CN105542285A - 一种用于聚合物的添加剂及其制备方法以及由其组成的聚合物组合物 - Google Patents

一种用于聚合物的添加剂及其制备方法以及由其组成的聚合物组合物 Download PDF

Info

Publication number
CN105542285A
CN105542285A CN201610089346.2A CN201610089346A CN105542285A CN 105542285 A CN105542285 A CN 105542285A CN 201610089346 A CN201610089346 A CN 201610089346A CN 105542285 A CN105542285 A CN 105542285A
Authority
CN
China
Prior art keywords
acid
butyl
additive
ester
tert
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610089346.2A
Other languages
English (en)
Inventor
不公告发明人
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Rianlon Corporation
Original Assignee
Huang Xiuru
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Huang Xiuru filed Critical Huang Xiuru
Priority to CN201610089346.2A priority Critical patent/CN105542285A/zh
Publication of CN105542285A publication Critical patent/CN105542285A/zh
Priority to PCT/CN2016/111233 priority patent/WO2017140168A1/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种如式X所示的用于聚合物的添加剂A，其包括如式X所示的化合物，

Description

一种用于聚合物的添加剂及其制备方法以及由其组成的聚合物组合物
技术领域
本发明涉及一种添加剂，具体涉及一种用于热塑性聚合物的添加剂及其制备方法以及由其组成的聚合物组合物。
背景技术
如上式所述的四(β-(3,5-二叔丁基-4-羟基苯基)丙酰氧基甲基)甲烷是一种重要的用于热塑性聚合物的商业添加剂。例如，它保护有机材料，尤其是热塑性聚合物以抵制热、氧化和/或光化的降解。一般来说，由2,6-二叔丁基苯酚和丙烯酸甲酯先进行加成反应，生成β-(3,5-二叔丁基-4-羟基苯基)丙酸甲酯，然后再与季戊四醇进行酯交换反应制得。
将上式所述的四(β-(3,5-二叔丁基-4-羟基苯基)丙酰氧基甲基)甲烷作为添加剂用于聚丙烯、聚苯乙烯、聚乙烯、聚酰胺、ABS等聚合物中，由于树脂的化学特性、物理特性和成型加工性能优异，而且廉价，所以被利用在以食品容器和医药品容器为首的广泛范围的用途中。但是，树脂在添加了四(β-(3,5-二叔丁基-4-羟基苯基)丙酰氧基甲基)甲烷之后，在盛装燃料、食用油、化妆品等有机液体时，有机液体容易从树脂制备的容器中透过，严重影响了正常使用。
而本发明人经大量研究惊奇的发现，当在上式所述的四(β-(3,5-二叔丁基-4-羟基苯基)丙酰氧基甲基)甲烷中加入特定含量含磷物质和含钛物质时，可使之对应的聚合物容器的有机物阻隔性能有极为明显的改善。
发明内容
本发明的目的在于提供一种用于聚合物的添加剂A，该添加剂A通过在四(β-(3,5-二叔丁基-4-羟基苯基)丙酰氧基甲基)甲烷中添加微量含磷物质和含钛物质，能明显改善聚合物制品的有机物阻隔性能。本发明是通过以下技术方案实现的：
一种用于聚合物的添加剂A，由如式X所示结构式的化合物组成：
式X，其化学名称可以为：四(β-(3,5-二叔丁基-4-羟基苯基)丙酰氧基甲基)甲烷。其中，基于添加剂A的总重量，磷元素和钛元素的总重量含量为10ppm-525ppm，更优选22ppm-308ppm。
其中，优选磷元素含量大于钛元素含量。
其中磷元素来源于含磷物质，含磷物质可以是下述的一种或一种以上的组合。
术语“含磷物质”在本文中是指或者包括元素磷以及有机和无机磷化合物和/或含磷化合物及其水解物或盐。
元素磷涉及四种同素异形体变体，为白磷，红磷，黑磷和紫磷。根据这些基本类型的不同，形成不同的晶体结构，从而也带来物理性能和反应性上的差异。本专利中优选使用红磷。
合适的无机磷化合物有利地包括(多)磷酸盐，如亚磷酸的未浓缩盐或磷酸的浓缩盐，如磷酸铵和多磷酸铵。
本发明使用的通式(I)或(II)的有机磷化合物(I)(II)可以选自有机磷化合物，如单体的有机磷化合物，或聚合物的有机磷化合物，无机的磷化合物等，其中，R1、R2和R3彼此独立地表示技术人员从现有技术获知的有机或无机基团。
取代基或基团R是彼此独立的，并且可以相同或不同，甚至完全没有。基团R优选可以分别彼此独立地表示：-H，取代或未取代的C1-C15-烷基，C1-C15-烯基，C3-C8-环烷基，C6-C18-芳基，C7-C30-烷芳基，C1-C8-烷氧基或C1-C8-烷硫基，或者-OH或-SH及其碱金属盐，碱土金属盐，铵盐。
式(I)磷化合物的任选取代基R的"烷基"部分表示可以是非支化或支化的饱和和不饱和脂族化合物，其中优选不饱和基团。取代基R优选包括具有不超过6，更优选不超过4或3，更优选不超过2个碳原子的短链烷基，或者苯基作为芳基。特别有用的磷化合物优选是尽可能未取代的。
