CN105584241B - Splice the production method of opal, radium-shine embossing pattern - Google Patents
Splice the production method of opal, radium-shine embossing pattern Download PDFInfo
- Publication number
- CN105584241B CN105584241B CN201410579681.1A CN201410579681A CN105584241B CN 105584241 B CN105584241 B CN 105584241B CN 201410579681 A CN201410579681 A CN 201410579681A CN 105584241 B CN105584241 B CN 105584241B
- Authority
- CN
- China
- Prior art keywords
- splicing
- pet film
- opal
- radium
- gloss oil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
A kind of splicing opal, the production method of radium-shine embossing pattern, unwinding device including being arranged successively setting, draw pressure roller, gloss oil apparatus for coating, pressing device, solidification equipment, initiative compression roller device and wrap-up, wherein, the unwinding device will unreel PET film, it is drawn respectively through the traction pressure roller to the gloss oil apparatus for coating under initiative compression roller effect, pressing device and solidification equipment, the gloss oil apparatus for coating coats gloss oil on the PET film surface, preset pattern is pressure bonded to the PET film coated with gloss oil by the movement of the pressing device, the PET after pressing device is solidified through the solidification equipment again, it is wound by the wrap-up, its equipment is simple, operating procedure is simple, cost is relatively low.
Description
Technical field
The present invention relates to packaging material field more particularly to the production methods of a kind of splicing opal, radium-shine embossing pattern.
Background technique
With the development of science and technology, producing more and more new packaging materials.Splicing opal, radium-shine embossing pattern can be made
For a kind of novel packaging material, not only appearance luster is bright-coloured beautiful, can be also used for anti-fake, primarily as tobacco and wine, changes
The wrapping paper of cosmetic, food, drug etc. uses, and more only has the manufacturer of a capability and strength that can be produced.So
And splicing opal at present, the production method of radium-shine embossing pattern are complex, the composed pattern of higher cost, production is compound
Film folding is easy to produce crackle.
Summary of the invention
In consideration of it, it is necessary to provide a kind of relatively simple, the production of lower-cost splicing opal, radium-shine embossing pattern
Method.
A kind of production method for splicing opal, radium-shine embossing pattern, includes the following steps:
PET film is unreeled on unwinding device；
The PET film is drawn to gloss oil apparatus for coating through traction pressure roller under initiative compression roller effect；
The gloss oil apparatus for coating coats gloss oil on the PET film surface；
Preset pattern is pressure bonded on the PET film coated with gloss oil by pressing device on the move；
Solidification equipment solidifies the PET film after pressing device pressing；
It is wound by wrap-up, completes the splicing to the opal, radium-shine embossing pattern of the PET film.
In some embodiments wherein, the gloss oil of the gloss oil apparatus for coating coating is UV gloss oil.
In some embodiments wherein, the pressing device includes: guided way, moves along what the guided way moved
Bar, be sheathed in the mobile bar and can along the mobile bar splicing seat, be fixedly connected on it is described splicing seat splicing die head,
Pattern is provided on the splicing die head, can be with the support seat of the splicing die head synchronizing moving, the splicing die head and described
Support seat is set to the two sides of the PET film, and the end of the support seat is additionally provided with ultraviolet lamp.
In some embodiments wherein, the ultraviolet lamp is LED ultraviolet lamp.
In some embodiments wherein, the moving direction of the mobile bar is identical with the transmission direction of the PET film.
In some embodiments wherein, the moving direction intersection of the moving direction of the mobile bar and the splicing seat.
In some embodiments wherein, the moving direction intersection of the moving direction of the mobile bar and the splicing seat
Angle is 90 degree.
In some embodiments wherein, the solidification equipment is UV lamp.
In some embodiments wherein, the PET film is 100um.
The production method of above-mentioned splicing opal, radium-shine embossing pattern, unwinding device, traction pressure including being arranged successively setting
Roller, gloss oil apparatus for coating, pressing device, solidification equipment, initiative compression roller device and wrap-up, wherein the unwinding device will
PET film is unreeled, is drawn respectively through the traction pressure roller to the gloss oil apparatus for coating, pressing and is filled under initiative compression roller effect
It sets and solidification equipment, the gloss oil apparatus for coating coats gloss oil on the PET film surface, mobile by the pressing device will
Preset pattern is pressure bonded to the PET film coated with gloss oil, then carries out through the solidification equipment to the PET after pressing device
Solidification is wound by the wrap-up, and equipment is simple, and operating procedure is simple, and cost is relatively low.
Detailed description of the invention
Fig. 1 be splice opal, radium-shine embossing pattern production line structural schematic diagram.
Fig. 2 is the step flow chart for splicing the production method of opal, radium-shine embossing pattern.
Specific embodiment
In order to be more clear the objectives, technical solutions, and advantages of the present invention, with reference to the accompanying drawings and embodiments, to this hair
It is bright to be further elaborated.It should be appreciated that the specific embodiments described herein are merely illustrative of the present invention, and do not have to
It is of the invention in limiting.
Referring to Fig. 1, the production method 100 of embodiment splicing opal, radium-shine embossing pattern includes being arranged successively to set
Unwinding device 110, the traction pressure roller 120, gloss oil apparatus for coating 130, pressing device 140, solidification equipment 150, initiative compression roller set
Device 160 and wrap-up 170.
Wherein, unwinding device 110 is for unreeling PET film.
Traction pressure roller 120 draws the PET film that unwinding device 110 unreels.
