CN105506689B - Battery steel shell made from a kind of battery steel shell duplex nickel plating technique and the technique - Google Patents
Battery steel shell made from a kind of battery steel shell duplex nickel plating technique and the technique Download PDFInfo
- Publication number
- CN105506689B CN105506689B CN201510965886.8A CN201510965886A CN105506689B CN 105506689 B CN105506689 B CN 105506689B CN 201510965886 A CN201510965886 A CN 201510965886A CN 105506689 B CN105506689 B CN 105506689B
- Authority
- CN
- China
- Prior art keywords
- steel shell
- nickel
- battery steel
- bright nickel
- plating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
A kind of battery steel shell duplex nickel plating technique, comprises the following steps：A, battery steel shell is pre-processed；B, pretreated battery steel shell surface is once electroplated, plating is covered with half light nickel coating；C, second time electroplating is carried out to the battery steel shell after step b processing, plating is covered with a bright nickel coating, and the oxidizing potential of the bright nickel plating layer is less than described half bright nickel coating.The invention also discloses one kind using battery steel shell made from above-mentioned technique.In the present invention, by plating the bright coating of one layer of not semi-bright nickel coating, then one layer of sulfur-bearing of re-plating of sulfur-bearing on present battery steel shell.Because the bright nickel current potential of sulfur-bearing is relatively negative, between bright nickel and semi-bright nickel, produce potential difference, form corrosion galvanic cell, the higher bright nickel of sulfur-bearing turns into anode, and the semi-bright nickel of bottom turns into negative electrode, and bright nickel layer, which turns into, sacrifices coating and be corroded, corrosive medium is delayed to the corrosion rate of iron-based body, significantly improves the decay resistance of coating.
Description
Technical field
The present invention relates to a kind of production technology of battery steel shell, refers in particular to a kind of battery steel shell duplex nickel plating technique and is somebody's turn to do
Battery steel shell made from technique.
Background technology
Battery steel shell is one of critical material for producing dry cell.The production of current battery box hat is divided into two major classes substantially,
One kind is nickel plated steel strip punch forming and then degreasing, antirust treatment, referred to as first nickel plated steel shell；Another kind is by steel strip stamping
Shaping and then degreasing, electronickelling processing, box hat is electroplated after being referred to as.In the prior art, for the barrel plating technology of rear plating box hat
The technology of last century the nineties is also maintained at present, by constantly improve, additive mode electronickelling is selected, due to battery skill
The continuous change of art, battery performance improve constantly, and service time of battery is increasingly longer, it is necessary to which the antiseptic property of battery steel shell also will
It is correspondingly improved, original nickel plated steel shell is difficult to meet the needs of high-performance, high-capacity battery.
The content of the invention
The present invention provides battery steel shell made from a kind of battery steel shell duplex nickel plating technique and the technique, and its main purpose exists
In overcoming the defects of existing battery steel shell is in corrosion resistance deficiency during long-term use.
In order to solve the above technical problems, the present invention adopts the following technical scheme that：
A kind of battery steel shell duplex nickel plating technique, comprises the following steps：A, battery steel shell is pre-processed；B, to pre- place
Battery steel shell surface after reason is once electroplated, and plating is covered with half light nickel coating；C, to the battery after step b processing
Box hat carries out second time electroplating, and plating is covered with a bright nickel coating, and the oxidizing potential of the bright nickel plating layer is less than half bright nickel plating
Layer.
Further, in stepb, the once plating includes battery steel shell being placed in a semi-bright nickel technique electroplate liquid
Middle plating 120 minutes, wherein semi-bright nickel technique electroplate liquid includes：300 g/l of nickel sulfate, 50 g/l of nickel chloride, boric acid 40
G/l, 0.15 g/l of cumarin, 0.15 g/l of formaldehyde, the pH of the semi-bright nickel technique electroplate liquid is 4.0, and solution temperature is
50℃。
Further, in step c, the battery steel shell that the second time electroplating is included after step b processing is placed in a light
Electroplated 60 minutes in bright nickel technique electroplate liquid, wherein bright nickel technique electroplate liquid includes：300 g/l of nickel sulfate, nickel chloride 50
G/l, 40 g/l of boric acid, the ml l of additive 10, the pH of the bright nickel technique electroplate liquid is 4.0, and solution temperature is 50 DEG C.
