CN105482579A - Zinc-rich steel structure anticorrosion coating - Google Patents
Zinc-rich steel structure anticorrosion coating Download PDFInfo
- Publication number
- CN105482579A CN105482579A CN201510882345.9A CN201510882345A CN105482579A CN 105482579 A CN105482579 A CN 105482579A CN 201510882345 A CN201510882345 A CN 201510882345A CN 105482579 A CN105482579 A CN 105482579A
- Authority
- CN
- China
- Prior art keywords
- parts
- coating
- zinc
- steel structure
- epoxy resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a zinc-rich steel structure anticorrosion coating. The coating comprises, by weight, 20-30 parts of acrylic acid modified resin, 10-20 parts of bisphenol A epoxy resin, 5-10 parts of diphenol propane epoxy resin, 4-10 parts of nanometer zinc oxide, 15-20 parts of zinc powder, 2-8 parts of titanium dioxide, 8-15 parts of ammonium polyphosphate, 1-5 parts of pentaerythritol, 10-15 parts of a siloxane grafted polymer, 1-5 parts of expandable graphite, 1-3 parts of cyclohexanone, 5-10 parts of ethylene triamine, 0.1-0.3 parts of manganese acetate and 20-25 parts of deionized water. The coating is rich in zinc, is anticorrosive, and has very good anticorrosive performance; an ester bond, an epoxy group and other structures contained in the coating make the coating have good adhesion with a steel structure; and the coating also has the advantages of good waterproof property, excellent wear resistance, excellent impact resistance, and excellent mechanical performances.
Description
Technical field
The invention belongs to steel structure protective field, be specifically related to a kind of rich zinc steel structure anti-corrosion paint.
Background technology
Mostly all be chronically exposed to outdoor with the steel construction that steel are prepared into, some is placed under water or underground, is easy to be subject to the impact of extraneous factor and burn into gets rusty, and therefore needs to be coated with last layer protective system on the surface of steel construction, is used for protecting steel construction.Anticorrosion of steel structure field mainly comprises zinc cathodic protection, epoxide resin protective, polyurethane protective etc., and be used for steel long-effective corrosion field, the existing steel structure coating anticorrosion cycle is short on the market, and water repelling property is poor, can not meet the demand of people.
Summary of the invention
For the deficiencies in the prior art, the invention provides a kind of rich zinc steel structure anti-corrosion paint, be rich in zinc, there is good antiseptic property, with steel construction have good cohesiveness.
Technical scheme of the present invention is: a kind of rich zinc steel structure anti-corrosion paint, is made up of the raw material of following parts by weight: acrylic acid modified resin 20-30 part, bisphenol A type epoxy resin 10-20 part, propane type epoxy resin of di phenolic group 5-10 part, nano zine oxide 4-10 part, zinc powder 15-20 part, titanium dioxide 2-8 part, ammonium polyphosphate 8-15 part, tetramethylolmethane 1-5 part, silicone grafted polymers 10-15 part, expansible black lead 1-5 part, pimelinketone 1-3 part, vinyl triamine 5-10 part, manganese acetate 0.1-0.3 part, deionized water 20-25 part.
Compared with prior art, the invention has the advantages that: be rich in zinc, corrosion-resistant, there is good antiseptic property; The structures such as the ehter bond contained, epoxy group(ing) and make itself and steel construction have good cohesiveness; There is good water tolerance; Wear-resisting, shock-resistant, good mechanical performance.
Embodiment
Below in conjunction with specific embodiment, the present invention is described in further detail.
Embodiment 1
A kind of rich zinc steel structure anti-corrosion paint, is made up of the raw material of following parts by weight: acrylic acid modified resin 20 parts, bisphenol A type epoxy resin 10 parts, propane type epoxy resin of di phenolic group 5 parts, nano zine oxide 4 parts, zinc powder 15 parts, titanium dioxide 2 parts, ammonium polyphosphate 8 parts, tetramethylolmethane 1 part, silicone grafted polymers 10 parts, expansible black lead 1 part, pimelinketone 1 part, vinyl triamine 5 parts, manganese acetate 0.1 part, deionized water 20 parts.
Embodiment 2
A kind of rich zinc steel structure anti-corrosion paint, is made up of the raw material of following parts by weight: acrylic acid modified resin 25 parts, bisphenol A type epoxy resin 15 parts, propane type epoxy resin of di phenolic group 8 parts, nano zine oxide 8 parts, zinc powder 18 parts, titanium dioxide 6 parts, ammonium polyphosphate 10 parts, tetramethylolmethane 3 parts, silicone grafted polymers 13 parts, expansible black lead 3 parts, pimelinketone 2 parts, vinyl triamine 8 parts, manganese acetate 0.2 part, deionized water 22 parts.
Embodiment 3
A kind of rich zinc steel structure anti-corrosion paint, is made up of the raw material of following parts by weight: acrylic acid modified resin 30 parts, bisphenol A type epoxy resin 20 parts, propane type epoxy resin of di phenolic group 10 parts, nano zine oxide 10 parts, zinc powder 20 parts, titanium dioxide 8 parts, ammonium polyphosphate 15 parts, tetramethylolmethane 5 parts, silicone grafted polymers 15 parts, expansible black lead 5 parts, pimelinketone 3 parts, vinyl triamine 10 parts, manganese acetate 0.3 part, deionized water 25 parts.
Describe the present invention by way of example above, but the invention is not restricted to above-mentioned specific embodiment, all any changes of doing based on the present invention or modification all belong to the scope of protection of present invention.
Claims (1)
1. a rich zinc steel structure anti-corrosion paint, is characterized in that: be made up of the raw material of following parts by weight: acrylic acid modified resin 20-30 part, bisphenol A type epoxy resin 10-20 part, propane type epoxy resin of di phenolic group 5-10 part, nano zine oxide 4-10 part, zinc powder 15-20 part, titanium dioxide 2-8 part, ammonium polyphosphate 8-15 part, tetramethylolmethane 1-5 part, silicone grafted polymers 10-15 part, expansible black lead 1-5 part, pimelinketone 1-3 part, vinyl triamine 5-10 part, manganese acetate 0.1-0.3 part, deionized water 20-25 part.