通式(I)或(II)的那些磷化合物的实例是有机磷化合物及其盐，如单体的有机磷化合物，包括磷酸酯化合物，磷酸酰胺酯化合物和磷腈化合物，亚磷酸的有机化合物，例如亚磷酸的酯，次磷酸的化合物，膦和膦氧化物，例如三苯基膦，三苯基膦氧化物和三甲苯膦氧化物等。
其中钛元素来源于含钛物质，含钛物质可以是下述的一种或一种以上的组合。
术语“含钛物质”只要为含有钛元素的物质即可，不特别限定，但是优选为二氧化钛的粉末。二氧化钛可以为无定形也可以是结晶。作为二氧化钛的晶型，可以举出锐钛矿型、金红石型、板钛矿型等。更优选为锐钛矿型或金红石型的二氧化钛。
作为含钛物质，也可以为其他含钛化合物或单体。作为上述化合物，可以举出例如钛盐、钛醇盐、氢氧化钛、氮化钛、硫化钛等。
作为钛盐，具体地说，可以举出三氯化钛、四氯化钛、硫化钛、硫酸钛等。作为钛醇盐，具体地说，可以举出乙醇钛、甲醇钛、叔丁醇钛、异丁醇钛、正丙醇钛、四异丙醇钛和它们的螯合物等。
对于二氧化钛的粒径优选为通过激光衍射法测定得到的、相当于体积基准的累积百分率50％的粒径(D50)在0.1～20μm的范围内，D50更优选在0.1～10μm的范围内，进一步优选在0.1～1μm的范围内。此外，二氧化钛通过激光衍射法测定得到的、相当于体积基准的累积百分率90％的粒径(D90)优选为0.1～20μm，更优选为0.1～10μm，进一步优选为0.2～1.5μm。
本发明还提供一种添加剂组合物，包含如式X所示结构式的化合物：
式X，
和至少一种不同于式X所述化合物的其它添加剂B，其中，基于添加剂组合物的总重量，磷元素和钛元素的总重量含量为10ppm-525ppm，更优选22ppm-308ppm；基于添加剂组合物的总重量，优选包含50至99.9％重量的一种如式X所述的化合物，和0.1至50％重量的至少一种不同于式X所述化合物的其它添加剂B，其中，基于添加剂组合物的总重量，磷元素和钛元素的总重量含量为10ppm-525ppm，更优选22ppm-308ppm。
所述其它添加剂B为以下物质的一种或一种以上：
1.抗氧剂，包括如下种类：
1.1烷基化单酚，例如2,6-二叔丁基-4-甲基苯酚、2-叔丁基-4,6-二甲基苯酚、2,6-二叔丁基-4-乙基苯酚、2,6-二叔丁基-4-正丁基苯酚、2,6-二叔丁基-4-异丁基苯酚、2,6-二环戊基-4-甲基苯酚、2-(α-甲基环己基)-4,6-二甲基苯酚、2,6-二(十八烷基)-4-甲基苯酚、2,4,6-三环己基苯酚、2,6-二叔丁基-4-甲氧基甲基苯酚，侧链为线性或支化的壬基酚例如2,6-二壬基-4-甲基苯酚、2,4-二甲基-6-(1'-甲基十一烷-1'-基)苯酚、2,4-二甲基-6-(1'-甲基十七烷-1'-基)苯酚、2,4-二甲基-6-(1'-甲基十三烷-1'-基)苯酚及其混合物。
1.2烷硫基甲基苯酚，例如2,4-二辛硫基甲基-6-叔丁基苯酚、2,4-二辛硫基甲基-6-甲基苯酚、2,4-二辛硫基甲基-6-乙基苯酚、2,6-二(十二烷硫基)甲基-4-壬基苯酚。
1.3氢醌类和烷基化氢醌类，例如2,6-二叔丁基-4-甲氧基苯酚、2,5-二叔丁基氢醌、2,5-二叔戊基氢醌、2,6-二苯基-4-十八烷氧基苯酚、2,6-二叔丁基氢醌、2,5-二叔丁基-4-羟基茴香醚、3,5-二叔丁基-4-羟基茴香醚、硬脂酸3,5-二叔丁基-4-羟基苯酯、己二酸双(3,5-二叔丁基-4-羟基苯基)酯。
1.4生育酚类，例如α-生育酚、β-生育酚、γ-生育酚、δ-生育酚及其混合物(维生素E)。
1.5羟基化硫代二苯醚，例如2,2'-硫代双(6-叔丁基-4-甲基苯酚)、2,2'-硫代双(4-辛基苯酚)、4,4'-硫代双(6-叔丁基-3-甲基苯酚)、4,4'-硫代双(6-叔丁基-2-甲基苯酚)、4,4'-硫代双(3,6-二仲戊基苯酚)、4,4'-双(2,6-二甲基-4-羟基苯基)二硫醚。
1.6亚烷基双酚，例如2,2'-亚甲基双(6-叔丁基-4-甲基苯酚)、2,2'-亚甲基双(6-叔丁基-4-乙基苯酚)、2,2'-亚甲基双[4-甲基-6-(α-甲基环己基)苯酚]、2,2'-亚甲基双(4-甲基-6-环己基苯酚)、2,2'-亚甲基双(6-壬基-4-甲基苯酚)、2,2'-亚甲基双(4,6-二叔丁基苯酚)、2,2'-亚乙基双(4,6-二叔丁基苯酚)、2,2'-亚乙基双(6-叔丁基-4-异丁基苯酚)、2,2'-亚甲基双[6-(α-甲基苄基)-4-壬基酚]、2,2'-亚甲基双[6-(α,α-二甲基苄基)-4-壬基酚]、4,4'-亚甲基双(2,6-二叔丁基苯酚)、4,4'-亚甲基双(6-叔丁基-2-甲基苯酚)、1,1-双(5-叔丁基-4-羟基-2-甲基苯基)丁烷、2,6-双(3-叔丁基-5-甲基-2-羟基苄基)-4-甲基苯酚、1,1,3-三(5-叔丁基-4-羟基-2-甲基苯基)丁烷、1,1-双(5-叔丁基-4-羟基-2-甲基苯基)-3-正十二烷基巯基丁烷、乙二醇双[3,3-双(3'-叔丁基-4'-羟基苯基)丁酸酯]、双(3-叔丁基-4-羟基-5-甲基苯基)二环戊二烯、双[2-(3'-叔丁基-2'-羟基-5'-甲基苄基)-6-叔丁基-4-甲基苯基]对苯二甲酸酯、1,1-双(3,5-二甲基-2-羟基苯基)丁烷、2,2-双(3,5-二叔丁基-4-羟基苯基)丙烷、2,2-双(5-叔丁基-4-羟基-2-甲基苯基)-4-正十二烷基巯基丁烷、1,1,5,5-四(5-叔丁基-4-羟基-2-甲基苯基)戊烷。
1.7O-、N-和S-苄基化合物，例如3,5,3',5'-四叔丁基-4,4'-二羟基二苄基醚、4-羟基-3,5-二甲基苄基巯基乙酸十八烷基酯、4-羟基-3,5-二叔丁基苄基巯基乙酸十三烷基酯、三(3,5-二叔丁基-4-羟基苄基)胺、双(4-叔丁基-3-羟基-2,6-二甲基苄基)二硫代对苯二甲酸酯、双(3,5-二叔丁基-4-羟基苄基)硫化物、3,5-二叔丁基-4-羟基苄基巯基乙酸异辛基酯。
1.8芳族羟基苄基化合物，例如1,3,5-三(3,5-二叔丁基-4-羟基苄基)-2,4,6-三甲基苯、1,4-双(3,5-二叔丁基-4-羟基苄基)-2,3,5,6-四甲基苯、2,4,6-三(3,5-二叔丁基-4-羟基苄基)苯酚。
