CN105513693B - A kind of electric wire - Google Patents
A kind of electric wire Download PDFInfo
- Publication number
- CN105513693B CN105513693B CN201610108954.3A CN201610108954A CN105513693B CN 105513693 B CN105513693 B CN 105513693B CN 201610108954 A CN201610108954 A CN 201610108954A CN 105513693 B CN105513693 B CN 105513693B
- Authority
- CN
- China
- Prior art keywords
- parts
- layer
- sent
- electric wire
- flame retardant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
Claims (4)
- A kind of 1. electric wire, it is characterised in that:Including matcoveredn, the protective layer is provided with three layers, distinguishes from outside to inside It is external protection, flame retardant coating and first screen layer, the external protection, flame retardant coating and the integrated setting of first screen layer, institute The cable main that protective layer is internally provided with more than one is stated, the cable main is provided with four layers, is exhausted respectively from outside to inside Edge layer, the first enhancement layer, secondary shielding layer and conductor, the second enhancement layer, institute are provided between the cable main and protective layer State flame retardant coating by match in parts by weight kaolin 30-50 parts, boric acid 20-24 parts, sodium metasilicate 18-20 parts, bauxite 28-30 Part, boron nitride 16-18 parts, silica 1 8-20 parts, mullite 23-30 parts, carborundum 22-24 parts, corundum 12-16 parts, oxidation Magnesium 16-18 parts, calcium oxide 12-14 parts, chromium oxide 16-20 parts, dicalcium silicate 12-16 parts, tricalcium silicate 12-16 parts and zirconium silicate 16-18 parts are made, and the external protection surface is provided with waterproof membrane, and fluorescence is provided between the external protection and flame retardant coating Layer, scale is provided with the external protection, the manufacture method of the flame retardant coating, includes following steps:1) kaolin 30-50 parts are taken to be sent into calcining furnace, calcining heat is gradually raised to 1100 DEG C from 880 DEG C, heating rate 10 DEG C/min, then calcined again at 1100 DEG C 2 hours, be incubated 2 hours, natural cooling discharging is standby;2) take bauxite 28-30 parts to be sent into airslide disintegrating mill and be ground into 200nm-300nm powder, then add boric acid 20-24 Part and sodium metasilicate 18-20 parts, it is sent into heater, temperature rises to 500-600 DEG C, continues 1-2 hours, standby;3) take mullite 23-30 parts, carborundum 22-24 parts and corundum 12-16 parts to be sent into airslide disintegrating mill and be ground into particle, then It is sent into mixer, stirs, it is standby;4) obtained raw material in step 1), step 2) and step 3) is sent into mixer, stirred, is sent into melting furnace, Temperature rises to 900-1000 DEG C, continues 2-3 hours, standby;5) magnesia 16-18 parts, calcium oxide 12-14 parts and chromium oxide 16-20 parts is taken to be sent into heater, temperature rises to 60-80 DEG C, then dicalcium silicate 12-16 parts, tricalcium silicate 12-16 parts and zirconium silicate 16-18 parts are added, and room temperature is naturally cooled to, it is standby;6) obtained material in step 5) is sent into step 4), temperature rises to 1000-1200 DEG C, continues 3-5 hours, is melted Melt thing, it is standby;7) cast maintenance in the fused mass injection mould in step 6) is stripped for 12 hours, then normal temperature conserves five days, you can electricity is made The flame retardant coating of line cable.
- A kind of 2. electric wire as claimed in claim 1, it is characterised in that:The external protection is resin insulating barrier.
- A kind of 3. electric wire as claimed in claim 1, it is characterised in that:Second enhancement layer be internally provided with one with On reinforcement.
- A kind of 4. electric wire as claimed in claim 1, it is characterised in that:It is provided between the conductor and secondary shielding layer Rubber layer.