Further, in step a, after pre-processing battery steel shell degreasing, washing, pickling and the acid for including sequentially carrying out
Wash this four procedure.
Further, in addition to the step d, the step d after the step c includes the battery sequentially carried out
Box hat recovery, washing, antirust treatment, dry this four procedure.
A kind of battery steel shell for improving corrosive nature, including a box hat base material and a bright nickel plating layer, the box hat base material
Surface covered with an oxidizing potential be more than the bright nickel plating layer half bright nickel coating, the upper surface of the half bright nickel coating
Covered with above-mentioned bright nickel plating layer.
Further, the thickness summation of described half bright nickel coating and bright nickel plating layer is 1.8 μm~2.3 μm.
Further, the thickness of described half bright nickel coating is 0.5 μm~1.5 μm.
Further, described half bright nickel coating is covered in the surface of box hat base material by one plating steps, described
Once plating includes box hat base material being placed in a semi-bright nickel technique electroplate liquid electroplating 120 minutes, wherein semi-bright nickel technique
Electroplate liquid includes：300 g/l of nickel sulfate, 50 g/l of nickel chloride, 40 g/l of boric acid, 0.15 g/l of cumarin, formaldehyde 0.15
G/l, the pH of the semi-bright nickel technique electroplate liquid is 4.0, and solution temperature is 50 DEG C.
Further, the bright nickel plating layer is covered in the upper table of described half bright nickel coating by a second time electroplating step
Face, the box hat base material that the second time electroplating includes will be covered with half bright nickel coating are placed in a bright nickel technique electroplate liquid and electroplated
60 minutes, wherein bright nickel technique electroplate liquid included：300 g/l of nickel sulfate, 50 g/l of nickel chloride, 40 g/l of boric acid, addition
The ml l of agent 10, the pH of the bright nickel technique electroplate liquid is 4.0, and solution temperature is 50 DEG C.
Compared to the prior art, beneficial effect caused by the present invention is:
1st, in the present invention, it is then electric again by plating the semi-bright nickel coating of one layer of not sulfur-bearing on present battery steel shell
Plate the bright coating of one layer of sulfur-bearing.Because the bright nickel current potential of sulfur-bearing is relatively negative, between bright nickel and semi-bright nickel, current potential is produced
Difference, form corrosion galvanic cell, the higher bright nickel of sulfur-bearing turns into anode, and the semi-bright nickel of bottom turns into negative electrode, bright nickel layer into
It is corroded to sacrifice coating, delays corrosive medium to the corrosion rate of iron-based body, significantly improves the decay resistance of coating.
2nd, not only antiseptic property significantly improves the coating as made from present invention process, and equal nickel plating layer thick antiseptic property is extremely
Double less, and the electric conductivity of coating, weldability, adhesion are good, can be well adapted for meeting high-performance, high power capacity
The demand of battery.
3rd, in the present invention, compared to more conventional pure nickel plating scheme, the method can significantly improve the antiseptic property of coating, together
When the elongation percentage of coating, electric conductivity, welding performance, adhesion it is unchanged, meet the raising of battery capacity and prolonging for service life
It is long.
Brief description of the drawings
Fig. 1 is the structural representation of battery steel shell described in the embodiment of the present invention one.
Fig. 2 is the preparation flow figure of battery steel shell described in the embodiment of the present invention one.
Fig. 3 is the structural representation of battery steel shell described in the embodiment of the present invention two.
