CN105505024A - Anti-corrosion polyvinyl chloride (PVC) paint - Google Patents
Anti-corrosion polyvinyl chloride (PVC) paint Download PDFInfo
- Publication number
- CN105505024A CN105505024A CN201410551504.2A CN201410551504A CN105505024A CN 105505024 A CN105505024 A CN 105505024A CN 201410551504 A CN201410551504 A CN 201410551504A CN 105505024 A CN105505024 A CN 105505024A
- Authority
- CN
- China
- Prior art keywords
- parts
- pvc
- polyvinyl chloride
- fluorine
- corrosion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
An anti-corrosion polyvinyl chloride (PVC) paint is mainly composed of the following components in parts by weight: 10 to 35 parts of PVC resin, 0.7 to 1.5 parts of dioctyl phthalate, 3.0 to 10 parts of xylene-formaldehyde resin, 7 to 14 parts of rutile type titanium dioxide, 8 to 15 parts of barite powder, 5 to 7 parts of talcum powder, 0.8 to 2 parts of bentonite, 0.5 to 2.5 parts of anionic carboxylic acid polymer, 0.3 to 1 part of fluorocarbon modified polysiloxane, 0.2 to 1.4 parts of polyether modified polysiloxane, 10 to 25 parts of cyclohexanone, and 3 to 5 parts of fluorine-phosphor-iron. The provided paint has the characteristics of excellent anti-corrosion performance, wide application range, convenience for construction, and long service life.
Description
Technical field
The invention belongs to technical field of coatings, particularly relate to industrial antisepsis erosion technical field of coatings.
Background technology
The protective system that existing market is commonly used has perchlorethylene paint, high-chlorinated polyethylene coating, the red coating such as polyvinyl chloride (PVC) coating, chlorinated rubber of firefly, they respectively have advantage, some solidity to corrosions are better, some kindlinesss are better, but it is thin and crisp that ubiquity paint film, the not high brushing number of channels of sticking power is many, the shortcomings such as work-ing life is short, and some erosion resistances are not good enough.
Summary of the invention
The object of the invention is one and there is excellent corrosion-proof performance, widely applicable, easy construction, the new anti-corrosion coating of long service life.
In order to solve the problems of the technologies described above, technical scheme provided by the invention is: a kind of corrosion-resistant polyvinyl chloride (PVC) coating, primarily of following component by weight composition polyvinyl chloride (PVC) RESINS 10-35 part, dioctyl phthalate (DOP) 0.7-1.5 part, xylene formaldehyde resin 3.0-10 part, rutile titanium white powder 7-14 part, ground barium sulfate 8-15 part, talcum powder 5-7 part, bentonite 0.8-2 part, anionic carboxylic acid polymkeric substance 0.5-2.5 part, fluorine-carbon modified polysiloxane 0.3-1 part, Siloxane-Oxyalkylene Copolymers 0.2-1.4 part, pimelinketone 10-25 part, fluorine ferrophosphorus 3-5 part.
Preparation method of the present invention: first polyvinyl chloride (PVC) RESINS, dioctyl phthalate (DOP), xylene formaldehyde resin, fluorine-carbon modified polysiloxane, Siloxane-Oxyalkylene Copolymers, pimelinketone are dropped in reactor, anionic carboxylic acid polymkeric substance and wilkinite is added under the stirring of 300 revs/min of speed, stir after adding rutile titanium white powder, ground barium sulfate, talcum powder, fluorine ferrophosphorus more successively after 25 minutes and continue stirring 20 minutes, then by material through being pumped to sand mill grinding 3-4 time when slurry fineness is less than 50 μm.
Embodiment
Embodiment one:
A kind of corrosion-resistant polyvinyl chloride (PVC) coating, primarily of following component by weight composition polyvinyl chloride (PVC) RESINS 10 parts, dioctyl phthalate (DOP) 0.7 part, xylene formaldehyde resin 5 parts, 7 parts, rutile titanium white powder, ground barium sulfate 8 parts, talcum powder 5 parts, bentonite 0.8 part, 1 part, anionic carboxylic acid polymkeric substance, fluorine-carbon modified polysiloxane 0.3 part, Siloxane-Oxyalkylene Copolymers 0.2 part, pimelinketone 10 parts, fluorine ferrophosphorus 3 parts.
Preparation method is: first by 10 parts of polyvinyl chloride (PVC) RESINS, 0.7 part of dioctyl phthalate (DOP), 5 parts of xylene formaldehyde resins, 0.2 part of fluorine-carbon modified polysiloxane, 0.3 part of Siloxane-Oxyalkylene Copolymers, 10 parts of pimelinketone drop in reactor, 1 part of anionic carboxylic acid polymkeric substance and 0.8 part of wilkinite is added under the stirring of 300 revs/min of speed, stir and add 7 parts of rutile titanium white powder more successively after 25 minutes, 8 parts of ground barium sulfates, 5 parts of talcum powder, stirring 20 minutes is continued after 3 parts of fluorine ferrophosphorus, again by material through being pumped to sand mill grinding 3-4 time when slurry fineness is less than 50 μm.
