CN105484048A - Milled finishing process for cashmere products - Google Patents
Milled finishing process for cashmere products Download PDFInfo
- Publication number
- CN105484048A CN105484048A CN201510949495.7A CN201510949495A CN105484048A CN 105484048 A CN105484048 A CN 105484048A CN 201510949495 A CN201510949495 A CN 201510949495A CN 105484048 A CN105484048 A CN 105484048A
- Authority
- CN
- China
- Prior art keywords
- cashmere sweater
- cashmere
- product
- fulling
- sweater product
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a finishing process for textiles, in particular to a milled finishing process for cashmere products. The milled finishing process for the cashmere products aims at enabling the textile texture to be tight, reducing the textile length and enhancing strength, elasticity and the heat retention property. The milled finishing process comprises the steps of enzyme submerging treatment, milling treatment, rinsing, dehydrating and drying and ironing forming. According to the milled finishing process, process conditions are optimized, operation is simple, time consumed is short, damage to cashmere is small, and shrinkage is almost resisted after treatment; besides, enzyme treatment is performed in a controlled mode, so that cashmere sweaters after treatment feel softer and full and are good in drapability, high in moisture absorption capacity and brighter in color.
Description
Technical field
The present invention relates to a kind of textile finishing process, particularly a kind of cashmere product fulling milling finishing technique.
Background technology
Cashmere product is soft because of it, warmth retention property is good, the features such as hygroscopicity is strong obtain liking of consumers in general, cashmere product especially cashmere sweater have passed through a variety of operation from suede to ready-made clothes, there is no the ready-made clothes of fulling milling to have remained various chemical greasy dirt, Chinese wax and even also have ether etc., fulling milling is exactly the process of washing in fact, and can well clean cashmere sweater, the object of woollen sweater fulling milling is mainly in order to improve inherent quality and the appearance effect of cashmere sweater product.
Summary of the invention
The object of the invention is to overcome the deficiencies in the prior art, provide one that fabric texture can be made tight, contraction in length, the cashmere product fulling milling finishing technique that brute force, elasticity and warmth retention property strengthen.
In order to achieve the above object, cashmere product fulling milling finishing technique of the present invention, comprises the steps:
1, ferment treatment is soaked: choose pectase and laccase, be dissolved in solution of sodium bisulfite, be immersed by cashmere sweater product, bath raio is 1:30-40, under 40 DEG C of-50 DEG C of conditions, soak 50-55 minute, stirs once every 10 minutes; Deactivation after ferment treatment, uses clear water rinsed clean, and dewaters;
2, fulling milling process: put into a conduit made of long bamboo oil accounting for cashmere sweater product weight 4%-5% in fulling mill, account for the softener of cashmere sweater product weight 1%-3% and account for the smooth agent of cashmere sweater product weight 2%-4%, put into cashmere sweater product; bath raio is 1:30; water temperature is 40 DEG C-50 DEG C, pH value is 6-7, and soak time is 30-60 minute; then drive fulling mill and carry out fulling milling, and the fulling milling time is 10-20min; 10-15min is soaked again after fulling milling;
3, rinsing: cashmere sweater product is cleaned with the clear water of 20 DEG C-30 DEG C, scavenging period is 10-15min;
4, dewatered drying: adopt drum-type dewatered drying all-in-one to carry out dewatered drying to cashmere sweater product, bake out temperature is 60-70 DEG C, and drying time is 20-30min;
5, whole boiling hot sizing: by the whole boiling hot sizing of cashmere sweater product after drying, cloth textured clear after arrangement, size is accurate.
The present invention is optimized process to process conditions, simple to operate, consuming time short, little to cashmere infringement, shrink hardly after process, and by controlledly carrying out ferment treatment, make the feel of the cashmere sweater after processing softer, plentiful, drapability is good, and wettability power is strong, and color is also more gorgeous.
Detailed description of the invention
Embodiment 1
1, soak ferment treatment: choose pectase and laccase, be dissolved in solution of sodium bisulfite, be immersed by cashmere sweater product, bath raio is 1:30, soak 55 minutes under 40 DEG C of conditions, stirred once every 10 minutes; Deactivation after ferment treatment, uses clear water rinsed clean, and dewaters;
2, fulling milling process: put into a conduit made of long bamboo oil accounting for cashmere sweater product weight 4% in fulling mill, account for the softener of cashmere sweater product weight 3% and account for the smooth agent of cashmere sweater product weight 2%, put into cashmere sweater product; bath raio is 1:30; water temperature is 40 DEG C, pH value is 6, and soak time is 30 minutes; then drive fulling mill and carry out fulling milling, and the fulling milling time is 20min; 10min is soaked again after fulling milling;
3, rinsing: cashmere sweater product is cleaned with the clear water of 20 DEG C, scavenging period is 15min;
4, dewatered drying: adopt drum-type dewatered drying all-in-one to carry out dewatered drying to cashmere sweater product, bake out temperature is 60 DEG C, and drying time is 30min;
5, whole boiling hot sizing: by the whole boiling hot sizing of cashmere sweater product after drying, cloth textured clear after arrangement, size is accurate.
