CN105503175A - Temperature-stable middle-dielectric-constant microwave dielectric ceramic CaTiNbBiO7 and preparation method thereof - Google Patents

Temperature-stable middle-dielectric-constant microwave dielectric ceramic CaTiNbBiO7 and preparation method thereof Download PDF

Info

Publication number
CN105503175A
CN105503175A CN201610010903.7A CN201610010903A CN105503175A CN 105503175 A CN105503175 A CN 105503175A CN 201610010903 A CN201610010903 A CN 201610010903A CN 105503175 A CN105503175 A CN 105503175A
Authority
CN
China
Prior art keywords
dielectric ceramic
conducted
dielectric
microwave dielectric
microwave
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610010903.7A
Other languages
Chinese (zh)
Inventor
郑彬宁
苏聪学
覃杏柳
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guilin University of Technology
Original Assignee
Guilin University of Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guilin University of Technology filed Critical Guilin University of Technology
Priority to CN201610010903.7A priority Critical patent/CN105503175A/en
Publication of CN105503175A publication Critical patent/CN105503175A/en
Pending legal-status Critical Current

Abstract

The invention discloses low-loss temperature-stable middle-dielectric-constant microwave dielectric ceramic CaTiNbBiO7 and a preparation method thereof. The method comprises the steps that 1, the chemical raw materials of CaCO3, TiO2, Nb2O5 and Bi2O3 powder are weighed and matched according to a stoichiometric formula CaTiNbBiO7; 2, wet ball milling and mixing are conducted on the raw materials obtained in the first step for 12 h, a ball milling medium adopts distilled water, and after drying is conducted, presintering is conducted for 6 h in the air atmosphere of 950 DEG C; 3, a binding agent is added to powder obtained in the second step, granulation is conducted, pressing forming is conducted, and sintering is conducted for 4 h in the air atmosphere of 1,025-1,075 DEG C. The binding agent adopts a polyvinyl alcohol solution with the mass concentration of 5%, and the addition amount of polyvinyl alcohol accounts for 3% of the total mass of the powder. According to the low-loss temperature-stable middle-dielectric-constant microwave dielectric ceramic CaTiVBiO7 and the preparation method thereof, the prepared ceramic is sintered well at 1,100 DEG C or below, the dielectric constant reaches 35.2-36.5, the value of the quality factor Qf reaches up to 48,900-56,100 GHz, the temperature coefficient of the resonant frequency is small, and the microwave dielectric ceramic has great application value in the industry.

