CN105504584A - Tasteless PVC modified material and preparation method thereof - Google Patents
Tasteless PVC modified material and preparation method thereof Download PDFInfo
- Publication number
- CN105504584A CN105504584A CN201511015859.0A CN201511015859A CN105504584A CN 105504584 A CN105504584 A CN 105504584A CN 201511015859 A CN201511015859 A CN 201511015859A CN 105504584 A CN105504584 A CN 105504584A
- Authority
- CN
- China
- Prior art keywords
- tasteless
- pvc
- weight ratio
- material modified
- mixture
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of PVC materials, in particular to a tasteless PVC modified material and a preparation method thereof. The tasteless PVC modified material is prepared from the following raw materials in parts by weight: 80 to 120 parts of PVC resin, 50 to 70 parts of a plasticizer, 20 to 30 parts of a filler, 3 to 7 parts of a tasteless heat stabilizer, 0.6 to 1 part of a lubricant and 1 to 2 parts of a deodorant. According to the tasteless PVC modified material disclosed by the invention, by adopting the raw materials and strictly controlling the weight proportion of the raw materials, the properties of the prepared tasteless PVC modified material exceed the national standard, and the tasteless PVC modified material is tasteless, environment-friendly, excellent in temperature resistance and weather resistance, high in strength, excellent in shock resistance, good in flame retardant efficiency, good in processing performance and excellent in combination property.
Description
Technical field
The present invention relates to PVC material technical field, it is material modified and preparation method thereof to be specifically related to a kind of tasteless PVC.
Background technology
The advantages such as polyvinyl chloride (PVC) is one of industrialization the earliest, broad-spectrum general-purpose thermoplastic plastic, and it has, and quality is light, intensity is high, insulation, fire-retardant, corrosion-resistant, high comprehensive performance, cheap and raw material sources are extensive; But also there is following shortcoming: 1, poor toughness, very easily embrittlement when being hit, therefore can not be used as structured material, in addition, the fragility temperature influence of polyvinyl chloride is very large, and general PVC product uses lower limit to be-15 DEG C, and the use lower limit of flexible PVC is-30 DEG C; 2, poor heat stability, it just starts to decomposite HCl 100 DEG C time, more rapid higher than decomposing when 150 DEG C, and the melt temperature of PVC is about 210 DEG C; 3, the viscosity of PVC is high, mobility extreme difference, limits it to a certain extent and uses.People often adopt methods such as adding filler, elastomerics, softening agent, thermo-stabilizer, processing aid, heat-proof modifier and flow ability modifying agent to improve the performance of PVC.
Application number is 200910155137.3 disclose a kind of PVC elastomer material, this material is prepared from by each component of following weight part: PVC95 ~ 105 weight part, calcium stearate 1.5 ~ 3 weight part, Zinic stearas 0.5 ~ 2 weight part, lubricant 0.5 ~ 2 weight part, vinyl chloride-vinyl acetate resin 8 ~ 16 weight part, thermoplastic styrene butadiene rubber 15 ~ 25 weight part, weighting agent 60 ~ 100 weight part.
Application number is 201010198789.8 disclose a kind of hard PVC injectable plastic material, and by weight percentage, its composition and content are: 800 type resins 45 ~ 75%, calcium carbonate 5 ~ 15%; Dibutyl ester 1 ~ 3%, stablizer 2 ~ 5%, chlorinatedpolyethylene (CPE) 1 ~ 5%, industrial paraffin 0.5 ~ 10%, titanium dioxide 0.5 ~ 10%, softening agent 0.5 ~ 1%.
Above-mentioned existing PVC material all can produce niff, therefore, researches and develops a kind of tasteless PVC material and seems particularly important.
Summary of the invention
In order to overcome the shortcoming and defect existed in prior art, the object of the present invention is to provide a kind of tasteless PVC material modified, this is material modified tasteless, environmental protection, and resistance to gentle weather resistance is excellent, intensity is high, excellent shock resistance, good flame retardation effect, processing characteristics is excellent, excellent combination property.
Another object of the present invention is to the preparation method providing a kind of tasteless PVC material modified, this preparation method's technique is simple, and convenient operation and control, steady quality, production efficiency is high, and production cost is low, can large-scale industrial production.