1.9三嗪化合物，例如2,4-双(辛基巯基)-6-(3,5-二叔丁基-4-羟基苯胺基)-1,3,5-三嗪、2-辛基巯基-4,6-双(3,5-二叔丁基-4-羟基苯胺基)-1,3,5-三嗪、2-辛基巯基-4,6-双(3,5-二叔丁基-4-羟基苯氧基)-1,3,5-三嗪、2,4,6-三(3,5-二叔丁基-4-羟基苯氧基)-1,2,3-三嗪、1,3,5-三(3,5-二叔丁基-4-羟基苄基)异氰脲酸酯、1,3,5-三(4-叔丁基-3-羟基-2,6-二甲基苄基)异氰脲酸酯、2,4,6-三(3,5-二叔丁基-4-羟基苯基乙基)-1,3,5-三嗪、1,3,5-三(3,5-二叔丁基-4-羟基苯基丙酰基)-六氢-1,3,5-三嗪、1,3,5-三(3,5-二环己基-4-羟基苄基)异氰脲酸酯。
1.10苄基膦酸酯，例如2,5-二叔丁基-4-羟基苄基膦酸二甲酯、3,5-二叔丁基-4-羟基苄基膦酸二乙酯、3,5-二叔丁基-4-羟基苄基膦酸二(十八烷基)酯、5-叔丁基-4-羟基-3-甲基苄基膦酸二(十八烷基)酯、3,5-二叔丁基-4-羟基苄基膦酸的单乙酯的钙盐。
1.11酰氨基苯酚类，例如4-羟基月桂酰替苯胺、4-羟基硬脂酰替苯胺、N-(3,5-二叔丁基-4-羟基苯基)氨基甲酸辛酯。
1.12β-(3,5-二叔丁基-4-羟基苯基)丙酸与如下一元醇或多元醇的酯：例如与甲醇、乙醇、正辛醇、异辛醇、十八烷醇、1,6-己二醇、1,9-壬二醇、乙二醇、1,2-丙二醇、新戊二醇、硫二甘醇、二甘醇、三甘醇、季戊四醇、三(羟乙基)异氰脲酸酯、N,N'-双(羟乙基)草酰胺、3-硫杂十一烷醇、3-硫杂十五烷醇、三甲基己二醇、三羟甲基丙烷、4-羟基甲基-1-磷杂-2,6,7-三氧杂双环[2.2.2]辛烷的酯。
1.13β-(5-叔丁基-4-羟基-3-甲基苯基)丙酸与如下一元醇或多元醇的酯：例如与甲醇、乙醇、正辛醇、异辛醇、十八烷醇、1,6-己二醇、1,9-壬二醇、乙二醇、1,2-丙二醇、新戊二醇、硫二甘醇、二甘醇、三甘醇、季戊四醇、三(羟乙基)异氰脲酸酯、N,N'-双(羟乙基)草酰胺、3-硫杂十一烷醇、3-硫杂十五烷醇、三甲基己二醇、三羟甲基丙烷、4-羟基甲基-1-磷杂-2,6,7-三氧杂双环[2.2.2]辛烷、3,9-双[2-{3-(3-叔丁基-4-羟基-5-甲基苯基)丙酰氧基}-1,1-二甲基乙基]-2,4,8,10-四氧杂螺[5.5]十一烷的酯。
1.14β-(3,5-二环己基-4-羟基苯基)丙酸与如下一元醇或多元醇的酯：例如与甲醇、乙醇、辛醇、十八烷醇、1,6-己二醇、1,9-壬二醇、乙二醇、1,2-丙二醇、新戊二醇、硫二甘醇、二甘醇、三甘醇、季戊四醇、三(羟乙基)异氰脲酸酯、N,N'-双(羟乙基)草酰胺、3-硫杂十一烷醇、3-硫杂十五烷醇、三甲基己二醇、三羟甲基丙烷、4-羟基甲基-1-磷杂-2,6,7-三氧杂双环[2.2.2]辛烷的酯。
1.153,5-二叔丁基-4-羟基苯基乙酸与如下一元醇或多元醇的酯：例如与甲醇、乙醇、辛醇、十八烷醇、1,6-己二醇、1,9-壬二醇、乙二醇、1,2-丙二醇、新戊二醇、硫二甘醇、二甘醇、三甘醇、季戊四醇、三(羟乙基)异氰脲酸酯、N,N'-双(羟乙基)草酰胺、3-硫杂十一烷醇、3-硫杂十五烷醇、三甲基己二醇、三羟甲基丙烷、4-羟基甲基-1-磷杂-2,6,7-三氧杂双环[2.2.2]辛烷的酯。
1.16β-(3,5-二叔丁基-4-羟基苯基)丙酸的酰胺，例如N,N'-双(3,5-二叔丁基-4-羟基苯基丙酰基)六亚甲基二胺、N,N'-双(3,5-二叔丁基-4-羟基苯基丙酰基)三亚甲基二胺、N,N'-双(3,5-二叔丁基-4-羟基苯基丙酰基)肼、N,N'-双[2-(3-[3,5-二叔丁基-4-羟基苯基]丙酰氧基)乙基]草酰胺。
2.紫外线吸收剂
2.12-羟基二苯甲酮类，例如4-羟基、4-甲氧基、4-辛氧基、4-癸氧基、4-十二烷氧基、4-苄氧基、4,2',4'-三羟基和2'-羟基-4,4'-二甲氧基衍生物。
2.2取代和未取代苯甲酸的酯，例如水杨酸4-叔丁基苯酯、水杨酸苯酯、水杨酸辛基苯酯、二苯甲酰间苯二酚、双(4-叔丁基苯甲酰)间苯二酚、苯甲酰间苯二酚、3,5-二叔丁基-4-羟基苯甲酸2,4-二叔丁基苯酯、3,5-二叔丁基-4-羟基苯甲酸十六烷基酯、3,5-二叔丁基-4-羟基苯甲酸十八烷基酯、3,5-二叔丁基-4-羟基苯甲酸2-甲基-4,6-二叔丁基苯酯。
2.3丙烯酸酯类，例如α-氰基-β,β-二苯基丙烯酸乙酯、α-氰基-β,β-二苯基丙烯酸异辛酯、α-甲酯基肉桂酸甲酯、α-氰基-β-甲基对甲氧基肉桂酸甲酯、α-氰基-β-甲基对甲氧基肉桂酸丁酯、α-甲酯基对甲氧基肉桂酸甲酯、N-(β-甲酯基-β-氰基乙烯基)-2-甲基二氢吲哚、四(α-氰基-β,β-二苯基)丙烯酸新戊基酯。
2.4镍化合物，例如2,2'-硫代双[4-(1,1,3,3-四甲基丁基)苯酚]的镍配合物，例如1:1或1:2配合物，其具有或不具有其他配体如正丁胺、三乙醇胺或N-环己基二乙醇胺，二丁基二硫代氨基甲酸镍，4-羟基-3,5-二叔丁基苄基膦酸的单烷基酯如甲酯或乙酯的镍盐，酮肟如2-羟基-4-甲基苯基十一烷基酮肟的镍配合物，1-苯基-4-月桂酰基-5-羟基吡唑的镍配合物，其具有或不具有其他配体。
