CN105481470A - 一种用于混凝土内部养护的添加剂 - Google Patents
一种用于混凝土内部养护的添加剂 Download PDFInfo
- Publication number
- CN105481470A CN105481470A CN201410479191.4A CN201410479191A CN105481470A CN 105481470 A CN105481470 A CN 105481470A CN 201410479191 A CN201410479191 A CN 201410479191A CN 105481470 A CN105481470 A CN 105481470A
- Authority
- CN
- China
- Prior art keywords
- water
- additive
- concrete
- reducing agent
- absorbent resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明的用于混凝土养护的添加剂，由无机保水材料和有机保水材料，即高吸水性树脂共同做为吸水材料。并还包括高效减水剂、二级粉煤灰，先将高吸水性树脂和无机保水材料磨细至500目以上，再将上述材料按照重量比：无机保水材料25-35份、高吸水性树脂3-5份、萘系高效减水剂25-35份、二级粉煤灰:40-60份的比例投入高速搅拌机搅拌均匀，即得养护添加剂成品。本发明施工方便，直接与混凝土原材料加入搅拌锅中，搅拌均匀，无需在混凝土表面洒水、喷涂或覆膜，混凝土即可达到自养护的目的；对混凝土内部结构无影响；无毒、无味，不含氯离子，不会对混凝土中钢筋产生锈蚀；抗压强度比高，传统养护剂抗压强度比≤95，本发明产品通过大量实验验证，抗压强度比≥100。
Description
技术领域
本发明设计一种混凝土添加剂，特别是设计一种具有使混凝土从内部供水，满足混凝土养护的混凝土添加剂。
背景技术
混凝土浇注以后，在硬化过程中必须要有必要的温度和湿度，以保证足够的水分使混凝土中的水泥水化反应完全进行，如不采取任何养护措施，混凝土将会由于水分蒸发过快而早期大量失水，水化反应速度减慢，造成混凝土表面出现脱皮、起砂或产生干缩裂缝等现象，混凝土强度和耐久性将随之降低。随着混凝土的结构越来越复杂，一些结构形式或结构特殊部位如地下室的侧壁等垂直薄壁结构，其混凝土的养护非常困难，水分很容易失去。另外，在炎热夏季施工的混凝土工程，如混凝土道路、机场跑道、大坝面板、港口码头等工程，在高温时水分蒸发很快，因此，使用混凝土养护添加剂，以防止混凝土中水分流失，是保证混凝土工程质量的主要措施。
目前，混凝土的养护方式有多种，其分别存在以下缺陷：1、洒水养护、铺草垫（薄膜）洒水养护，这些措施只是针对混凝土表面进行养护，使混凝土表面失水减少，且浪费人财物力；2、混凝土表面喷洒、涂刷养护剂是在混凝土表面形成薄膜阻止混凝土内部水分蒸发而进行养护，该方法可能因施工人员责任心或混凝土结构复杂或混凝土工程环境不利喷砂涂刷，给混凝土工程质量带来隐患；3、用多孔结构的轻集料或陶粒，通过毛细作用吸水保证混凝土水泥的水化，但该方法吸水能力低，且施工中容易造成轻集料上浮影响施工，同时也会降低混凝土强度，影响混凝土工程质量。4、用单纯的高吸水性树脂做混凝土养护剂，该类材料一般为高分子材料，在混凝土内部分散性较差，不宜混合均匀，且吸水后颗粒较大，后期干缩后对混凝土强度有较大的影响。
发明内容
本发明的目的在于提出一种以无机保水材料和高吸水性树脂共同作用的混凝土养护添加剂，使其吸水颗粒更细，不影响混凝土后期强度，能在混凝土终凝前为水泥水化反应持续供水，达到混凝土自养护的目的。
本发明的目的是这样实现的：用于混凝土养护的添加剂，由无机保水材料和有机保水材料，即高吸水性树脂共同做为吸水材料。并还包括高效减水剂、二级粉煤灰，先将高吸水性树脂和无机保水材料磨细至500目以上，再将上述材料按照重量比：无机保水材料25-35份、高吸水性树脂3-5份、萘系高效减水剂25-35份、二级粉煤灰:40-60份的比例投入高速搅拌机搅拌均匀，即得养护添加剂成品。
本发明的一种混凝土养护添加剂，其原理为无机保水材料和有机保水材料，即高吸水树脂共同做为吸水材料，在混凝土搅拌过程中吸收两者本身重量15~30倍水分，混凝土浇注成型，在混凝土终凝前为水泥水化持续提供水化用水，从而达到混凝土自养护的目的。混凝土无需浇水养护、无需喷洒涂刷，也无需覆盖草垫或薄膜，使施工工序得到简化，无机保水材料和有机保水材料的共同作用，不但降低了生产成本，同时少量的高吸水性树脂在养护结束后留下的空洞有益于混凝土耐久性的提升。