Object of the present invention is achieved through the following technical solutions: a kind of tasteless PVC is material modified, the material modified raw material comprising following weight part of described tasteless PVC:
Polyvinyl chloride resin 80-120 part
Softening agent 50-70 part
Weighting agent 20-30 part
Tasteless thermo-stabilizer 3-7 part
Lubricant 0.6-1.0 part
Deodovization agent 1-2 part.
Tasteless PVC of the present invention is material modified by adopting above-mentioned raw materials, and the strict weight proportion controlling each raw material, the material modified properties of obtained tasteless PVC is all beyond national standard, tasteless, environmental protection, and resistance to gentle weather resistance is excellent, intensity is high, excellent shock resistance, good flame retardation effect, processing characteristics is excellent, excellent combination property.
Preferably, the mixture that is made up of with weight ratio 2-4:1 calcium carbide process PVC resin and ethylene process polyvinyl chloride resin of described polyvinyl chloride resin.
The present invention is by adopting calcium carbide process PVC resin and ethylene process polyvinyl chloride resin as the composite use of polyvinyl chloride resin, and to control its weight ratio be 2-4:1, makes plasticize speed fast, easily processes.
Preferably, described softening agent is the mixture be made up of with weight ratio 1.5-2.5:0.8-1.2:1 hexanaphthene 1,2-dioctyl phthalate diisononyl esters, triethyl citrate and epoxy soybean oil.
The present invention adopts 1,2-dioctyl phthalate diisononyl esters, triethyl citrate and epoxy soybean oil are as the composite use of softening agent, and to control its weight ratio be 1.5-2.5:0.8-1.2:1, three kinds of softening agent are environment-friendly plasticizer, the reactive force between PVC molecular chain can be reduced, the fusing point of the second-order transition temperature of PVC plastic, yield temperature and contained crystallite is all reduced, improves the plasticity-of resin, make goods softness, resistance to low temperature good.
Preferably, the mixture that is made up of with weight ratio 1-2:0.8-1.2:1 water-ground limestone, light calcium carbonate and kaolin of described weighting agent.
The present invention is by adopting water-ground limestone, light calcium carbonate and kaolin as the composite use of weighting agent, and to control its weight ratio be 1-2:0.8-1.2:1, good with the consistency of polyvinyl chloride resin, thus improves intensity and the shock resistance of material.
Preferably, the mixture that is made up of with weight ratio 0.8-1.2:0.5-1.5:1 Bis(lauroyloxy)dioctyltin, Imarcaptoacetate dioctyltin and single-ethylhexyl maleate dioctyl tin of described tasteless thermo-stabilizer.
The present invention is by adopting Bis(lauroyloxy)dioctyltin, Imarcaptoacetate dioctyltin and single-ethylhexyl maleate dioctyl tin as the composite use of tasteless thermo-stabilizer, and to control its weight ratio be 0.8-1.2:0.5-1.5:1, three kinds of stablizers are organotin stabilizer, there is goodish thermostability, light stability and the transparency and tinting strength, and good processability.
Preferably, the mixture that is made up of with weight ratio 1.5-2.5:0.8-1.2:1 oxidized polyethlene wax, pentaerythritol stearate and ethylene bis stearic acid amide of described lubricant.
The present invention adopts oxidized polyethlene wax as external lubricant, can reduce the friction of PVC melt and mould, machine barrel; Adopt pentaerythritol stearate and ethylene bis stearic acid amide as internal lubricant, the intermolecular friction of PVC melt can be reduced; Three kinds of lubricants can make material in the course of processing, improve the mobility of material and the release property of goods with the composite use of weight ratio 1.5-2.5:0.8-1.2:1.
Preferably, the mixture that is made up of with weight ratio 2-4:1.8-2.2:1 sodium bicarbonate, Sodium Benzoate and glyceryl monostearate of described deodovization agent.
The present invention is by adopting sodium bicarbonate, Sodium Benzoate and glyceryl monostearate as the composite use of deodovization agent, and to control its weight ratio be 2-4:1.8-2.2:1, to smell, there is extremely strong adsorptive power, there is excellent resistance toheat simultaneously, can have good dispersiveness in macromolecular material, taste removal is effective.