2.5位阻胺，例如双(1-十一烷氧基-2,2,6,6-四甲基-4-哌啶基)碳酸酯、双(2,2,6,6-四甲基-4-哌啶基)癸二酸酯、双(2,2,6,6-四甲基-4-哌啶基)琥珀酸酯、双(1,2,2,6,6-五甲基-4-哌啶基)癸二酸酯、双(1-辛氧基-2,2,6,6-四甲基-4-哌啶基)癸二酸酯、双(1,2,2,6,6-五甲基-4-哌啶基)正丁基-3,5-二叔丁基-4-羟基苄基丙二酸酯、1-(2-羟乙基)-2,2,6,6-四甲基-4-羟基哌啶与琥珀酸的缩合物、N,N'-双(2,2,6,6-四甲基-4-哌啶基)六亚甲基二胺与4-叔辛基氨基-2,6-二氯-1,3,5-三嗪的线性或环状缩合物、三(2,2,6,6-四甲基-4-哌啶基)次氮基三乙酸酯、四(2,2,6,6-四甲基-4-哌啶基)-1,2,3,4-丁烷四甲酸酯、1,1'-(1,2-亚乙基)-双(3,3,5,5-四甲基哌嗪酮)、4-苯甲酰基-2,2,6,6-四甲基哌啶、4-硬脂氧基-2,2,6,6-四甲基哌啶、双(1,2,2,6,6-五甲基哌啶基)-2-正丁基-2-(2-羟基-3,5-二叔丁基苄基)丙二酸酯、3-正辛基-7,7,9,9-四甲基-1,3,8-三氮杂螺[4.5]癸-2,4-二酮、双(1-辛氧基-2,2,6,6-四甲基哌啶基)癸二酸酯、双(1-辛氧基-2,2,6,6-四甲基哌啶基)琥珀酸酯、N,N'-双-(2,2,6,6-四甲基-4-哌啶基)六亚甲基二胺与4-吗啉基-2,6-二氯-1,3,5-三嗪的线性或环状缩合物、2-氯-4,6-双(4-正丁基氨基-2,2,6,6-四甲基哌啶基)-1,3,5-三嗪与1,2-双(3-氨基丙基氨基)乙烷的缩合物、2-氯-4,6-二(4-正丁基氨基-1,2,2,6,6-五甲基哌啶基)-1,3,5-三嗪与1,2-双(3-氨基丙基氨基)乙烷的缩合物、8-乙酰基-3-十二烷基-7,7,9,9-四甲基-1,3,8-三氮杂螺[4.5]癸烷-2,4-二酮、3-十二烷基-1-(2,2,6,6-四甲基-4-哌啶基)吡咯烷-2,5-二酮、3-十二烷基-1-(1,2,2,6,6-五甲基-4-哌啶基)吡咯烷-2,5-二酮、4-十六烷氧基-和4-硬脂氧基-2,2,6,6-四甲基哌啶的混合物、N,N'-双(2,2,6,6-四甲基-4-哌啶基)六亚甲基二胺与4-环己基氨基-2,6-二氯-1,3,5-三嗪的缩合物、1,2-双(3-氨基丙基氨基)乙烷与2,4,6-三氯-1,3,5-三嗪以及4-丁基氨基-2,2,6,6-四甲基哌啶的缩合物(CAS登记号[136504-96-6])；1,6-己二胺与2,4,6-三氯-1,3,5-三嗪以及N,N-二丁胺与4-丁基氨基-2,2,6,6-四甲基哌啶的缩合物(CAS登记号[192268-64-7])；N-(2,2,6,6-四甲基-4-哌啶基)正十二烷基琥珀酰亚胺、N-(1,2,2,6,6-五甲基-4-哌啶基)正十二烷基琥珀酰亚胺、2-十一烷基-7,7,9,9-四甲基-1-氧杂-3,8-二氮杂-4-氧代螺[4,5]癸烷、7,7,9,9-四甲基-2-环十一烷基-1-氧杂-3,8-二氮杂-4-氧代螺[4,5]癸烷与表氯醇的反应产物、1,1-双(1,2,2,6,6-五甲基-4-哌啶基氧基羰基)-2-(4-甲氧基苯基)乙烯、N,N'-双甲酰基-N,N'-双(2,2,6,6-四甲基-4-哌啶基)六亚甲基二胺、4-甲氧基亚甲基丙二酸与1,2,2,6,6-五甲基-4-羟基哌啶的二酯、聚[甲基丙基-3-氧基-4-(2,2,6,6-四甲基-4-哌啶基)]硅氧烷、马来酸酐-α-烯烃共聚物与2,2,6,6-四甲基-4-氨基哌啶或1,2,2,6,6-五甲基-4-氨基哌啶的反应产物、2,4-双[N-(1-环己氧基-2,2,6,6-四甲基哌啶-4-基)-N-丁基氨基]-6-(2-羟乙基)氨基-1,3,5-三嗪、1-(2-羟基-2-甲基丙氧基)-4-十八烷酰氧基-2,2,6,6-四甲基哌啶、5-(2-乙基己酰基)氧基甲基-3,3,5-三甲基-2-吗啉酮、Sanduvor(Clariant；CAS登记号[106917-31-1])、5-(2-乙基己酰基)氧基甲基-3,3,5-三甲基-2-吗啉酮、2,4-双[(1-环己氧基-2,2,6,6-哌啶-4-基)丁基氨基]-6-氯-s-三嗪与N,N'-双(3-氨基丙基)乙二胺)的反应产物、1,3,5-三(N-环己基-N-(2,2,6,6-四甲基哌嗪-3-酮-4-基)氨基)-s-三嗪、1,3,5-三(N-环己基-N-(1,2,2,6,6-五甲基哌嗪-3-酮-4-基)氨基)-s-三嗪。
2.6草酰胺，例如4,4'-二辛氧基草酰替苯胺、2,2'-二乙氧基草酰替苯胺、2,2'-二辛氧基-5,5'-二叔丁基草酰替苯胺、2,2'-二(十二烷氧基)-5,5'-二叔丁基草酰替苯胺、2-乙氧基-2'-乙基草酰替苯胺、N,N'-双(3-二甲基氨基丙基)草酰胺、2-乙氧基-5-叔丁基-2'-乙基草酰替苯胺及其与2-乙氧基-2'-乙基-5,4'-二叔丁基草酰替苯胺的混合物、邻-和对-甲氧基二取代草酰替苯胺的混合物以及邻-和对-乙氧基二取代草酰替苯胺的混合物。
2.72-(2-羟基苯基)-1,3,5-三嗪类，例如2,4,6-三(2-羟基-4-辛氧基苯基)-1,3,5-三嗪、2-(2-羟基-4-辛氧基苯基)-4,6-双(2,4-二甲基苯基)-1,3,5-三嗪、2-(2,4-二羟基苯基)-4,6-双(2,4-二甲基苯基)-1,3,5-三嗪、2,4-双(2-羟基-4-丙氧基苯基)-6-(2,4-二甲基苯基)-1,3,5-三嗪、2-(2-羟基-4-辛氧基苯基)-4,6-双(4-甲基苯基)-1,3,5-三嗪、2-(2-羟基-4-十二烷氧基苯基)-4,6-双(2,4-二甲基苯基)-1,3,5-三嗪、2-(2-羟基-4-十三烷氧基苯基)-4,6-双(2,4-二甲基苯基)-1,3,5-三嗪、2-[2-羟基-4-(2-羟基-3-丁氧基丙氧基)苯基]-4,6-双(2,4-二甲基)-1,3,5-三嗪、2-[2-羟基-4-(2-羟基-3-辛氧基丙氧基)苯基]-4,6-双(2,4-二甲基)-1,3,5-三嗪、2-[4-(十二烷氧基/十三烷氧基-2-羟基丙氧基)-2-羟基苯基]-4,6-双(2,4-二甲基苯基)-1,3,5-三嗪、2-[2-羟基-4-(2-羟基-3-十二烷氧基丙氧基)苯基]-4,6-双(2,4-二甲基苯基)-1,3,5-三嗪、2-(2-羟基-4-己氧基)苯基-4,6-二苯基-1,3,5-三嗪、2-(2-羟基-4-甲氧基苯基)-4,6-二苯基-1,3,5-三嗪、2,4,6-三[2-羟基-4-(3-丁氧基-2-羟基丙氧基)苯基]-1,3,5-三嗪、2-(2-羟基苯基)-4-(4-甲氧基苯基)-6-苯基-1,3,5-三嗪、2-{2-羟基-4-[3-(2-乙基己基-1-氧基)-2-羟基丙氧基]苯基}-4,6-双(2,4-二甲基苯基)-1,3,5-三嗪、2,4-双(4-[2-乙基己氧基]-2-羟基苯基)-6-(4-甲氧基苯基)-1,3,5-三嗪。