Embodiment 2
1, soak ferment treatment: choose pectase and laccase, be dissolved in solution of sodium bisulfite, be immersed by cashmere sweater product, bath raio is 1:40, soak 50 minutes under 50 DEG C of conditions, stirred once every 10 minutes; Deactivation after ferment treatment, uses clear water rinsed clean, and dewaters;
2, fulling milling process: put into a conduit made of long bamboo oil accounting for cashmere sweater product weight 5% in fulling mill, account for the softener of cashmere sweater product weight 1% and account for the smooth agent of cashmere sweater product weight 4%, put into cashmere sweater product; bath raio is 1:30; water temperature is 50 DEG C, pH value is 7, and soak time is 60 minutes; then drive fulling mill and carry out fulling milling, and the fulling milling time is 10min; 15min is soaked again after fulling milling;
3, rinsing: cashmere sweater product is cleaned with the clear water of 30 DEG C, scavenging period is 10min;
4, dewatered drying: adopt drum-type dewatered drying all-in-one to carry out dewatered drying to cashmere sweater product, bake out temperature is 70 DEG C, and drying time is 20min;
5, whole boiling hot sizing: by the whole boiling hot sizing of cashmere sweater product after drying, cloth textured clear after arrangement, size is accurate.
Embodiment 3
1, soak ferment treatment: choose pectase and laccase, be dissolved in solution of sodium bisulfite, be immersed by cashmere sweater product, bath raio is 1:35, soak 53 minutes under 45 DEG C of conditions, stirred once every 10 minutes; Deactivation after ferment treatment, uses clear water rinsed clean, and dewaters;
2, fulling milling process: put into a conduit made of long bamboo oil accounting for cashmere sweater product weight 5% in fulling mill, account for the softener of cashmere sweater product weight 2% and account for the smooth agent of cashmere sweater product weight 3%, put into cashmere sweater product; bath raio is 1:30; water temperature is 45 DEG C, pH value is 6, and soak time is 45 minutes; then drive fulling mill and carry out fulling milling, and the fulling milling time is 15min; 12min is soaked again after fulling milling;
3, rinsing: cashmere sweater product is cleaned with the clear water of 25 DEG C, scavenging period is 13min;
4, dewatered drying: adopt drum-type dewatered drying all-in-one to carry out dewatered drying to cashmere sweater product, bake out temperature is 65 DEG C, and drying time is 25min;
5, whole boiling hot sizing: by the whole boiling hot sizing of cashmere sweater product after drying, cloth textured clear after arrangement, size is accurate.
Claims (1)
1. a cashmere product fulling milling finishing technique, is characterized in that: comprise the steps:
(1), ferment treatment is soaked: choose pectase and laccase, be dissolved in solution of sodium bisulfite, be immersed by cashmere sweater product, bath raio is 1:30-40, under 40 DEG C of-50 DEG C of conditions, soak 50-55 minute, stirs once every 10 minutes; Deactivation after ferment treatment, uses clear water rinsed clean, and dewaters;
(2), fulling milling process: put into a conduit made of long bamboo oil accounting for cashmere sweater product weight 4%-5% in fulling mill, account for the softener of cashmere sweater product weight 1%-3% and account for the smooth agent of cashmere sweater product weight 2%-4%, put into cashmere sweater product; bath raio is 1:30; water temperature is 40 DEG C-50 DEG C, pH value is 6-7, and soak time is 30-60 minute; then drive fulling mill and carry out fulling milling, and the fulling milling time is 10-20min; 10-15min is soaked again after fulling milling;
(3), rinsing: clean cashmere sweater product with the clear water of 20 DEG C-30 DEG C, scavenging period is 10-15min;
(4), dewatered drying: adopt drum-type dewatered drying all-in-one to carry out dewatered drying to cashmere sweater product, bake out temperature is 60-70 DEG C, and drying time is 20-30min;
(5), whole boiling hot sizing: by the whole boiling hot sizing of cashmere sweater product after drying, cloth textured clear after arrangement, size is accurate.