Preferably, described tasteless PVC is material modified also comprises impact modifier 5-10 part, and described impact modifier is the mixture that the chlorinatedpolyethylene of 25%-45% and the ethylene-vinyl acetate copolymer of vinyl acetate between to for plastic unit content 5%-25% form with weight ratio 1.5-2.5:1 by chlorinity.
Chlorinatedpolyethylene (CPE) is a kind of properties-correcting agent of thermoplastics, has good over-all properties.Appropriate CPE is added, the processing characteristics that can reduce the melt viscosity of resin, improve mobility, improve plastics in polyvinyl chloride (PVC) resin; The work-ing life of the shock strength of PVC, resistance to low temperature, weathering performance, prolongation goods can also be improved.CPE also contributes to the dispersed of calcium carbonate and polyvinyl chloride resin; And when the chlorinity (weight content) of chlorinatedpolyethylene is for 25%-45%, make the resistance to impact shock of material best.
Ethylene-vinyl acetate copolymer (EVA) can be used as the impact modifying agent of PVC, has good flexibility, obdurability, lower temperature resistance (-58 DEG C still have pliability), weathering resistance, stress cracking resistance, heat sealer, agglutinating value(of coal), the transparency and glossiness; Also there is the elasticity as rubber simultaneously, excellent chemical stability, thermostability (heat decomposition temperature 229 ~ 230 DEG C), ozone resistance, nontoxicity, good processibility and dyeability; Fine with the miscibility of filler, even if fill more filler, also unlikelyly have a strong impact on its physical and mechanical property.
EVA is as the impact modifying agent of PVC, its effect is different with the content of vinyl acetate between to for plastic in multipolymer, when the content of vinyl acetate between to for plastic is low, with the poor compatibility of PVC, reinforced effects is poor, and goods are opaque, along with the increase of vinyl acetate between to for plastic unit content, the consistency of multipolymer and PVC improves, and reinforced effects improves, and the goods transparency is also better; But the content of vinyl acetate between to for plastic also can not be too high, during vinyl acetate between to for plastic unit content 5%-25%, obviously can improve the shock strength of PVC, compared with the impact modifying agent containing carbon-carbon double bond, also there is the good advantage of ageing resistance.
The present invention is by adopting chlorinatedpolyethylene and ethylene-vinyl acetate copolymer as the composite use of impact modifier, and to control its weight ratio be 1.5-2.5:1, the high temperature resistant of material and resistance to low temperature can be improved, the processing characteristics that can also reduce the melt viscosity of material, improve mobility, improve plastics, improves the work-ing life of the shock strength of material, weathering performance, prolongation goods.
Described tasteless PVC is material modified also comprises fire retardant 1-5 part, slipping agent 0.05-0.15 part and pigment powder 0.01-0.05 part; The mixture that described fire retardant is made up of with weight ratio 0.5-1.5:1 antimonous oxide and zinc borate.
Antimonous oxide and lime borate are inorganic environment-friendly fire retardant, the present invention is by adopting antimonous oxide and zinc borate as the composite use of fire retardant, and to control its weight ratio be 0.5-1.5:1, good flame retardant effect can be reached, Drawing abillity and mechanical property can also be improved.
Described slipping agent is the mixture be made up of with weight ratio 1.5-2.5:0.8-1.2:1 erucicamide, amine hydroxybenzene and N, N'-ethylene bis stearamide.
The present invention is by adopting erucicamide, amine hydroxybenzene and N, N'-ethylene bis stearamide is as slipping agent and to control its weight ratio be 1.5-2.5:0.8-1.2:1, mechanical resistant stirring capacity and fingerprinting stress can be strengthened, finished product good forming effect, any surface finish, the extensibility of finished product can also be strengthened, easy-to-draw not easily broken.
Described pigment powder is particle diameter at the titanium dioxide of 1-5 μm; The mixture that described titanium dioxide is made up of with weight ratio 1:1.5-2.5 Rutile type Titanium Dioxide and anatase thpe white powder.
The present invention adopts particle diameter at the titanium dioxide of 1-5 μm as pigment powder, further employing Rutile type Titanium Dioxide and the composite use of anatase thpe white powder, and to control its weight ratio be 1:1.5-2.5, there is superior whiteness, tinting strength, opacifying power, weathering resistance, thermotolerance and chemical stability, particularly there is no toxicity.