3.金属减活剂，例如N,N'-二苯基草酰胺、N-水杨醛-N'-水杨酰肼、N,N'-双(水杨酰)肼、N,N'-双(3,5-二叔丁基-4-羟基苯基丙酰)肼、3-水杨酰氨基-1,2,4-***、双(亚苄基)草酰二肼、草酰替苯胺、间苯二甲酰二肼、癸二酰双苯基肼、N,N'-二乙酰己二酰二肼、N,N'-双(水杨酰)草酰二肼、N,N'-双(水杨酰)硫代丙酰二肼。
4.亚磷酸酯和亚膦酸酯，例如亚磷酸三苯酯、亚磷酸二苯基烷基酯、亚磷酸苯基二烷基酯、亚磷酸三(壬基苯基)酯、亚磷酸三月桂基酯、亚磷酸三(十八烷基)酯、二硬脂基季戊四醇二亚磷酸酯、亚磷酸三(2,4-二叔丁基苯基)酯、二异癸基季戊四醇二亚磷酸酯、双(2,4-二叔丁基苯基)季戊四醇二亚磷酸酯、双(2,4-二枯基苯基)季戊四醇二亚磷酸酯、双(2,6-二叔丁基-4-甲基苯基)季戊四醇二亚磷酸酯、二异癸氧基季戊四醇二亚磷酸酯、双(2,4-二叔丁基-6-甲基苯基)季戊四醇二亚磷酸酯、双(2,4,6-三(叔丁基苯基)季戊四醇二亚磷酸酯、三硬脂基山梨糖醇三亚磷酸酯、4,4'-亚联苯基二亚膦酸四(2,4-二叔丁基苯基)酯、6-异辛氧基-2,4,8,10-四叔丁基-12H-二苯并[d,g]-1,3,2-二氧杂磷杂八环、亚磷酸双(2,4-二叔丁基-6-甲基苯基)甲酯、亚磷酸双(2,4-二叔丁基-6-甲基苯基)乙酯、6-氟-2,4,8,10-四叔丁基-12-甲基二苯并[d,g]-1,3,2-二氧杂磷杂八环、2,2',2”-次氮基[三乙基三(3,3',5,5'-四叔丁基-1,1'-联苯-2,2'-二基)亚磷酸酯]、(3,3',5,5'-四叔丁基-1,1'-联苯-2,2'-二基)亚磷酸2-乙基己酯、5-丁基-5-乙基-2-(2,4,6-三叔丁基苯氧基)-1,3,2-二氧杂磷杂环丙烷。
5.羟胺，例如N,N-二苄基羟胺、N,N-二乙基羟胺、N,N-二辛基羟胺、N,N-二月桂基羟胺、N,N-二(十四烷基)羟胺、N,N-二(十六烷基)羟胺、N,N-二(十八烷基)羟胺、N-十六烷基-N-十八烷基羟胺、N-十七烷基-N-十八烷基羟胺、衍生自氢化牛油脂肪胺的N,N-二烷基羟胺。
6.硝酮，例如N-苄基-α-苯基硝酮、N-乙基-α-甲基硝酮、N-辛基-α-庚基硝酮、N-月桂基-α-十一烷基硝酮、N-十四烷基-α-十三烷基硝酮、N-十六烷基-α-十五烷基硝酮、N-十八烷基-α-十七烷基硝酮、N-十六烷基-α-十七烷基硝酮、N-十八烷基-α-十五烷基硝酮、N-十七烷基-α-十七烷基硝酮、N-十八烷基-α-十六烷基硝酮、衍生自N,N-二烷基羟胺(衍生自氢化牛油脂肪胺)的硝酮。
7.硫代协合剂，例如硫代二丙酸二月桂基酯、硫代二丙酸二肉豆蔻基酯、硫代二丙酸二硬脂基酯或二硬脂基二硫醚。
8.过氧化物清除剂，例如β-硫代二丙酸的酯，例如月桂基酯、硬脂基酯、肉豆蔻基酯或十三烷基酯、巯基苯并咪唑或2-巯基苯并咪唑的锌盐、二丁基二硫代氨基甲酸锌、二(十八烷基)二硫醚、季戊四醇四(β-十二烷基巯基)丙酸酯。
9.聚酰胺稳定剂，例如与碘和/或磷化合物组合的铜盐和二价锰盐。
10.碱性共稳定剂，例如三聚氰胺、聚乙烯吡咯烷酮、双氰胺、氰脲酸三烯丙基酯、脲衍生物、肼衍生物、胺、聚酰胺、聚氨酯、高级脂肪酸的碱金属盐和碱土金属盐，例如硬脂酸钙、硬脂酸锌、山酸镁、硬脂酸镁、蓖麻醇酸钠和棕榈酸钾、焦儿茶酸锑或焦儿茶酸锌。
11.成核剂，例如无机物质如滑石，金属氧化物如二氧化钛或氧化镁，优选碱土金属的磷酸盐、碳酸盐或硫酸盐；有机化合物如单-或聚羧酸及其盐，例如4-叔丁基苯甲酸、己二酸、二苯基乙酸、琥珀酸钠或苯甲酸钠；聚合化合物如离子共聚物(离聚物)。尤其优选为1,3:2,4-双(3',4'-二甲基亚苄基)山梨糖醇、1,3:2,4-二(对甲基二亚苄基)山梨糖醇和1,3:2,4-二(亚苄基)山梨糖醇。
12.其他添加剂，例如增塑剂、润滑剂、乳化剂、颜料、流变添加剂、催化剂、流动调节剂、荧光增白剂、阻燃剂、抗静电剂和发泡剂。
优选的添加剂B为：
1)本发明以外的其它抗氧化剂。
2)加工添加剂如防滑/防结块添加剂、增塑剂、荧光增白剂、抗静电剂和发泡剂。
3)紫外光吸收剂。
本发明还提供一种聚合物组合物，包含重量含量为30-99.9％的聚合物，重量含量为0-60％的填料，重量含量为0.1-10％的本发明制备的用于聚合物的添加剂A。
本发明还提供一种聚合物组合物，包含重量含量为30-99.9％的聚合物，重量含量为0-60％的填料，重量含量为0.1-10％的添加剂组合物。
本发明可以使用的聚合物是热固性和热塑性聚合物，选自以下物质中的一种或一种以上：
1.单烯烃和二烯烃的聚合物，例如聚丙烯、聚异丁烯、聚丁烯、聚4-甲基戊烯、聚乙烯基环己烷、聚异戊二烯或聚丁二烯、以及环烯烃的聚合物，例如环戊烯或降冰片烯的聚合物，聚乙烯(可任选交联)，例如高密度聚乙烯(HDPE)、高密度和高分子量聚乙烯(HDPE-HMW)、高密度和超高分子量聚乙烯(HDPE-UHMW)、中密度聚乙烯(MDPE)、低密度聚乙烯(LDPE)、线性低密度聚乙烯(LLDPE)。
2.在1中提及的聚合物的混合物，例如聚丙烯与聚异丁烯的混合物、聚丙烯与聚乙烯的混合物(例如PP/HDPE、PP/LDPE)以及不同类型聚乙烯的混合物(例如LDPE/HDPE)。