Fig. 4 is the preparation flow figure of battery steel shell described in the embodiment of the present invention two.
Fig. 5 is the rust-proof effect instance graph that battery steel shell carries out salt mist experiment in the prior art.
Fig. 6 is the rust-proof effect instance graph that battery steel shell carries out salt mist experiment described in the embodiment of the present invention one.
Fig. 7 is the rust-proof effect instance graph that battery steel shell carries out salt mist experiment described in the embodiment of the present invention two.
Fig. 8 is the rust-proof effect instance graph that battery steel shell carries out Bluepoint experiment in the prior art.
Fig. 9 is the rust-proof effect instance graph that battery steel shell carries out Bluepoint experiment described in the embodiment of the present invention one.
Figure 10 is the rust-proof effect instance graph that battery steel shell carries out Bluepoint experiment described in the embodiment of the present invention two.
Embodiment
Illustrate the embodiment of the present invention with reference to the accompanying drawings.
Embodiment one
Referring to Figures 1 and 2.A kind of battery steel shell 1 for improving corrosive nature, including a box hat base material 2 and a bright nickel plating
Layer 3, the surface of the box hat base material 2 are more than half bright nickel coating 4 of the bright nickel plating layer 3 covered with an oxidizing potential, should
The upper surface of half bright nickel coating 4 is covered with above-mentioned bright nickel plating layer 3.
Referring to Figures 1 and 2.As the preferred scheme of the present embodiment, the half bright nickel coating 4 and bright nickel plating layer 3
Thickness summation is 1.8 μm~2.3 μm.The thickness for being more highly preferred to half bright nickel coating 4 described in scheme as the present embodiment is
0.5 μm~1.5 μm.
Referring to Figures 1 and 2.The thickness of the wherein described bright nickel coating 4 of semi-gloss can be 1.2 μm, while bright nickel plating layer 3
Thickness can be 0.8 μm.
Referring to Figures 1 and 2.The preparation method of above-mentioned battery steel shell 1 is：
A kind of battery steel shell duplex nickel plating technique, comprises the following steps：
A, battery steel shell 1 is pre-processed.This step can be preferably：The pretreatment of battery steel shell 1 includes sequentially carrying out
Degreasing → washing → pickling → acid after wash this four procedure.
B, the pretreated surface of battery steel shell 1 is once electroplated, plating is covered with half light nickel coating.This step can
To be preferably：The once plating includes battery steel shell 1 being placed in a semi-bright nickel technique electroplate liquid electroplating 120 minutes, its
Middle semi-bright nickel technique electroplate liquid includes：300 g/l of nickel sulfate, 50 g/l of nickel chloride, 40 g/l of boric acid, cumarin 0.15
G/l, 0.15 g/l of formaldehyde, the pH of the semi-bright nickel technique electroplate liquid is 4.0, and solution temperature is 50 DEG C.
C, second time electroplating is carried out to the battery steel shell 1 after step b processing, plating is covered with a bright nickel coating, the light
The oxidizing potential of nickel coating 3 is less than described half bright nickel coating 4.This step can be preferably：The second time electroplating includes passing through
Battery steel shell 1 after step b processing, which is placed in a bright nickel technique electroplate liquid, electroplates 60 minutes, wherein bright nickel technique electroplate liquid
Including：300 g/l of nickel sulfate, 50 g/l of nickel chloride, 40 g/l of boric acid, the ml l of additive 10, bright nickel technique electricity
The pH of plating solution is 4.0, and solution temperature is 50 DEG C.
D, battery steel shell 1 is sequentially carried out reclaiming → wash → antirust treatment → and dries this four procedure.
