CN105543537A - Cupboard - Google Patents
Cupboard Download PDFInfo
- Publication number
- CN105543537A CN105543537A CN201510974040.0A CN201510974040A CN105543537A CN 105543537 A CN105543537 A CN 105543537A CN 201510974040 A CN201510974040 A CN 201510974040A CN 105543537 A CN105543537 A CN 105543537A
- Authority
- CN
- China
- Prior art keywords
- tempering
- time
- alloy material
- room temperature
- hours
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a cupboard. The cupboard comprises a metal frame made of an alloy material which is processed through tempering. The alloy material comprises 1-2% of B, 1.1% of As, 0.7% of Na, 0.8% of Po, 0.4% of Al, 0.6% of La, and the balance Cu and inevitable impurities. The tempering process of the alloy material comprises the following steps that 1, first tempering is conducted at the temperature of 525 DEG C, the tempering time lasts for 6.5 h, and then the alloy material is air cooled to the room temperature; 2, second tempering is conducted at the temperature of 575 DEG C, the tempering time lasts for 5.5 h, and then the alloy material is air cooled to the room temperature; and 3, third tempering is conducted at the temperature of 625 DEG C, the tempering time lasts for 4.5 h, and then the alloy material is air cooled to the room temperature. The metal frame used for the cupboard is light in weight, high in strength, resistant to corrosion, abrasion and oxidation, good in weather resistance and long in service life.
Description
Technical field
The present invention relates to cabinet.
Background technology
Cabinet is generally provided with metal support body, and to metal support body performance requriements higher.
Summary of the invention
The object of the present invention is to provide a kind of cabinet, its metal support body is made up of the alloy material through temper, and metal frame body weight is light, intensity is high, corrosion-resistant, abrasion-resistant, anti-oxidant, weather resistance good, and duration of service is long.
For achieving the above object, technical scheme of the present invention is a kind of cabinet of design, and comprise metal support body, described metal support body is made up of the alloy material through temper, and by weight percentage, the composition of this alloy material is:
B:1～2%，
As:1.1%，
Na:0.7%，
Po:0.8%，
Al:0.4%，
La:0.6%，
Surplus is Cu and inevitable impurity;
Described alloy material carries out temper as follows:
1) carry out first time tempering in 525 DEG C, tempering time is 6.5 hours, and then air cooling is to room temperature;
2) carry out second time tempering in 575 DEG C, tempering time is 5.5 hours, and then air cooling is to room temperature;
3) carry out third time tempering in 625 DEG C, tempering time is 4.5 hours, and then air cooling is to room temperature.
Preferably, cabinet, comprises metal support body, and described metal support body is made up of the alloy material through temper, and by weight percentage, the composition of this alloy material is:
B:1%，
As:1.1%，
Na:0.7%，
Po:0.8%，
Al:0.4%，
La:0.6%，
Surplus is Cu and inevitable impurity;
Described alloy material carries out temper as follows:
1) carry out first time tempering in 525 DEG C, tempering time is 6.5 hours, and then air cooling is to room temperature;
2) carry out second time tempering in 575 DEG C, tempering time is 5.5 hours, and then air cooling is to room temperature;
3) carry out third time tempering in 625 DEG C, tempering time is 4.5 hours, and then air cooling is to room temperature.
Preferably, cabinet, comprises metal support body, and described metal support body is made up of the alloy material through temper, and by weight percentage, the composition of this alloy material is:
B:2%，
As:1.1%，
Na:0.7%，
Po:0.8%，
Al:0.4%，
La:0.6%，
Surplus is Cu and inevitable impurity;
Described alloy material carries out temper as follows:
1) carry out first time tempering in 525 DEG C, tempering time is 6.5 hours, and then air cooling is to room temperature;
2) carry out second time tempering in 575 DEG C, tempering time is 5.5 hours, and then air cooling is to room temperature;
3) carry out third time tempering in 625 DEG C, tempering time is 4.5 hours, and then air cooling is to room temperature.
Advantage of the present invention and beneficial effect are: provide a kind of cabinet, and its metal support body is made up of the alloy material through temper, and metal frame body weight is light, intensity is high, corrosion-resistant, abrasion-resistant, anti-oxidant, weather resistance good, and duration of service is long.
Embodiment
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.