3.单烯烃和二烯烃彼此之间或与其他乙烯基单体的共聚物，例如乙烯/丙烯共聚物、线性低密度聚乙烯(LLDPE)及其与低密度聚乙烯(LDPE)的混合物、丙烯/丁-1-烯共聚物、丙烯/异丁烯共聚物、乙烯/丁-1-烯共聚物、乙烯/己烯共聚物、乙烯/甲基戊烯共聚物、乙烯/庚烯共聚物、乙烯/辛烯共聚物、乙烯/乙烯基环己烷共聚物、乙烯/环烯烃共聚物(例如乙烯/降冰片烯，例如COC)、乙烯/1-烯烃共聚物(其中1-烯烃原位产生)；丙烯/丁二烯共聚物、异丁烯/异戊二烯共聚物、乙烯/乙烯基环己烯共聚物、乙烯/丙烯酸烷基酯共聚物、乙烯/甲基丙烯酸烷基酯共聚物、乙烯/乙酸乙烯酯共聚物或乙烯/丙烯酸共聚物及其盐(离聚物)、以及乙烯与丙烯及二烯(例如己二烯、二环戊二烯或亚乙基降冰片烯)的三元共聚物；和这些共聚物彼此之间的混合物以及与上述1)中提及的聚合物的混合物，例如聚丙烯/乙烯-丙烯共聚物、LDPE/乙烯-乙酸乙烯酯共聚物(EVA)、LDPE/乙烯-丙烯酸共聚物(EAA)、LLDPE/EVA、LLDPE/EAA及其与其他聚合物(如聚酰胺)的混合物。
4.烃树脂(例如C5-C9)，包括其氢化改性产物(例如增粘剂)及聚亚烷基和淀粉的混合物。
1-4的均聚物及共聚物可具有任何立体结构，包括间规、等规、半等规或无规；其中优选无规聚合物。也包括立体嵌段聚合物。
5.聚苯乙烯、聚对甲基苯乙烯、聚α-甲基苯乙烯。
6.衍生自乙烯基芳族单体的芳族均聚物和共聚物，所述单体包括苯乙烯、α-甲基苯乙烯、乙烯基甲苯的所有异构体，特别是对乙烯基甲苯、乙基苯乙烯的所有异构体、丙基苯乙烯、乙烯基联苯、乙烯基萘和乙烯基蒽及其混合物。均聚物和共聚物可具有任何立体结构，包括间规、等规、半等规或无规；其中优选无规聚合物。也包括立体嵌段聚合物。
6a.包括上述乙烯基芳族单体及选自下述共聚单体的共聚物：乙烯、丙烯、二烯、腈、酸、马来酸酐类、马来酰亚胺类、乙酸乙烯酯和氯乙烯或丙烯酸系衍生物及其混合物，例如苯乙烯/丁二烯、苯乙烯/丙烯腈、苯乙烯/乙烯(共聚物)、苯乙烯/甲基丙烯酸烷基酯、苯乙烯/丁二烯/丙烯酸烷基酯、苯乙烯/丁二烯/甲基丙烯酸烷基酯、苯乙烯/马来酸酐、苯乙烯/丙烯腈/丙烯酸甲酯；苯乙烯共聚物与其他聚合物(例如聚丙烯酸酯、二烯聚合物或乙烯/丙烯/二烯三元共聚物)的高抗冲混合物；以及苯乙烯的嵌段共聚物如苯乙烯/丁二烯/苯乙烯、苯乙烯/异戊二烯/苯乙烯、苯乙烯/乙烯/丁烯/苯乙烯或苯乙烯/乙烯/丙烯/苯乙烯。
6b.由上述6中提及的聚合物氢化衍生的氢化芳族聚合物，尤其是包括由无规聚苯乙烯氢化制得的聚环己基乙烯(PCHE)，通常称为聚乙烯基环己烷(PVCH)。
6c.由上述6a中提及的聚合物氢化衍生的氢化芳族聚合物。
7.乙烯基芳族单体(如苯乙烯或α-甲基苯乙烯)的接枝共聚物，例如苯乙烯接枝的聚丁二烯、苯乙烯接枝的聚丁二烯-苯乙烯或聚丁二烯-丙烯腈共聚物；苯乙烯和丙烯腈(或甲基丙烯腈)接枝的聚丁二烯；苯乙烯、丙烯腈和甲基丙烯酸甲酯接枝的聚丁二烯；苯乙烯和马来酸酐接枝的聚丁二烯；苯乙烯、丙烯腈和马来酸酐或马来酰亚胺接枝的聚丁二烯；苯乙烯和马来酰亚胺接枝的聚丁二烯；苯乙烯和丙烯酸烷基酯或甲基丙烯酸烷基酯接枝的聚丁二烯；苯乙烯和丙烯腈接枝的乙烯/丙烯/二烯三元共聚物；苯乙烯和丙烯腈接枝的聚丙烯酸烷基酯或聚甲基丙烯酸烷基酯；苯乙烯和丙烯腈接枝的丙烯酸酯/丁二烯共聚物、及其与6)中所列共聚物的混合物，例如称为ABS、MBS、ASA或AES聚合物的共聚物的混合物。
8.含卤素的聚合物，例如聚氯丁二烯、氯化橡胶、异丁烯-异戊二烯的氯化或溴化共聚物(卤丁橡胶)、氯化或氯磺化聚乙烯、乙烯和氯化乙烯的共聚物、表氯醇均聚物及共聚物，尤其是含卤素的乙烯基化合物的聚合物，例如聚氯乙烯、聚偏二氯乙烯、聚氟乙烯、聚偏二氟乙烯；及其共聚物如氯乙烯/偏二氯乙烯、氯乙烯/乙酸乙烯酯或偏二氯乙烯/乙酸乙烯酯共聚物。
9.衍生自α,β-不饱和酸及其衍生物的聚合物，例如聚丙烯酸酯和聚甲基丙烯酸酯；聚甲基丙烯酸甲酯、聚丙烯酰胺和聚丙烯腈，其用丙烯酸丁酯进行抗冲击改性。
10.在9中所提及的单体彼此之间的共聚物或与其他不饱和单体的共聚物，例如丙烯腈/丁二烯共聚物、丙烯腈/丙烯酸烷基酯共聚物、丙烯腈/丙烯酸烷氧基烷基酯或丙烯腈/乙烯基卤共聚物或丙烯腈/甲基丙烯酸烷基酯/丁二烯三元共聚物。
11.衍生自不饱和醇及胺或其酰基衍生物或缩醛的聚合物，例如聚乙烯醇、聚乙酸乙烯酯、聚硬脂酸乙烯酯、聚苯甲酸乙烯酯、聚马来酸乙烯酯、聚乙烯醇缩丁醛、聚邻苯二甲酸烯丙基酯或聚烯丙基三聚氰胺；及其与上述1中所提及的烯烃的共聚物。
12.环醚的均聚物和共聚物，例如聚亚烷基二醇、聚氧化乙烯、聚氧化丙烯或其与二缩水甘油基醚的共聚物。
13.聚缩醛如聚甲醛和含有氧化乙烯作为共聚单体的那些聚甲醛；用热塑性聚氨酯、丙烯酸酯或MBS改性的聚缩醛。
14.聚苯醚和聚苯硫醚、以及聚苯醚与苯乙烯聚合物或聚酰胺的混合物。
15.聚氨酯，其一方面衍生自羟基封端的聚醚、聚酯或聚丁二烯，另一方面衍生自脂族或芳族多异氰酸酯及其前体。
16.聚酰胺和共聚酰胺，其衍生自二胺和二羧酸和/或衍生自氨基羧酸或相应内酰胺，例如聚酰胺4、聚酰胺6、聚酰胺6/6、6/10、6/9、6/12、4/6、12/12、聚酰胺11、聚酰胺12、由间二甲苯二胺和己二酸获得的芳族聚酰胺；在存在或不存在作为改性剂的弹性体下由六亚甲基二胺与间苯二甲酸和/或对苯二甲酸制备的聚酰胺，例如聚-2,4,4-三甲基六亚甲基对苯二甲酰胺或聚间亚苯基间苯二甲酰胺；以及上述聚酰胺与聚烯烃、烯烃共聚物、离聚物或化学键合或接枝的弹性体的嵌段共聚物；或与聚醚，例如与聚乙二醇、聚丙二醇或聚四亚甲基二醇的嵌段共聚物；以及用EPDM或ABS改性的聚酰胺或共聚酰胺；以及在加工过程中缩合的聚酰胺(RIM聚酰胺体系)。
