CN105566731A - 一种高黑高亮黑色母粒及其制备方法 - Google Patents
一种高黑高亮黑色母粒及其制备方法 Download PDFInfo
- Publication number
- CN105566731A CN105566731A CN201410553003.8A CN201410553003A CN105566731A CN 105566731 A CN105566731 A CN 105566731A CN 201410553003 A CN201410553003 A CN 201410553003A CN 105566731 A CN105566731 A CN 105566731A
- Authority
- CN
- China
- Prior art keywords
- black
- preparation
- temperature
- density polyethylene
- wax
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种高黑高亮黑色母粒及其制备方法。包括以下重量份的组成成分,炭黑BP717?50%,低密度聚乙烯LDPE-1C7A?14.2%,线性低密度聚乙烯LLDPE-2650?19.09%,聚乙烯蜡AC-6A?11.54%,滑剂蜡H-50S?4.67%,抗氧剂AO-50?0.5%,包括如下工艺流程,搅拌-密炼-造粒-脱水-封装。本发明与现有技术相比,对被改性塑料物性的影响小,且易于稀释于塑料制品中,同时具有高黑度、高蓝相、高亮度及优良的分散性等优点,极具推广价值。
Description
技术领域
本发明涉及一种色母粒及其制备方法,特别涉及一种高黑高亮黑色母粒及其制备方法。
背景技术
色母粒是一种新型高分子材料专用着色剂,它通常由颜料、载体和添加剂三种基本要素组成,用于塑料制品的染色。
黑色母粒是塑胶加工中最常用的一种色母粒,它是由高比例的颜料或添加剂与热塑性树脂,经良好分散而成的塑料着色剂,其所选用的树脂对着色剂具有良好润湿和分散作用,并且与被着色材料具有良好的相容性。它广泛应用于塑料加工行业,如注塑成型、挤出成型和吹塑成型等。
塑料改性是将石油化工企业生产出的大批量通用树脂通过物理的、化学的、机械的方法,改善或增加其功能,在电、磁、光、热、耐老化、阻燃、机械性能等方面达到特殊环境条件下使用的功能。
然而,现有技术黑色母改性对被改性塑料物性的影响较大,且很难做到高黑度高蓝相与高炭黑含量同时兼具。
发明内容
本发明所要解决的技术问题是:提供一种高黑高亮黑色母粒及其制备方法,解决了现有技术中黑色母粒对被改性塑料的物性影响较大、且很难同时兼具高黑度高蓝相与高炭黑含量的难题。
一种高黑高亮黑色母粒,包括以下重量份的组成成分:
炭黑BP71750%,
低密度聚乙烯LDPE-1C7A14.2%,
线性低密度聚乙烯LLDPE-265019.09%,
聚乙烯蜡AC-6A11.54%,
滑剂蜡H-50S4.67%,
抗氧剂AO-500.5%。
一种高黑高亮黑色母粒的制备方法,包括如下工艺流程:
搅拌-密炼-造粒-脱水-封装。
所述搅拌是指依次将线性低密度聚乙烯LLDPE-2650、聚乙烯蜡AC-6A、滑剂蜡H-50S和抗氧剂AO-50依次按19.09%、11.54%、4.67%以及0.5%的比例投入高速搅拌机进行搅拌,搅拌时间是10分钟,搅拌温度是60℃,然后静候1小时,得到混合物a。
所述密炼是指所述混合物a和50%的炭黑BP717、14.2%的低密度聚乙烯LDPE-1C7A置入连续式双螺杆密炼机密炼,所述双螺杆密炼机的温度分布为,一段温度44-46℃、二段温度94-96℃,所述出料口的温度是249-251℃,转子水温是29-31℃,所述双螺杆密炼机的转速为每分钟420转,密炼后得到混合物b。
所述造粒是指将混合物b输入单螺杆挤出机,所述单螺杆挤出机的温度分布是,从入料口到挤出机切粒模头一段,分别是100-120℃、200℃、180-200℃,螺杆水温是30-40℃,切粒模头温度是250℃,切粒水温是55-70℃,所述单螺杆挤出机料压是100MPa。
所述封装是指聚乙烯袋封装。