Embodiment two:
A kind of corrosion-resistant polyvinyl chloride (PVC) coating, primarily of following component by weight composition polyvinyl chloride (PVC) RESINS 20 parts, dioctyl phthalate (DOP) 1 part, xylene formaldehyde resin 5 parts, 10 parts, rutile titanium white powder, ground barium sulfate 10 parts, talcum powder 6 parts, bentonite 1 part, 1.5 parts, anionic carboxylic acid polymkeric substance, fluorine-carbon modified polysiloxane 0.5 part, Siloxane-Oxyalkylene Copolymers 1 part, pimelinketone 20 parts, fluorine ferrophosphorus 4 parts.
Preparation method of the present invention: first by 20 parts of polyvinyl chloride (PVC) RESINS, 1 part of dioctyl phthalate (DOP), 5 parts of xylene formaldehyde resins, 0.5 part of fluorine-carbon modified polysiloxane, 1 part of Siloxane-Oxyalkylene Copolymers, 20 parts of pimelinketone drop in reactor, 1.5 parts of anionic carboxylic acid polymkeric substance and 1 part of wilkinite is added under the stirring of 300 revs/min of speed, stir and add 10 parts of rutile titanium white powder more successively after 25 minutes, 10 parts of ground barium sulfates, 6 parts of talcum powder, stirring 20 minutes is continued after 4 parts of fluorine ferrophosphorus, again by material through being pumped to sand mill grinding 3-4 time when slurry fineness is less than 50 μm.
Embodiment three:
A kind of corrosion-resistant polyvinyl chloride (PVC) coating, primarily of following component by weight composition polyvinyl chloride (PVC) RESINS 35 parts, dioctyl phthalate (DOP) 1.5 parts, xylene formaldehyde resin 10 parts, 14 parts, rutile titanium white powder, ground barium sulfate 15 parts, talcum powder 7 parts, bentonite 2 parts, 2.5 parts, anionic carboxylic acid polymkeric substance, fluorine-carbon modified polysiloxane 1 part, Siloxane-Oxyalkylene Copolymers 1.4 parts, pimelinketone 5 parts, fluorine ferrophosphorus 5 parts.
Preparation method of the present invention: first by 35 parts of polyvinyl chloride (PVC) RESINS, 1.5 parts of dioctyl phthalate (DOP)s, 10 parts of xylene formaldehyde resins, 1 part of fluorine-carbon modified polysiloxane, 1.4 parts of Siloxane-Oxyalkylene Copolymers, 5 parts of pimelinketone drop in reactor, 2.5 parts of anionic carboxylic acid polymkeric substance and 2 parts of wilkinites are added under the stirring of 300 revs/min of speed, stir and add 14 parts of rutile titanium white powder more successively after 25 minutes, 15 parts of ground barium sulfates, 7 parts of talcum powder, stirring 20 minutes is continued after 5 parts of fluorine ferrophosphorus, again by material through being pumped to sand mill grinding 3-4 time when slurry fineness is less than 50 μm.
Claims (2)
1. a corrosion-resistant polyvinyl chloride (PVC) coating, is characterized in that primarily of following component by weight composition polyvinyl chloride (PVC) RESINS 10-35 part, dioctyl phthalate (DOP) 0.7-1.5 part, xylene formaldehyde resin 3.0-10 part, rutile titanium white powder 7-14 part, ground barium sulfate 8-15 part, talcum powder 5-7 part, bentonite 0.8-2 part, anionic carboxylic acid polymkeric substance 0.5-2.5 part, fluorine-carbon modified polysiloxane 0.3-1 part, Siloxane-Oxyalkylene Copolymers 0.2-1.4 part, pimelinketone 10-25 part, fluorine ferrophosphorus 3-5 part.
2. the preparation method of a kind of corrosion-resistant polyvinyl chloride (PVC) coating according to claim 1, it is characterized in that first by polyvinyl chloride (PVC) RESINS, dioctyl phthalate (DOP), xylene formaldehyde resin, fluorine-carbon modified polysiloxane, Siloxane-Oxyalkylene Copolymers, pimelinketone drops in reactor, anionic carboxylic acid polymkeric substance and wilkinite is added under the stirring of 300 revs/min of speed, stir and add rutile titanium white powder successively again after 25 minutes, ground barium sulfate, talcum powder, stirring is continued 20 minutes after fluorine ferrophosphorus, again by material through being pumped to sand mill grinding 3-4 time when slurry fineness is less than 50 μm.