The technical scheme that the present invention specifically implements is:
Embodiment 1
A kind of cabinet, comprise metal support body, described metal support body is made up of the alloy material through temper, and by weight percentage, the composition of this alloy material is:
B:1～2%，
As:1.1%，
Na:0.7%，
Po:0.8%，
Al:0.4%，
La:0.6%，
Surplus is Cu and inevitable impurity;
Described alloy material carries out temper as follows:
1) carry out first time tempering in 525 DEG C, tempering time is 6.5 hours, and then air cooling is to room temperature;
2) carry out second time tempering in 575 DEG C, tempering time is 5.5 hours, and then air cooling is to room temperature;
3) carry out third time tempering in 625 DEG C, tempering time is 4.5 hours, and then air cooling is to room temperature.
Embodiment 2
Cabinet, comprises metal support body, and described metal support body is made up of the alloy material through temper, and by weight percentage, the composition of this alloy material is:
B:1%，
As:1.1%，
Na:0.7%，
Po:0.8%，
Al:0.4%，
La:0.6%，
Surplus is Cu and inevitable impurity;
Described alloy material carries out temper as follows:
1) carry out first time tempering in 525 DEG C, tempering time is 6.5 hours, and then air cooling is to room temperature;
2) carry out second time tempering in 575 DEG C, tempering time is 5.5 hours, and then air cooling is to room temperature;
3) carry out third time tempering in 625 DEG C, tempering time is 4.5 hours, and then air cooling is to room temperature.
Embodiment 3
Cabinet, comprises metal support body, and described metal support body is made up of the alloy material through temper, and by weight percentage, the composition of this alloy material is:
B:2%，
As:1.1%，
Na:0.7%，
Po:0.8%，
Al:0.4%，
La:0.6%，
Surplus is Cu and inevitable impurity;
Described alloy material carries out temper as follows:
1) carry out first time tempering in 525 DEG C, tempering time is 6.5 hours, and then air cooling is to room temperature;
2) carry out second time tempering in 575 DEG C, tempering time is 5.5 hours, and then air cooling is to room temperature;
3) carry out third time tempering in 625 DEG C, tempering time is 4.5 hours, and then air cooling is to room temperature.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (3)
1. cabinet, is characterized in that, comprises metal support body, and described metal support body is made up of the alloy material through temper, and by weight percentage, the composition of this alloy material is:
B:1～2%，
As:1.1%，
Na:0.7%，
Po:0.8%，
Al:0.4%，
La:0.6%，
Surplus is Cu and inevitable impurity;
Described alloy material carries out temper as follows:
1) carry out first time tempering in 525 DEG C, tempering time is 6.5 hours, and then air cooling is to room temperature;
2) carry out second time tempering in 575 DEG C, tempering time is 5.5 hours, and then air cooling is to room temperature;
3) carry out third time tempering in 625 DEG C, tempering time is 4.5 hours, and then air cooling is to room temperature.
2. cabinet according to claim 1, is characterized in that, comprises metal support body, and described metal support body is made up of the alloy material through temper, and by weight percentage, the composition of this alloy material is:
B:1%，
As:1.1%，
Na:0.7%，
Po:0.8%，
Al:0.4%，
La:0.6%，
Surplus is Cu and inevitable impurity;
Described alloy material carries out temper as follows:
1) carry out first time tempering in 525 DEG C, tempering time is 6.5 hours, and then air cooling is to room temperature;
2) carry out second time tempering in 575 DEG C, tempering time is 5.5 hours, and then air cooling is to room temperature;
3) carry out third time tempering in 625 DEG C, tempering time is 4.5 hours, and then air cooling is to room temperature.
3. cabinet according to claim 1, is characterized in that, comprises metal support body, and described metal support body is made up of the alloy material through temper, and by weight percentage, the composition of this alloy material is:
B:2%，
As:1.1%，
Na:0.7%，
Po:0.8%，
Al:0.4%，
La:0.6%，
Surplus is Cu and inevitable impurity;
Described alloy material carries out temper as follows:
1) carry out first time tempering in 525 DEG C, tempering time is 6.5 hours, and then air cooling is to room temperature;
2) carry out second time tempering in 575 DEG C, tempering time is 5.5 hours, and then air cooling is to room temperature;
3) carry out third time tempering in 625 DEG C, tempering time is 4.5 hours, and then air cooling is to room temperature.