Gloss oil apparatus for coating 130 is used to coat gloss oil on the PET film surface.Preferably, the gloss oil apparatus for coating 130
The gloss oil of coating is UV gloss oil.
Pressing device 140 is removable, for preset pattern to be pressure bonded to the PET film coated with gloss oil.It is preferred that
Ground, pressing device 140 can move in the x direction and the y direction.
Specifically, pressing device 140 includes: guided way 141, the mobile bar 142 moved along the guided way 141, is arranged
In in the mobile bar 142 and can along the mobile bar 142 splicing seat 143, be fixedly connected on it is described splicing seat 143 splicing
Die head 144, it is described splicing die head 144 on be provided with pattern, can with it is described splicing 144 synchronizing moving of die head support seat 145, institute
It states splicing die head 144 and the support seat 145 is set to the two sides of the PET film, the end (not shown) of the support seat 145
It is additionally provided with ultraviolet lamp (not shown).
It is further preferred that ultraviolet lamp is LED ultraviolet lamp.
Preferably, the moving direction of the mobile bar 143 is identical with the transmission direction of the PET film.
Preferably, the moving direction intersection of the moving direction of the mobile bar 143 and the splicing seat 144, further,
The angle of intersection is 90 degree.
Solidification equipment 150 is preferably UV lamp solidification.
Preferably, above-mentioned PET film with a thickness of 100um.
Referring to Fig. 2, production method 100 production the splicing opal, radium-shine embossment of above-mentioned splicing opal, radium-shine embossing pattern
The course of work of pattern is as follows:
Step S110: PET film is unreeled on the unwinding device 110；
Step S120: the PET film is drawn through the traction pressure roller 120 to institute under the initiative compression roller 160 effect
It states on gloss oil apparatus for coating 130；
Step S130: gloss oil apparatus for coating 130 coats gloss oil on the PET film surface, it is preferable that the gloss oil painting arranges
The gloss oil for setting 130 coatings is UV gloss oil；
Step S140: pressing device 140 is on the move for being pressure bonded to the PET coated with gloss oil for preset pattern
On film；
Step S150: PET film of 150 pairs of the solidification equipment after pressing device presses solidifies；
Step S160: winding by the wrap-up 170, completes to the opal of above-mentioned PET film, radium-shine embossing pattern
Splicing.
The production method 100 of above-mentioned splicing opal, radium-shine embossing pattern, including be arranged successively setting unwinding device 110,
Draw pressure roller 120, gloss oil apparatus for coating 130, pressing device 140, solidification equipment 150, initiative compression roller device 160 and wrap-up
170, wherein the unwinding device 110 will unreel PET film, through the traction pressure roller 120 under the initiative compression roller 160 effect
It is drawn respectively to the gloss oil apparatus for coating 130, pressing device 140 and solidification equipment 150, the gloss oil apparatus for coating 130 exists
The PET film surface coats gloss oil, and preset pattern is pressure bonded to coated with light by the movement of the pressing device 140
The PET film of oil, then solidify through 150 couples of the solidification equipment PET after pressing device 140, by the wrap-up
170 windings, complete the splicing to the opal, radium-shine embossing pattern of PET film, and equipment is simple, and operating procedure is simple, cost compared with
It is low.
The above is only a preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art
Member, various improvements and modifications may be made without departing from the principle of the present invention, these improvements and modifications also should be regarded as
Protection scope of the present invention.
Claims (8)
1. the production method of a kind of splicing opal, radium-shine embossing pattern, which is characterized in that include the following steps:
PET film is unreeled on unwinding device；
The PET film is drawn to gloss oil apparatus for coating through traction pressure roller under initiative compression roller effect；
The gloss oil apparatus for coating coats gloss oil on the PET film surface；
Preset pattern is pressure bonded on the PET film coated with gloss oil by pressing device on the move, the pressing device packet
The mobile bar for including guided way and being moved along the guided way, the transmission direction of the moving direction of the mobile bar and the PET film
It is identical；
Solidification equipment solidifies the PET film after pressing device pressing；
It is wound by wrap-up, completes the splicing to the opal, radium-shine embossing pattern of the PET film.
2. the production method of splicing opal, radium-shine embossing pattern as described in claim 1, which is characterized in that the gloss oil applies
The gloss oil of cloth apparatus coating is UV gloss oil.
3. the production method of splicing opal, radium-shine embossing pattern as described in claim 1, which is characterized in that the pressing dress
It sets further include: be sheathed on the splicing seat that can be moved in the mobile bar and along the mobile bar, be fixedly connected on the splicing seat
Splicing die head, it is described splicing die head on be provided with pattern, can with it is described splicing die head synchronizing moving support seat, the splicing
Die head and the support seat are set to the two sides of the PET film, and the end of the support seat is additionally provided with ultraviolet lamp.
4. the production method of splicing opal, radium-shine embossing pattern as claimed in claim 3, which is characterized in that the ultraviolet lamp
For LED ultraviolet lamp.
5. the production method of splicing opal, radium-shine embossing pattern as claimed in claim 3, which is characterized in that the mobile bar
Moving direction and it is described splicing seat moving direction intersection.
6. the production method of splicing opal, radium-shine embossing pattern as claimed in claim 5, which is characterized in that the mobile bar
Moving direction and it is described splicing seat moving direction intersection angle be 90 degree.
7. the production method of splicing opal, radium-shine embossing pattern as described in claim 1, which is characterized in that the solidification dress
It is set to UV lamp.
8. the production method of splicing opal, radium-shine embossing pattern as described in claim 1, which is characterized in that the PET film is
100um。