17.聚酯，其衍生自二羧酸和二醇和/或衍生自羟基羧酸或相应的内酯或交酯，例如聚对苯二甲酸乙二醇酯、聚对苯二甲酸丁二醇酯、聚-1,4-二羟甲基环己烷对苯二甲酸酯、聚萘二甲酸亚烷基酯和聚羟基苯甲酸酯以及衍生自羟基封端聚醚的共聚醚酯；以及用聚碳酸酯或MBS改性的聚酯。共聚酯可包括，例如(但不限于)：聚琥珀酸丁二醇酯/对苯二甲酸丁二醇酯、聚己二酸丁二醇酯/对苯二甲酸丁二醇酯、聚己二酸四亚甲基酯/对苯二甲酸四亚甲基酯、聚琥珀酸丁二醇酯/己二酸丁二醇酯、聚琥珀酸丁二醇酯/碳酸酯、聚-3-羟基丁酸酯/3-羟基辛酸酯共聚物、聚-3-羟基丁酸酯/3-羟基己酸酯/3-羟基癸酸酯三元共聚物。此外，脂族聚酯可包括，例如(但不限于)：聚(羟基链烷酸酯)类，尤其为聚丙内酯、聚丁内酯、聚新戊内酯、聚戊内酯和聚己内酯、聚琥珀酸乙二醇酯、聚琥珀酸丙二醇酯、聚琥珀酸丁二醇酯、聚琥珀酸六亚甲基酯、聚己二酸乙二醇酯、聚己二酸丙二醇酯、聚己二酸丁二醇酯、聚己二酸六亚甲基酯、聚草酸乙二醇酯、聚草酸丙二醇酯、聚草酸丁二醇酯、聚草酸六亚甲基酯、聚癸二酸乙二醇酯、聚癸二酸丙二醇酯、聚癸二酸丁二醇酯及聚乳酸(PLA)以及用聚碳酸酯或MBS改性的相应聚酯。术语“聚乳酸(PLA)”表示优选为聚-L-丙交酯的均聚物及其与其他聚合物的任何共混物或合金；乳酸或丙交酯与其他单体的共聚物，所述其他单体例如羟基羧酸如乙醇酸、3-羟基丁酸、4-羟基丁酸、4-羟基戊酸、5-羟基戊酸、6-羟基己酸及其环状形式；术语“乳酸”或“丙交酯”包括L-乳酸、D-乳酸、其混合物及二聚物，即L-丙交酯、D-丙交酯、内消旋丙交酯及其任何混合物。
18.聚碳酸酯和聚酯碳酸酯。
19.聚酮。
20.聚砜、聚醚砜和聚醚酮。
21.交联聚合物，其一方面衍生自醛，另一方面衍生自酚类、脲类和三聚氰胺类，例如苯酚/甲醛树脂、尿素/甲醛树脂及三聚氰胺/甲醛树脂。
22.干性和非干性醇酸树脂。
23.不饱和聚酯树脂，其衍生自饱和和不饱和二羧酸与多元醇以及作为交联剂的乙烯基化合物的共聚酯，及其低可燃性的含卤改性产物。
24.可交联丙烯酸系树脂，其衍生自取代的丙烯酸酯，例如丙烯酸环氧酯、氨基甲酸酯丙烯酸酯或聚酯丙烯酸酯。
25.用三聚氰胺树脂、尿素树脂、异氰酸酯、异氰脲酸酯、多异氰酸酯或环氧树脂交联的醇酸树脂、聚酯树脂和丙烯酸酯树脂。
26.交联环氧树脂，其衍生自脂族、脂环族、杂环族或芳族缩水甘油基化合物，例如双酚A及双酚F的二缩水甘油醚的产物，其在存在或不存在促进剂下使用常规硬化剂如酸酐或胺交联。
27.上述聚合物的共混物(聚合物共混物)，例如PP/EPDM、聚酰胺/EPDM或ABS、PVC/EVA、PVC/ABS、PVC/MBS、PC/ABS、PBTP/ABS、PC/ASA、PC/PBT、PVC/CPE、PVC/丙烯酸酯、POM/热塑性PUR、PC/热塑性PUR、POM/丙烯酸酯、POM/MBS、PPO/HIPS、PPO/PA66及共聚物、PA/HDPE、PA/PP、PA/PPO、PBT/PC/ABS或PBT/PET/PC。
28.天然和合成的有机材料，其为纯单体化合物或这些化合物的混合物，例如矿物油、动物和植物脂肪、油和蜡、或基于合成酯(例如邻苯二甲酸酯、己二酸酯、磷酸酯或偏苯三酸酯)的油、脂肪和蜡、以及合成酯与矿物油的任意重量比的混合物，典型地为用作纺丝组合物的那些、以及这些材料的水性乳液。
优选的有机材料为：
1)烯烃单体如乙烯和丙烯以及更高级1-烯烃如1-丁烯、1-戊烯、1-己烯或1-辛烯的均聚物和共聚物。优选聚乙烯LDPE和LLDPE、HDPE和聚丙烯。
2)烯烃单体与二烯烃单体如丁二烯、异戊二烯和环烯烃如降冰片烯的均聚物和共聚物。
3)一种或多种1-烯烃和/或二烯烃与一氧化碳和/或与其他乙烯基单体，包括但不限于乙酸乙烯酯、乙烯基酮、苯乙烯、马来酸酐和氯乙烯的共聚物。
4)聚乙烯醇。
5)其他热塑性塑料如聚苯乙烯、苯乙烯-丙烯腈共聚物、丙烯腈-丁二烯-苯乙烯共聚物、聚氯乙烯、聚偏二氯乙烯、聚乙酸乙烯酯、聚乙烯醇丁醛、乙烯-乙烯醇共聚物、聚对苯二甲酸乙二醇酯(PET)、聚对苯二甲酸丁二醇酯(PBT)、液晶聚酯(LCP)、聚缩醛(例如POM)、聚酰胺(PA)、聚碳酸酯、聚氨酯和聚苯硫醚(PPS)；两种或更多种这些树脂形成的聚合物共混物或聚合物合金；以及通过添加填料如玻璃纤维、碳纤维、半碳化纤维、纤维素纤维和玻璃珠、阻燃剂、发泡剂、抗微生物剂、交联剂、聚烯烃树脂细粉、聚烯烃蜡、亚乙基双酰胺蜡、金属皂等单独或组合至这些树脂获得的化合物。另一方面，热固性树脂的实例可包括热固性树脂如环氧树脂、蜜胺树脂和不饱和聚酯树脂；以及通过掺入填料如玻璃纤维、碳纤维、半碳化纤维、纤维素纤维和玻璃珠、阻燃剂等单独或组合至这些树脂获得的化合物。
其他优选的聚合物为：天然或合成来源的可生物降解聚合物，包括但不限于聚琥珀酸乙二醇酯，聚琥珀酸丁二醇酯，聚琥珀酸丁二醇酯/己二酸丁二醇酯，聚琥珀酸丁二醇酯/碳酸丁二醇酯，聚琥珀酸丁二醇酯/对苯二甲酸丁二醇酯，聚己内酯，聚(羟基链烷酸酯)，聚-3-羟基丁酸酯，聚乳酸，聚酯酰胺或这些材料与天然或改性淀粉、多糖、木素、木粉、纤维素或几丁质的共混物。
所述聚合物优选为热塑性天然或合成聚合物，尤其是选自上述组中的一种。优选聚烯烃均聚物或共聚物，淀粉改性聚烯烃或淀粉基聚合物复合材料，特别优选聚乙烯、聚丙烯、聚乙烯共聚物或聚丙烯共聚物。
所述填料包括：例如碳酸钙、二氧化硅、玻璃纤维、玻璃泡、滑石、高岭土、云母、硫酸钡、金属氧化物和氢氧化物、炭黑、石墨、木粉、其他天然产物的粉、合成纤维、用作填料的硬脂酸盐如硬脂酸钙或硬脂酸锌。
本发明的聚合物模塑组合物适用于生产纤维、涂料、膜或模塑品。
本发明还提供一种用于制备聚合物组合物的方法，包括将本发明的用于聚合物的添加剂A和/或本发明的添加剂组合物与聚合物粒料和可有可无的填料在混合机中混合，和在相对高的温度下在挤出机装置中将它们在聚合物熔体中匀化，并随后引出该匀化的聚合物挤出物，冷却，切粒。挤出机装置选自单螺杆挤出机，或双螺杆挤出机。优选的加工温度对于聚苯乙烯是170至200℃，对于聚丙烯是200至300℃，对于聚对苯二甲酸乙二醇酯(PET)是250至290℃，对于聚对苯二甲酸丁二醇酯(PBT)是230至270℃，对于聚酰胺-6(PA6)是260至290℃，对于聚酰胺-66(PA66)是260至290℃，和对于聚碳酸酯是280至320℃。可用于本发明的配混组合装置是单螺杆挤出机，或双螺杆挤出机，用于本发明的有效螺杆长度在单螺杆挤出机的情况下是20至4OD；本发明中的有效螺杆长度在双螺杆挤出机的情况下是8至48D。