Another object of the present invention is achieved through the following technical solutions: the preparation method that a kind of tasteless PVC is material modified, comprises the steps:
(1) take above-mentioned raw materials mixing by weight ratio, put into high speed blender, at 100-140 DEG C of temperature, stir 15-25min;
(2) raw material after stirring is passed through twin screw extruder extruding pelletization, obtained tasteless PVC is material modified.
Preparation method's technique of the present invention is simple, and convenient operation and control, steady quality, production efficiency is high, and production cost is low, can large-scale industrial production.
Preferably, in described step (2), the extruder temperature of twin screw extruder is: a district temperature 138-160 DEG C, two district temperature 135-160 DEG C, three district temperature 135-155 DEG C, four district temperature 132-150 DEG CHe five district temperature 130-148 DEG C.
Beneficial effect of the present invention is: the material modified properties of tasteless PVC of the present invention is all beyond national standard, tasteless, environmental protection, and resistance to gentle weather resistance is excellent, intensity is high, excellent shock resistance, good flame retardation effect, processing characteristics is excellent, excellent combination property.Tasteless PVC of the present invention is material modified meets the International Environmental Protection standards such as REACH, ROHS, PAHS, N-P, can be widely used in the industrial circles such as automobile, electronic apparatus, instrument, weaving and building.
Preparation method's technique of the present invention is simple, and convenient operation and control, steady quality, production efficiency is high, and production cost is low, can large-scale industrial production.
Embodiment
For the ease of the understanding of those skilled in the art, below in conjunction with embodiment, the present invention is further illustrated, and the content that embodiment is mentioned not is limitation of the invention.
Embodiment 1
A kind of tasteless PVC is material modified, the material modified raw material comprising following weight part of described tasteless PVC:
Polyvinyl chloride resin 80 parts
50 parts, softening agent
Weighting agent 20 parts
Tasteless thermo-stabilizer 3 parts
Lubricant 0.6 part
Deodovization agent 1 part.
The mixture that described polyvinyl chloride resin is made up of with weight ratio 2:1 calcium carbide process PVC resin and ethylene process polyvinyl chloride resin.
Described softening agent is the mixture be made up of with weight ratio 1.5:0.8:1 hexanaphthene 1,2-dioctyl phthalate diisononyl esters, triethyl citrate and epoxy soybean oil.
The mixture that described weighting agent is made up of with weight ratio 1:0.8:1 water-ground limestone, light calcium carbonate and kaolin.
The mixture that described tasteless thermo-stabilizer is made up of with weight ratio 0.8:0.5:1 Bis(lauroyloxy)dioctyltin, Imarcaptoacetate dioctyltin and single-ethylhexyl maleate dioctyl tin.
The mixture that described lubricant is made up of with weight ratio 1.5:0.8:1 oxidized polyethlene wax, pentaerythritol stearate and ethylene bis stearic acid amide.
The mixture that described deodovization agent is made up of with weight ratio 2:1.8:1 sodium bicarbonate, Sodium Benzoate and glyceryl monostearate.
Described tasteless PVC is material modified also comprises impact modifier 5 parts, and described impact modifier is the mixture that the chlorinatedpolyethylene of 25% and the ethylene-vinyl acetate copolymer of vinyl acetate between to for plastic unit content 5% form with weight ratio 1.5:1 by chlorinity.
Described tasteless PVC is material modified also comprises fire retardant 1 part, slipping agent 0.05 part and 0.01 part, pigment powder; The mixture that described fire retardant is made up of with weight ratio 1.1:1 antimonous oxide and zinc borate; Described slipping agent is the mixture be made up of with weight ratio 1.5:0.8:1 erucicamide, amine hydroxybenzene and N, N'-ethylene bis stearamide; Described pigment powder is particle diameter at the titanium dioxide of 1 μm; The mixture that described titanium dioxide is made up of with weight ratio 1:1.5 Rutile type Titanium Dioxide and anatase thpe white powder.