In the present embodiment, it is then electric again by plating the semi-bright nickel coating of one layer of not sulfur-bearing on present battery steel shell 1
Plate the bright coating of one layer of sulfur-bearing.Because the bright nickel current potential of sulfur-bearing is relatively negative, between bright nickel and semi-bright nickel, current potential is produced
Difference, form corrosion galvanic cell, the higher bright nickel of sulfur-bearing turns into anode, and the semi-bright nickel of bottom turns into negative electrode, bright nickel layer into
It is corroded to sacrifice coating, delays corrosive medium to the corrosion rate of iron-based body, significantly improves the decay resistance of coating.
Embodiment two
Reference picture 3 and Fig. 4.A kind of battery steel shell 1 of corrosion resistance improvement, including a box hat base material 2, a bright nickel plating
The half bright oxidizing potential of nickel coating 4 and one that 3, one oxidizing potential of layer is more than the bright nickel plating layer 3 is less than the bright plating
The high-sulfur nickel coating 5 of nickel dam 3, the half bright nickel coating 4 are covered in the surface of the box hat base material 2, half bright nickel plating
The upper surface of layer 4 is covered with the high-sulfur nickel coating 5, and the upper surface of the high-sulfur nickel coating 5 is covered with the bright nickel plating layer
3。
Reference picture 3 and Fig. 4.As the preferred scheme of the present embodiment, the half bright nickel coating 4, high-sulfur nickel coating 5 and
The thickness summation of bright nickel plating layer 3 is 1.8 μm~2.3 μm.As the scheme that is more highly preferred to of the present embodiment, the high-sulfur nickel plating
The thickness of layer 5 is 0.8 μm~1.2 μm.As the preferred plan of the present embodiment, the thickness of the high-sulfur nickel coating 5 is 1 μm.
Referring to Figures 1 and 2.The thickness of the wherein described bright nickel coating 4 of semi-gloss can be 0.4 μm, while bright nickel plating layer 3
Thickness can be 0.6 μm.The thickness of the high-sulfur nickel coating 5 can be 1 μm.
Reference picture 3 and Fig. 4.The preparation method of above-mentioned battery steel shell 1 is：
A kind of 1 three layers of nickel plating technology of battery steel shell, comprise the following steps：
A, battery steel shell 1 is pre-processed.This step can be preferably：The pretreatment of battery steel shell 1 includes sequentially carrying out
Degreasing → washing → pickling → acid after wash this four procedure.
B, the pretreated surface of battery steel shell 1 is once electroplated, plating is covered with half light nickel coating.This step can
To be preferably：The once plating includes battery steel shell 1 being placed in a semi-bright nickel technique electroplate liquid electroplating 100 minutes, its
Middle semi-bright nickel technique electroplate liquid includes：300 g/l of nickel sulfate, 50 g/l of nickel chloride, 40 g/l of boric acid, cumarin 0.15
G/l, 0.15 g/l of formaldehyde, the pH of the semi-bright nickel technique electroplate liquid is 4.0, and solution temperature is 50 DEG C.
C, second time electroplating is carried out to the battery steel shell 1 after step b processing, plating is covered with a high-sulfur nickel coating.This step
Can be preferably：The second time electroplating includes that high-sulfur nickel technique electricity will be placed in including the battery steel shell 1 after step b processing
Electroplated 20 minutes in plating solution, wherein high-sulfur nickel technique electroplate liquid includes：300 g/l of nickel sulfate, 50 g/l of nickel chloride, boric acid 40
G/l, 1 g/l of benzene sulfinic acid sodium salt, 0.5 g/l of butynediols, 1 g/l of saccharin, the pH of the high-sulfur nickel technique electroplate liquid is
2.5, solution temperature is 50 DEG C.
D, the battery steel shell 1 after step c processing is electroplated three times, plating is covered with a bright nickel plating layer 3.This step
Can be preferably：The battery steel shell 1 that the plating three times is included after step c processing is placed in a bright nickel technique electroplate liquid
Plating 60 minutes, wherein bright nickel technique electroplate liquid includes：300 g/l of nickel sulfate, 50 g/l of nickel chloride, 40 g/l of boric acid,
The ml l of additive 10, the pH of the bright nickel technique electroplate liquid is 4.0, and solution temperature is 50 DEG C.
