CN105462358A - Gel pen ink - Google Patents

Abstract

The invention relates to a gel pen ink which is prepared from the following raw materials in parts by weight: 9-15 parts of PVC (polyvinyl chloride) resin powder, 4-8 parts of triethanolamine, 3-8 parts of sodium benzoate, 6-11 parts of triethylenetetramine, 3-8 parts of organosilicon defoaming agent, 4-8 parts of acrylic acid emulsion, 1.2-2 parts of stabilizer, 15-19 parts of cis-1,4-polyisoprene, 6-10 parts of oxidated castor oil, 3.2-8 parts of alcohol lubricant, 4.3-7 parts of starch, 6-12 parts of sodium maleate-olefin copolymer and 3.2-8 parts of light calcium carbonate. The gel pen ink is smooth for writing, can not have the phenomena of ink gap and the like, can be used for a long time, and enhances the economic benefit.

Description

A kind of gel ink pen ink

Technical field

The present invention relates to a kind of gel ink pen ink.

Background technology

Though gel ink pen gel pen belongs to ballpoint pen series products together, it writes principle, nib structure, it is similar with traditional oiliness ballpoint pen to add T_32 skill etc., because adopting ink performance difference, has special requirement to nib.In recent years, gel pen was rapid at Chinese development, had greatly the gesture replacing ballpoint pen, and many Zhi Bi enterprises all proceed to and produce neutral ballpoint pen, produce and progressively increase, define production and marketing heat.But the ink on market, after for some time used, there will be and writes slack phenomenon, even there is disconnected black phenomenon, cause the waste of resource.

Summary of the invention

For the deficiencies in the prior art, the problem to be solved in the present invention is, provides a kind of gel ink pen ink, fluent writing, and not easily occur the phenomenons such as disconnected ink, use that can be permanent, improves economic benefit.

For solving prior art problem, technical scheme provided by the invention is, a kind of gel ink pen ink, and it is made up of the raw material of following parts by weight:

PVC resin powder 9-15 part, trolamine 4-8 part, Sodium Benzoate 3-8 part, triethylene tetramine 6-11 part, silicone antifoam agent 3-8 part, ACRYLIC EMULSION 4-8 part, stablizer 1.2-2 part, cis-Isosorbide-5-Nitrae-polyisoprene 15-19 part, blown castor oil 6-10 part, alcohol type emollients 3.2-8 part, starch 4.3-7 part, multipolymer 6-12 part of sodium maleate and alkene, light calcium carbonate 3.2-8 part.

Further, a kind of gel ink pen ink, it is made up of the raw material of following parts by weight:

PVC resin powder 12 parts, trolamine 6 parts, Sodium Benzoate 5.5 parts, triethylene tetramine 9 parts, silicone antifoam agent 5.5 parts, ACRYLIC EMULSION 6 parts, stablizer 1.6 parts, cis-Isosorbide-5-Nitrae-polyisoprene 17 parts, blown castor oil 8 parts, alcohol type emollients 5.7 parts, starch 5.9 parts, the multipolymer of sodium maleate and alkene 9 parts, light calcium carbonate 5.4 parts.

The invention has the beneficial effects as follows: gel ink pen ink of the present invention, fluent writing, not easily occur the phenomenons such as disconnected ink, use that can be permanent, improves economic benefit.

Embodiment

embodiment 1

A kind of gel ink pen ink, it is made up of the raw material of following parts by weight:

PVC resin powder 9 parts, trolamine 4 parts, Sodium Benzoate 3 parts, triethylene tetramine 6 parts, silicone antifoam agent 3 parts, ACRYLIC EMULSION 4 parts, stablizer 1.2 parts, cis-Isosorbide-5-Nitrae-polyisoprene 15 parts, blown castor oil 6 parts, alcohol type emollients 3.2 parts, starch 4.3 parts, the multipolymer of sodium maleate and alkene 6 parts, light calcium carbonate 3.2 parts.

embodiment 2

A kind of gel ink pen ink, it is made up of the raw material of following parts by weight:

PVC resin powder 15 parts, trolamine 8 parts, Sodium Benzoate 8 parts, triethylene tetramine 11 parts, silicone antifoam agent 8 parts, ACRYLIC EMULSION 8 parts, stablizer 2 parts, cis-Isosorbide-5-Nitrae-polyisoprene 19 parts, blown castor oil 10 parts, alcohol type emollients 8 parts, starch 7 parts, the copolymer 1 of sodium maleate and alkene 2 parts, light calcium carbonate 8 parts.

embodiment 3

A kind of gel ink pen ink, it is made up of the raw material of following parts by weight:

PVC resin powder 12 parts, trolamine 6 parts, Sodium Benzoate 5.5 parts, triethylene tetramine 9 parts, silicone antifoam agent 5.5 parts, ACRYLIC EMULSION 6 parts, stablizer 1.6 parts, cis-Isosorbide-5-Nitrae-polyisoprene 17 parts, blown castor oil 8 parts, alcohol type emollients 5.7 parts, starch 5.9 parts, the multipolymer of sodium maleate and alkene 9 parts, light calcium carbonate 5.4 parts.

Claims (2)

1. a gel ink pen ink, is characterized in that: it is made up of the raw material of following parts by weight:

PVC resin powder 9-15 part, trolamine 4-8 part, Sodium Benzoate 3-8 part, triethylene tetramine 6-11 part, silicone antifoam agent 3-8 part, ACRYLIC EMULSION 4-8 part, stablizer 1.2-2 part, cis-Isosorbide-5-Nitrae-polyisoprene 15-19 part, blown castor oil 6-10 part, alcohol type emollients 3.2-8 part, starch 4.3-7 part, multipolymer 6-12 part of sodium maleate and alkene, light calcium carbonate 3.2-8 part.

2. gel ink pen ink according to claim 1, is characterized in that: it is made up of the raw material of following parts by weight:

PVC resin powder 12 parts, trolamine 6 parts, Sodium Benzoate 5.5 parts, triethylene tetramine 9 parts, silicone antifoam agent 5.5 parts, ACRYLIC EMULSION 6 parts, stablizer 1.6 parts, cis-Isosorbide-5-Nitrae-polyisoprene 17 parts, blown castor oil 8 parts, alcohol type emollients 5.7 parts, starch 5.9 parts, the multipolymer of sodium maleate and alkene 9 parts, light calcium carbonate 5.4 parts.