CN105564121B - Image technique under ceramic glaze - Google Patents
Image technique under ceramic glaze Download PDFInfo
- Publication number
- CN105564121B CN105564121B CN201410536990.0A CN201410536990A CN105564121B CN 105564121 B CN105564121 B CN 105564121B CN 201410536990 A CN201410536990 A CN 201410536990A CN 105564121 B CN105564121 B CN 105564121B
- Authority
- CN
- China
- Prior art keywords
- pattern
- temperature
- hours
- uniform velocity
- image
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses image techniques under a kind of ceramic glaze, it is characterised in that processing step is as follows：Gypsum image seal is first made, image pattern is carved, seal is made in gypsum surface；Pattern transfers again, is transferred pattern to seal on not dry ceramic body；Then upper glaze, the glaze on the green body around pattern, then sprinkle equal frits powder is uniformly applied at pattern；Last shove charge is fired；The present invention at relief image by individually imposing first-class frit powder, and surface is smooth at image under the ceramic glaze after firing, and pattern is glittering and translucent, not only meets aesthetic requirements, but also improve practicability, and porcelain facing is made to be easier to clean, and cannot deposit dirt.
Description
Technical field
The present invention relates to a kind of ceramic preparation processes, more particularly to image technique under a kind of ceramic glaze.
Background technology
China's ceramics have a long history, and are the outstanding representatives of human civilization progress, spread all over now we life it is each
Field improves our quality of life.With the progress of technique, ceramic quality is also promoted constantly, various in the market
Ceramic system it is various in style it is tinkling of jades meet the eye on every side, the practicality and decorative all stronger mostly aesthetics is from moulding to improve
Innovation, also has and improves ornamental value by picture on surface, such as image under glaze, the stereoscopic effect as surface relief, but due to by work
Skill influences, and pattern image surface often will appear uneven phenomenon, its large scale application be affected, still up for technology
It improves.
Invention content
To solve the above-mentioned problems, the present invention provides image techniques under a kind of ceramic glaze.
The technical solution adopted by the present invention is：Image technique under a kind of ceramic glaze, it is characterised in that processing step is as follows：
A, gypsum image seal is made, image pattern is carved, seal is made in gypsum surface；
B, pattern transfers, and is transferred pattern to seal on not dry ceramic body；
C, upper glaze, the glaze on the green body around pattern, then sprinkle equal frits powder is uniformly applied at pattern；
D, it fires, green body is put into kiln and is fired by following temperature curve：It heats up 2 hours first stage, temperature is from room temperature
At the uniform velocity it is warming up to 400 DEG C；The second stage that heats up 2 hours, temperature is at the uniform velocity warming up to 900 DEG C from 400 DEG C；It heats up the phase III 1.5
Hour, temperature is at the uniform velocity warming up to 1100 DEG C from 900 DEG C；The fourth stage that heats up 2.5 hours, temperature is at the uniform velocity warming up to from 1100 DEG C
1310℃；Holding stage 1 to 3 hour, 1310 DEG C to 1300 DEG C of temperature range；Then cool down 2 hours first stage, temperature is at the uniform velocity
It is down to 1100 DEG C；The second stage that cools down 2.5 hours, temperature is at the uniform velocity down to 900 DEG C；Cool down 2.5 hours phase IIIs, temperature is at the uniform velocity
It is down to 500 DEG C；The fourth stage that cools down 3 hours, temperature is at the uniform velocity down to room temperature；It comes out of the stove firing.
Further, pattern is in and uniformly applies last and pattern before sprinkling equal frits powder in the processing step c
The same glaze of green body of surrounding.
The present invention at relief image by individually imposing first-class frit powder, surface at image under the ceramic glaze after firing
Bright and clean smooth, pattern is glittering and translucent, not only the stereoscopic effect as surface relief, but also light transmission viewing development is beautiful and generous, meets
Aesthetic requirements also improve practicability, and porcelain facing is made to be easier to clean, and cannot deposit dirt.