E, battery steel shell 1 is sequentially carried out reclaiming → wash → antirust treatment → and dries this four procedure.
In the present embodiment, by setting 3 and half bright nickel coating 4 of bright nickel plating layer, and in the light plating of double layer nickel
Between 3 and half bright nickel coating 4 of nickel dam, the high-sulfur that strike plating last layer thickness is about 1 μm or so plates nickel coating, due to three layers of nickel
Between potential difference be present, the half bright current potential of nickel coating 4 is more than the current potential of bright nickel plating layer 3, and the current potential of bright nickel plating layer 3 plates more than high-sulfur
The current potential of nickel dam 5, thus in corrosion process, the more negative coating of current potential is preferentially corroded, so in three layers of nickel system as anode
The anti-corrosion capability of half bright nickel coating 4 can arrive great lifting, be advantageous to further delay corrosive medium to iron-based body
Corrosion rate, and significantly improve the decay resistance of coating.
Embodiment three
Choose the Corrosion Protection analysis that three groups of samples carry out experiment product
The thickness of coating of each sample（Middle part thickness μm outside box hat）
| 1 | 2 | 3 | 4 | 5 | |
| Sample A | 2.03 | 1.98 | 1.94 | 2.13 | 1.89 |
| Sample B | 1.98 | 2.00 | 1.88 | 1.99 | 2.09 |
| Sample C | 2.12 | 1.95 | 2.22 | 1.97 | 1.90 |
Wherein sample A is using battery steel shell 1 made from existing electroplating technology, and sample B is battery described in embodiment one
Box hat 1, sample C are battery steel shell 1 described in embodiment two.
Fig. 5 shows the rust-proof effect instance graph of the progress of battery steel shell 1 salt mist experiment in the prior art.Fig. 6 shows the present invention
Battery steel shell 1 described in embodiment one carries out the rust-proof effect instance graph of salt mist experiment.Fig. 7 shows institute in the embodiment of the present invention two
State the rust-proof effect instance graph that battery steel shell 1 carries out salt mist experiment.
The condition of above salt mist experiment is：Using 5%Nacl solution spraying continuous to sample 8 hours.
Reference picture 5, Fig. 6 and Fig. 7.Sample A is existing common individual layer nickel technique, rust area 10%, protects 3 grades.Sample B
Double layer nickel technique, rust area are less than 0.25%, protect 8 grades.Tri- layers of nickel techniques of sample C, zero defect, protect 10 grades.By above-mentioned
Understand, battery steel shell 1 made from the duplex nickel plating technique disclosed using embodiment one is obtained relative to existing common individual layer nickel technique
The battery steel shell 1 obtained, its corrosion resistance lifting several times.
And battery steel shell 1 made from three layers of nickel plating technology of the disclosure of embodiment two is used, because it is the half of double layer nickel
Between bright and bright nickel, high-sulfur nickel that strike plating a layer thickness is about 1um or so, depend between three layers of nickel and current potential be present
Difference, semi-bright nickel current potential are more than bright nickel current potential, and bright nickel current potential is more than high-sulfur nickel current potential, thus in corrosion process, current potential compared with
Negative coating is preferentially corroded, so the anti-corrosion capability of the semi-bright nickel in three layers of nickel system, than in bilayer as anode
It is higher in nickel, thus the corrosion resistance of battery steel shell 1 described in embodiment two is relative to battery steel shell 1 described in embodiment one
Several times are lifted again.
Example IV
Choose the Corrosion Protection analysis that three groups of samples carry out experiment product
The thickness of coating of each sample（Middle part thickness μm outside box hat）
| 1 | 2 | 3 | 4 | 5 | |
| Sample A | 2.03 | 1.98 | 1.94 | 2.13 | 1.89 |
| Sample B | 1.98 | 2.00 | 1.88 | 1.99 | 2.09 |
| Sample C | 2.12 | 1.95 | 2.22 | 1.97 | 1.90 |
Wherein sample A is using battery steel shell 1 made from existing electroplating technology, and sample B is battery described in embodiment one
Box hat 1, sample C are battery steel shell 1 described in embodiment two.