具体实施方式
下面通过具体实施方式来进一步说明本发明，以下实施例为本发明较佳的实施方式，但本发明的实施方式并不受下述实施例的限制。
实施例1：
选择二丁基氧化锡为催化剂，将催化剂和反应原料3,5-二叔丁基-4-羟基苯丙酸甲酯(市售)和季戊四醇(市售)加入反应釜中，其中3,5-二叔丁基-4-羟基苯丙酸甲酯380g，季戊四醇42g，两者的摩尔比约为4.2，催化剂用量为0.3g，调节反应釜压力为650Pa，在175℃下反应7h后升温至200℃继续反应1h，降温至145℃，进行半小时的中和反应。得到的产物选择甲醇为结晶溶剂，冷却结晶抽滤即可得到目标产品。
实施例2-8，对比例1-3
将实施例1制备的化合物分别与含磷物质复配，通过调整聚合物添加剂A中实施例1产物的重量，得到特定磷元素含量的聚合物添加剂C。具体复配方法为，首先将实施例1制备的化合物与含磷物质复配成具有较高磷元素含量的母样，测得磷元素的重量含量，然后根据最终结果所需要的磷元素的含量计算第二次含量。再以同样方法得到含钛元素的聚合物添加剂D。按照最终需要的磷元素和钛元素的含量比例，称取对应比例的聚合物添加剂C和聚合物添加剂D，得到聚合物添加剂A。
红磷：分析纯，济宁百川化工有限公司
磷酸二氢钾：常州市川磷化工有限公司
三苯基膦：上海长根化学科技有限公司
纳米二氧化钛：T104943，上海阿拉丁生化科技股份有限公司
钛酸四丁酯：上海阿拉丁生化科技股份有限公司
二氯二茂钛：上海阿拉丁生化科技股份有限公司
其中，
实施例2、5中的磷元素来自：红磷
实施例3、6中的磷元素来自：磷酸二氢钾
实施例4、7、8中的磷元素来自：三苯基膦
实施例2、5中的钛元素来自：纳米二氧化钛
实施例3、6中的钛元素来自：钛酸四丁酯
实施例4、7、8中的钛元素来自：二氯二茂钛
表1
将实施例1制备的化合物分别按照上述方法复配，具体含量如表2所示：
其中，
对比例1中的磷元素来自：红磷
对比例2中的磷元素来自：磷酸二氢钾
对比例3中的磷元素来自：三苯基膦
对比例1中的钛元素来自：纳米二氧化钛
对比例2中的钛元素来自：钛酸四丁酯
对比例3中的钛元素来自：二氯二茂钛
表2
实施例9-15，对比例4-6
将实施例2-8及对比例1-3所得的聚合物添加剂在按表3和表4所述产品组分重量含量百分比称取。
聚乙烯：FB2230，北欧化工
聚酰胺：PA6，广州新汇美达公司，M2400
紫外光吸收剂：山东青岛华恩化工有限公司，UV327
玻璃纤维：PPG，ChopVantage3540
滑石粉：LuzenacR7
当聚合物选自聚乙烯时，将上述聚乙烯和其它各组分先放入转速约为1000rpm的高速混合器中干混合1分钟，如有滑石粉，则加入滑石粉填料再混合2分钟。将混合的原料置于双螺杆挤出机中经熔融挤出，造粒，其工艺条件为：一区200℃，二区210℃，三区220℃，四区215℃；双螺杆挤出机长径比为40，螺杆转速为450转/分钟，停留时间为1分钟，压力为10Mpa。
当聚合物选自聚酰胺时，将上述聚酰胺和其它各组分先放入转速约为1000rpm的高速混合器中干混合3分钟，将混合的原料置于双螺杆挤出机中经熔融挤出，造粒，其工艺条件为：螺筒各分区温度保持在280℃，双螺杆挤出机长径比为40，螺杆转速为450转/分钟；停留时间为1分钟，压力为10Mpa。
表3(百分重量)
表4(百分重量)
对比例4 对比例5 对比例6
对比例1产物 0.3
对比例2产物 0.1
对比例3产物 0.5
聚乙烯 79.7 69.1
聚酰胺 99.9
紫外光吸收剂 0.4
滑石粉 20
玻璃纤维 30
有机物阻隔性能(mg/天) 49.3 62.4 78.3
有机物阻隔性能：
使用实施例9－15、对比例4－6得到的聚合物组合物，制备外径10mm、壁厚2mm、长度100mm的管，将其一个端部密封，向内部加满乙醇和甲苯按照60/40体积比混合得到的有机物液体，然后将另一端部也密封，测定整体重量，接着将管放入60摄氏度烘箱中放置50天，测定重量变化，评价有机物阻隔性能。

Claims (6)

1.一种用于聚合物的添加剂A，包括如式X所示结构式的化合物：
其中，基于添加剂A的总重量，磷元素和钛元素的总重量含量为10ppm-525ppm，更优选22ppm-308ppm，
2.如权利要求1所述的聚合物添加剂A中，其特征在于：磷元素含量大于钛元素含量。
3.一种添加剂组合物，其特征在于，包含如式X所示结构式的化合物：
和至少一种不同于式X所述化合物的其它添加剂B，其中，基于添加剂组合物的总重量，磷元素和钛元素的总重量含量为10ppm-525ppm，更优选22ppm-308ppm；基于添加剂组合物的总重量，优选包含50至99.9％重量的一种如式X所述的化合物，和0.1至50％重量的至少一种不同于式X所述化合物的其它添加剂B，其中，基于添加剂组合物的总重量，磷元素和钛元素的总重量含量为10ppm-525ppm，更优选22ppm-308ppm。
4.一种聚合物组合物，其特征在于，包含如权利要求1至2中任一项所述的用于聚合物的添加剂A，或如权利要求3中所述的添加剂组合物。
5.如权利要求4中所要求的聚合物组合物，其特征在于，包含重量含量为30-99.9％的聚合物，重量含量为0-60％的填料，重量含量为0.1-10％的如权利要求1至2中任一项所述的用于聚合物的添加剂A或重量含量为0.1-10％如权利要求3中所述的添加剂组合物。
6.一种如权利要求4至5中任一项所要求的聚合物组合物，其特征在于，所述聚合物为聚丙烯、聚乙烯、ABS、聚苯乙烯、聚酰胺、聚氯乙烯、聚酯、聚甲醛中的一种或多种组合物，优选聚酰胺、聚乙烯、ABS中的一种或多种。
CN201610089346.2A 2016-02-17 2016-02-17 一种用于聚合物的添加剂及其制备方法以及由其组成的聚合物组合物 Pending CN105542285A (zh)