Specific implementation mode
Image technique, specific process step are as follows under ceramic glaze of the present invention：Design pattern is carved by intaglio and sun first
Gimmick engraving turns image pattern seal is made in gypsum surface in gypsum surface；Ceramic body is made again, with seal by pattern
It is transferred on not dry ceramic body, forms stereo carving image on ceramic body；Then first on the green body around pattern
Glaze, then sprinkle equal frits powder is uniformly applied at pattern, first-class frit powder dosage can be adjusted according to the pattern depression scale of construction
Section, the recess scale of construction can be spread greatly more, and being recessed, the scale of construction is small relatively rarely to spread；Green body is finally put into kiln to press
Face temperature curve is fired：It heats up 2 hours first stage, temperature is at the uniform velocity warming up to 400 DEG C from room temperature；The second stage that heats up 2 hours,
Temperature is at the uniform velocity warming up to 900 DEG C from 400 DEG C；It heats up 1.5 hours phase IIIs, temperature is at the uniform velocity warming up to 1100 DEG C from 900 DEG C；It rises
Warm fourth stage 2.5 hours, temperature is at the uniform velocity warming up to 1310 DEG C from 1100 DEG C；Holding stage 1 to 3 hour, temperature range 1310
DEG C to 1300 DEG C；Then cool down 2 hours first stage, temperature is at the uniform velocity down to 1100 DEG C；The second stage that cools down 2.5 hours, temperature
At the uniform velocity it is down to 900 DEG C；Cool down 2.5 hours phase IIIs, temperature is at the uniform velocity down to 500 DEG C；The fourth stage that cools down 3 hours, temperature is even
Prompt drop is to room temperature；It comes out of the stove firing.The present invention at relief image by individually imposing first-class frit powder, the ceramic glaze after firing
Surface is smooth at lower image, and pattern is glittering and translucent, and the stereoscopic effect as embossment is watched on surface, and light transmission viewing development is beautiful and generous,
Not only meet aesthetic requirements, but also improve practicability, porcelain facing is made to be easier to clean, cannot deposit dirt.
The fluctuating depth that moulding is carved on gypsum image seal will be calculated by ceramics by light transmission capacity, and light developing pattern needs
A bit with regard to green body thickness, light developing pattern needs local, the light developing figure thinner with regard to green body at gray scale bottom in gray scale high place
Case is exactly by the green body thin and thick difference pattern that light is formed through different gray scales caused by difference under light illumination.
When the present invention is implemented at pattern also can before uniform painting sprinkles equal frits powder on once with the base around pattern
It is larger to be suitable for the filling scale of construction for the same glaze of body.
It is only present pre-ferred embodiments in summary, all equivalent modifications done according to the application and prior art addition are equal
It is considered as the technology of the present invention scope.
Claims (1)
1. image technique under a kind of ceramic glaze, it is characterised in that processing step is as follows：
A, gypsum image seal is made, image pattern is carved, seal is made in gypsum surface；
B, pattern transfers, and is transferred pattern to seal on not dry ceramic body；
C, upper glaze, the glaze on the green body around pattern, then sprinkle equal frits powder is uniformly applied at pattern；
D, it fires, green body is put into kiln and is fired by following temperature curve：Heat up 2 hours first stage, temperature from room temperature at the uniform velocity
It is warming up to 400 DEG C；The second stage that heats up 2 hours, temperature is at the uniform velocity warming up to 900 DEG C from 400 DEG C；It heats up 1.5 hours phase IIIs,
Temperature is at the uniform velocity warming up to 1100 DEG C from 900 DEG C；The fourth stage that heats up 2.5 hours, temperature is at the uniform velocity warming up to 1310 DEG C from 1100 DEG C；
Holding stage 1 to 3 hour, 1310 DEG C to 1300 DEG C of temperature range；Then cool down 2 hours first stage, temperature is at the uniform velocity down to
1100℃；The second stage that cools down 2.5 hours, temperature is at the uniform velocity down to 900 DEG C；Cool down 2.5 hours phase IIIs, temperature is at the uniform velocity down to
500℃；The fourth stage that cools down 3 hours, temperature is at the uniform velocity down to room temperature；It comes out of the stove firing, pattern is in uniformly in the processing step c
Painting, which sprinkles, waits last glaze same as the green body around pattern before frits powder.