本发明与现有技术相比,有益效果在于:本黑色母粒高炭黑含量的添加减少了助剂对被改性塑料物性的影响,且易于稀释于塑料制品中,同时具有高黑度、高蓝相、高亮度及优良的分散性等优点,极具推广价值。
具体实施方式
为能进一步了解本发明的发明内容、特点及功效,兹例举以下实施例,详细说明本发明。
实施例1
一种高黑高亮黑色母粒,包括以下重量份的组成成分:
炭黑BP71750%,
低密度聚乙烯LDPE-1C7A14.2%,
线性低密度聚乙烯LLDPE-265019.09%,
聚乙烯蜡AC-6A11.54%,
滑剂蜡H-50S4.67%,
抗氧剂AO-500.5%。
一种高黑高亮黑色母粒的制备方法,包括如下工艺流程:
搅拌-密炼-造粒-脱水-封装。
所述搅拌是指依次将线性低密度聚乙烯LLDPE-2650、聚乙烯蜡AC-6A、滑剂蜡H-50S和抗氧剂AO-50依次按19.09%、11.54%、4.67%以及0.5%的比例投入高速搅拌机进行搅拌,搅拌时间是10分钟,搅拌温度是60℃,然后静候1小时,得到混合物a。
所述密炼是指所述混合物a和50%的炭黑BP717、14.2%的低密度聚乙烯LDPE-1C7A置入连续式双螺杆密炼机密炼,所述双螺杆密炼机的温度分布为,一段温度44-46℃、二段温度94-96℃,所述出料口的温度是249-251℃,转子水温是29-31℃,所述双螺杆密炼机的转速为每分钟420转,密炼后得到混合物b。
所述造粒是指将混合物b输入单螺杆挤出机,所述单螺杆挤出机的温度分布是,从入料口到挤出机切粒模头一段,分别是100-120℃、200℃、180-200℃,螺杆水温是30-40℃,切粒模头温度是250℃,切粒水温是55-70℃,所述单螺杆挤出机料压是100MPa。
所述封装是指聚乙烯袋封装。
实施例2
塑料改性测试
分别以树脂PC和PC/ABS为例,研究由实施例1得到的本黑色母粒BKE-2501和市场上现有的黑色母粒1064对被改性塑料物性的影响,测试结果如下表所示:
测试结果分析:由上表可知,加入5%的BKE-2501较加入5%的1064对树脂PC和PC/ABS的物性影响小;且反色率亮度轴L的数值变小,黑度高,黄蓝轴B的数值较小,蓝相高。
对所公开的实施例的上述说明,使本领域专业技术人员能够实现或使用本发明,本文所定义一般原理可以在不脱离本发明的精神或范围的情况下,在其他实施例中实现。本发明的范围由权利要求及其等同物限定。
Claims (6)
1.一种高黑高亮黑色母粒,其特征在于:包括以下重量份的组成成分,
炭黑BP71750%,
低密度聚乙烯LDPE-1C7A14.2%,
线性低密度聚乙烯LLDPE-265019.09%,
聚乙烯蜡AC-6A11.54%,
滑剂蜡H-50S4.67%,
抗氧剂AO-500.5%。
2.根据权利要求1所述的一种高黑高亮黑色母粒的制备方法,其特征在于:包括如下工艺流程,
搅拌-密炼-造粒-脱水-封装。
3.根据权利要求2所述的一种高黑高亮黑色母粒的制备方法,其特征在于:所述搅拌是指依次将线性低密度聚乙烯LLDPE-2650、聚乙烯蜡AC-6A、滑剂蜡H-50S和抗氧剂AO-50依次按19.09%、11.54%、4.67%以及0.5%的比例投入高速搅拌机进行搅拌,搅拌时间是10分钟,搅拌温度是60℃,然后静候1小时,得到混合物a。
4.根据权利要求2所述的一种高黑高亮黑色母粒的制备方法,其特征在于:所述密炼是指所述混合物a和50%的炭黑BP717、14.2%的低密度聚乙烯LDPE-1C7A置入连续式双螺杆密炼机密炼,所述双螺杆密炼机的温度分布为,一段温度44-46℃、二段温度94-96℃,所述出料口的温度是249-251℃,转子水温是29-31℃,所述双螺杆密炼机的转速为每分钟420转,密炼后得到混合物b。
5.根据权利要求2所述的一种高黑高亮黑色母粒的制备方法,其特征在于:所述造粒是指将混合物b输入单螺杆挤出机,所述单螺杆挤出机的温度分布是,从入料口到挤出机切粒模头一段,分别是100-120℃、200℃、180-200℃,螺杆水温是30-40℃,切粒模头温度是250℃,切粒水温是55-70℃,所述单螺杆挤出机料压是100MPa。
6.根据权利要求2所述的一种高黑高亮黑色母粒的制备方法,其特征在于:所述封装是指聚乙烯袋封装。