CN105505145A - Low-resistance powder paint - Google Patents
Low-resistance powder paint Download PDFInfo
- Publication number
- CN105505145A CN105505145A CN201610093947.0A CN201610093947A CN105505145A CN 105505145 A CN105505145 A CN 105505145A CN 201610093947 A CN201610093947 A CN 201610093947A CN 105505145 A CN105505145 A CN 105505145A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder paint
- resistance powder
- powder coating
- carbon black
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses low-resistance powder paint. The low-resistance powder paint is prepared from, by weight, 60-70 parts of carboxyl-terminated polyester resin, 3-5 parts of hydroxyalkyl amide, 10-12 parts of conductive carbon black, 8-10 parts of aluminite powder, 4-5 parts of a conductive auxiliary, 1-3 parts of a luster-enhancing agent and 0.5-0.8 part of a flatting agent. The obtained low-resistance powder paint has good anticorrosion and antistatic performance and can have an effective protection effect after the surface of an electronic equipment container or shell, the surface of equipment sensitive to static discharge and the surface of household appliances are coated with the powder paint.
Description
Technical field
The invention belongs to technical field of coatings, be specifically related to a kind of low resistance powder coating.
Background technology
Electrostatic is when being separated after two kinds of material close contacts again, a kind of material passes to another kind of material and positively charged electronics, and another kind of material obtains electronics and electronegative generation.Although electrostatic electricity is little, because its voltage is very high, easily electric discharge occur and produce static sparking and set off an explosion, and electrostatic also can impact the normal operation of electronics.
Low resistance powder coating and antistatic powder coating, refer to the functional coating having certain conduction current and eliminate electrostatic, have the performance such as electromagnetic shielding, protection against corrosion, all have extensive use in each fields such as hyundai electronics, building, transport, military affairs.
Summary of the invention
The object of the present invention is to provide a kind of low resistance powder coating; there is good protection against corrosion, antistatic property; be coated in freight container or the shell of electronics, to the equipment of electrostatic discharge sensitive and the surface of home appliance, effective provide protection can be played.
For achieving the above object, the present invention adopts following technical scheme:
A kind of low resistance powder coating, it is raw materials used comprises by weight: terminal carboxyl polyester resin 60-70 part, hydroxyalkyl amide 3-5 part, graphitized carbon black 10-12 part, aluminium powder 8-10 part, conductive auxiliary agent 4-5 part, optical brightener 1-3 part, flow agent 0.5-0.8 part.
Preferably, it raw materials usedly comprises by weight: terminal carboxyl polyester resin 70 parts, hydroxyalkyl amide 3.8 parts, graphitized carbon black 12 parts, aluminium powder 8.4 parts, conductive auxiliary agent 4.2 parts, optical brightener 1 part, flow agent 0.6 part.
The preparation method of described low resistance powder coating is by after terminal carboxyl polyester resin, hydroxyalkyl amide, graphitized carbon black, aluminium powder, conductive auxiliary agent, optical brightener, flow agent mixing, melt extruded by forcing machine, then pulverize after extruded stock fragmentation, sieve through micro mist again, to obtain final product.
remarkable advantage of the present invention is: gained low resistance powder coating of the present invention, has good protection against corrosion, antistatic property, and its surface resistivity is 5 × 10
4~ 2 × 10
5Ω/cm, is coated in freight container or the shell of electronics, to the equipment of electrostatic discharge sensitive and the surface of home appliance, can be played effective provide protection.
Embodiment
More being convenient to make content of the present invention understand, below in conjunction with embodiment, technical solutions according to the invention are described further, but the present invention being not limited only to this.
Embodiment 1
A kind of low resistance powder coating, it is raw materials used comprises by weight: terminal carboxyl polyester resin 70 parts, hydroxyalkyl amide 3.8 parts, graphitized carbon black 12 parts, aluminium powder 8.4 parts, conductive auxiliary agent 4.2 parts, optical brightener 1 part, flow agent 0.6 part.
After tested, after gained powder coating film forming, its hardness>=2H, glossiness 60-100%, resistivity 5 × 10
4Ω/cm.
Embodiment 2
A kind of low resistance powder coating, it is raw materials used comprises by weight: terminal carboxyl polyester resin 60 parts, hydroxyalkyl amide 3 parts, graphitized carbon black 10 parts, aluminium powder 8 parts, conductive auxiliary agent 4 parts, optical brightener 2 parts, flow agent 0.5 part.
After tested, after gained powder coating film forming, its hardness>=2H, glossiness 60-100%, resistivity 9 × 10
4Ω/cm.
Embodiment 3
A kind of low resistance powder coating, it is raw materials used comprises by weight: terminal carboxyl polyester resin 65 parts, hydroxyalkyl amide 5 parts, graphitized carbon black 11 parts, aluminium powder 10 parts, conductive auxiliary agent 5 parts, optical brightener 3 parts, flow agent 0.8 part.
After tested, after gained powder coating film forming, its hardness>=2H, glossiness 60-100%, resistivity 2 × 10
5Ω/cm.
The foregoing is only preferred embodiment of the present invention, all equalizations done according to the present patent application the scope of the claims change and modify, and all should belong to covering scope of the present invention.
Claims (3)
1. a low resistance powder coating, is characterized in that: raw materials usedly comprise by weight: terminal carboxyl polyester resin 60-70 part, hydroxyalkyl amide 3-5 part, graphitized carbon black 10-12 part, aluminium powder 8-10 part, conductive auxiliary agent 4-5 part, optical brightener 1-3 part, flow agent 0.5-0.8 part.
2. low resistance powder coating according to claim 1, is characterized in that: raw materials usedly comprise by weight: terminal carboxyl polyester resin 70 parts, hydroxyalkyl amide 3.8 parts, graphitized carbon black 12 parts, aluminium powder 8.4 parts, conductive auxiliary agent 4.2 parts, optical brightener 1 part, flow agent 0.6 part.
3. low resistance powder coating according to claim 1, it is characterized in that: its preparation method is by after terminal carboxyl polyester resin, hydroxyalkyl amide, graphitized carbon black, aluminium powder, conductive auxiliary agent, optical brightener, flow agent mixing, melt extruded by forcing machine, then pulverize after extruded stock fragmentation, sieve through micro mist again, to obtain final product.