The preparation method that tasteless PVC is material modified, comprises the steps:
(1) take above-mentioned raw materials mixing by weight ratio, put into high speed blender, at 100 DEG C of temperature, stir 25min;
(2) raw material after stirring is passed through twin screw extruder extruding pelletization, obtained tasteless PVC is material modified.
In described step (2), the extruder temperature of twin screw extruder is: district's temperature 138 DEG C, two district's temperature 135 DEG C, three district's temperature 135 DEG C, four district's temperature 132 DEG CHe five district temperature 130 DEG C.
Embodiment 2
A kind of tasteless PVC is material modified, the material modified raw material comprising following weight part of described tasteless PVC:
Polyvinyl chloride resin 90 parts
55 parts, softening agent
Weighting agent 22 parts
Tasteless thermo-stabilizer 4 parts
Lubricant 0.7 part
Deodovization agent 1.2 parts.
The mixture that described polyvinyl chloride resin is made up of with weight ratio 2.5:1 calcium carbide process PVC resin and ethylene process polyvinyl chloride resin.
Described softening agent is the mixture be made up of with weight ratio 1.8:0.9:1 hexanaphthene 1,2-dioctyl phthalate diisononyl esters, triethyl citrate and epoxy soybean oil.
The mixture that described weighting agent is made up of with weight ratio 1.2:0.9:1 water-ground limestone, light calcium carbonate and kaolin.
The mixture that described tasteless thermo-stabilizer is made up of with weight ratio 0.9:0.8:1 Bis(lauroyloxy)dioctyltin, Imarcaptoacetate dioctyltin and single-ethylhexyl maleate dioctyl tin.
The mixture that described lubricant is made up of with weight ratio 1.8:0.9:1 oxidized polyethlene wax, pentaerythritol stearate and ethylene bis stearic acid amide.
The mixture that described deodovization agent is made up of with weight ratio 2.5:1.9:1 sodium bicarbonate, Sodium Benzoate and glyceryl monostearate.
Described tasteless PVC is material modified also comprises impact modifier 6 parts, and described impact modifier is the mixture that the chlorinatedpolyethylene of 30% and the ethylene-vinyl acetate copolymer of vinyl acetate between to for plastic unit content 10% form with weight ratio 1.8:1 by chlorinity.
Described tasteless PVC is material modified also comprises fire retardant 2 parts, slipping agent 0.08 part and 0.02 part, pigment powder; The mixture that described fire retardant is made up of with weight ratio 1.2:1 antimonous oxide and zinc borate; Described slipping agent is the mixture be made up of with weight ratio 1.8:0.9:1 erucicamide, amine hydroxybenzene and N, N'-ethylene bis stearamide; Described pigment powder is particle diameter at the titanium dioxide of 2 μm; The mixture that described titanium dioxide is made up of with weight ratio 1:1.8 Rutile type Titanium Dioxide and anatase thpe white powder.
The preparation method that tasteless PVC is material modified, comprises the steps:
(1) take above-mentioned raw materials mixing by weight ratio, put into high speed blender, at 110 DEG C of temperature, stir 22min;
(2) raw material after stirring is passed through twin screw extruder extruding pelletization, obtained tasteless PVC is material modified.
In described step (2), the extruder temperature of twin screw extruder is: district's temperature 140 DEG C, two district's temperature 140 DEG C, three district's temperature 135 DEG C, four district's temperature 135 DEG CHe five district temperature 135 DEG C.
Embodiment 3
A kind of tasteless PVC is material modified, the material modified raw material comprising following weight part of described tasteless PVC:
Polyvinyl chloride resin 100 parts
60 parts, softening agent
Weighting agent 25 parts
Tasteless thermo-stabilizer 5 parts
Lubricant 0.8 part
Deodovization agent 1.5 parts.
The mixture that described polyvinyl chloride resin is made up of with weight ratio 3:1 calcium carbide process PVC resin and ethylene process polyvinyl chloride resin.
Described softening agent is the mixture be made up of with weight ratio 2:1:1 hexanaphthene 1,2-dioctyl phthalate diisononyl esters, triethyl citrate and epoxy soybean oil.
The mixture that described weighting agent is made up of with weight ratio 1.5:1:1 water-ground limestone, light calcium carbonate and kaolin.
