effect measuring of table 1 anti-haze mouth mask of the present invention
As can be seen from Table 1, air box registration in the container of anti-haze mask material sealing of the present inventionAll more than 80 (good), and in the container of common mouth mask sealing, air box registration is 39 (severe dirtsDye); After 2 hours, take out mask material of the present invention and common mouth mask and observe, mask material of the present invention is compared generalPort cover is obviously dirty, and color is obviously more black more grey.
In sum, anti-haze mouth mask of the present invention can effectively filter the air pollutants such as PM2.5.
The aforementioned description to concrete exemplary of the present invention is in order to illustrate and the object of illustration.These descriptions not want the present invention to be defined as disclosed precise forms, and obviously, according to above-mentionedInstruction, can much change and change. Exemplary embodiment is selected and the object described existsIn explaining certain principles of the present invention and practical application thereof, thereby make those skilled in the art can be realNow and utilize various exemplary of the present invention and various selection and change.Scope of the present invention is intended to be limited by claims and equivalents thereof.

Claims (9)

1. an anti-haze mouth mask, selects active carbon cloth, cotton gauze and nonwoven as base material, its spyLevy and be, its preparation method comprises the steps:
(1) active carbon cloth, cotton gauze are immersed in bactericidal composition, the time is 2-3h, then willIt takes out dry for standby;
(2) filter material composition and deionized water are pressed to 1:10 weight proportion, stir, heat to 40 DEG C,Insert nonwoven, it is immersed in liquid, after absorption 6h, take out dry, for subsequent use;
(3) mouth mask body is according to being respectively from outside to inside nonwoven, cotton gauze, active carbon cloth, nonwovenCloth, cotton gauze totally five layers stack in order;
(4) mouth mask is carried out sewing, prunes, cut, the 30min that heats in the baking oven of 60-80 DEG C, getsGo out coolingly, obtain described anti-haze mouth mask.
2. anti-haze mouth mask according to claim 1, is characterized in that described bactericidal compositionComprise by weight following component: 30 parts of deionized waters, 5 parts of wormwoods, 3 parts of pomelo peels, kuh-seng 2Part, 2 parts of Tea Polyphenols, 3 parts of honeysuckles, lavender 3 Fen, pivots hold 3 parts of 2 parts and peppermints.
3. anti-haze mouth mask according to claim 2, is characterized in that described bactericidal compositionPreparation method, comprise the steps:
(1) wormwood, kuh-seng, honeysuckle, lavender are mixed, be placed in marmite and add pure water and do not have medicineFace, soaks 3min, and big fire renews and decocts 30min after boiling, and decocts altogether 2 times, filters, and merges and decocts for 2 timesBoil liquid, obtain solution A;
(2) pomelo peel, Tea Polyphenols, pivot are held, peppermint mixes, and adds deionized water to soak after 20min,Big fire is boiled to renew and is decocted 3min, and Guan Huo filters, and obtains solution B;
(3) step (1) gained solution A and step (2) gained solution B are mixed, obtain instituteThe bactericidal composition of stating.
4. anti-haze mouth mask according to claim 1, is characterized in that, described filter material compositionComprise by weight following component: NACF 30-40 part, sodium carbonate 10-15 part, vitamin C3-5 part, diatomite 5-10 part, mulberry bark extract 10-15 part, luffa are concocted thing 10-15 part and stoneChina ink alkene 0.8-1.0 part.
5. anti-haze mouth mask according to claim 4, is characterized in that, described filter material compositionComprise by weight following component: 38 parts of NACFs, 12 parts, sodium carbonate, 4 parts of vitamin Cs,8 parts, diatomite, 10 parts of mulberry bark extracts, luffa are concocted 0.8 part of 10 parts of things and Graphene.
6. anti-haze mouth mask according to claim 4, is characterized in that described NACFSpecific area be 950-1550m2/ g, micro-pore diameter is 5-100A.
7. anti-haze mouth mask according to claim 4, is characterized in that, the described root bark of white mulberry extractsThe preparation method of thing is: get the root bark of white mulberry and clean, dry in the shade, pulverize; Add the organic solution of equivalent, at waterThe lixiviate that refluxes in bath, then soak, uses Buchner funnel suction filtration, fully after washing filtrate; Filtrate is trueThe empty concentrate that concentrates to obtain, by concentrate, at drying box inner drying, obtaining solid content is mulberry bark extract.
8. anti-haze mouth mask according to claim 4, is characterized in that, described luffa is concoctedThe preparation method of thing is: luffa cleaned and dried, be cut into segment, stir to yellow degree of being with wheat bran,Luffa takes out, and sieve removes wheat bran, obtains described luffa and concocts thing.
9. anti-haze mouth mask according to claim 4, is characterized in that, the ratio of described GrapheneSurface area 2630m2/ g, fracture strength 130GPa, thermal conductivity factor 5000W/mK.
CN201610030398.2A 2016-01-18 2016-01-18 Sterilization and filtration composition for anti-fog-and-haze mouth mask Pending CN105595469A (en)