CN105564123A - Manufacture method of cloisonne - Google Patents
Manufacture method of cloisonne Download PDFInfo
- Publication number
- CN105564123A CN105564123A CN201510939880.3A CN201510939880A CN105564123A CN 105564123 A CN105564123 A CN 105564123A CN 201510939880 A CN201510939880 A CN 201510939880A CN 105564123 A CN105564123 A CN 105564123A
- Authority
- CN
- China
- Prior art keywords
- carcass
- copper
- preparation
- copper tire
- cloisonne enamel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a manufacture method of cloisonne. The method comprises the following steps: I. manufacturing a padding: shearing a red copper sheet in a designed shape to form a plurality of copper padding units and beating the copper padding units by a hammer; connecting a plurality of copper padding units; and coating a gap between two adjacent copper padding units with a welding flux and welding to form a copper padding mold; II. filigreeing: forming a pattern with flattened red copper wires through tweezers and adhering the pattern on the copper padding mold, scattering silver soldering powder on the surface of the copper padding mold and then placing the copper padding mold in a roasting oven to be roasted, so as to form a body; III. performing acid pickling, leveling and wire arrangement to the body and then glazing the surface of the body; IV. polishing: polishing the glazed surface of the body until to be smooth; and V. gold-plating: placing the polished body into a gold-plating tank to be plated. The manufacture method can reduce the defective rate and thus achieve the purpose of reducing the manufacture cost.
Description
Technical field
The present invention relates to the making of cloisonne enamel, particularly, relate to a kind of preparation method of cloisonne enamel.
Background technology
At present, the manufacturing process of cloisonne enamel is comparatively loaded down with trivial details, and loaded down with trivial details manufacturing process can make the difficulty of the making increasing cloisonne enamel, and be subject to the impact of operating personnel in addition, produced faulty materials are more, and then waste more cost.
Therefore, provide one can reduction in the numbers of seconds, and then to reach the cloisonne enamel preparation method reducing cost of manufacture object be the problem that the present invention needs solution badly.
Summary of the invention
The object of this invention is to provide a kind of preparation method of cloisonne enamel, this preparation method can reduction in the numbers of seconds, and then reaches the object reducing cost of manufacture.
To achieve these goals, the invention provides a kind of preparation method of cloisonne enamel, described preparation method comprises the following steps:
Step one, to make base, copper sheet is cut shape to form multiple copper tire unit according to designing requirement, beats described multiple copper tire unit with iron hammer; Described multiple copper tire unit is connected, applies welding agent at the gap place of adjacent described two copper tire unit and weld, to be formed as the moulding of copper tire;
Step 2, to wire inlay, with tweezers, the copper wire of flattening broken into pattern according to designing requirement, stick in the moulding of described copper tire, and on the surface of described copper tire moulding is loose silver soldering medicinal powder, be then placed on roasting kiln roasting, to be formed as carcass;
Step 3, described carcass carried out pickling, flatly to live and whole silk, then at the surface glazing of described carcass;
Step 4, polishing, polish by the glaze paint of grit by described carcass;
Step 5, gold-plated, the carcass after glaze paint is polished be placed into carry out in plating bath gold-plated.
Preferably, in step 3, glaze is filled in the silking space of described carcass, and carries out roasting under described carcass being arranged on the temperature of 800-900 DEG C.
Preferably, in step 3, with metal scuppit, glaze is filled in the silking space of described carcass.
Preferably, after step 4, also comprise described carcass through pickling, decontamination and Sha Liang before step 5.
Preferably, in step 4, also comprise and with Huangshi, charcoal, the glaze paint of described carcass being polished.
Preferably, described preparation method also comprises step 6, embedding gem on the carcass after gold-plated.
Preferably, in step 2, the sintering temperature in described roaster is 800-900 DEG C.
According to technique scheme, copper sheet is first cut shape to be formed as multiple copper tire unit according to designing requirement by the present invention, then beats multiple copper tire unit with iron hammer; And multiple copper tire unit is connected, apply welding agent at the gap place of arbitrary neighborhood two copper tire unit afterwards and weld, to be formed as the moulding of copper tire; Afterwards the copper wire of flattening is broken into pattern according to designing requirement, sticks in the moulding of copper tire, and on the surface of copper tire moulding is loose silver soldering medicinal powder, and be placed on roasting kiln roasting, to be formed as carcass; Namely such pattern is welded in the moulding of copper tire firmly, to be formed as carcass.Carcass carried out pickling afterwards again, put down and live and get final product glazing after whole silk, namely glazing is filled in silking space with glaze, through high-temperature roasting, the glaze of powdery can be melted into glaze paint.Repetition like this two to three times, glaze paint is equal with silking space; And then glaze paint is polished, every uneven part all needs repeatedly to polish, and finally with scraper, glaze paint is struck off brighten, the carcass after again glaze paint being polished afterwards be placed on carry out in plating bath gold-plated.
Other features and advantages of the present invention are described in detail in detailed description of the invention part subsequently.
Detailed description of the invention
Below the specific embodiment of the present invention is described in detail.Should be understood that, detailed description of the invention described herein, only for instruction and explanation of the present invention, is not limited to the present invention.
In the present invention, when not doing contrary explanation, the nouns of locality be included in term such as " upper and lower, left and right, inside and outside " only represents the orientation of this term under normal service condition, or being commonly called as of understanding for those skilled in the art, and should not be considered as the restriction to this term.