The mixture that described tasteless thermo-stabilizer is made up of with weight ratio 1:1:1 Bis(lauroyloxy)dioctyltin, Imarcaptoacetate dioctyltin and single-ethylhexyl maleate dioctyl tin.
The mixture that described lubricant is made up of with weight ratio 2:1:1 oxidized polyethlene wax, pentaerythritol stearate and ethylene bis stearic acid amide.
The mixture that described deodovization agent is made up of with weight ratio 3:2:1 sodium bicarbonate, Sodium Benzoate and glyceryl monostearate.
Described tasteless PVC is material modified also comprises impact modifier 8 parts, and described impact modifier is the mixture that the chlorinatedpolyethylene of 35% and the ethylene-vinyl acetate copolymer of vinyl acetate between to for plastic unit content 15% form with weight ratio 2:1 by chlorinity.
Described tasteless PVC is material modified also comprises fire retardant 3 parts, slipping agent 0.1 part and 0.03 part, pigment powder; The mixture that described fire retardant is made up of with weight ratio 1.3:1 antimonous oxide and zinc borate; Described slipping agent is the mixture be made up of with weight ratio 2:1:1 erucicamide, amine hydroxybenzene and N, N'-ethylene bis stearamide; Described pigment powder is particle diameter at the titanium dioxide of 3 μm; The mixture that described titanium dioxide is made up of with weight ratio 1:2 Rutile type Titanium Dioxide and anatase thpe white powder.
The preparation method that tasteless PVC is material modified, comprises the steps:
(1) take above-mentioned raw materials mixing by weight ratio, put into high speed blender, at 120 DEG C of temperature, stir 20min;
(2) raw material after stirring is passed through twin screw extruder extruding pelletization, obtained tasteless PVC is material modified.
In described step (2), the extruder temperature of twin screw extruder is: district's temperature 160 DEG C, two district's temperature 160 DEG C, three district's temperature 155 DEG C, four district's temperature 150 DEG CHe five district temperature 148 DEG C.
Embodiment 4
A kind of tasteless PVC is material modified, the material modified raw material comprising following weight part of described tasteless PVC:
Polyvinyl chloride resin 110 parts
65 parts, softening agent
Weighting agent 28 parts
Tasteless thermo-stabilizer 6 parts
Lubricant 0.9 part
Deodovization agent 1.8 parts.
The mixture that described polyvinyl chloride resin is made up of with weight ratio 3.5:1 calcium carbide process PVC resin and ethylene process polyvinyl chloride resin.
Described softening agent is the mixture be made up of with weight ratio 2.2:1.1:1 hexanaphthene 1,2-dioctyl phthalate diisononyl esters, triethyl citrate and epoxy soybean oil.
The mixture that described weighting agent is made up of with weight ratio 1.8:1.1:1 water-ground limestone, light calcium carbonate and kaolin.
The mixture that described tasteless thermo-stabilizer is made up of with weight ratio 1.1:1.2:1 Bis(lauroyloxy)dioctyltin, Imarcaptoacetate dioctyltin and single-ethylhexyl maleate dioctyl tin.
The mixture that described lubricant is made up of with weight ratio 2.2:1.1:1 oxidized polyethlene wax, pentaerythritol stearate and ethylene bis stearic acid amide.
The mixture that described deodovization agent is made up of with weight ratio 3.5:2.1:1 sodium bicarbonate, Sodium Benzoate and glyceryl monostearate.
Described tasteless PVC is material modified also comprises impact modifier 9 parts, and described impact modifier is the mixture that the chlorinatedpolyethylene of 40% and the ethylene-vinyl acetate copolymer of vinyl acetate between to for plastic unit content 20% form with weight ratio 2.2:1 by chlorinity.
Described tasteless PVC is material modified also comprises fire retardant 4 parts, slipping agent 0.12 part and 0.04 part, pigment powder; The mixture that described fire retardant is made up of with weight ratio 1.4:1 antimonous oxide and zinc borate; Described slipping agent is the mixture be made up of with weight ratio 2.2:1.1:1 erucicamide, amine hydroxybenzene and N, N'-ethylene bis stearamide; Described pigment powder is particle diameter at the titanium dioxide of 4 μm; The mixture that described titanium dioxide is made up of with weight ratio 1:2.2 Rutile type Titanium Dioxide and anatase thpe white powder.