与传统混凝土养护方法相比，本发明具有以下优点：1）施工方便，直接与混凝土原材料加入搅拌锅中，搅拌均匀，无需在混凝土表面洒水、喷涂或覆膜，混凝土即可达到自养护的目的；2）对混凝土内部结构无影响；3）无毒、无味，不含氯离子，不会对混凝土中钢筋产生锈蚀；4）抗压强度比高，传统养护剂抗压强度比≤95，本发明产品通过大量实验验证，抗压强度比≥100。
具体实施方式：本发明不受下述实施例的限制，可根据本发明的技术方案与实际情况来确定具体的实施方式。
实施例1：选择原材料按照重量比：改性锂硅粉：聚丙烯酸钠：萘系高效减水剂：二级粉煤灰=35：5：35：40投入高速搅拌机，搅拌20min后，即得养护添加剂成品，将该养护添加剂成品按水泥用量的3%与水泥、砂石等原材料一起投入混凝土搅拌机即可。经试验验证，掺有本发明的混凝土在自然养护条件下与未掺本发明产品标养的混凝土相比，早期强度（3d、7d）提高120-140%，后期强度（28d）提高110-130%。改性锂硅粉为无机保水材料，聚丙烯酸钠为高吸水性树脂，以下实施例均同。
实施例2：选择原材料按照重量比：改性锂硅粉：聚丙烯酸钠：萘系高效减水剂：二级粉煤灰=35：5：35：60投入高速搅拌机，搅拌20min后，即得养护添加剂成品，将该养护添加剂成品按水泥用量的3%与水泥、砂石等原材料一起投入混凝土搅拌机即可。经试验验证，掺有本发明的混凝土在自然养护条件下与未掺本发明产品标养的混凝土相比，早期强度（3d、7d）提高110-130%，后期强度（28d）提高100-120%。
实施例3：选择原材料按照重量比：改性锂硅粉：聚丙烯酸钠：萘系高效减水剂：二级粉煤灰=30：4：30：50投入高速搅拌机，搅拌20min后，即得养护添加剂成品，将该养护添加剂成品按水泥用量的3%与水泥、砂石等原材料一起投入混凝土搅拌机即可。经试验验证，掺有本发明的混凝土在自然养护条件下与未掺本发明产品标养的混凝土相比，早期强度（3d、7d）提高115-135%，后期强度（28d）提高100-115%。
实施例4：选择原材料按照重量比：改性锂硅粉：聚丙烯酸钠：萘系高效减水剂：二级粉煤灰=28：4：31：45投入高速搅拌机，搅拌20min后，即得养护添加剂成品，将该养护添加剂成品按水泥用量的3%与水泥、砂石等原材料一起投入混凝土搅拌机即可。经试验验证，掺有本发明的混凝土在自然养护条件下与未掺本发明产品标养的混凝土相比，早期强度（3d、7d）提高130-150%，后期强度（28d）提高120-140%。
实施例5：选择原材料按照重量比：改性锂硅粉：聚丙烯酸钠：萘系高效减水剂：二级粉煤灰=26：3.5：27：52投入高速搅拌机，搅拌20min后，即得养护添加剂成品，将该养护添加剂成品按水泥用量的3%与水泥、砂石等原材料一起投入混凝土搅拌机即可。经试验验证，掺有本发明的混凝土在自然养护条件下与未掺本发明产品标养的混凝土相比，早期强度（3d、7d）提高110-135%，后期强度（28d）提高100-120%。
以上技术特征构成了本发明的最佳实施例，其具有较强的适应性和最佳实施效果，可根据实际需要增减非必要技术特征。
Claims (10)
1.一种用于混凝土养护的添加剂，其特征在于：由无机保水材料和有机保水材料，即高吸水性树脂共同做为吸水材料。
2.如权利要求1所述的用于混凝土养护的添加剂，其特征在于：由无机保水材料、高吸水性树脂、高效减水剂、二级粉煤灰组成养护添加剂成品，上述材料重量比：无机保水材料25-35份、高吸水性树脂3-5份、高效减水剂25-35份、二级粉煤灰:40-60份。
3.如权利要求1所述的用于混凝土养护的添加剂，其特征在于：无机保水材料选用改性锂硅粉，高效减水剂选用萘系高效减水剂，高吸水性树脂选用聚丙烯酸钠。
4.如权利要求1所述的用于混凝土养护的添加剂，其特征在于：改性锂硅粉：聚丙烯酸钠：萘系高效减水剂：二级粉煤灰=35：5：35：40。
5.如权利要求1所述的用于混凝土养护的添加剂，其特征在于：改性锂硅粉：聚丙烯酸钠：萘系高效减水剂：二级粉煤灰=35：5：35：60。
6.如权利要求1所述的用于混凝土养护的添加剂，其特征在于：改性锂硅粉：聚丙烯酸钠：萘系高效减水剂：二级粉煤灰=30：4：30：50。
7.如权利要求1所述的用于混凝土养护的添加剂，其特征在于：改性锂硅粉：聚丙烯酸钠：萘系高效减水剂：二级粉煤灰=28：4：31：45。
8.如权利要求1所述的用于混凝土养护的添加剂，其特征在于：改性锂硅粉：聚丙烯酸钠：萘系高效减水剂：二级粉煤灰=26：3.5：27：52。
9.如权利要求1所述的用于混凝土养护的添加剂，其特征在于：所述高吸水性树脂和无机保水材料磨细至500目以上。
10.如权利要求2所述的用于混凝土养护的添加剂，其特征在于：养护添加剂成品按水泥用量的3%与水泥、砂石一起投入混凝土搅拌机搅拌。