Fig. 8 shows the rust-proof effect instance graph of the progress of battery steel shell 1 Bluepoint experiment in the prior art.Fig. 9 shows the present invention
Battery steel shell 1 described in embodiment one carries out the rust-proof effect instance graph of Bluepoint experiment.Figure 10 is shown in the embodiment of the present invention two
The battery steel shell 1 carries out the rust-proof effect instance graph of Bluepoint experiment.
The above Bluepoint experiment condition be：Sample is carried out after filter paper is soaked 5 minutes with the potassium ferricyanide+sodium chloride solution
Covering.
Reference picture 8, Fig. 9 and Figure 10.Sample A is existing common individual layer nickel technique, and it has serious Bluepoint, and area is very
Greatly.Sample B uses double layer nickel technique, slight Bluepoint.Sample C uses three layers of nickel technique, no Bluepoint.
In summary, battery steel shell 1 is relative to existing common made from the duplex nickel plating technique disclosed using embodiment one
The battery steel shell 1 that individual layer nickel technique obtains, its corrosion resistance lifting several times, and the three layers of nickel plating technology disclosed in embodiment two
Obtained battery steel shell 1 lifts several times again relative to the battery steel shell 1 in embodiment one, its corrosion resistance.
Additive used is to be used to improve battery steel shell coating surface state in field of electroplating, improve in description above
The electroplating additive of its electrical property and welding performance, such additives are the common technology in the field, thus herein not to it
Specific composition is described in detail.
The embodiment of the present invention is above are only, but the design concept of the present invention is not limited thereto, it is all to utilize this
Conceive the change that unsubstantiality is carried out to the present invention, the behavior for invading the scope of the present invention all should be belonged to.
Claims (3)
1. a kind of battery steel shell duplex nickel plating technique, it is characterised in that comprise the following steps：A, battery steel shell is located in advance
Reason；B, pretreated battery steel shell surface is once electroplated, plating is covered with half light nickel coating；C, to passing through step b
Battery steel shell after processing carries out second time electroplating, and plating is covered with a bright nickel coating, and the oxidizing potential of the bright nickel plating layer is less than institute
Half bright nickel coating is stated, in stepb, the once plating includes battery steel shell being placed in a semi-bright nickel technique electroplate liquid
Plating 120 minutes, wherein semi-bright nickel technique electroplate liquid includes：300 g/l of nickel sulfate, 50 g/l of nickel chloride, 40 grams of boric acid/
Liter .15 g/l of cumarin 0 .15 g/l of formaldehyde 0, the pH of the semi-bright nickel technique electroplate liquid is 4 .0, and solution temperature is
50 DEG C, in step c, the battery steel shell that the second time electroplating is included after step b processing is placed in bright nickel technique plating
Electroplated 60 minutes in liquid, wherein bright nickel technique electroplate liquid includes：300 g/l of nickel sulfate, 50 g/l of nickel chloride, boric acid 40
G/l, the ml l of additive 10, the pH of the bright nickel technique electroplate liquid is 4 .0, and solution temperature is 50 DEG C.
A kind of 2. battery steel shell duplex nickel plating technique as claimed in claim 1, it is characterised in that：In step a, pretreatment includes
This four procedure is washed after the battery steel shell degreasing, washing, pickling and the acid that sequentially carry out.
A kind of 3. battery steel shell duplex nickel plating technique as claimed in claim 2, it is characterised in that：Also it is located at the step including one
Battery steel shell recovery that step d after c, the step d include sequentially carrying out, washing, antirust treatment, dry this four work
Sequence.