The preparation method that tasteless PVC is material modified, comprises the steps:
(1) take above-mentioned raw materials mixing by weight ratio, put into high speed blender, at 130 DEG C of temperature, stir 18min;
(2) raw material after stirring is passed through twin screw extruder extruding pelletization, obtained tasteless PVC is material modified.
In described step (2), the extruder temperature of twin screw extruder is: district's temperature 155 DEG C, two district's temperature 155 DEG C, three district's temperature 150 DEG C, four district's temperature 148 DEG CHe five district temperature 145 DEG C.
Embodiment 5
A kind of tasteless PVC is material modified, the material modified raw material comprising following weight part of described tasteless PVC:
Polyvinyl chloride resin 120 parts
70 parts, softening agent
Weighting agent 30 parts
Tasteless thermo-stabilizer 7 parts
Lubricant 1.0 parts
Deodovization agent 2 parts.
The mixture that described polyvinyl chloride resin is made up of with weight ratio 4:1 calcium carbide process PVC resin and ethylene process polyvinyl chloride resin.
Described softening agent is the mixture be made up of with weight ratio 2.5:1.2:1 hexanaphthene 1,2-dioctyl phthalate diisononyl esters, triethyl citrate and epoxy soybean oil.
The mixture that described weighting agent is made up of with weight ratio 2:1.2:1 water-ground limestone, light calcium carbonate and kaolin.
The mixture that described tasteless thermo-stabilizer is made up of with weight ratio 1.2:1.5:1 Bis(lauroyloxy)dioctyltin, Imarcaptoacetate dioctyltin and single-ethylhexyl maleate dioctyl tin.
The mixture that described lubricant is made up of with weight ratio 2.5:1.2:1 oxidized polyethlene wax, pentaerythritol stearate and ethylene bis stearic acid amide.
The mixture that described deodovization agent is made up of with weight ratio 4:2.2:1 sodium bicarbonate, Sodium Benzoate and glyceryl monostearate.
Described tasteless PVC is material modified also comprises impact modifier 10 parts, and described impact modifier is the mixture that the chlorinatedpolyethylene of 45% and the ethylene-vinyl acetate copolymer of vinyl acetate between to for plastic unit content 25% form with weight ratio 2.5:1 by chlorinity.
Described tasteless PVC is material modified also comprises fire retardant 5 parts, slipping agent 0.15 part and 0.05 part, pigment powder; The mixture that described fire retardant is made up of with weight ratio 1.5:1 antimonous oxide and zinc borate; Described slipping agent is the mixture be made up of with weight ratio 2.5:1.2:1 erucicamide, amine hydroxybenzene and N, N'-ethylene bis stearamide; Described pigment powder is particle diameter at the titanium dioxide of 5 μm; The mixture that described titanium dioxide is made up of with weight ratio 1:2.5 Rutile type Titanium Dioxide and anatase thpe white powder.
The preparation method that tasteless PVC is material modified, comprises the steps:
(1) take above-mentioned raw materials mixing by weight ratio, put into high speed blender, at 140 DEG C of temperature, stir 15min;
(2) raw material after stirring is passed through twin screw extruder extruding pelletization, obtained tasteless PVC is material modified.
In described step (2), the extruder temperature of twin screw extruder is: district's temperature 160 DEG C, two district's temperature 160 DEG C, three district's temperature 155 DEG C, four district's temperature 150 DEG CHe five district temperature 148 DEG C.