The invention provides a kind of preparation method of cloisonne enamel, described preparation method comprises the following steps: step one, make base, and copper sheet is cut shape to form multiple copper tire unit according to designing requirement, beats described multiple copper tire unit with iron hammer; Described multiple copper tire unit is connected, applies welding agent at the gap place of adjacent described two copper tire unit and weld, to be formed as the moulding of copper tire; Step 2, to wire inlay, with tweezers, the copper wire of flattening broken into pattern according to designing requirement, stick in the moulding of described copper tire, and on the surface of described copper tire moulding is loose silver soldering medicinal powder, be then placed on roasting kiln roasting, to be formed as carcass; Step 3, described carcass carried out pickling, flatly to live and whole silk, then at the surface glazing of described carcass; Step 4, polishing, polish by the glaze paint of grit by described carcass; Step 5, gold-plated, the carcass after glaze paint is polished be placed into carry out in plating bath gold-plated.Aim of the present invention be to provide a kind of can the preparation method of reduction in the numbers of seconds, and then reach the object reducing cost of manufacture.Copper sheet is first cut shape to be formed as multiple copper tire unit according to designing requirement by this preparation method, then beats multiple copper tire unit with iron hammer; And multiple copper tire unit is connected, apply welding agent at the gap place of arbitrary neighborhood two copper tire unit afterwards and weld, to be formed as the moulding of copper tire; Afterwards the copper wire of flattening is broken into pattern according to designing requirement, sticks in the moulding of copper tire, and on the surface of copper tire moulding is loose silver soldering medicinal powder, and be placed on roasting kiln roasting, to be formed as carcass; Namely such pattern is welded in the moulding of copper tire firmly, to be formed as carcass.Carcass carried out pickling afterwards again, put down and live and get final product glazing after whole silk, namely glazing is filled in silking space with glaze, through high-temperature roasting, the glaze of powdery can be melted into glaze paint.Repetition like this two to three times, glaze paint is equal with silking space; And then glaze paint is polished, every uneven part all needs repeatedly to polish, and finally with scraper, glaze paint is struck off brighten, the carcass after again glaze paint being polished afterwards be placed on carry out in plating bath gold-plated.
In a preferred embodiment, in step 3, glaze is filled in the silking space of described carcass, and carries out roasting under described carcass being arranged on the temperature of 800-900 DEG C.For being merged on carcass by glaze as much as possible, under carcass being arranged on the temperature of 800-900 DEG C, carry out roasting.
One more preferred embodiment in, in step 3, with metal scuppit, glaze is filled in the silking space of described carcass.For the composition preventing other materials from affecting glaze, with metal scuppit, glaze is filled in the silking space of carcass.
In a preferred embodiment, after step 4, also comprise described carcass through pickling, decontamination and Sha Liang before step 5.For ensureing the quality of cloisonne enamel as much as possible, before carcass being placed on plating bath, also comprising and carcass is carried out pickling, decontamination and Sha Liang.
In addition, in step 4, selecting for increasing, also comprising and with Huangshi, charcoal, the glaze paint of described carcass being polished.
In a preferred embodiment, be that the technique increasing cloisonne enamel is worth, described preparation method also comprises step 6, embedding gem on the carcass after gold-plated.
In addition, for making graphic-print as much as possible in the moulding of copper tire, in step 2, the sintering temperature in described roaster is 800-900 DEG C.
More than describe the preferred embodiment of the present invention in detail; but the present invention is not limited to the detail in above-mentioned embodiment, within the scope of technical conceive of the present invention; can carry out multiple simple variant to technical scheme of the present invention, these simple variant all belong to protection scope of the present invention.
It should be noted that in addition, each concrete technical characteristic described in above-mentioned detailed description of the invention, in reconcilable situation, can be combined by any suitable mode, in order to avoid unnecessary repetition, the present invention illustrates no longer separately to various possible combination.
In addition, also can be combined between various different embodiment of the present invention, as long as it is without prejudice to thought of the present invention, it should be considered as content disclosed in this invention equally.
Claims (7)
1. a preparation method for cloisonne enamel, is characterized in that, described preparation method comprises the following steps:
Step one, to make base, copper sheet is cut shape to form multiple copper tire unit according to designing requirement, beats described multiple copper tire unit with iron hammer; Described multiple copper tire unit is connected, applies welding agent at the gap place of adjacent described two copper tire unit and weld, to be formed as the moulding of copper tire;
Step 2, to wire inlay, with tweezers, the copper wire of flattening broken into pattern according to designing requirement, stick in the moulding of described copper tire, and on the surface of described copper tire moulding is loose silver soldering medicinal powder, be then placed on roasting kiln roasting, to be formed as carcass;
Step 3, described carcass carried out pickling, flatly to live and whole silk, then at the surface glazing of described carcass;
Step 4, polishing, polish by the glaze paint of grit by described carcass;
Step 5, gold-plated, the carcass after glaze paint is polished be placed into carry out in plating bath gold-plated.
2. the preparation method of cloisonne enamel according to claim 1, is characterized in that, in step 3, is filled into by glaze in the silking space of described carcass, and carries out roasting under described carcass being arranged on the temperature of 800-900 DEG C.
3. the preparation method of cloisonne enamel according to claim 2, is characterized in that, in step 3, is filled in the silking space of described carcass by glaze with metal scuppit.
4. the preparation method of cloisonne enamel according to claim 1, is characterized in that, after step 4, also comprises described carcass through pickling, decontamination and Sha Liang before step 5.
5. the preparation method of cloisonne enamel according to claim 1, is characterized in that, in step 4, also comprises and the glaze paint of described carcass being polished with Huangshi, charcoal.
6. the preparation method of cloisonne enamel according to claim 1, is characterized in that, described preparation method also comprises step 6, embedding gem on the carcass after gold-plated.
7. the preparation method of cloisonne enamel according to claim 1, is characterized in that, in step 2, the sintering temperature in described roaster is 800-900 DEG C.