Description

A kind of temperature-stable medium dielectric constant microwave medium microwave dielectric ceramic CaTiNbBiO 7and preparation method thereof
Technical field
The present invention relates to dielectric ceramic material, particularly relate to dielectric ceramic material of the microwave devices such as ceramic substrate, resonator and the wave filter used for the manufacture of microwave frequency and preparation method thereof.
Background technology
Microwave dielectric ceramic refers to and to be applied in microwave frequency band (mainly UHF and SHF frequency range) circuit as dielectric material and to complete the pottery of one or more functions, the components and parts such as resonator, wave filter, dielectric substrate and medium wave circuit are widely used as in modern communication, it is the key foundation material of modern communication technology, in portable mobile phone, automobile telephone, cordless telephone, telestar susceptor and military radar etc., there is very important application, in the miniaturization, integrated process of modern communication instrument, just playing increasing effect.
Be applied to the dielectric ceramic of microwave frequency band, the requirement of following dielectric characteristics should be met: (1) seriation DIELECTRIC CONSTANT ε rto adapt to the requirement of different frequency and different application occasion; (2) high quality factor q value or low dielectric loss tan δ to reduce noise, general requirement Qf>=3000GHz; (3) the temperature factor τ of resonant frequency ?little of as far as possible to ensure the thermostability that device has had, general requirement-10ppm/ DEG C≤τ ?≤+10ppm/ DEG C.From late 1930s, just someone attempts dielectric substance to be applied to microwave technology in the world, and prepares TiO 2microwave dielectric filter, but its temperature coefficient of resonance frequency τ ?too greatly cannot be practical.Since the seventies in last century, start the large-scale development to medium ceramic material, according to relative permittivity ε rsize from use frequency range different, usually the microwave-medium ceramics be developed and developing can be divided into 4 classes.
(1) ultralow dielectric microwave dielectric ceramic, main representative is Al 2o 3-TiO 2, Y 2baCuO 5, MgAl 2o 4and Mg 2siO 4deng, its ε r≤ 20, quality factor q × f>=50000GHz, τ ?≤ 10ppm/ ° of C.Be mainly used in microwave base plate and high-end microwave device.
(2) low ε rwith the microwave dielectric ceramic of high q-factor, mainly BaO-MgO-Ta 2o 5, BaO-ZnO-Ta 2o 5or BaO-MgO-Nb 2o 5, BaO-ZnO-Nb 2o 5system or the composite system MWDC material between them.Its ε r=20 ~ 35, Q=(1 ~ 2) × 10 4(under f>=10GHz), τ ?≈ 0.Be mainly used in the microwave communication equipments such as the direct broadcasting satellite of f >=8GHz as dielectric resonance device.
(3) medium ε rwith the microwave dielectric ceramic of Q value, mainly with BaTi 4o 9, Ba 2ti 9o 20(Zr, Sn) TiO 4deng the MWDC material for base, its ε r=35 ~ 45, Q=(6 ~ 9) × 10 3(under f=3 ~-4GHz), τ ?≤ 5ppm/ ° of C.Be mainly used in microwave military radar in 4 ~ 8GHz range of frequency and communication system as dielectric resonance device.
(4) high ε rand the microwave dielectric ceramic that Q value is lower, be mainly used in civilian mobile communcations system in 0.8 ~ 4GHz range of frequency, this is also the emphasis of microwave dielectric ceramic research.Since the eighties, the people such as Kolar, Kato in succession find and have studied perovskite-like tungsten bronze type BaO-Ln 2o 3-TiO 2series (Ln=La, Sm, Nd or Pr etc. are called for short BLT system), complex perovskite structure CaO-Li 2o-Ln 2o 3-TiO 2series, lead base series material, Ca 1-xln 2x/3tiO 3be contour ε rmicrowave dielectric ceramic, the wherein BaO-Nd of BLT system 2o 3-TiO 2material dielectric constant reaches 90, lead base series (Pb, Ca) ZrO 3specific inductivity reaches 105.
The sintering temperature of these material systems is generally higher than 1300 ° of C above, can not directly and the low melting point metal such as Ag and Cu burn formation laminated ceramic capacitor altogether.In recent years, along with LTCC Technology (LowTemperatureCo-firedCeramics, the requirement of development LTCC) and the development of microwave multilayer device, researchist both domestic and external has carried out exploring widely and studying to some low fever's system materials, mainly adopt devitrified glass or glassceramic composites system, because low melting glass has relatively high dielectric loss mutually, the existence of glassy phase substantially increases the dielectric loss of material.Therefore development is the emphasis of current research without the low fired microwave dielectric ceramic material of glassy phase.
Can in the process of low fired microwave dielectric ceramic materials in exploration and development of new, the material systems such as the Li based compound that intrinsic sintering temperature is low, Bi based compound, tungstate architecture compound and tellurate architecture compound get the attention and research, but due to three performance index (ε of microwave dielectric ceramic rwith Qf and τ ?) between be that the relation of mutually restriction is (see document: the restricting relation between microwave dielectric ceramic materials dielectric properties, Zhu Jianhua, Liang Fei, Wang little Hong, Lv Wenzhong, electronic component and material, phase March the 3rd in 2005), meet three performance requriementss and the single-phase microwave-medium ceramics of low temperature sintering is considerably less, mainly their temperature coefficient of resonance frequency is usually excessive or quality factor are on the low side and cannot application request.Current is the summary of experience drawn by great many of experiments to the research major part of microwave-medium ceramics, but complete theory is not had to set forth the relation of microtexture and dielectric properties, therefore, in theory also cannot predict its microwave dielectric property such as temperature coefficient of resonance frequency and quality factor from the composition of compound and structure, which greatly limits the development of low temperature co-fired technology and microwave multilayer device.Explore and low-temperature sintering can have near-zero resonance frequency temperature coefficient (-10ppm/ DEG C≤τ with exploitation simultaneously ?≤+10ppm/ DEG C) be that those skilled in the art thirst for solving always but are difficult to the difficult problem that succeeds all the time with the microwave dielectric ceramic of higher figure of merit.We are to CaTiNbBiO 7, CaTiTaBiO 7and SrTiNbBiO 7series compound carried out the research of microwave dielectric property, find that their sintering temperature is lower than 1100 DEG C, wherein SrTiNbBiO 7loss is too large and cannot find resonance peak, and CaTiTaBiO 7less but the temperature coefficient of resonance frequency (τ bigger than normal of loss ?=46ppm/ DEG C) and cannot as practical microwave-medium ceramics.
Summary of the invention
The object of this invention is to provide the application of a kind of bismuthate as temperature-stable medium dielectric constant microwave medium microwave dielectric ceramic, and prepare the method for this microwave dielectric ceramic.This microwave dielectric ceramic has good thermostability and low-loss, simultaneously can low-temperature sintering.
The chemical constitution of microwave dielectric ceramic material of the present invention is CaTiNbBiO 7.
Preparation method's step of this microwave dielectric ceramic material is:
(1) by chemical feedstocks CaCO 3, TiO 2, Nb 2o 5and Bi 2o 3powder is formula CaTiNbBiO stoichiometrically 7weigh batching.
(2) step (1) raw material wet ball-milling is mixed 12 hours, ball-milling medium is distilled water, pre-burning 6 hours in 950 DEG C of air atmosphere after oven dry.
(3) in the powder that step (2) is obtained, binding agent is added and after granulation, then compression moulding, finally in 1025 ~ 1075 DEG C of air atmosphere, sinter 4 hours; Described binding agent adopts mass concentration to be the polyvinyl alcohol solution of 5%, and polyvinyl alcohol addition accounts for 3% of powder total mass.
Advantage of the present invention: CaTiNbBiO 7ceramic sintering temperature is low, and raw materials cost is low; Specific inductivity reaches 35.2 ~ 36.5, the temperature factor τ of its resonant frequency ?little, temperature stability is good; Quality factor q f value, up to 48900-56100GHz, can be widely used in the manufacture of the microwave devices such as various medium substrate, resonator and wave filter, can meet the technology needs of low temperature co-fired technology and microwave multilayer device.
Embodiment
Embodiment:
Table 1 shows 3 specific embodiments and microwave dielectric property thereof that form different sintering temperature of the present invention.Its preparation method is described above, carries out the evaluation of microwave dielectric property by cylindrical dielectric resonator method; Adopt X-ray diffraction analysis to carry out material phase analysis, all samples is one-component ceramic.
This pottery can be widely used in the manufacture of the microwave devices such as various medium substrate, resonator and wave filter, can meet the technology needs of the system such as mobile communication and satellite communications.
Table 1:

Claims (1)

1. bismuthate is as an application for temperature-stable medium dielectric constant microwave medium microwave dielectric ceramic, it is characterized in that the chemical constitution of described microwave dielectric ceramic is: CaTiNbBiO 7, its specific inductivity is 35.2 ~ 36.5, and temperature coefficient of resonance frequency is 5ppm/ DEG C;
Preparation method's concrete steps of described microwave dielectric ceramic are:
(1) by chemical feedstocks CaCO 3, TiO 2, Nb 2o 5and Bi 2o 3powder is formula CaTiNbBiO stoichiometrically 7weigh batching;
(2) step (1) raw material wet ball-milling is mixed 12 hours, ball-milling medium is distilled water, pre-burning 6 hours in 950 DEG C of air atmosphere after oven dry;
(3) in the powder that step (2) is obtained, binding agent is added and after granulation, then compression moulding, finally in 1025 ~ 1075 DEG C of air atmosphere, sinter 4 hours; Described binding agent adopts mass concentration to be the polyvinyl alcohol solution of 5%, and polyvinyl alcohol addition accounts for 3% of powder total mass.
CN201610010903.7A 2016-01-09 2016-01-09 Temperature-stable middle-dielectric-constant microwave dielectric ceramic CaTiNbBiO7 and preparation method thereof Pending CN105503175A (en)