The material modified mechanical and physical performance of the tasteless PVC that embodiment 1-5 obtains is as shown in table 1:
Table 1
| Test event | Standard value | Embodiment 1 | Embodiment 2 | Embodiment 3 | Embodiment 4 | Embodiment 5 |
| Tensile strength (MPa) | ≥15.0 | 23.6 | 24.8 | 25.3 | 22.4 | 24.1 |
| Flexural strength (MPa) | ≥15.0 | 49.2 | 52.1 | 54.9 | 45.7 | 50.5 |
| Elongation at break (%) | ≥150 | 297 | 304 | 315 | 295 | 310 |
| Heat-drawn wire (DEG C) | ≥50.0 | 117.2 | 118.2 | 120.8 | 114.9 | 118.3 |
| Impact embrittlement temperature (DEG C) | ≤-20 | -25 | -30 | -30 | -25 | -30 |
| Heat-stable time (min) when 200 DEG C | ≥60 | 100 | 120 | 110 | 90 | 100 |
| Hardness/Shore D | ≥50 | 82 | 84 | 85 | 80 | 83 |
| Fire-retardant | V0 | V0 | V0 | V0 | V0 | V0 |
| Odor detection | Irritant smell | Tasteless | Tasteless | Tasteless | Tasteless | Tasteless |
As can be seen from Table 1, the material modified properties of the tasteless PVC that the present invention obtains is all beyond national standard, tasteless, environmental protection, and resistance to gentle weather resistance is excellent, and intensity is high, excellent shock resistance, good flame retardation effect, and processing characteristics is excellent, excellent combination property.
Above-described embodiment is the present invention's preferably implementation, and in addition, the present invention can also realize by alternate manner, and any apparent replacement is all within protection scope of the present invention without departing from the inventive concept of the premise.
Claims (10)
1. a tasteless PVC is material modified, it is characterized in that: the material modified raw material comprising following weight part of described tasteless PVC:
Polyvinyl chloride resin 80-120 part
Softening agent 50-70 part
Weighting agent 20-30 part
Tasteless thermo-stabilizer 3-7 part
Lubricant 0.6-1.0 part
Deodovization agent 1-2 part.
2. the tasteless PVC of one according to claim 1 is material modified, it is characterized in that: the mixture that described polyvinyl chloride resin is made up of with weight ratio 2-4:1 calcium carbide process PVC resin and ethylene process polyvinyl chloride resin.
3. the tasteless PVC of one according to claim 1 is material modified, it is characterized in that: described softening agent is the mixture be made up of with weight ratio 1.5-2.5:0.8-1.2:1 hexanaphthene 1,2-dioctyl phthalate diisononyl esters, triethyl citrate and epoxy soybean oil.
4. the tasteless PVC of one according to claim 1 is material modified, it is characterized in that: the mixture that described weighting agent is made up of with weight ratio 1-2:0.8-1.2:1 water-ground limestone, light calcium carbonate and kaolin.
5. the tasteless PVC of one according to claim 1 is material modified, it is characterized in that: the mixture that described tasteless thermo-stabilizer is made up of with weight ratio 0.8-1.2:0.5-1.5:1 Bis(lauroyloxy)dioctyltin, Imarcaptoacetate dioctyltin and single-ethylhexyl maleate dioctyl tin.
6. the tasteless PVC of one according to claim 1 is material modified, it is characterized in that: the mixture that described lubricant is made up of with weight ratio 1.5-2.5:0.8-1.2:1 oxidized polyethlene wax, pentaerythritol stearate and ethylene bis stearic acid amide.
7. the tasteless PVC of one according to claim 1 is material modified, it is characterized in that: the mixture that described deodovization agent is made up of with weight ratio 2-4:1.8-2.2:1 sodium bicarbonate, Sodium Benzoate and glyceryl monostearate.
8. the tasteless PVC of one according to claim 1 is material modified, it is characterized in that: described tasteless PVC is material modified also comprises impact modifier 5-10 part, described impact modifier is the mixture that the chlorinatedpolyethylene of 25%-45% and the ethylene-vinyl acetate copolymer of vinyl acetate between to for plastic unit content 5%-25% form with weight ratio 1.5-2.5:1 by chlorinity.
9. the preparation method that a kind of tasteless PVC as described in any one of claim 1-8 is material modified, is characterized in that: comprise the steps:
(1) take above-mentioned raw materials mixing by weight ratio, put into high speed blender, at 100-140 DEG C of temperature, stir 15-25min;
(2) raw material after stirring is passed through twin screw extruder extruding pelletization, obtained tasteless PVC is material modified.
10. the preparation method that a kind of tasteless PVC according to claim 9 is material modified, it is characterized in that: in described step (2), the extruder temperature of twin screw extruder is: a district temperature 138-160 DEG C, two district temperature 135-160 DEG C, three district temperature 135-155 DEG C, four district temperature 132-150 DEG CHe five district temperature 130-148 DEG C.